MEASURING HYSTERESIS LOOPS OF FERROELECTRIC POLYMERS USING THE CONSTANT CHARGING CURRENT CORONA TRIODE

A novel method is proposed for measuring the hysteresis loops of ferroelectric polymers. The samples need to have only one electrode and are poled by corona discharge in a constant current corona triode. It is shown how the sample surface potential and the charging current are related to the remanent polarization and coercive field, so that the hysteresis loops can be obtained. An illustrative example is given for samples of beta-PVDF for which the hysteresis cycles were remarkably close to those obtained with the traditional Sawyer-Tower circuit. Values of 80 MV/m and 70 mC/m2 were estimated for the coercive field and remanent polarization, respectively.

On the equivalence of the mechanisms governing switching and hysteresis phenomena

The nucleation and growth model, which is usually applied to switching phenomena, is adapted for explaining surface potential measurements on the P(VDF-TrFE) (polyvinylidene fluoride-trifluoroethylene) copolymer obtained in a constant current corona triode. It is shown that the growth is one-dimensional and that the nucleation rate is unimportant, probably because surface potential measurements take much longer than the switching ones. The surface potential data can therefore be accounted for by a growth model in which the velocity of growth varies exponentially with the electric field. Since hysteresis loops can be obtained from surface potential measurements, it is suggested that similar mechanisms can be used when treating switching and hysteresis phenomena, provided that account is taken of the difference in the time scale of the measurements.

Improvement of electrical properties of Sr-modified (Pb,Ca)TiO3 thin films grown by soft chemistry route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Dielectric and ferroelectric characteristics of barium zirconate titanate ceramics prepared from mixed oxide method

Barium zirconium titanate (BZT) ceramics were prepared by mixed oxide method. X-ray diffraction showed the presence of a single phase while Raman scattering confirmed structural transitions as a function of different Zr/Ti ratio. The addition of Zr strongly influenced the crystal structure and electrical properties of the ceramics. A typical hysteresis loops were observed for all investigated compositions. BZT ceramics with 15 mol% Zr have shown a ferroelectric to paraelectric transition at around 77 degrees C. (C) 2007 Published by Elsevier B.V.

Effect of annealing atmosphere on phase formation and electrical characteristics of bismuth ferrite thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld analysys and electrical properties of lanthanum doped BiFeO3 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Niobium doped Bi4Ti3O12 ceramics obtained by the polymeric precursor method

Pure and niobium doped bismuth titanate ceramics (Bi4Ti3-xNbxO12 (BTN)), with x ranging from 0 to 0.4 were prepared by the polymeric precursor method. X-ray diffraction showed no secondary phases. Increasing niobium content leads to more resistive ceramics. The shape and size of the grains are strongly influenced by the niobiurn added to the system. The dielectric constant is not influenced by the niobium addition while hysteresis loops are significantly narrowed. (c) 2006 Elsevier B.V All rights reserved.

Electric measurements with constant current: A practical method for characterizing dielectric films

This article assesses the use of the constant current (CC) method for characterizing dielectric films. The method is based on charging the sample with a constant current (current stress) and measuring the corresponding voltage rise under the closed circuit condition. Our article shows that the CC method is an alternative to the constant voltage stressing method to study the electric properties of nonpolar, ferroelectric, and polar polymers. The method was tested by determining the dielectric constant of polytetrafluoroethylene, and investigating the electric conduction in poly(ethylene terephthalate). For the ferroelectric polymer poly(vinylidene fluoride), it is shown that hysteresis loops and the dependence of the ferroelectric polarization on the electric field can be obtained. (C) 2001 American Institute of Physics.

The influence of crystallization route on the properties of lanthanum-doped Bi4Ti3O12 thin films prepared from polymeric precursors

Pure and lanthanum-doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. The spin-coated films were specular and crack-free and crystalline after annealing at 700 degreesC for 2 h. Crystallinity and morphological evaluation were examined by X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Multilayered films obtained using the intermediate-crystalline layer route present a dense microstructure with spherical grains. Films obtained using the intermediate-amorphous layer, present elongated grains around 250 nm in size. The dielectric and ferroelectric properties of the lanthanum-doped Bi4Ti3O12 films are strongly affected by the crystallization route. The hysteresis loops are fully saturated with a remnant polarization and drive voltage of the films, heat-treated by the intermediate-crystalline (P-r = 20.2 muC/cm(2) and V = 1.35 V) and for the film heat-treated by amorphous route (P-r = 22.4 muC/cm(2) and V = 2.99 V). (C) 2004 Elsevier B.V. All rights reserved.

Influence of the solution pH on the morphological, structural and electrical properties of Bi3.50La0.50Ti3O12 thin films obtained by the polymeric precursor method

Lanthanum-doped Bi4Ti3O12 thin films (BLT) were deposited on Pt/Ti/SiO2/Si substrates using a polymeric precursor solution. The spin-coated films were specular, crack-free and crystalline after annealing at 700 degrees C for 2 h. Crystallinity and morphological evaluation were examined by X ray diffraction (YRD) and atomic force microscopy (AFM). The stability of the formed complex is of extreme importance for the formation of the perovskite phase. Films obtained from acid pH solution present elongated grains around 200 ran in size, whereas films obtained from basic solution present a dense microstructure with spherical grains (100 nm). The dielectric and ferroelectric properties of the BLT films are strongly affected by the solution pH. The hysteresis loops are fully saturated with a remnant polarization and coercive voltage of P-r=20.2 mu C/cm(2) and V-c = 1.35 V and P-r= 15 mu C/cm(2) and V-c = 1.69 V for the films obtained from basic and acid solutions, respectively. (C) 2005 Elsevier B.V. All rights reserved.

