Study of polycrystalline Cu2ZnSnS4 films by Raman scattering

Cu2ZnSnS4 (CZTS) is a p-type semiconductor that has been seen as a possible low-cost replacement for Cu(In,Ga)Se2 in thin film solar cells. So far compound has presented difficulties in its growth, mainly, because of the formation of secondary phases like ZnS, CuxSnSx+1, SnxSy, Cu2−xS and MoS2. X-ray diffraction analysis (XRD), which is mostly used for phase identification cannot resolve some of these phases from the kesterite/stannite CZTS and thus the use of a complementary technique is needed. Raman scattering analysis can help distinguishing these phases not only laterally but also in depth. Knowing the absorption coefficient and using different excitation wavelengths in Raman scattering analysis, one is capable of profiling the different phases present in multi-phase CZTS thin films. This work describes in a concise form the methods used to grow chalcogenide compounds, such as, CZTS, CuxSnSx+1, SnxSy and cubic ZnS based on the sulphurization of stacked metallic precursors. The results of the films’ characterization by XRD, electron backscatter diffraction and scanning electron microscopy/energy dispersive spectroscopy techniques are presented for the CZTS phase. The limitation of XRD to identify some of the possible phases that can remain after the sulphurization process are investigated. The results of the Raman analysis of the phases formed in this growth method and the advantage of using this technique in identifying them are presented. Using different excitation wavelengths it is also analysed the CZTS film in depth showing that this technique can be used as non destructive methods to detect secondary phases.

Adhesion and wear behaviour of NCD coatings on Si3N4 by micro-abrasion tests

Nanocrystalline diamond (NCD) coatings offer an excellent alternative for tribological applications, preserving most of the intrinsic mechanical properties of polycrystalline CVD diamond and adding to it an extreme surface smoothness. Silicon nitride (Si3N4) ceramics are reported to guarantee high adhesion levels to CVD microcrystalline diamond coatings, but the NCD adhesion to Si3N4 is not yet well established. Micro-abrasion tests are appropriate for evaluating the abrasive wear resistance of a given surface, but they also provide information on thin film/substrate interfacial resistance, i.e., film adhesion. In this study, a comparison is made between the behaviour of NCD films deposited by hot-filament chemical vapour deposition (HFCVD) and microwave plasma assisted chemical vapour deposition (MPCVD) techniques. Silicon nitride (Si3N4) ceramic discs were selected as substrates. The NCD depositions by HFCVD and MPCVD were carried out using H2–CH4 and H2–CH4–N2 gas mixtures, respectively. An adequate set of growth parameters was chosen for each CVD technique, resulting in NCD films having a final thickness of 5 m. A micro-abrasion tribometer was used, with 3 m diamond grit as the abrasive slurry element. Experiments were carried out at a constant rotational speed (80 r.p.m.) and by varying the applied load in the range of 0.25–0.75 N. The wear rate for MPCVD NCD (3.7±0.8 × 10−5 m3N−1m−1) is compatible with those reported for microcrystalline CVD diamond. The HFCVD films displayed poorer adhesion to the Si3N4 ceramic substrates than the MPCVD ones. However, the HFCVD films show better wear resistance as a result of their higher crystallinity according to the UV Raman data, despite evidencing premature adhesion failure.

Comfort and functionality of pregnant women's feet study of kinetic parameters with silicon insoles

As gestantes, fruto das suas alterações fisiológicas e biomecânicas, constituem uma população de risco relativamente a dores ou lesões do sistema músculo-esquelético, nomeadamente, nos membros inferiores e coluna. Os objectivos deste estudo consistiram em avaliar: (i) a dor e o conforto dos pés durante a marcha: sem o uso de qualquer palmilha nas gestantes e no grupo de controlo; com a aplicação de uma palmilha de retropé e com a aplicação de uma palmilha completa (nas gestantes); (ii) a distribuição das pressões plantares e, (iii) as forças de reacção do solo nas mesmas condições experimentais. Avaliámos ainda a duração das diferentes fases do ciclo de marcha nas gestantes, com e sem palmilhas, e no grupo de controlo, sem o uso de palmilha. Os nossos resultados mostraram que: (i) as gestantes demoram mais tempo a completar a fase de apoio da marcha, (ii) têm um aumento significativo de dores nos pés, face ao grupo de controlo, (iii) as gestantes sentem menos dor e mais conforto quando realizam marcha, com palmilhas, especialmente com a palmilha completa, (iv) a palmilha completa redistribui as forças, diminui os valores de pressão e aumenta a área de contacto do pé com o solo. Os nossos resultados sugerem que, o uso da palmilha completa de silicone, durante a marcha, pode ser eficaz na melhoria da sintomatologia dolorosa e no aumento do conforto da grávida.

