BOND STRENGTH DURABILITY of SELF-ETCHING ADHESIVES and RESIN CEMENTS TO DENTIN

Objectives: To evaluate the microtensile bond strength (mu TBS) of one-(Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). Material and Methods: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n = 10). The restored teeth were stored in distilled water at 37 C for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm(2) cross-sectional area, which were subjected to mu TBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The mu TBS data in MPa were subjected to three-way analysis of variance and Tukey's test (alpha = 0.05). Results: The interaction effect for all three factors was statistically significant (three-way ANOVA, p < 0.001). All eight experimental means (MPa) were compared by the Tukey's test (p < 0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4 +/- 7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4 +/- 11.6); Xeno III/C&B/24 h (40.3 +/- 12.9); Xeno III/Variolink II/24 h (25.8 +/- 10.5); Tyrian-One Step Plus / C&B/90 d (22.1 +/- 12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2 +/- 14.2); Xeno III/C&B/90 d (27.0 +/- 13.5); Xeno III/Variolink II/90 d (33.0 +/- 8.9). Conclusions: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.

Bond strength and morphology of resin materials applied to the occlusal surface of primary molars

International Journal of Paediatric Dentistry 2012; 22: 435441 Background. Hydrophilic adhesives may be used as pit and fissure sealants (sealants), but there is concern about the ability of self-etching adhesives to bond sealants to enamel. Aim. To study the bond strength (BS) and morphology of adhesive systems used as sealants. Design. OptiBond FL, OptiBond All-in-One, combined OptiBond All-in-One + OptiBond FL adhesive, and Fluroshield were applied to the occlusal surfaces of 16 primary molars (n = 4). Teeth were stored in distilled water (24 h at 37 degrees C) and sectioned through the interface to obtain sticks (0.8 mm2) tested under a tensile load (0.5 mm/min). Failure modes were observed. Data were analysed by ANOVA and Tukeys tests (a = 5%). The morphology of 12 primary molars was examined in terms of the etching pattern and resin reproduction. Results. Differences in the BS were found (P = 0.001), with OptiBond FL showing the highest (36.84 +/- 5.7 MPa), Fluroshield (24.26 +/- 2.13 MPa) and OptiBond All-in-One (17.12 +/- 4.97 MPa) similar, and OptiBond All-in-One + OptiBond FL adhesive the lowest (9.8 +/- 2.94 MPA). OptiBond FL showed the best results in terms of morphology. Conclusion. Under the conditions of this study, OptiBond FL was the best material to be used for sealing.

Roughness of Human Enamel Surface Submitted to Different Prophylaxis Methods

The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber clip and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Industria e Comercio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi A dante Indtistrias Medico Odontologicas Ltda, Ribeirao Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel stuface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.

Degradation of sulfamethoxazole in water by solar photo-Fenton. Chemical and toxicological evaluation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Photodegradation of the pharmaceuticals amoxicillin, bezafibrate and paracetamol by the photo-Fenton process - Application to sewage treatment plant effluent

Photodegradation of the pharmaceuticals amoxicillin (AMX), bezafibrate (BZF) and paracetamol (PCT) in aqueous solutions via the photo-Fenton process was investigated under black-light and solar irradiation. The influences of iron source, initial H2O2 concentration and matrix (distilled water and sewage treatment plant effluent) on degradation efficiency were discussed in detail. The results showed that (i) the degradation of the drugs was favored in the presence of potassium ferrioxalate (FeOx) in comparison to Fe(NO3)(3): (ii) the increase of the H2O2 concentration improved the efficiency of AMX and BZF oxidation; however, the same was not observed for PCT: (iii) the influence of the matrix was observed for the degradation of BZF and PCT: (iv) under solar irradiation, the oxidation of the BZF and PCT is faster than under black-light irradiation. All these pharmaceuticals can be efficiently degraded employing the process evaluated. (C) 2008 Elsevier B.V. All rights reserved.

