A homovalent doping in PMN ceramics by using lithium and scandium cations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Voltage-composition profile and synchrotron X-ray structural analysis of low and high temperature LixCoO2 host material

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Aspects of solid state formation and properties of Sn(0.9)Ti(0.1)O(2) system doped with CoO and Nb(2)O(5)

The effect of calcination temperature during the formation of the solid solution Sn(0.9)Ti(0.1)O(2) doped with 1.00 mol % CoO and 0.05 mol % Nb(2)O(5) is presented. The structural characteristics of this system were studied using X-ray diffraction, and the changes in phase formation were analyzed using the Rietveld method. With an increase in calcination temperature, there is increasing miscibility of Ti into the (Ti,Sn)O(2) phase and near 1000 degrees C, and the remaining TiO(2) (anatase) was transformed into the rutile phase. The sintering process, monitored using dilatometry, suggests two mass transport mechanisms, one activated close to 900 degrees C associated with the presence of TiO(2) (anatase) and the second mechanism, occurring between 1200 and 1300 degrees C, is attributed to a faster grain boundary diffusion caused by oxygen vacancies. (C) 2008 International Centre for Diffraction Data.

Rietveld analysis of mechanically activated BaCO(3)-TiO(2) system

BaTiO(3) powders were prepared through mechanical activation chemistry and analyzed by Rietveld refinement with X-ray diffraction data. Raw BaCO(3) and TiO(2) powders were dry milled for 5 and 20 h and then calcinated for 2 and 4 h at 800 degrees C. The milling process was found to have broken up the BaCO(3) and TiO(2) crystals into smaller crystals and formed only small amounts ( 1.5 wt%) of BaTiO(3). Subsequence calcinations for 2 and 4 h at 800 degrees C successfully produced large amounts (>97.7 wt%) of BaTiO(3) crystals. The calcination process also generated microstrains and crystallite-size anisotropy in BaTiO(3). An increase in the calcination time from 2 to 4 h increased the BaTiO(3) weight percentage and the crystal lite-shape anisotropy, but decreased the tetragonal distortion anisotropic microstrains in BaTiO(3) crystals. (C) 2008 International Centre for Diffraction Data.

Pearlitic reaction in Cu-10wt%Al alloy with Ag additions

The pearlitic reaction in Cu-10wt%Al alloy with additions of 4, 6, 8, and 10wt%Ag was studied using scanning electron microscopy, energy dispersive X-ray microanalysis, in situ X-ray diffractometry, and microhardness measurements. The results indicated that the presence of Ag changes the pearlitic phase microstructure and its mechanical properties, because of the influence of Ag in the pearlitic phase growth mechanism. (C) 2008 International Centre for Diffraction Data.

Crystal structure of isotibolone: a major degradation product of tibolone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synchrotron structural characterization of electrochemically synthesized hexacyanoferrates containing K(+): A revisited analysis of electrochemical redox

The presumably soluble KFe(+3)[Fe(2+)(CN)(6)] structure of electrochemically synthesized hexacyanoferrate materials (Prussian Blue) containing K(+) ions was determined for the first time in this study. Prior to drawing conclusions from a structural analysis, the main goal was to make a precise analysis of the inferred soluble structure, that is, KFe(+3) [Fe(2+)(CN)(6)], which is frequently referred to in the literature as the final stable electrochemically synthesized structure. Indeed, a successful X-ray powder diffraction experiment using X-ray synchrotron radiation was made of a powder placed in a 0.5 mm diameter borosilicate glass capillary, which was obtained by removing sixty 90 nm thin films from the substrates on which they were prepared. However, the conclusions were highly unexpected, because the structure showed that the [Fe(CN)61 group was absent from similar to 25% of the structure, invalidating the previously presumed soluble KFe(+3)[Fe(2+)(CN)(6)] structure. This information led to the conclusion that the real structure of Prussian Blue electrochemically synthesized after the stabilization process is Fe(4)[Fe(CN)(6)](3)center dot mH(2)O containing a certain fraction of inserted K(+) ions. In fact, based on an electrogravimetric analysis (Gimenez-Romero et al., J. Phys. Chem. B 2006, 110, 2715 and 19352) complemented by the Fourier maps. it is possible to affirm that the K(+) was part of the water crystalline substructure. Therefore, the interplay mechanism was reexamined considering more precisely the role played by the water crystalline substructure and the K+ alkali metal ion. As a final conclusion, it is proposed that the most precise way to represent the structure of electrochemically synthesized and stabilized hexacyanoferrate materials is Fe(4)(3+) Fe(2+)(CN)(6)](3)center dot[K(h)(+)center dot OH(h)(-)center dot mH(2)O]. The importance of this result is that the widespread use of the terms soluble and insoluble in the electrochemical literature could be reconsidered. Indeed, only one type of structure is insoluble, and that is Fe(4)[Fe(CN)(6)](3)center dot mH(2)O hence, the use of the terms soluble and insoluble is inappropriate from a structural point of view. The result of the presence of the [Fe(CN)61 vacancy a, roup is that the water Substructure cannot be ignored in the ionic interplay mechanism which controls the intercalation and redox process, as was previously confirmed by electrogravimetric analyses (Gimenez-Romero et al., J. Phys. Chem. B 2006, 110, 2715 Garcia-Jareno et al., Electrochim. Acta 1998, 44, 395: Kulesza, Inorg. Chem. 1990, 29, 2395).