Shane Meadows’ country: analysis of the film this is England (2006)

This Is England is social realist film portraying racism and poverty in 1980s Britain through the eyes of Shaun, a 12 year old boy, who has lost his father in the Falklands war and as to come to terms with his own identity, the difficult transition from childhood to adolescence and the need to fit in a determined group/tribe/gang. The following article aims at analysing relevant aspects depicted from the film emphasizing the so much debated reality of life during 80s. In This is England Shane Meadows manages to rediscover his own self geography, by revisiting his adolescent years. It is a biographical film about the importance of peer pressure and the results of an excess of nationalism, at the same time it typifies some issues related to the 80s youth culture.

Adsorptive stripping voltammetric determination of venlafaxine in urine with a mercury film microelectrode

An adsorptive stripping voltammetric procedure for the determination of the antidepressant venlafaxine in urine using a mercury film microelectrode wasdeveloped. The method is based on controlled adsorptive accumulation of the drug at the potential of 1.00V (vs. Ag/AgCl) in the presence of 1.25 x10 -2 molL- 1 borate buffer (pH 8.7). Urine samples were analyzed directly after performing a ten-fold dilution with the supporting electrolyte but without other pretreatment. The limit of detection obtained for a 30 s collection time was 0.693x 10- 6 mol L -1. Recovery experimentsgave good results at the 10 -6 mol L- 1 level (bias less 5% were obtained).

Voltammetric determination of dialifos in soils with a mercury film ultramicroelectrode

An extraction-adsorptive stripping voltammetric procedure for the determination of the pesticide dialifos in soil samples using microwave-assisted solvent extraction and a mercury film ultramicroelectrode was developed. The method is based on the use of hexane-acetone solvent (1:1, v/v) and on controlled adsorptive accumulation of the insecticide at the potential of -0.10V (versus Ag/AgCl) in the presence of Britton-Robinson buffer (pH 2.0). Soil sample extracts were analyzed directly after drying and redissolution with the supporting electrolyte, but without other pretreatment. The limit of detection obtained for a 10sec collection time was 2.0x10-8 mol L-1. Recovery experiments for the global procedure, at the 0.100µgg-1 level, gave satisfactory average and standard deviation results for the two different soils tested.

Study of vanadium doped ZnO films prepared by dc reactive magnetron sputtering at different substrate temperatures

ZnO films doped with vanadium (ZnO:V) have been prepared by dc reactive magnetron sputtering technique at different substrate temperatures (RT–500 C). The effects of the substrate temperature on ZnO:V films properties have been studied. XRD measurements show that only ZnO polycrystalline structure has been obtained, no V2O5 or VO2 crystal phase can be observed. It has been found that the film prepared at low substrate temperature has a preferred orientation along the (002) direction. As the substrate temperature is increased, the (002) peak intensity decreases. When the substrate temperature reaches the 500 C, the film shows a random orientation. SEM measurements show a clear formation of the nano-grains in the sample surface when the substrate temperature is higher than 400 C. The optical properties of the films have been studied by measuring the specular transmittance. The refractive index has been calculated by fitting the transmittance spectra using OJL model combined with harmonic oscillator.