Photodegradation of sulfamethoxazole in various aqueous media: Persistence, toxicity and photoproducts assessment

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Photodegradation of lincomycin and diazepam in sewage treatment plant effluent by photo-Fenton process

First, the effect of ferrioxalate or iron nitrate on the photo-Fenton degradation efficiency of the pharmaceuticals lincomycin (LCM) and diazepam (DZP) was evaluated. The degradation of both pharmaceuticals was improved in the presence of ferrioxalate in relation to Fe(NO(3)), either under black-light or solar irradiation. The degradation of the pharmaceuticals was then evaluated when present in an effluent from sewage treatment plant (STP) under black-light irradiation. Pharmaceuticals oxidation was not influenced by the matrix, since very similar results were obtained when compared to the experiments carried out in distilled water. However, DOC removal was slightly affected by the matrix, due probably to the generation of recalcitrant intermediates during effluent photodegradation and to the high content of inorganic carbon of STP effluent. Even so, high DOC removal percentages were achieved, 65% for lincomycin and 80% for diazepam after 60 min irradiation. (C) 2010 Elsevier B.V. All rights reserved.

Carbon Nuclear Magnetic Resonance Spectroscopic Profiles coupled to Partial Least-Squares Multivariate Regression for Prediction of Several Physicochemical Parameters of Brazilian Commercial Gasoline

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Multivariate calibrations in gas chromatographic profiles for prediction of several physicochemical parameters of Brazilian commercial gasoline

Several Brazilian commercial gasoline physicochemical parameters, such as relative density, distillation curve (temperatures related to 10%, 50% and 90% of distilled volume, final boiling point and residue), octane numbers (motor and research octane number and anti-knock index), hydrocarbon compositions (olefins, aromatics and saturates) and anhydrous ethanol and benzene content was predicted from chromatographic profiles obtained by flame ionization detection (GC-FID) and using partial least square regression (PLS). GC-FID is a technique intensively used for fuel quality control due to its convenience, speed, accuracy and simplicity and its profiles are much easier to interpret and understand than results produced by other techniques. Another advantage is that it permits association with multivariate methods of analysis, such as PLS. The chromatogram profiles were recorded and used to deploy PLS models for each property. The standard error of prediction (SEP) has been the main parameter considered to select the "best model". Most of GC-FID-PLS results, when compared to those obtained by the Brazilian Government Petroleum, Natural Gas and Biofuels Agency - ANP Regulation 309 specification methods, were very good. In general, all PLS models developed in these work provide unbiased predictions with lows standard error of prediction and percentage average relative error (below 11.5 and 5.0, respectively). (C) 2007 Elsevier B.V. All rights reserved.

Reimplante mediato de dentes tratados ou não com solução de hipoclorito de sódio a 1% - estudo histomorfométrico em ratos

Foi avaliada a influência do hipoclorito de sódio a 1% no reparo do periodonto de incisivos reimplantados tardiamente em ratos. Os dentes foram mantidos em meio ambiente durante 30 minutos e a seguir imersos em hipoclorito de sódio a 1%, por 25 minutos. Os animais foram sacrificados aos 10, 30 ou 60 dias. Os cortes histológicos foram obtidos no sentido transversal dos terços cervical, médio e apical e delineados com um aumento de 52 vezes. Os eventos observados sobre a superfície radicular foram medidos quanto a sua extensão através de um sistema analisador de imagens (Mini-Mop, Carl Zeiss). Aos 10 dias, observou-se a predominância de tecido conjuntivo fibroso no grupo tratado. Aos 30 e 60 dias observou-se o aumento da anquilose e reabsorção por substituição, assim como neoformação limitada de ligamento periodontal. No grupo controle, aos 30 e 60 dias, foram observadas áreas de reabsorções mais extensas e profundas, quando comparadas ao grupo tratado. Os resultados possibilitaram as seguintes conclusões quando comparado o grupo tratado com o controle: a) leva à formação de tecido conjuntivo semelhante a uma cápsula fibrosa no período inicial do reparo; b) possibilita uma limitada neoformação de ligamento periodontal; c) ocasiona uma superfície de anquilose mais extensa; d) não impede a reabsorção por substituição.

