Influence of pulse repetition rate of Er : YAG laser and dentin depth on tensile bond strength of dentin-resin interface

The study evaluated the in vitro influence of pulse-repetition rate of Er:YAG laser and dentin depth on tensile bond strength of dentin-resin interface. Dentin surfaces of buccal or lingual surfaces from human third molars were submitted to tensile test in different depths (superficial, 1.0 and 1.5 mm) of the same dental area, using the same sample. Surface treatments were acid conditioning solely (control) and Er:YAG laser irradiation (80 mJ) followed by acid conditioning, with different pulse-repetition rates (1, 2, 3, or 4 Hz). Single bond/Z-250 system was used. The samples were stored in distilled water at 37 degrees C for 24 h, and then the first test (superficial dentine) was performed. The bond failures were analyzed. Following, the specimens were identified, grounded until 1.0- and 1.5-mm depths, submitted again to the treatments and to the second and, after that, to third-bond tests on a similar procedure and failure analysis. ANOVA and Tukey test demonstrated a significant difference (p < 0.001) for treatment and treatment X depth interaction (p < 0.05). The tested depths did not show influence (p > 0.05) on the bond strength of dentin-resin interface. It may be concluded that Er:YAG laser with 1, 2, 3, or 4 Hz combined with acid conditioning did not increase the resin tensile bond strength to dentin, regardless of dentin depth. (C) 2007 Wiley Periodicals, Inc.

Effect of blood contamination on the shear bond strength at resin/dentin interface in primary teeth

Purpose: To assess in vitro the shear bond strength at the resin/dentin interface in primary teeth after contamination with fresh human blood. Methods: 75 crowns of primary molars were embedded in acrylic resin and mechanically ground to expose a flat dentin surface. The specimens were randomly assigned to five groups (n=15), according to the surface treatment. Group I (control) had no blood contamination. The other groups were blood-contaminated and subjected to different post-contamination protocols: in Group 2, the surfaces were rinsed with water; in Group 3, the surfaces were air-dried; in Group 4, the surfaces were rinsed and air-dried; and in Group 5, no post-contamination treatment was done. In all groups, a 3-mm dentin bonding site was demarcated, Single Bond adhesive system was applied and resin composite cylinders were bonded. After 24 hours in distilled water, shear bond strength was tested at a crosshead speed of 0.5 mm/minute. Results: Means (in MPa) were: Group 1: 7.1 (+/- 4.2); Group 2: 4.0 (+/- 1.8); Group 3: 0.9 (+/- 0.7); Group 4: 3.9 (+/- 2.2) and Group 5: 1.3 (+/- 1.5). Data were analyzed statistically by the Kruskal-Wallis test at 5% significance level. Groups 2 and 4 were similar to each other (P > 0.05) and both ware similar to Group 1 (P > 0.05). These groups (2, 3 and 4) had statistically significantly higher bond strengths than Groups 3 and 5 (P < 0.05). Blood contamination negatively affected the shear bond strength to primary tooth dentin. Among the blood-contaminated groups, water-rinsed specimens had higher bond strengths than those that were exclusively air-dried or not submitted to any post-contamination protocol before adhesive application.

Bond strength of fibre glass and carbon fibre posts to the root canal walls using different resin cements

The aim of the study was to evaluate the bond strength of fibre glass and carbon fibre posts in the root canal walls cemented with self-adhesive (RelyX-Unicem) and chemical (Cement-Post) resin cements. Forty maxillary canines were divided into four groups according to the cement and post used and submitted to the push-out test (0.5 mm min(-1)). The data were submitted to statistical analysis (2-way ANOVA, Bonferroni - P < 0.05) and fracture analysis by Scanning Electronic Microscopy. Fibre glass presented the best results when cemented with RelyX-Unicem and Cement-Post (P < 0.05). RelyX-Unicem presented the highest bond strength values for both posts (P < 0.05). Fracture analysis showed predominance of cohesive fracture of post for RelyX-Unicem and adhesive fracture between dentin/cement and mixed for Cement-Post. The bond strength values were significantly affected by the type of post and cement used and the highest values were found for fibre glass posts and RelyX-Unicem.

