Fluoride release/recharge from restorative materials: effect of fluoride gels and time

This study examined the differences in fluoride release and recharge among four restorative materials following treatment with APF or neutral fluoride gel for one or four minutes. Specimens were immersed in 2 mL of deionized water, while fluoride release was measured at 24-hour intervals for 15 days using an ion-selective electrode and analyzer. The materials were then treated with the fluoride gels. The fluoride release was measured for 15 days. ANOVA (p<0.05) showed higher fluoride release for Ketac-Fil before fluoride application and for Vitremer and Fuji 11 LC after application of APF gel. APF gel yielded higher fluoride release when compared to neutral gel, regardless of the material. Fluoride recharge and release was greater after the four-minute APF gel application, with no difference between the times of application for the neutral gel (p>0.05), except for Ketac-Fil. The pattern of release before and after application of the gels was similar and was higher at day 16 compared to day one for the APF gel for resin materials, with higher release at day 15 compared to the initial for Fuji 11 LC and Vitremer. Et was concluded that RM-GICs were the most effective materials with regards to fluoride release after application of APF gel for four minutes.

In vitro cytotoxicity of five glass-ionomer cements

To evaluate the cytotoxic effects of five glass-ionomer cements (GICs) on an odontoblast cell line (MDPC-23), disks of every material were prepared and divided into Group 1: Vitrebond, Group 2: Vitremer, Group 3: Fuji IILC, Group 4: Fuji IX GP, Group 5: Ketac-Molar, Group 6: Z-100 (positive control). In Group 7, phosphate-buffered saline solution (negative control) was applied on filter paper. After placing the samples in the bottom of wells, the cells (30,000 cells/cm(2)) were plated and incubated for 72 h. The cell number was counted, the cell morphology was assessed by scanning electron microscopy and the cell metabolism was evaluated using methyltetrazolium assay. The statistical analysis of Kruskal-Wallis was used to determine if the scores obtained for the cell metabolism and number of cells were different at the 95% confidence level. In groups 1, 2, 3, 4, 5, and 6 the materials decreased the cell number by 74.5% 75.5%, 45.5%, 29.5%, 32.5%, and 88.5%, respectively. In groups 1, 2, 3, 4, and 5, the experimental GICs reduced the cell metabolism by 79%, 84%, 54%, 40%, and 42.5%, respectively. Despite the fact that all experimental materials were cytotoxic to the MDPC-23 cells, the GICs were the least cytotoxic. on the other hand, the RMGICs caused the highest cytophatic effects. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

EFFECT of ULTRASONIC EXCITATION on THE MICROTENSILE BOND STRENGTH of GLASS IONOMER CEMENTS TO DENTIN AFTER DIFFERENT WATER STORAGE TIMES

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Tissue response to experimental dental cements prepared from a modified power glass composition

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Determination of the properties of an experimental glass polyalkenoate cement prepared from niobium silicate powder containing fluoride

Objectives. The purpose of this paper is to modify the conventional calcium fluoro-aluminosilicate glass, which is used in the formation of glass ionomer cements (CIGs) by the niobium addition and to study the properties of GICs obtained.Materials and methods. Sol-gel process was used to prepare the powder at lower temperature than fusion method. Glass-ceramic powder obtained in this way was used to prepare the GICs. The properties such as working and setting times, microhardness and diametral tensile strength were evaluated for the experimental GICs and a commercial luting cement.Results. The ideal powder:liquid (P:L) ratio determined to prepare the experimental GICs was equal to 1:1. The cements prepared using this ratio showed working and setting times similar to the commercial GICs. in mechanical tests it was observed that microhardness and diametral tensile strength of the experimental GICs decreased significantly with the reduction of P:L ratio. on the other hand, the results obtained in microhardness tests indicated that the presence of niobium was a positive factor.Significance. The chemical process allows the development of glass-ceramic powder at 600 degrees C which is the goal of the present paper. It was concluded that GICs containing niobium might be used in dental applications and these results encourage further researches on other compositions. (c) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Uso das técnicas de infravermelho e de ressonância magnética nuclear na caracterização da reação ácido-base de um cimento odontológico experimental

