Ferroelectric properties and leakage current characteristics of Bi3.25La0.75Ti3O12 thin films prepared by the polymeric precursor method

The ferroelectric properties and leakage current mechanisms of preferred oriented Bi3.25La0.75Ti3O12 (BLT) thin films deposited on La0.5Sr0.5CoO3 by the polymeric precursor method were investigated. These films showed excellent ferroelectric properties in terms of large remnant polarization (2P(r)) of 47.6 mu C/cm(2) and (2E(c)) of 55 kV/cm, fatigue-free characteristics up to 10(10) switching cycles, and a current density of 0.7 mu A/cm(2) at 10 kV/cm. X-ray diffraction and scanning electron microscope investigations indicate that the deposited films exhibit a dense, well-crystallized microstructure having random orientations and with a rather smooth surface morphology. The improved ferroelectric and leakage current characteristics can be ascribed to the platelike grains of the BLT films, which make the domain walls easier to be switched under external field.

Ferroelectric characteristics of BiFeO3 thin films prepared via a simple chemical solution deposition

BiFeO3 (BFO) thin films were fabricated on Pt(111)/Ti/SiO2/Si substrates by using a polymeric precursor solution under appropriate crystallization conditions. The capacitance dependence on voltage is strongly nonlinear, confirming the ferroelectric properties of the films resulting from the domain switching. The leakage current density increases with annealing temperature. The polarization electric field curves could be obtained in BFO films annealed at 500 degrees C, free of secondary phases. X-ray photoelectron spectroscopy spectra of films annealed at 500 degrees C indicated that the oxidation state of Fe was purely 3+, demonstrating that our films possess stable chemical configurations. (c) 2007 American Institute of Physics.

MEASURING HYSTERESIS LOOPS OF FERROELECTRIC POLYMERS USING THE CONSTANT CHARGING CURRENT CORONA TRIODE

A novel method is proposed for measuring the hysteresis loops of ferroelectric polymers. The samples need to have only one electrode and are poled by corona discharge in a constant current corona triode. It is shown how the sample surface potential and the charging current are related to the remanent polarization and coercive field, so that the hysteresis loops can be obtained. An illustrative example is given for samples of beta-PVDF for which the hysteresis cycles were remarkably close to those obtained with the traditional Sawyer-Tower circuit. Values of 80 MV/m and 70 mC/m2 were estimated for the coercive field and remanent polarization, respectively.

Structural and ferroelectric properties of Pb1-xSrxTiO3 thin films

Strontium-modified lead titanate (PST) thin films with composition Pb1-xSrxTiO3 (0.10 < x &LE; 0.60) were grown on Pt/Ti/SiO2/Si substrates using a soft chemical process. The crystallization of the PST thin films was achieved by heat treatment at 600&DEG;C. The structural and microstructural modifications in the films were studied using X-ray diffraction (XRD) and atomic force microscopy, respectively. The XRD study shows that the lattice parameters of polycrystalline PST thin films calculated from X-ray data indicate a decrease in lattice tetragonality with the increase in strontium content in these films. This indicates a gradual change from tetragonal to cubic structure. By atomic force microscopy analysis, the average grain size of the thin films was systematically reduced with the increase in Sr content. The dielectric property of the thin films was found to be strongly dependent on the Sr concentration. With 60 at.% Sr content, a ferroelectric to paraelectric phase transition was observed at room temperature.

Ferroelectric materials with photoluminescent properties

Amorphous LiNbO3 thin films processed by polymeric precursor method exhibited efficient luminescence at room temperature. The films were deposited on silicon substrates and treated at 200degreesC for different times. The photoluminescence emission yield decreases with the increase of the treatment time and disappears for crystalline films. A theoretical-experimental study was performed on amorphous and crystalline materials to understand the influence of the defects on the photoluminescence properties. The theoretical band gap obtained by the difference of energy between the HOMO and LUMO levels is larger for crystalline structure when compared with amorphous material. This result, which is in agreement with experimental band gaps obtained from optical measurements, revealed the emergence of new electronic levels for the amorphous material, which are localized in the wide band gap of the crystalline structure. These new electronic levels may explain the photoluminescence observed at room temperature for LiNbO3 amorphous films.