Chemical and Morphological Features of Dental Composite Resin: Influence of Light Curing Units and Immersion Media

Aims: The study evaluated the influence of light curing units and immersion media on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Light curing units with different power densities and mode of application used were XL 3000 (480 mW/cm(2)), Jet Lite 4000 Plus (1230mW/cm(2)), and Ultralume Led 5 (790 mW/cm(2)) and immersion media were artificial saliva, Coke(R), tea and coffee, totaling 12 experimental groups. Specimens (10 mm X 2 mm) were immersed in each respective Solution for 5 min, three times a day, during 60 days and stored in artificial saliva at 37 degrees C +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. Findings: Groups immersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calcium at the material surface. Regarding coffee, there was a reasonable chemical degradation with loss of load particles and deposition of ions. For tea, superficial degradation occurred in specific areas with deposition of calcium, carbon. potassium and phosphorus. For Coke(R), excessive matrix degradation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion: Light curing units did not influence the superficial morphology of composite resin tested, but the immersion beverages did. Coke(R) affected material`s surface more than did the other tested drinks. Microsc. Res. Tech. 73:176-181, 2010. (c) 2009 Wiley-Liss Inc.

Effect of Three Methods for Cleaning Dentures on Biofilms Formed In Vitro on Acrylic Resin

Purpose: The aim of this study was to evaluate the effect of three denture hygiene methods against different microbial biofilms formed on acrylic resin specimens. Materials and methods: The set (sterile stainless steel basket and specimens) was contaminated (37 degrees C for 48 hours) by a microbial inoculum with 106 colony-forming units (CFU)/ml (standard strains: Staphylococcus aureus, Streptococcus mutans, Escherichia coli, Candida albicans, Pseudomonas aeruginosa, and Enterococcus faecalis; field strains: S. mutans, C. albicans, C. glabrata, and C. tropicalis). After inoculation, specimens were cleansed by the following methods: (1) chemical: immersion in an alkaline peroxide solution (Bonyplus tablets) for 5 minutes; (2) mechanical: brushing with a dentifrice for removable prostheses (Dentu Creme) for 20 seconds; and (3) a combination of chemical and mechanical methods. Specimens were applied onto a Petri plate with appropriate culture medium for 10 minutes. Afterward, the specimens were removed and the plates incubated at 37 degrees C for 48 hours. Results: Chemical, mechanical, and combination methods showed no significant difference in the reduction of CFU for S. aureus, S. mutans (ATCC and field strain), and P. aeruginosa. Mechanical and combination methods were similar and more effective than the chemical method for E. faecalis, C. albicans (ATCC and field strain), and C. glabrata. The combination method was better than the chemical method for E. coli and C. tropicalis, and the mechanical method showed intermediate results. Conclusion: The three denture hygiene methods showed different effects depending on the type of microbial biofilms formed on acrylic base resin specimens.

Influence of Post and Resin Cement on Stress Distribution of Maxillary Central Incisors Restored with Direct Resin Composite

The current study evaluated the influence of two endodontic post systems and the elastic modulus and film thickness of resin cement on stress distribution in a maxillary central incisor (MCI) restored with direct resin composite using finite element analysis (FEA). A three-dimensional model of an MCI with a coronary fracture and supporting structures was performed. A static chewing pressure of 2.16 N/mm(2) was applied to two areas on the palatal surface of the composite restoration. Zirconia ceramic (ZC) and glass fiber (GF) posts were considered. The stress distribution was analyzed in the post, dentin and cement layer when ZC and GF posts were fixed to the root canals using resin cements of different elastic moduli (7.0 and 18.6 GPa) and different layer thicknesses (70 and 200 mu m). The different post materials presented a significant influence on stress distribution with lesser stress concentration when using the GF post. The higher elastic modulus cement created higher stress levels within itself. The cement thicknesses did not present significant changes.