Thermodynamic pathway for the formation of SnSe and SnSe2 polycrystalline thin films by selenization of metal precursors

In this work, tin selenide thin films (SnSex) were grown on soda lime glass substrates by selenization of dc magnetron sputtered Sn metallic precursors. Selenization was performed at maximum temperatures in the range 300 °C to 570 °C. The thickness and the composition of the films were analysed using step profilometry and energy dispersive spectroscopy, respectively. The films were structurally and optically investigated by X-ray diffraction, Raman spectroscopy and optical transmittance and reflectance measurements. X-Ray diffraction patterns suggest that for temperatures between 300 °C and 470 °C, the films are composed of the hexagonal-SnSe2 phase. By increasing the temperature, the films selenized at maximum temperatures of 530 °C and 570 °C show orthorhombic-SnSe as the dominant phase with a preferential crystal orientation along the (400) crystallographic plane. Raman scattering analysis allowed the assignment of peaks at 119 cm−1 and 185 cm−1 to the hexagonal-SnSe2 phase and those at 108 cm−1, 130 cm−1 and 150 cm−1 to the orthorhombic-SnSe phase. All samples presented traces of condensed amorphous Se with a characteristic Raman peak located at 255 cm−1. From optical measurements, the estimated band gap energies for hexagonal-SnSe2 were close to 0.9 eV and 1.7 eV for indirect forbidden and direct transitions, respectively. The samples with the dominant orthorhombic-SnSe phase presented estimated band gap energies of 0.95 eV and 1.15 eV for indirect allowed and direct allowed transitions, respectively.

Hopping conduction and persistent photoconductivity in Cu2ZnSnS4 thin films

The temperature dependence of electrical conductivity and the photoconductivity of polycrystalline Cu2ZnSnS4 were investigated. It was found that at high temperatures the electrical conductivity was dominated by band conduction and nearest-neighbour hopping. However, at lower temperatures, both Mott variable-range hopping (VRH) and Efros–Shklovskii VRH were observed. The analysis of electrical transport showed high doping levels and a large compensation ratio, demonstrating large degree of disorder in Cu2ZnSnS4. Photoconductivity studies showed the presence of a persistent photoconductivity effect with decay time increasing with temperature, due to the presence of random local potential fluctuations in the Cu2ZnSnS4 thin film. These random local potential fluctuations cannot be attributed to grain boundaries but to the large disorder in Cu2ZnSnS4.

Admittance spectroscopy of Cu2ZnSnS4 based thin film solar cells

In this report, we propose an AC response equivalent circuit model to describe the admittance measurements of Cu2ZnSnS4 thin film solar cell grown by sulphurization of stacked metallic precursors. This circuit describes the contact resistances, the back contact, and the heterojunction with two trap levels. The study of the back contact resistance allowed the estimation of a back contact barrier of 246 meV. The analysis of the trap series with varying temperature revealed defect activation energies of 45 meV and 113 meV. The solar cell’s electrical parameters were obtained from the J-V curve: conversion efficiency, 1.21%; fill factor, 50%; open circuit voltage, 360 mV; and short circuit current density, 6.8 mA/cm2.

Mo bilayer for thin film photovoltaics revisited

Thin film solar cells based on Cu(In,Ga)Se2 as an absorber layer use Mo as the back contact. This metal is widely used in research and in industry but despite this, there are only a few published studies on the properties of Mo. Properties such as low resistivity and good adhesion to soda lime glass are hard to obtain at the same time. These properties are dependent on the deposition conditions and are associated with the overall stress state of the film. In this report, a study of the deposition of a Mo bilayer is carried out by analysing first single and then bilayers. The best properties of the bilayer were achieved when the bottom layer was deposited at 10 × 10−3 mbar with a thickness of 500 nm and the top layer deposited at 1 × 10−3 mbar with a thickness of 300 nm. The films deposited under these conditions showed good adhesion and a sheet resistivity lower than 0.8 .

A tecnologia fotovoltaica de película fina. Afinal como estamos?