Glass ionomer cements (GICs) are products of the acid-base setting reaction between an finely fluoro-alumino silicate glass powder and poly(acrylic acid) in aqueous solution. The sol gel method is an adequate route of preparation of the glasses used to obtain the GICs. The objective of this paper was to compare two powders: a commercial and an experimental and to investigate the structural changes during hardening of the cements by FTIR and Al MAS NMR. These analyses showed that the experimental glass powder reacted with organic acid to form the GICs and it is a promising material to manufacture dental cements.

Preparation and evaluation of an experimental luting glass ionomer cement to be used in dentistry

The aim of this paper is to compare the fluoride-releasing and mechanical properties of an experimental luting glass ionomer cement, which has a modified composition and a commercial luting cement. The experimental powder was obtained by sol-gel process and then, it was used to prepare the experimental cements. The properties of cement pastes, such as setting time and working time, microhardness and diametral tensile strength were determined. Fluoride release from GICs was evaluated at time intervals of 1, 7, 14, 21 and 28 days in deionized water. Atomic force microscopy (AFM) analyses showed that the surface of the experimental cements is more homogeneous than commercial GICs. The mechanical properties and the measure of liberation of fluoride of the two cements were influenced by ratio powder:liquid and chemical composition of the precursor powders. Experimental cements released less fluoride than commercial cements. However, this liberation was more constant during the analyzed period. Thus, the results obtained in this study indicated that the composition of the experimental powder modified by the niobium can lead the formation of the polysalt matrix with good mechanical properties. In other words, we can say that experimental powder offered considerable promise for exploitation in dental field.

Development of an experimental glass ionomer cement containing niobium and fluoride

Glass ionomer cements (GICs) are currently used for various dental applications such as luting cements or as restorative materials. The calcium fluoro-alumino-silicate system is the basis for degradable glasses used to obtain the GICs. The purpose of the present paper is to add niobium to conventional glass system because according to previous papers niobium addition improves the chemical resistance and the mechanical properties of glasses. Therefore, the GICs prepared from these glasses would result in cements with higher chemical and mechanical resistance. The niobium fluoride powders were prepared using the sol-gel process and were characterized by X-ray diffraction, differential thermal analysis (DTA) and Al-27 and Si-29 MAS NMR. The results obtained by XRD showed that the powders prepared by this method are glass-ceramic. In the DTA curve was detected the presence of T-g and T-c temperatures. The analysis of MAS NMR spectra indicated that the framework of the powders is formed by SiO4 and AlO4 linked tetrahedra which are essential structures to yield the cements. Thus, we concluded that niobium fluoride silicate powders can be used in the preparation of GICs. (c) 2005 Elsevier B.V. All rights reserved.

Evaluation of glass ionomer cements properties obtained from niobium silicate glasses prepared by chemical process

Glass ionomer cements (GICs) are glass and polymer composite materials. These materials currently find use in the dental field. The purpose of this work is to obtain systems based on composition 4.5SiO(2)-3Al(2)O(3)-XNb2O5-2CaO to be used in Dentistry. The systems were prepared by chemical route at 700 degrees C. The results obtained by XRD and DTA showed that all systems prepared are glasses. The structures of the obtained glasses were compared to commercial material using Al-27 and Si-29 MAS NMR. The analysis of MAS NMR spectra indicated that the systems developed and commercial material are formed by SiO4 and AlO4 linked tetrahedra. The properties of glass ionomer cements based on the glasses prepared with several niobium contents were studied. Setting and working times of the cement pastes, microhardness and diametral tensile strength were evaluated for the experimental GICs and commercial luting cements. It was concluded that setting time of the cement pastes increased with increasing niobium content of the glasses (X). The properties to the GICs such as setting time and microhardness were influenced by niobium content. (c) 2005 Elsevier B.V. All rights reserved.