Influence of NaHCO(3) Powder on Translucency of Microfilled Composite Resin Immersed in Different Mouthrinses

The regular use of mouthrinses, particularly when combined with the use of air-powder polishing, could affect the appearance of tooth-colored restorations. The current study sought to evaluate the effect of NaHCO(3) powder on translucency of a microfilled composite resin immersed in different mouthrinses, at distinct evaluation periods. Eighty disk-shaped specimens of composite resin (Durafill VS, Heraeus Kulzer GmbH & Co. KG, Hanau, Germany) were prepared. The composite specimens were then randomly allocated into two groups according to the surface treatment: exposure to NaHCO(3) powder (10 seconds) or nonexposure, and they were randomly assigned into four subgroups, according to the mouthrinses employed (N = 10): Periogard (Colgate/Palmolive, Sao Bernardo do Campo, SP, Brazil), Cepacol (Aventis Pharma, Sao Paulo, SP, Brazil), Plax (Colgate/Palmolive), and distilled water (control group). The samples were immersed for 2 minutes daily, 5 days per week, over a 4-month test period. Translucency was measured with a transmission densitometer at seven evaluation periods. Statistical analyses (analysis of variance and Tukey`s test) revealed that: distilled water presented higher translucency values (86.72%); Periogard demonstrated the lowest translucency values (72.70%); and Plax (74.05%) and Cepacol (73.32%) showed intermediate translucency values, which were statistically similar between them (p > 0.01). NaHCO(3) air-powder polishing increased the changes in translucency associated with the mouthrinses. Air-powder polishing alone had no effect on material translucency. Translucency percent was gradually decreased from 1 week of immersion up to 4 months. It may be concluded that the NaHCO(3) powder and the tested mouthrinses have affected the translucency of microfilled composite resin, according to the tested time. CLINICAL SIGNIFICANCE During the last decade, the demand for composite resin restorations has grown considerably, however, controversy persists regarding the effect of surface roughness on color stability.

Influence of water flow rate on shear bond strength of resin composite to Er : YAG cavity preparation

Purpose: To evaluate in vitro the influence of water flow rate on shear bond strength of a resin composite to enamel and dentin after Er:YAG cavity preparation. Methods: Ten bovine incisors were selected and roots removed. Crowns were sectioned in four pieces, resulting in 40 samples that were individually embedded in polyester resin (n=10), and ground to plane the enamel and expose the dentin. The bonding site was delimited and samples were randomly assigned according to cavity preparation: (1) Er:YAG/1.0 mL/minute; (2) Er:YAG/1.5 mL/minute; (3) Er:YAG/2.0 mL/minute and (4) High speed handpiece/bur (control group). Samples were fixed to a metallic device, where composite resin cylinders were prepared. Subsequently, they were stored for 24 hours and subjected to a shear bond strength test (500N at 0.5 mm/minute). Results: Means (MPa) were: enamel: 1: 12.8; 2: 16.8; 3: 17.5; 4: 36.0 and Dentin: 1: 13.6; 2: 18.7; 3: 12.1; 4: 21.3. Data were submitted to ANOVA and Tukey`s test. Adhesion to enamel was more efficient than for dentin. The cavities prepared with conventional bur (control) presented higher statistically significant bond strength values (P<0.05) than for Er:YAG laser for both enamel and dentin. No significant differences were observed between water flow rates employed during enamel ablation. For dentin, the shear bond strength of 2.0 mL/minute water flow rate was lower than for 1.5 mL/minute and 1.0 mL/minute rates. The Er:YAG laser adversely affected shear bond strength of resin composite to both enamel and dentin, regardless of the water flow rate used.

