Characterization of nickel-niobium composite electrocoatings

The electrodeposition of nickel based composites is been performed in order to improve properties of nickel layers, such as hardness, wear resistance, lubrication, corrosion resistance and catalytic activity. In the present work Nb powders (20 mu m average size) and Ni were codeposited on 1020 carbon steel by galvanostatic electrolysis of Watts bath, using 10, 20 and 40 mA/cm(2) cathodic current density and 240, 400 and 550 rpm electrolyte stirring rate. The morphology and texture of the coatings, Nb incorporated volume fraction, microhardness, adhesion to the substrate and corrosion behavior were evaluated. The Ni-Nb composite layers presented a rough morphology with randomly oriented Ni grains, whereas pure Ni coatings were smooth and showed highly preferred orientation in the [110] or [100] direction. The volume fraction of Nb in the composites determined by image analysis ranged from 8.5 to 19%. The 400 rpm stirring rate led to the highest Nb content (16 to 19016) for all current densities investigated The microhardness of the composite layers was higher than that of pure Ni coatings due to refining of Ni grains induced by incoporation of Nb particles. The adhesion of the coatings estimated qualitatively by bend test was found satisfactory. The Ni-Nb composites presented lower corrosion rate than Ni coatings in both 3% NaCl and 20% H2SO4 solutions.