Preparation of SrBi2Ta2O9 ferroelectric thick films by electrophoretic deposition using aqueous suspensions

SrBi2Ta2O9 ferroelectric thick films were prepared by electrophoretic deposition (EPD). For that, ceramic powders were prepared by chemical method in order to obtain compounds with chemical homogeneity. The polymeric precursor method was used for the synthesis of the SrBi2Ta2O9 powder. The crystallographic structure of the powder was examined by X-ray diffraction, and the surface area was determined by single point BET adsorption. The 0.03 vol% suspension was formed by dispersing the powder in water using two different polymers as dispersants: an ester polyphosphate (C213) and an ammonium polyacrilate (Darvan 821-A). The influence of the different dispersants on the powder surface properties were investigated by zeta potential measurements. The films were deposited on platinum-coated alumina and Pt/Ti/SiO2/Si substrates by electrophoretic deposition using a 4 mA constant current, for 10 min, with two parallel electrodes placed at a separation distance of 3 min in the suspension. Several cycles of deposition-drying of the deposit was carried out until the desired thickness was obtained. After thermal treatment at temperatures ranging from 700 to 1000degreesC, the films were characterized by X-ray diffraction and scanning electron microscopy.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Stress-induced ordering due heavy interstitial atoms in Nb-0.3 wt.% Ti alloys

The mechanical properties of metals with bee structure, such as niobium and their alloys, are changed of a significant way by the introduction of heavy interstitial elements. These interstitial elements (oxygen, for example) present in the metallic matrix occupy octahedral sites and constitute an elastic dipole of tetragonal symmetry and might produce anelastic relaxation. Polycrystalline samples of Nb-0.3 wt.% Ti (Nb-Ti) alloy with oxygen in solid solution were analysed. The anelastic spectroscopy measurements had been made in a torsion pendulum, with frequencies in the Hz range, in a temperature range between 300 and 700 K. The results showed thermally activated relaxation structures were identified four relaxation process attributed to stress-induced ordering of single oxygen, nitrogen and carbon atoms around niobium and stress-induced ordering of single oxygen atoms around titanium atoms. (c) 2005 Elsevier B.V. All rights reserved.

Influence of temperature on the dielectric and ferroelectric properties of bismuth titanate thin films obtained by the polymeric precursor method

The (1 1 7) and (0 0 1 0)-oriented Bi4Ti3O12 thin films were fabricated on Pt/Ti/SiO2/Si substrates by using a polymeric precursor solution under appropriate crystallization conditions. Atomic force microscopy and scanning electron microscopy showed relatively large grains, which is typical for this system. The capacitance dependence on voltage is strongly non-linear, confirming the ferroelectric properties of the films resulting from the domain switching. The (1 1 7)-oriented films exhibited a higher remanent polarization (23.7 μ C cm(-2)) than the (0 0 1 0)-oriented films (11.8 μ C cm(-2)). Fatigue tests revealed that the temperature of thermal treatment and degree of orientation affect the performance of the device. © 2005 Elsevier B.V. All rights reserved.

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.

Structure, microstructure, ferroelectric/electromechanical properties and retention characteristics of [Bi1-x Nb (x) ]FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermistor behaviour and electric conduction analysis of Ni-doped niobate ferroelectric: the role of multiple beta parameters

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Leakage current, ferroelectric and structural properties in Pb(1-x)Ba(x)TiO(3) thin films prepared by chemical route

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure, ferroelectric/magnetoelectric properties and leakage current density of (Bi0.85Nd0.15)FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Investigation of Ferroelectric Layered Perovskite Barium Bismuth Tantalate Prepared by Solid-State Reaction

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)