The characterisation of the protective film formed by benzotriazole on the 90/10 copper-nickel alloy surface in H2SO4 media

The nature of the protective film formed by benzotriazole (BTAH) on the surface of the 90/10 CuNi alloy in deaerated 0.5 mol L-1 H2SO4 solution containing Fe(III) ions as oxidant was investigated by weight-loss, calorimetric measurements, and by surface-enhanced Raman spectroscopy (SERS). The SERS measurements show that the protective film is composed by the [Cu(I)BTA](n), polymeric complex and that the BTAH molecules are also adsorbed on the electrode surface. A modification of the BET isotherm for adsorption of gases ill solids is proposed to describe the experimental results obtained from weight-loss experiments that suggest an adsorption in multilayers. Electrochemical studies of copper and nickel in 0.5 mol L-1 H2SO4 in presence and absence of BTAH have also been made as an aid to interpret the results. The calculated adsorption free energy of the cuprous benzotriazolate on the surface of the alloy is in accordance with the value for pure copper. (C) 2007 Elsevier Ltd. All rights reserved.

Determinação de minoxidil em formulações farmacêuticas usando permanganometria

Um método clássico para a determinação de minoxidil em formulações farmacêuticas é proposto baseado na reação redox entre KMnO4 e o minoxidil. Os melhores resultados na permanganometria foram obtidos usando concentrações de 1,00 x 10-2 mol L-1 para o permanganato. O minoxidil foi usado como titulante na concentração de 2,00 x 10-2 mol L-1 diluído em solução de H2SO4 2,00 mol L-1. As recuperações para método proposto foram da ordem de 94,5 a 95,2 % dependendo da amostra comercial. O método proposto foi aplicado à amostras comerciais contendo minoxidil e comparado com resultados obtidos a partir de procedimentos cromatográficos com erros relativos da ordem de -1 a -5,26%. O procedimento se mostrou simples, rápido e pode ser uma alternativa para a determinação de minoxidil em amostras farmacêuticas, nas quais a concentração do fármaco é relativamente elevada.

Potentiometric determination of Minoxidil in topical use pharmaceutical samples

A potentiometric titration method for the determination of minoxidil based on its redox reaction with K2Cr2O7 is described. The best results were observed using 1.00 x 10-3 mol L-1 K2Cr2O7 and 1.00 x 10-2 mol L-1 minoxidil solutions, and the minoxidil as titrant in 2.00 mol L-1 H2SO4 medium. The method was applied to commercial samples and compared with the results from a chromatographic procedure. Recoveries from 97.4 to 98.7 % were observed depending on the sample. Comparison with the chromatographic procedure reveled agreement within 90% confidence level.

Comparison of three decontamination methods for Mycobacterium bovis isolation

Sixty samples of tissue fragments with lesions suggestive of tuberculosis from bovine abattoirs, kept in saturated solution of sodium borate, were subjected to four treatments: 4% NaOH (Petroff Method), 12 % H2SO4 and 1.5% HPC (1-Hexadecylpyridinium Chloride) decontamination, and physiological saline solution (control). The HPC method showed the lowest contamination rate (3%) when compared to control (88%, p<0.001), NaOH (33%, p<0.001) and H2SO4 (21.7%, p<0.002). Regarding the isolation success, the HPC method was better (40%) than the control (3%, p<0.001), NaOH (13%, p=0.001) and H2SO4 (1.7%, p<0.001) methods. These results indicate that HPC is an alternative to the Petroff method.

Characterization of nickel-niobium composite electrocoatings

The electrodeposition of nickel based composites is been performed in order to improve properties of nickel layers, such as hardness, wear resistance, lubrication, corrosion resistance and catalytic activity. In the present work Nb powders (20 mu m average size) and Ni were codeposited on 1020 carbon steel by galvanostatic electrolysis of Watts bath, using 10, 20 and 40 mA/cm(2) cathodic current density and 240, 400 and 550 rpm electrolyte stirring rate. The morphology and texture of the coatings, Nb incorporated volume fraction, microhardness, adhesion to the substrate and corrosion behavior were evaluated. The Ni-Nb composite layers presented a rough morphology with randomly oriented Ni grains, whereas pure Ni coatings were smooth and showed highly preferred orientation in the [110] or [100] direction. The volume fraction of Nb in the composites determined by image analysis ranged from 8.5 to 19%. The 400 rpm stirring rate led to the highest Nb content (16 to 19016) for all current densities investigated The microhardness of the composite layers was higher than that of pure Ni coatings due to refining of Ni grains induced by incoporation of Nb particles. The adhesion of the coatings estimated qualitatively by bend test was found satisfactory. The Ni-Nb composites presented lower corrosion rate than Ni coatings in both 3% NaCl and 20% H2SO4 solutions.