Bond Strength of Fiber Posts in Different Root Thirds Using Resin Cement

Purpose: The aim of the study was to assess the in vitro bond strength (BS) of glass fiber posts (GF) and carbon fiber posts (CF) in the cervical, middle, and apical thirds of root canals cemented with RelyX-Unicem (RX) and Cement-Post (CP). Materials and Methods: Forty maxillary canines were divided into 4 groups (n = 10) according to the cement and post used: group 1: GF and RX; group 2: CF and RX; group 3: GF and CP; group 4: CF and CP. The push-out test was applied in the cervical, middle and apical thirds of each specimen to assess bond strength of the cement/post complex to the root canal wall. The data obtained were submitted to ANOVA (Bonferroni test, p < 0.05), and fracture analysis was done with SEM. Results: The GF posts presented the best results when cemented with RX and with CF (p < 0.05). RX presented the highest BS values for both GF and CF (p < 0.05). For all the groups, BS was higher in the cervical third, followed by the middle and apical thirds. Fracture analysis showed a predominance of cohesive fracture of posts for RX, and a predominance of adhesive fracture between dentin/cement, and mixed failure mode for CP. Conclusion: GF posts cemented with RX presented the highest BS values in all root thirds.

Adsorption Isotherms for Removal of Linoleic Acid from Ethanolic Solutions Using the Strong Anion Exchange Resin Amberlyst A26 OH

Adsorption isotherms for the removal of linoleic acid from aqueous ethanol were measured using a strong anion exchange resin (Amberlyst A26 OH). The data for linoleic acid were compared with previously published results for oleic acid. The equilibrium data were correlated using the Langmuir and Freundlich isotherms. Lower average deviations between experimental and calculated results were obtained with the Langmuir model. The capacity of the resin for adsorbing linoleic acid was evaluated at different water contents in ethanol, 100 w = 0.50 to 15.27, and at 298.15 K. The water content in ethanol does not influence significantly the equilibrium behavior, and the strong anion exchange resin has a good performance in the removal of linoleic acid from the liquid phase.

Activation of Leishmania (Leishmania) amazonensis arginase at low temperature by binuclear Mn(2+) center formation of the immobilized enzyme on a Ni(2+) resin

In Leishmania, arginase is responsible for the production of ornithine, a precursor of polyamines required for proliferation of the parasite. In this work, the activation kinetics of immobilized arginase enzyme from L. (L.) amazonensis were studied by varying the concentration of Mn(2+) applied to the nickel column at 23 degrees C. The intensity of the binding of the enzyme to the Ni(2+) resin was directly proportional to the concentration of Mn(2+). Conformational changes of the enzyme may occur when the enzyme interacts with immobilized Ni(2+), allowing the following to occur: (1) entrance of Mn(2+) and formation of the metal bridge; (2) stabilization and activation of the enzyme at 23 degrees C; and (3) an increase in the affinity of the enzyme to Ni(2+) after the Mn(2+) activation step. The conformational alterations can be summarized as follows: the interaction with the Ni(2+) simulates thermal heating in the artificial activation by opening a channel for Mn(2+) to enter. (C) 2010 Elsevier Inc. All rights reserved.

EPR in the Characterization of the Shade Effect on Translucence, Remaining Free Radicals, and Polymerization Depth of Commercially Available Resin Composites

The aim of this study was to assess the relation between the number of free radicals generated and the polymerization depth in two different commercial brands of resin composites with different colors and translucence. Electron paramagnetic resonance quantified the radical populations through relative intensity (I (r)) of free radicals generated, and radical decay was monitored. Sample translucence and the classical polymerization depth were measured. The analysis indicated that resin with more color pigments (MA4, I (r) = 0.73 a.u) or more opacity components (ODA2, I (r) = 0.84 a.u) generated smaller populations of free radicals and have the lower polymerization depth than clearer (M, I (r) = 1.20 a.u and MA2, I (r) = 1.02) or more translucent (OEA2, I (r) = 1.00 a.u) composites for the same light-curing time. It seems that irradiation doses have to be adequate to more colored and less translucent resins.

