Mechanical and thermal cycling effects on the flexural strength of glass ceramics fused to titanium

This study evaluated the effects of mechanical and thermal cycling on the flexural strength (ISO 9693) of three brands of ceramics fused to commercially pure titanium (cpTi). Metallic frameworks of 25 x 3 x 0.5 mm dimensions (N = 84) were cast in cpTi, followed by 150-mu m aluminum oxide airborne particle abrasion at a designated area of the frameworks (8 x 3 mm). Bonder and opaque ceramic were applied on the frameworks, and then the corresponding ceramic (Triceram, Super Porcelain Ti-22, Vita Titankeramik) was fired onto them (thickness: 1 mm). Half of the specimens from each ceramic-metal combination were randomly tested without aging (only water storage at 37 degrees C for 24 hours), while the other half were mechanically loaded (20,000 cycles under 10 N load, immersion in distilled water at 37 degrees C) and thermocycled (3,000 cycles, between 5-55 degrees C, dwell time of 13 seconds). After the flexural strength test, failure types were noted. Mechanical and thermal cycling decreased the mean flexural strength values significantly (p<0.05) for all the three ceramic-cpTi combinations tested when compared to the control group. In all the three groups, failure type was exclusively adhesive at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface except for a visible oxide layer.

A retrospective look at esthetic resin composite and glass-ionomer Class III restorations: A 2-year clinical evaluation

Objective: A restorative material for Class III cavities must, besides being functional, be esthetically satisfactory, providing good working conditions and several shade and color options. A clinical evaluation was initiated to compare the suitability of resin composite and glass-ionomer cement materials for such restorations.Method and materials: Forty-two Class III conservative cavities, esthetically important because of facial extensions, were selected. Resin composite restorations were placed in 21 cavities, and the remaining 21 were restored with glass-ionomer cement. The following characteristics were studied: color or-esthetics, anatomic shape, surface texture, staining, marginal infiltration, dental plaque retention, and occurrence of fracture. After 24 months, the restorations were evaluated.Results: the only statistically significant difference between the resin composite and glass-ionomer cement restorations in the experimental period involved color or esthetics.Conclusion: Resin composites and glass-ionomer materials provide excellent functional and esthetic results in Class III cavities when properly indicated.

Effect of partial crystallization on the mechanical properties and cytotoxicity of bioactive glass from the 3CaO center dot P2O5-SiO2-MgO system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Compositional and structural changes at the anodic surface of thermally poled soda-lime float glass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Degradation of the surface of a metasilicate glass due to atmosphere moisture

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and evaluation of an experimental luting glass ionomer cement to be used in dentistry

The aim of this paper is to compare the fluoride-releasing and mechanical properties of an experimental luting glass ionomer cement, which has a modified composition and a commercial luting cement. The experimental powder was obtained by sol-gel process and then, it was used to prepare the experimental cements. The properties of cement pastes, such as setting time and working time, microhardness and diametral tensile strength were determined. Fluoride release from GICs was evaluated at time intervals of 1, 7, 14, 21 and 28 days in deionized water. Atomic force microscopy (AFM) analyses showed that the surface of the experimental cements is more homogeneous than commercial GICs. The mechanical properties and the measure of liberation of fluoride of the two cements were influenced by ratio powder:liquid and chemical composition of the precursor powders. Experimental cements released less fluoride than commercial cements. However, this liberation was more constant during the analyzed period. Thus, the results obtained in this study indicated that the composition of the experimental powder modified by the niobium can lead the formation of the polysalt matrix with good mechanical properties. In other words, we can say that experimental powder offered considerable promise for exploitation in dental field.

Ferroelectric characteristics of SrBi4Ti4O15 thin films grown on Pt/Ti/SiO2/Si substrates by the soft chemical method

Ferroelectric SrBi4Ti4O15 thin films were successfully prepared on a Pt(111)/Ti/SiO2/Si(100) substrate for the first time by spin coating, using the polymeric precursor method. X-ray diffraction patterns of the films indicate that they are polycrystalline in nature. Atomic force microscopy (AFM) analyses showed that the surface of these films is smooth, dense and crack-free with low surface roughness (6.4 nm). At room temperature and at a frequency of 1 MHz, the dielectric constant and the dissipation factor were, respectively, 150 and 0.022. The C-V characteristics of perovskite thin film prepared at low temperature show normal ferrolectric behaviour. The remanent polarization and coercive field for the films deposited were 5.4 mu C/cm(2) and 8 5 kV/cm, respectively. All the capacitors showed good polarization fatigue characteristics at least up to 1 x 10(10) bipolar pulse cycles indicating that SrBi4Ti4O15 thin films can be a promising material for use in nonvolatile memories. (c) 2005 Elsevier B.V. All rights reserved.