Co-electrodeposition and characterization of Cu-Si(3)N(4) composite coatings

Smooth copper coatings containing well-distributed silicon nitride particles were obtained by co-electrodeposition in acidic sulfate bath. The cathodic current density did not show significant influence on incorporated particle volume fraction, whereas the increase of particle concentration in the bath led to its decrease. The increase of stirring rate increased the amount of embedded particles. The microhardness of the composite layers was higher than that of pure copper deposits obtained under the same conditions due to dispersion-strengthening and copper matrix grain refinement and increased with the increase of incorporated particle volume fraction. The microhardness of composites also increased with the increase of current density due to copper matrix grain refining. The composite coatings presented higher strength but lower ductility than pure copper layers. Pure copper and composite coatings showed the same corrosion resistance in 0.5 wt.% H(2)SO(4) solution at room temperature. (C) 2011 Elsevier B.V. All rights reserved.

Platinum nanoparticles embledded in layer-by-layer films from SnO2/polyallylamine for ethanol electrooxidation

Self-assembled films from SnO2 and polyallylamine (PAH) were deposited on gold via ionic attraction by the layer-by-layer(LbL) method. The modified electrodes were immersed into a H2PtCl6 solution, a current of 100 mu A was applied, and different electrodeposition times were used. The SnO2/PAH layers served as templates to yield metallic platinum with different particle sizes. The scanning tunnel microscopy images show that the particle size increases as a function of electrodeposition time. The potentiodynamic profile of the electrodes changes as a function of the electrodeposition time in 0.5 mol L-1 H2SO4, at a sweeping rate of 50mVs(-1). Oxygen-like species are formed at less positive potentials for the Pt-SnO2/PAH film in the case of the smallest platinum particles. Electrochemical impedance spectroscopy measurements in acid medium at 0.7 V show that the charge transfer resistance normalized by the exposed platinum area is 750 times greater for platinum electrode (300 k Omega cm(2)) compared with the Pt-SnO2/PAH film with 1 min of electrodeposition (0.4 k Omega cm(2)). According to the Langmuir-Hinshelwood bifunctional mechanism, the high degree of coverage with oxygen-like species on the platinum nanoparticles is responsible for the electrocatalytic activity of the Pt-SnO2/PAH concerning ethanol electrooxidation. With these features, this Pt-SnO2/PAH film may be grown on a proton exchange membrane (PEM) in direct ethanol fuel cells (DEFC). (c) 2008 Elsevier B.V. All rights reserved.

Effect of W on PtSn/C catalysts for ethanol electrooxidation

Binary and ternary Pt-based catalysts were prepared by the Pechini-Adams modified method on carbon Vulcan XC-72, and different nominal compositions were characterized by TEM and XRD. XRD showed that the electrocatalysts consisted of the Pt displaced phase, suggesting the formation of a solid solution between the metals Pt/W and Pt/Sn. Electrochemical investigations on these different electrode materials were carried out as a function of the electrocatalyst composition, in acid medium (0.5 mol dm(-3) H2SO4) and in the presence of ethanol. The results obtained at room temperature showed that the PtSnW/C catalyst display better catalytic activity for ethanol oxidation compared to PtW/C catalyst. The reaction products (acetaldehyde, acetic acid and carbon dioxide) were analyzed by HPLC and identified by in situ infrared reflectance spectroscopy. The latter technique also allowed identification of the intermediate and adsorbed species. The presence of linearly adsorbed CO and CO2 indicated that the cleavage of the C-C bond in the ethanol substrate occurred during the oxidation process. At 90 degrees C, the Pt85Sn8W7/C catalyst gave higher current and power performances as anode material in a direct ethanol fuel cell (DEFC).

On the open-circuit interaction between methanol and oxidized platinum electrodes

In the present work, results of the interaction between methanol and oxidized platinum surfaces as studied via transients of open-circuit potentials are presented. The surface oxidation before the exposure to interaction with 0.5 M methanol was performed at different polarization times at 1.4 V vs reversible hydrogen electrode (RHE). In spite of the small changes in the initial oxide content, the increase of the pre-polarization time induces a considerable increase of the time needed for the oxide consumption during its interaction with methanol. The influence of the identity of the chemisorbing anion on the transients was also investigated in the following media: 0.1 M HClO4, 0.5 M H2SO4, and 0.5 M H2SO4 + 0.1 mM Cl-. It was observed that the transient time increases with the energy of anion chemisorption and, more importantly, without a change in the shape of the transient, meaning that free platinum sites are available at the topmost layer all over the transient and not only in the potential region of small oxide `coverage`. The impact of the pre-polarization time and the effect of anion chemisorption on the transients are rationalized in terms of the presence of surface and subsurface oxygen driven by place exchange.