Effect of Pre-Heating Resin Composite and Light-Curing Units on Monomer Conversion

The purpose of this study was to evaluate the effect of pre-heating resin composite photo-cured with light-curing units (LCU) by FT-IR. Twenty specimens were made in a metallic mold (4 mm diameter x 2 mm thick) from composite resin-Tetric Ceram (R) (Ivoclar/Vivadent) at room temperature (25 degrees C) and pre heated to 37, 54, and 60 degrees C. The specimens were cured with halogen curing light (QTH) and light emitted by diodes (LED) during 40 s. Then, the specimens were pulverized, pressed with KBr and analyzed with FT-IR. The data were submitted to statistical analysis of variance and Kruskal-Wallis test. Study data showed no statistically significant difference to the degree of conversion for the different light curing units (QTH and LED) (p > 0.05). With the increase of temperature there was significant increase in the degree of conversion (p < 0.05). In this study were not found evidence that the light curing unit and temperature influenced the degree of conversion.

Influence of different light sources and photo-activation methods on degree of conversion and polymerization shrinkage of a nanocomposite resin

The purpose of this study was to evaluate the influence of different light sources and photo-activation methods on degree of conversion (DC%) and polymerization shrinkage (PS) of a nanocomposite resin (Filtek (TM) Supreme XT, 3M/ESPE). Two light-curing units (LCUs), one halogen-lamp (QTH) and one light-emitting-diode (LED), and two different photo-activation methods (continuous and gradual) were investigated in this study. The specimens were divided in four groups: group 1-power density (PD) of 570 mW/cm(2) for 20 s (QTH); group 2-PD 0 at 570 mW/cm(2) for 10 s + 10 s at 570 mW/cm(2) (QTH); group 3-PD 860 mW/cm(2) for 20 s (LED), and group 4-PD 125 mW/cm(2) for 10 s + 10 s at 860 mW/cm(2) (LED). A testing machine EMIC with rectangular steel bases (6 x 1 x 2 mm) was used to record the polymerization shrinkage forces (MPa) for a period that started with the photo-activation and ended after two minutes of measurement. For each group, ten repetitions (n = 40) were performed. For DC% measurements, five specimens (n = 20) for each group were made in a metallic mold (2 mm thickness and 4 mm diameter, ISO 4049) and them pulverized, pressed with bromide potassium (KBr) and analyzed with FT-IR spectroscopy. The data of PS were analyzed by Analysis of Variance (ANOVA) with Welch`s correction and Tamhane`s test. The PS means (MPa) were: 0.60 (G1); 0.47 (G2); 0.52 (G3) and 0.45 (G4), showing significant differences between two photo-activation methods, regardless of the light source used. The continuous method provided the highest values for PS. The data of DC% were analyzed by Analysis of Variance (ANOVA) and shows significant differences for QTH LCUs, regardless of the photo-activation method used. The QTH provided the lowest values for DC%. The gradual method provides lower polymerization contraction, either with halogen lamp or LED. Degree of conversion (%) for continuous or gradual photo-activation method was influenced by the LCUs. Thus, the presented results suggest that gradual method photo-activation with LED LCU would suffice to ensure adequate degree of conversion and minimum polymerization shrinkage.

Measurement of shrinkage of composite resin by laser speckle contrast analysis

The aim of this study was to evaluate the shrinkage of a microhybrid dental composite resin photo-activated by one LED with different power densities by means of speckle technique. The dental composite resin Filtek (TM) Z-250 (3M/ESPE) at color A(2) was used for the samples preparation. Uncured composite was packed in a metallic mold and irradiated during 20 s from 100 to 1000 mW cm(-2). For the photo-activation of the samples, it was used a LED prototype (Light Emission Diode) with wavelength centered at 470 nm and adjustable power density until 1 W cm(-2). The speckle patterns obtained from the bottom composite surfaces were monitored using a CCD camera without lens. The speckle field is recorded in a digital picture and stored by CCD camera as the carrier of information on the displacement of the tested surface. The calculated values were obtained for each pair of adjacent patterns and the changes in speckle contrast as a function of time were obtained from six repeated measurements. The speckle contrasts obtained from the bottom surface with 100 mW cm(-1) were smaller than those than the other power densities. The higher power densities provided the higher shrinkage.