Todos nós estamos familiarizados com os painéis fotovoltaicos comuns, os silicon wafer-based (“bolacha/pastilha” de silício), que possuem atualmente uma quota superior a 80% [1-3] no mercado solar fotovoltaico. Desde o seu “aparecimento” em 1950, foram realizados avanços em diferentes vertentes, como a eficiência, durabilidade, custos e tecnologias de produção [2, 4, 5], sendo que no início deste século se começaram a desenvolver e a criar expectativas positivas crescentes acerca do que se designa de células fotovoltaicas de película fina ou TFPC (thin film photovoltaic cells). Certamente, já todos ouvimos notícias nos últimos anos do seu desenvolvimento e de aplicações variadas (vestuário, fachadas, etc), pelo que este artigo visa elucidar o leitor acerca do que são, do seu grau de investigação e desenvolvimento (I&D) e da posição no mercado atual e futura.

Film thickness in a ball-on-disc contact lubricated with greases, bleed oils and base oils

Three different lubricating greases and their bleed and base oils were compared in terms of film thickness in a ball-on-disc test rig through optical interferometry. The theoretical values calculated according to Hamrock's equation are in close agreement with the base oil film thickness measurements, which validates the selected experimental methodology. The grease and bleed oil film thickness under fully flooded lubrication conditions presented quite similar behaviour and levels. Therefore, the grease film thickness under full film conditions might be predicted using their bleed oil properties, namely the viscosity and pressure-viscosity coefficient. The base and bleed oil lubricant parameter LP are proportional to the measured film thickness. A relationship between grease and the corresponding bleed oil film thickness was evidenced.

Influence of the abrasive particles size in the micro-abrasion wear tests of TiAlSiN thin coatings

Ball rotating micro-abrasion tribometers are commonly used to carry out wear tests on thin hard coatings. In these tests, different kinds of abrasives were used, as alumina (Al2O3), silicon carbide (SiC) or diamond. In each kind of abrasive, several particle sizes can be used. Some studies were developed in order to evaluate the influence of the abrasive particle shape in the micro-abrasion process. Nevertheless, the particle size was not well correlated with the material removed amount and wear mechanisms. In this work, slurry of SiC abrasive in distilled water was used, with three different particles size. Initial surface topography was accessed by atomic force microscopy (AFM). Coating hardness measurements were performed with a micro-hardness tester. In order to evaluate the wear behaviour, a TiAlSiN thin hard film was used. The micro-abrasion tests were carried out with some different durations. The abrasive effect of the SiC particles was observed by scanning electron microscopy (SEM) both in the films (hard material) as in the substrate (soft material), after coating perforation. Wear grooves and removed material rate were compared and discussed.

Wuthering heights on the screen: exploring the relations between film adaptation and subtitling

This essay aims to confront the literary text Wuthering Heights by Emily Brontë with five of its screen adaptations and Portuguese subtitles. Owing to the scope of the study, it will necessarily afford merely a bird‘s eye view of the issues and serve as a starting point for further research. Accordingly, the following questions are used as guidelines: What transformations occur in the process of adapting the original text to the screen? Do subtitles update the film dialogues to the target audience‘s cultural and linguistic context? Are subtitles influenced more by oral speech than by written literary discourse? Shouldn‘t subtitles in fact reflect the poetic function prevalent in screen adaptations of literary texts? Rather than attempt to answer these questions, we focus on the objects as phenomena. Our interdisciplinary undertaking clearly involves a semio-pragmatic stance, at this stage trying to avoid theoretical backdrops that may affect our apprehension of the objects as to their qualities, singularities, and conventional traits, based on Lucia Santaella‘s interpretation of Charles S. Peirce‘s phaneroscopy. From an empirical standpoint, we gather features and describe peculiarities, under the presumption that there are substrata in subtitling that point or should point to the literary source text, albeit through the mediation of a film script and a particular cinematic style. Therefore, we consider how the subtitling process may be influenced by the literary intertext, the idiosyncrasies of a particular film adaptation, as well as the socio-cultural context of the subtitler and target audience. First, we isolate one of the novel‘s most poignant scenes – ‗I am Heathcliff‘ – taking into account its symbolic play and significance in relation to character and plot construction. Secondly, we study American, English, French, and Mexican adaptations of the excerpt into film in terms of intersemiotic transformations. Then we analyze differences between the film dialogues and their Portuguese subtitles.