Conducting nylon, cotton and wool yarns by continuous vapor polymerization of pyrrole

Conductive textile yarns were prepared by a continuous vapor polymerization method; the application of polypyrrole by the continuous vapor polymerization method used is designed for the easy adaptation into industrial procedures. The resultant conductive yarns were examined by longitudinal and cross-sectional views, clearly showing the varying levels of penetration of the polymer into the yarn structure. It was found that for wool the optimum specific resistance was achieved by using the 400 TPM yarn with a FeCl3 solution concentration of 80 g/L FeCl3 to produce 1.69 Ω g/cm2. For cotton yarn, the optimum specific resistance of 1.53 Ω g/cm2 was obtained with 80 g/L of a FeCl3 solution.

Pulsed plasma polymerization of hexamethyldisiloxane onto wool : control of moisture vapor transmission rate and surface adhesion

A new fabric with potential in medical textiles has been developed by application of a surface coating on wool using pulsed plasma polymerization of HMDSO. This coating enabled a controllable MVTR and surface adhesion. MVTR in the range recommended for optimum wound healing was obtained by varying frequency, monomer pressure and deposition time. Lower surface adhesion was achieved. Peeling tests, contact angle measurements, SPM force curves and ATR FT-IR were used to characterize the surfaces for both wool and a PE model substrate. All these results were consistent with a decrease in surface energy after PP-HMDSO treatment. ATR FT-IR results showed a siloxane film with less organic Si(CH₃)_n groups and more SiOSi cross-links.

High rates of oxygen reduction over a vapor phase-polymerized PEDOT electrode

The air electrode, which reduces oxygen (O₂), is a critical component in energy generation and storage applications such as fuel cells and metal/air batteries. The highest current densities are achieved with platinum (Pt), but in addition to its cost and scarcity, Pt particles in composite electrodes tend to be inactivated by contact with carbon monoxide (CO) or by agglomeration. We describe an air electrode based on a porous material coated with poly(3,4-ethylenedioxythiophene) (PEDOT), which acts as an O₂ reduction catalyst. Continuous operation for 1500 hours was demonstrated without material degradation or deterioration in performance. O₂ conversion rates were comparable with those of Pt-catalyzed electrodes of the same geometry, and the electrode was not sensitive to CO. Operation was demonstrated as an air electrode and as a dissolved O₂ electrode in aqueous solution.

Facile fabrication of superhydrophobic conductive graphite nanoplatelet/vapor-grown carbon fiber/polypropylene composite coatings

The fabrication of superhydrophobic surfaces with mechanical durability is challenging because the surface microstructure is easily damaged. Herein, we report superhydrophobic conductive graphite nanoplatelet (GNP)/vapor-grown carbon fiber (VGCF)/polypropylene (PP) composite coatings with mechanical durability by a hot-pressing method. The as-prepared GNP/VGCF/PP composite coatings showed water contact angle (WCA) above 150° and sliding angle (SA) less than 5°. The superhydrophobicity was improved with the increase of VGCF content in the hybrid GNP and VGCF fillers. The more VGCFs added in the GNP/VGCF/PP composite coating, the higher porosity on the surface was formed. Compared to the GNP/PP and VGCF/PP composite coatings, the GNP and VGCF hybrid fillers exhibited more remarkable synergistic effect on the electrical conductivity of the GNP/VGCF/PP composite coatings. The GNP/VGCF/PP composite coating with GNP:VGCF = 2:1 possessed a sheet resistance of 1 Ω/sq. After abrasion test, the rough microstructure of the GNP/VGCF/PP (2:1) composite coating was mostly restored and the composite coating retained superhydrophobicity, but not for the VGCF/PP composite coating. When the superhydrophobic surface is mechanically damaged with a loss of superhydrophobicity, it can be easily repaired by a simple way with adhesive tapes. Moreover, the oil-fouled composite surface can regenerate superhydrophobicity by wetting the surface with alcohol and subsequently burning off alcohol.

Epitaxial growth of multi-structure sno2 by chemical vapor deposition

The nanowire and whisker heterostructures of tin dioxide were fabricated by the chemical vapor deposition technique. It was demonstrated that various structures of tin oxide can be obtained by controlling the thickness of gold layer and the partial pressure of source vapor at growing sites. 12.5 and 25 nm thicknesses are preferable for the epitaxial growth of nanowires and heterostructure through vapor-liquid-solid mechanism, respectively. The tin dioxide whiskers with core-shell structure were fabricated by vapor-solid mechanism. Meanwhile, the influences of various factors on the tin dioxide growth are also discussed.