Efeito alelopático de sabugueiro e capim-limão na germinação de picão-preto e soja

As plantas invasoras são constantes e diminuem a produtividade das culturas por competirem por espaço, nutrientes e água. Dessa forma, os agricultores adotam, em grande escala, produtos químicos eficientes no controle da lavoura e com alta toxicidade ao meio ambiente. Existem, no entanto, formas alternativas para o controle de invasoras, por meio de aleloquímicos presentes em algumas plantas, dentre elas, as medicinais. Este trabalho tem como objetivo analisar as propriedades alelopáticas dos extratos das plantas medicinais Cymbopogon citratus (DC) Stapf. e Sambucus australis Cham. and Schltdl. em inibir a germinação de Bidens pilosa L., sem interferir na germinação de Glycine max L. Merrill. Os extratos foram obtidos triturando-se 200 g de folhas com 1 L de água destilada. As sementes foram mantidas em B.O.D. à temperatura de 25ºC, com fotoperíodo de 12h de luz. Nas condições em que foram realizados os experimentos, constatou-se que o extrato de capim-limão inibiu a germinação de picão-preto sem que este inibisse a germinação da soja, enquanto o extrato de sabugueiro inibiu a germinação de picão-preto e a germinação da soja. Assim, indica-se a utilização do capim-limão, como um herbicida natural para o picão-preto.

Avaliação manométrica do esôfago distal de coelhos submetidos a fundoplicatura total laparotômica e laparoscópica

Racional - A fundoplicatura total, procedimento empregado no tratamento da doença do refluxo gastroesofágico, pode ser realizada segundo duas técnicas de abordagem: laparotômica e laparoscópica. Objetivo - Analisar o esfíncter inferior do esôfago de coelhos submetidos a fundoplicatura total laparotômica e laparoscópica. Material e Métodos - em 40 coelhos machos foram realizados estudos eletromanométricos do esôfago segundo a técnica de puxada intermitente da sonda e infusão contínua dos cateteres com água destilada. Estes estudos permitiram a análise de dois parâmetros: amplitude da pressão no esfíncter inferior do esôfago (mm Hg) e comprimento do esfíncter inferior do esôfago em condições basais (momento 1). Os 40 animais foram divididos em quatro grupos de 10, na dependência do procedimento cirúrgico realizado: grupo 1: fundoplicatura total laparotômica; grupo 2: laparotomia mediana e dissecção da transição gastroesofágica; grupo 3: fundoplicatura total laparoscópica; grupo 4: pneumoperitônio e dissecção da transição gastroesofágica. No momento 2 (1 semana após os procedimento cirúrgicos) foram realizados estudos eletromanométricos do esôfago em todos os animais. Resultados - Nos animais do grupo 1 (fundoplicatura laparotômica) e do grupo 3, foi observado aumento da amplitude da pressão e do comprimento do esfíncter inferior do esôfago. Naqueles dos grupos 2 e 4, não foi observada alteração da amplitude e do comprimento do esfíncter inferior do esôfago. Conclusões - A fundoplicatura interfere na barreira anti-refluxo gastroesofágica, tornando-a mais eficiente, uma vez que a pressão e o comprimento do esfíncter inferior do esôfago elevam-se no pós-operatório desta intervenção. Este efeito foi observado nas duas técnicas de abordagem estudadas, laparotômica e laparoscópica.

Características químicas de substratos utilizados na produção de mudas de cacaueiros

O objetivo deste trabalho foi realizar monitoramento químico de seis substratos utilizados na produção de mudas de cacaueiros. Os substratos receberam 10 volumes (100mL, cada) de água destilada, e no lixiviado coletado foram determinados o pH, a condutividade elétrica (CE) e os teores de sódio (Na) e potássio (K) em solução. Os valores de pH variaram de 5,0 a 8,0 em Plantmax® e composto do tegumento da amêndoa do cacau (CTAC), respectivamente. Verificou-se que, a partir do primeiro volume lixiviado, a CE de todos os substratos foi reduzida. Foram encontradas correlações positivas para a CE em relação ao K e Na da fibra de coco (FC) (r=0,83 e 0,72 P<0,05) e CTAC (r=0,98 e 0,99 P<0,05). Os resultados indicam que a FC e o CTAC deveriam ser usados após pré-lavagens. Verificou-se que, embora a FC apresente na primeira lixiviação valor de CE superior aos demais substratos, o valor ideal da 2,0 dSm-1 é alcançado na segunda lixiviação. Os teores de K e Na são um indicativo do valor da CE em FC e CTAC.