Platinum-coated nanostructured oxides for active catalytic electrodes

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SnO2 nanoparticles functionalized in amorphous silica and glass

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Synchrotron structural characterization of electrochemically synthesized hexacyanoferrates containing K(+): A revisited analysis of electrochemical redox

The presumably soluble KFe(+3)[Fe(2+)(CN)(6)] structure of electrochemically synthesized hexacyanoferrate materials (Prussian Blue) containing K(+) ions was determined for the first time in this study. Prior to drawing conclusions from a structural analysis, the main goal was to make a precise analysis of the inferred soluble structure, that is, KFe(+3) [Fe(2+)(CN)(6)], which is frequently referred to in the literature as the final stable electrochemically synthesized structure. Indeed, a successful X-ray powder diffraction experiment using X-ray synchrotron radiation was made of a powder placed in a 0.5 mm diameter borosilicate glass capillary, which was obtained by removing sixty 90 nm thin films from the substrates on which they were prepared. However, the conclusions were highly unexpected, because the structure showed that the [Fe(CN)61 group was absent from similar to 25% of the structure, invalidating the previously presumed soluble KFe(+3)[Fe(2+)(CN)(6)] structure. This information led to the conclusion that the real structure of Prussian Blue electrochemically synthesized after the stabilization process is Fe(4)[Fe(CN)(6)](3)center dot mH(2)O containing a certain fraction of inserted K(+) ions. In fact, based on an electrogravimetric analysis (Gimenez-Romero et al., J. Phys. Chem. B 2006, 110, 2715 and 19352) complemented by the Fourier maps. it is possible to affirm that the K(+) was part of the water crystalline substructure. Therefore, the interplay mechanism was reexamined considering more precisely the role played by the water crystalline substructure and the K+ alkali metal ion. As a final conclusion, it is proposed that the most precise way to represent the structure of electrochemically synthesized and stabilized hexacyanoferrate materials is Fe(4)(3+) Fe(2+)(CN)(6)](3)center dot[K(h)(+)center dot OH(h)(-)center dot mH(2)O]. The importance of this result is that the widespread use of the terms soluble and insoluble in the electrochemical literature could be reconsidered. Indeed, only one type of structure is insoluble, and that is Fe(4)[Fe(CN)(6)](3)center dot mH(2)O hence, the use of the terms soluble and insoluble is inappropriate from a structural point of view. The result of the presence of the [Fe(CN)61 vacancy a, roup is that the water Substructure cannot be ignored in the ionic interplay mechanism which controls the intercalation and redox process, as was previously confirmed by electrogravimetric analyses (Gimenez-Romero et al., J. Phys. Chem. B 2006, 110, 2715 Garcia-Jareno et al., Electrochim. Acta 1998, 44, 395: Kulesza, Inorg. Chem. 1990, 29, 2395).

Pump excited state absorption in holmium-doped fluoride glass

The primary excited state absorption processes relating to the (5)I(6) -> (5)I(7) 3 mu m laser transition in singly Ho(3+)-doped fluoride glass have been investigated in detail using time-resolved fluorescence spectroscopy. Selective laser excitation of the (5)I(6) and (5)I(7) energy levels established the occurrence of two excited state absorption transitions from these energy levels that compete with previously described energy transfer upconversion processes. The (5)I(7) -> (5)I(4) excited state absorption transition has peak cross sections at 1216 nm (sigma(esa)=2.8x10(-21) cm(2)), 1174 nm (sigma(esa)=1x10(-21) cm(2)), and 1134 nm (sigma(esa)=7.4x10(-22) cm(2)) which have a strong overlap with the (5)I(8) -> (5)I(6) ground state absorption. on the other hand, it was established that the excited state absorption transition (5)I(6) -> (5)S(2) had a weak overlap with ground state absorption. Using numerical solution of the rate equations, we show that Ho(3+)-doped fluoride fiber lasers employing pumping at 1100 nm rely on excited state absorption from the lowest excited state of Ho(3+) to maintain a population inversion and that energy transfer upconversion processes compete detrimentally with the excited state absorption processes in concentrated Ho(3+)-doped fluoride glass. (c) 2008 American Institute of Physics.

Color tunability of intense upconversion emission from Er3+-Yb3+ co-doped SiO2-Ta2O5 glass ceramic planar waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Refractive index changes in photochromic SbPO4-WO3 glass by exposure to band-gap radiation

We report photoinduced photo-darkening in SbPO4-WO3 glass by exposure to 532 nm light with a power density of 143 mW/cm(2). The time of exposure was varied between 0 and 256 min following which visible photo-darkening, peaking at 850 nm was observed. Spectrophotometer measurement of absorption was performed for both treated and untreated regions of the sample. Time exposure to below band-gap light results in a single exponent Gaussian absorption function over an exceptionally wide range of wavelengths (500 nm-1600 nm), with a 1/e width of 647.5 nm. Kramers-Kronig transform of the change in the absorption indicates a negative local change in the refractive index. The dispersed refractive index change at 1550 nm, Delta n, is calculated to be similar to -5 x 10(-8). The peak absorption increases with time of exposure and the photo-darkening remains irreversible at room temperature. Crown Copyright (C) 2010 Published by Elsevier B.V. All rights reserved.