Using thermal and spectroscopic data to investigate the thermal behavior of epinephrine

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and spectroscopic investigation on N,N-dimethylbenzylamine based cyclopalladated compounds containing isonicotinamide

Synthesis, spectroscopic characterization and thermal analysis of the [Pd(dmba)(Cl)(iso)] (1), [Pd(dmba)(NCO)(iso)] (2), [Pd(dmba)(N(3))(iso)] (3) and [Pd(dmba)(Br)(iso)] (4) (dmba = N,N'-dimethylbenzylamine; iso = isonicotinamide) compounds are described in this work. The complexes were investigated by infrared spectroscopy (IR), differential thermal analysis (DTA) and thermogravimetry (TG) and the residues of the thermal decomposition were identified as Pd(o) by X-ray powder diffraction. The thermal stability order of the complexes varied as [Pd(dmba)(Cl)(iso)] (1) > [Pd(dmba)(Br)(iso)] (4) > [Pd(dmba)(NCO)(iso)] (2) > [Pd(dmba)(N(3))(iso)] (3).

Synthesis, characterization, and thermal behavior of palladium(II) coordination compounds containing isonicotinamide

Palladium(II) coordination compounds of general formula trans-[PdX(2)(isn)(2)], X = Cl(-) (1), N(3) (-) (2), SCN(-) (3), NCO(-) (4), isn = isonicotinamide; were synthesized and characterized in solid state by elemental analysis, infrared spectroscopy, and simultaneous TG-DTA. TG experiments reveal that the compounds 1-4 undergo thermal decomposition in three or four stages, yielding Pd(0) as final residue, according to calculus and identification by X-ray powder diffraction.

Synthesis, spectral and thermal studies on dicarboxylate-bridged palladium(II) coordination polymers. Part I

This work describes the synthesis, IR and (13)C CPMAS NMR spectroscopic as well the thermal characterization of the new dicarboxylate complexes [Pd(2)(ox)(2)(4,4'-bipy)]n (1), [Pd(2)(ox)(2)(bpe)](n) (2) and [Pd(2)(ox)(2)(pz)](n) (3) {ox = oxalate, bipy = 4,4'-bipyridine, bpe = 1,2-bis(4-pyridyl)ethane, pz = pyrazine}. TG experiments reveal that compounds 1-3 undergo thermal decomposition in three steps. Metal palladium was the final product of the thermal decompositions, which was identified by X-ray powder diffraction.

Caracterização de cálculos renais por análise térmica

Dez amostras de cálculos renais foram estudadas por Análise Elementar de CHN (EA), Espectroscopia de Absorção no Infravermelho (IV) e Difração de raios X pelo método de Pó (XRD). O comportamento térmico das amostras foi estudado por Termogravimetria/Termogravimetria Derivada (TG/DTG) e por Calorimetria Exploratória Diferencial (DSC). Os resultados de EA, Espectroscopia de Absorção IV e XRD mostraram a presença de estruvita [NH4Mg(PO4).6H2O], apatita, oxalato de cálcio monohidratado e oxalato de cálcio dihidratado. As curvas TG e DSC permitiram classificar as amostras em dois grupos diferentes: Grupo I mostrando comportamento térmico típico de estruvita e Grupo II apresentando um perfil termoanalítico característico de mistura de oxalatos.

Different particle size silicas from water glass.

Non-crystalline silica was obtained with different particle sizes. Samples were prepared from soluble sodium silicate (water glass) and sulfuric acid solutions. Dialysis was performed for sodium sulfate elimination. Products were dried in a microwave oven, milled and characterized by X-ray powder diffraction, infrared spectrum and sedigraphic analysis. Products milled for more than 120 minutes showed uniform particle size distribution with average silica particle size of 4.5 mu m.

Synthesis, spectral and thermal studies on pyrazolate-bridged palladium(II) coordination polymers

Synthesis, spectroscopic characterization and thermal behavior of pyrazolate-bridged palladium complexes [Pd(mu-Pz)(2)](n) (1), [Pd(mu-mPz)(2)](n) (2), [Pd(mu-dmPz)(2)](n) (3), [Pd(mu-IPz)(2)](n) (4) {pyrazolate (Pz(-)), 4-methylpyrazolate (mPz(-)), 3,5-dimethylpyrazolate (dmPz(-)), 4-iodopyrazolate (IPz(-))} have been described in this work. The exobidentate coordination mode of pyrazolato ligands in 1-4 was inferred on basis of IR spectroscopic evidences. TG investigations indicated that the introduction of substituents at the 4 position in the pyrazolyl moiety into coordination polymers do not affect significantly their thermal stability, whereas at the 3 and 5 position reduced the stability of the main chain. Metal palladium was the final product of the thermal decompositions, which was identified by X-ray powder diffraction.

Thermal study of cyclopalladated complexes of the type [Pd-2(dmba)(2)X-2(bpe)] - (X=NO3-, Cl-, N-3(-), NCO-, NCS-; bpe=trans-1,2-bis(4-pyridyl)ethylene)

The synthesis, characterization and thermal analysis of the novel cyclometallated compounds [Pd-2(dmba)(2)Cl-2(mu-bpe)] (1), [Pd-2(dmba)(2)(N-3)(2)(mu-bpe)] (2), [Pd-2(dmba)(2)(NCO)(2)(mu-bpe)] (3), [Pd-2(dmba)(2)(SCN)(2)(mu-bpe)] (4), [Pd-2(dmba)(2)(NO3)(2)(mu-bpe)] (5) (bpe=trans-1,2-bis(4-pyridyl)ethylene; dmba=N,N-dimethylbenzylamine) are described. The thermal stability of [Pd-2(dmba)(2)X-2(mu-bpe)] complexes varies in the sequence 1 > 4 > 3 > 2 > 5. The final residues of the thermal decompositions were characterized as metallic palladium by X-ray powder diffraction.