Preparation of new glass systems by the polymeric precursor method for dental applications

Glass ionomer cements (GICs) are largely employed in Dentistry for several applications, such as luting cements for the attachment of crowns, bridges, and orthodontic brackets as well as restorative materials. The development of new glass systems is very important in Dentistry to improve of the mechanical properties and chemical stability. The aim of this study is the preparation of two glass systems containing niobium in their compositions for use as GICs. Glass systems based on the composition SiO2,Al2O3-Nb2O5-CaO were prepared by chemical route at 700degreesC. The XRD and DTA results confirmed that the prepared materials are glasses. The structures of the obtained glasses were compared to commercial material using FTIR, Al-27 and Si-29 MAS-NMR. The analysis of FTIR and MAS-NMR spectra indicated that the systems developed and commercial material are formed by SiO4 and AlO4 linked tetrahedra. These structures are essential to get the set time control and to have cements. These results encourage further applications of the experimental glasses in the formation of GICs. (C) 2004 Elsevier B.V. All rights reserved.

Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (α = 5%). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

In vitro surface roughness of different glass ionomer cements indicated for ART restorations

Aim: The aim of this in vitro study was to evaluate the surface roughness of three glass ionomer cements (GICs) indicated for ART restorations. Methods: Ten cylindrical specimens of three commercial glass ionomers cements (Vidrion R - S.S. White, Maxxion R - FGM and Vitromolar DFL) were prepared (n=30) without surface finishing or protection. Twenty-four hours after preparation, the surface roughness measurements were obtained as the mean of three readings of the surface of each specimen by profilometry. The roughness values (Ra, μm) were subjected to one-way ANOVA and Tukey's test (p<0.05). Results: No statistically significant differences were observed between Vidrion R (0.18 ± 0.05) and Vitromolar (0.21 ± 0.05), whereas Maxxion R presented significantly higher roughness values than those of the other materials. Conclusions: It may be concluded that characteristics of particle size and composition of the different GICs affected their surface roughness 24 h after preparation.

Avaliação da liberação de íon fluoreto de cimentos ionoméricos antes e após a recarga e com proteção da superfície

Objective: To evaluate fluoride ion release from two anhydrous glass ionomer cements (GICs) and two resin-modified GICs (RMGICs) before and after recharge with 2% neutral sodium fluoride for 4 min and after surface protection of the Maxxion R GIC with an adhesive system, a cavity varnish and a colorless nail polish. Method: A stainless steel 2x6 mm matrix was used for fabricating 5 specimens of each material, which were immersed in 5 mL of deionized water, renewed every 24 h. Measurements with a potentiometer were performed on days 1, 2, 9 and 17, in the 1st and 2nd phases, and the specimens were buffered with a TISAB III solution. In the 2nd phase, the specimens were subjected to recharge and immersed again in 5 mL of deionized water. In the 3rd phase, the GIC surfaces were protected and readings were made at 5 min, 24 h, 48 h and 72 h. Tukey's post-hoc and Student's t tests were used for statistical analyses (p<0.05). Results: There was statistically significant difference in the comparison between the 1st and 2nd phases for all materials, except at day 2 for Vidrion R and VitroFil LC. In the 3rd phase, it was observed that for all materials, comparison of the first 5 min with the other times revealed statistically significant differences among the means of fluoride ion release. In the comparison with the other times, both the varnish and the colorless nail polish presented statistically significant difference between 24 and 48 h as well as between 24 and 72 h. Conclusion: The anhydrous GICs were more effective in fluoride ion release and recharge compared with the RMGICs. Maxxion R presented a homogeneous and statistically significant behavior in both phases. All materials for surface protection were efficient and the colorless nail polish had the best behavior.

Aplicação de ondas de ultra-som sobre cimentos de ionômero de vidro: rugosidade superficial e perda de massa após ensaio de escovação

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efeito da excitação ultrasônica na resistência máxima à tração e de união à dentina de cimentos de ionômero de vidro, após diferentes períodos de armazenamento