Determinação do ponto de colheita e indução à abertura floral do crisântemo cultivar White Polaris em diferentes concentrações de sacarose

Realizou-se pesquisa objetivando determinar o melhor entre quatro pontos de colheita da haste floral de crisântemos de maço do tipo pompom cv. White Polaris a concentração mais adequada de sacarose para tratamento de pulsing dessas hastes: estas foram colhidas em estufa de produção comercial, nos pontos preestabelecidos e transportadas para laboratório, onde foram totalmente imersas em água de torneira, à sombra, durante três horas. Selecionaram-se as hastes pela uniformidade do seu desenvolvimento e cortaram-nas sob água na base do caule, entre 50 e 60 cm, e identificadas, o que permitiu avaliar as mudanças morfológicas associadas às inflorescências individuais. As hastes foram distribuídas e mantidas nos diferentes tratamentos de pulsing durante 24 horas, à luz branca contínua de 1.500 lux, 60 a 90% de umidade relativa do ar e temperatura ambiente de 25 ± 2°C. Após o tratamento de pulsing, as hastes foram transferidas para água destilada, permanecendo por 10 horas sob luz branca contínua, nas mesmas condições de laboratório citadas. A vida floral em vaso começou a ser avaliada na instalação do experimento, após o tratamento de pulsing, e terminou quando as folhas e pétalas perderam a turgescência e o valor decorativo. As hastes colhidas em estádio de botão (25 e 50% de abertura das inflorescências apicais) não alcançaram o ponto de abertura adequado em nenhuma das seis concentrações de sacarose (0 a 146,07 mol/m³); as concentrações de 116,9 146,1 mol/m³, porém, estimularam, em geral, a abertura de botões. Os pontos de colheita 1 e 2 (100 e 75% de abertura das inflorescências apicais respectivamente) apresentaram bons resultados em todas as concentrações de sacarose.

Manutenção da qualidade e aumento da longevidade floral de crisântemo cv. White polaris

0 objetivo do trabalho foi determinar o melhor tratamento pós-colheita para manutenção floral e aumento da longevidade de crisântemo de maço do tipo pompom (Dendranthema grandiflorum (Ramat.) S. Kitamura) cv. White Polaris. Estabeleceu-se como ponto de colheita o momento em que as hastes apresentavam três inflorescências apicais com as pétalas externas em ângulo de 45° em relação à horizontal. Durante o ensaio em laboratório, as hastes, colhidas em estufa de produção comercial, após totalmente imersas em água de torneira, à sombra, durante três horas, foram cortadas sob água na base do caule entre 50 e 60 cm. As hastes foram distribuídas nos diferentes tratamentos de pulsing durante 24 horas, com luz contínua de 1.500 lux, 60 a 90% de umidade relativa do ar e temperatura ambiente de 25 ± 2°C. No primeiro experimento, testou-se a eficiência de 8-hidroxiquinolina (8-HQ) e tiabendazole (TBZ) como germicidas de manutenção da qualidade na solução de pulsing; testaram-se, também, dois reguladores de crescimento, a saber: ácido giberélico (GA3), 6-benzilaminopurina (6-BA) ou a mistura dos dois, com o objetivo de preservar a cor e a turgidez da folhagem. Os melhores resultados foram com 8-HQ (0,69 mol/m³) e GA3 (0,058 mo1/m³). No segundo experimento, avaliaram-se os seguintes inibidores de etileno: tiossulfato de prata (STS), nitrato de prata (AgNO3) e cloreto de cobalto (COC1(2)). A melhor resposta foi obtida com AgNO3 (2,9 e 4,4 mo1/m³).