Effect of the excess of bismuth on the morphology and properties of the BaBi2Ta2O9 ceramics

In this study, the effect of bismuth content on the crystal structure, morphology and electric properties of barium-bismuth-tantalate (BBT) ceramics was explored with the aid of X-ray diffraction (XRD), scanning electron microcopy (SEM), dielectric properties and ferroelectric hysteresis loops. BaBi2Ta2O9 (BBT) ceramics have been successfully prepared by the solid-state reaction. The BBT phase was crystallized at 900 degreesC for 2 h. The excess of bismuth controls the grain size, affecting the density of the material. Measurements of dieletric constant and dieletric losses confirm that the material is a ferroeletric with a Curie temperature around 77 degreesC. The dieletric constant measured at room temperature was 400, with a dielectric loss of 0.03. Both the phase-transition behaviour and ferroelectric properties, such as spontaneous polarization (P-s), showed a dependence on Bi content. (C) 2004 Elsevier B.V. All rights reserved.

Influence of temperature on the microstructure and electrical properties of BBT thin films

The BBT films were prepared by a spin-coating process from the polymeric precursor method (Pechini process). In order to study the influence of the temperature on the BBT microstructure and electrical properties, the films were deposited on platinum coated silicon substrates and annealed from 700degreesC to 800degreesC for 2 hours in oxygen atmosphere. The crystallinity of the films was examined by X-ray diffraction while the surface morphology was analysed by atomic force microscope. The dielectric properties and dissipation factor of BaBi2Ta2O9 films at 1 MHz were observed. The polarization-electric field hysteresis loops revealed the ferroelectric characteristics of BaBi2Ta2O9 thin films.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Dielectric and fatigue properties of Pb(Zr0.53Ti0.47)O-3 thin films prepared from oxide precursors method

Fatigue is an important problem to be considered if a ferroelectric film is used for non-volatile memory devices. In this phenomena, the remanent polarization and coercive field properties degrades in cycles which increase in hysteresis loops. The reasons have been attributed to different mechanisms such as a large voltage applied on ferroelectric film in every reading process in Ferroelectric Random Access Memory (FeRAM) or memories for digital storage in computer, grain size effects and others. The aim of this work is to investigate the influence of the crystallization kinetics on dielectric and ferroelectric properties of the Pb(Zr0.53Ti0.47)O-3 thin films prepared by an alternative chemical method. Films were crystallized in air on Pt/Ti/SiO2/Si substrates at 700 degrees C for 1 hour, in conventional thermal annealing (CTA), and at 700 degrees C for 1 min and 700 degrees C 5 min, using a rapid thermal annealing (RTA) process. Final films were crack free and presented an average of 750 nm in thickness. Dielectric properties were studied in the frequency range of 100 Hz - 1 MHz. All films showed a dielectric dispersion at low frequency. Ferroelectric properties were measured from hysteresis loops at 10 kHz. The obtained remanent polarization (P-r) and coercive field (E-c) were 3.7 mu C/cm(2) and 71.9 kV/cm respectively for film crystallized by CTA while in films crystallized by RTA these parameters were essentially the same. In the fatigue process, the P, value decreased to 14% from the initial value after 1.3 x 10(9) switching cycles, for film by CTA, while for film crystallized by RTA for 5 min, P, decreased to 47% from initial value after 1.7 x 10(9) switching cycles.

AMS and grain shape fabric of the Late Palaeozoic diamictites of the Southeastern Paran Basin, Brazil

Diamictites interbedded with marine shales and turbidites onlap the eastern border of the Parana Basin (Southern Brazil). These poorly sorted sediments were deposited during the Permo-Carboniferous glaciation, and their matrix-supported clasts show no preferred orientation. These massive rocks have been studied using anisotropy of magnetic susceptibility (AMS) and grain shape fabric. Hysteresis loops and thermomagnetic measurements show that AMS depends mostly on the paramagnetic clays, but fine ferromagnetic particles also contribute to the anisotropy. The coarse silt to sand grain preferred orientation study supports the use of AMS in describing the diamictite fabric, at least regarding the orientation of the foliation. AMS and grain shape data reveal subhorizontal to weakly inclined magnetic and grain shape foliation parallel to the regional bedding. The magnetic lineations are normally scattered within the foliation plane in agreement with the oblate AMS ellipsoids found in these rocks. Both fabric patterns are consistent with deposition by subaqueous mudflows that were resedimented downslope, with elastic supply from continental sources. The off-vertical grain shape foliation poles suggest that the deposition of diamictites was controlled by the depocentre topography of the Rio do Sul sub-basin.