Comparison of physical and mechanical properties of microwave-polymerized acrylic resin after disinfection in sodium hypochlorite solutions

This study evaluated the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin after immersion in sodium hypochlorite (NaOCl), simulating 20 min of disinfection daily during 180 days. Forty disk-shaped (15 x 4 mm) and 40 rectangular (65 x 10 x 3 mm) specimens were prepared with a microwave-polymerized acrylic resin (Onda-Cryl). Specimens were immersed in either 0.5% NaOCl, 1% NaOCl, Clorox/Calgon and distilled water (control). Color measurements were determined by a portable colorimeter. Three parallel lines, separated by 1.0 mm, were registered on each specimen before and after immersion procedures to analyze the surface roughness. The flexural strength was measured using a 3-point bending test in a universal testing machine with a 50 kgf load cell and a crosshead speed of 1 mm/min. Data were analyzed statistically by ANOVA and Tukey's test (?=0.05). There was no statistically significant differences (p>0.05) among the solutions for color, surface roughness and flexural strength. It may be concluded that immersion in NaOCl solutions simulating short-term daily use during 180 days did not influence the color stability, surface roughness and flexural strength of a microwave-polymerized acrylic resin.

Polymerization shrinkage stress of composites photoactivated by different light sources

The purpose of this study was to compare the polymerization shrinkage stress of composite resins (microfilled, microhybrid and hybrid) photoactivated by quartz-tungsten halogen light (QTH) and light-emitting diode (LED). Glass rods (5.0 mm x 5.0 cm) were fabricated and had one of the surfaces air-abraded with aluminum oxide and coated with a layer of an adhesive system, which was photoactivated with the QTH unit. The glass rods were vertically assembled, in pairs, to a universal testing machine and the composites were applied to the lower rod. The upper rod was placed closer, at 2 mm, and an extensometer was attached to the rods. The 20 composites were polymerized by either QTH (n=10) or LED (n=10) curing units. Polymerization was carried out using 2 devices positioned in opposite sides, which were simultaneously activated for 40 s. Shrinkage stress was analyzed twice: shortly after polymerization (t40s) and 10 min later (t10min). Data were analyzed statistically by 2-way ANOVA and Tukey's test (a=5%). The shrinkage stress for all composites was higher at t10min than at t40s, regardless of the activation source. Microfilled composite resins showed lower shrinkage stress values compared to the other composite resins. For the hybrid and microhybrid composite resins, the light source had no influence on the shrinkage stress, except for microfilled composite at t10min. It may be concluded that the composition of composite resins is the factor with the strongest influence on shrinkage stress.

Permeability of different groups of maxillary teeth after 38% hydrogen peroxide internal bleaching

This study evaluated the influence of internal tooth bleaching with 38% hydrogen peroxide (H2O2) on the permeability of the coronal dentin in maxillary anterior teeth and premolars. Seventy teeth (14 per group) were used: central incisors (CI), lateral incisor (LI), canines (C), first premolars (1PM) and second premolars (2PM). Pulp chamber access and transversal sectioning at 2 mm from the cementoenamel junction were performed and the specimens were divided into 2 groups (n= 7): a) no treatment and b) bleaching with 38% H2O2. The bleaching agent was applied to the buccal surface and to the pulp chamber for 10 min. This procedure was repeated 3 times. The specimens were processed histochemically with copper sulfate and rubeanic acid, sectioned longitudinally, and digitalized in a scanner. The area of stained dentin was measured using Image Tool software. Data were analyzed statistically by ANOVA and Tukey's HSD test (?=0.05). There was statistically significant difference (p<0.001) among the untreated groups, CI (0.23 ± 0.26) having the lowest permeability and LI (10.14 ± 1.89) the highest permeability. Among the bleached groups, dentin permeability was increased in all groups of teeth except for 2PM. It may be concluded that bleaching with 38% H2O2 affected dentin permeability near the pulp chamber in maxillary anterior teeth and in first and second premolars.

Effect of fluoride-containing solutions on the surface of cast commercially pure titanium

This study evaluated the effects of fluoride-containing solutions on the surface of commercially pure titanium (CP Ti) obtained by casting. CP Ti specimens were fabricated and randomly assigned to 5 groups (n=10): group 1: stored in distilled water at 37 ± 1ºC; group 2: stored in distilled water at 37 ± 1ºC and daily immersed in 0.05% NaF for 3 min; group 3: stored in distilled water at 37 ± 1ºC and daily immersed in 0.2% NaF for 3 min; group 4: stored in distilled water at 37 ± 1ºC; and immersed in 0.05% NaF every 15 days for 3 min; and group 5: stored in distilled water at 37 ± 1ºC and immersed in 0.2% NaF every 15 days for 3 min. Surface roughness was measured with a profilometer immediately after metallographic polishing of the specimens (T0) and at 15-day intervals until completing 60 days of experiment (T15, T30, T45, T60). Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). There was no statistically significant difference (p>0.05) in surface roughness among the solutions. In conclusion, fluoride-containing solutions (pH 7.0) used as mouthwashes do not damage the surface of cast CP Ti and can be used by patients with titanium-based restorations.

Retention force of T-bar clasps for titanium and cobalt-chromium removable partial dentures

The objective of this study was to evaluate the retention force of T-bar clasps made from commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) alloy by the insertion/removal test simulating 5 years use. Thirty-six frameworks were cast from CP Ti (n=18) and Co-Cr alloy (n=18) with identical prefabricated patterns on refractory casts from a distal extension mandibular hemi-arch segment. The castings were made on a vacuum-pressure machine, under vacuum and argon atmosphere. Each group was subdivided in three, corresponding to 0.25 mm, 0.50 mm and 0.75 mm undercuts, respectively. No polishing procedures were performed to ensure uniformity. The specimens were subjected to an insertion/removal test and data was analyzed statistically to compare CP Ti and Co-Cr alloy in the same undercut (Student's t-test for independent samples) and each material in different undercuts (one-way ANOVA) (p=0.05). Comparisons between materials revealed significant differences (p=0.017) only for the 0.50-mm undercut. No significant differences (p>0.05) were found when comparing the same material for the undercuts. It may be concluded that for different undercuts, both Co-Cr alloy and CP Ti had no significant differences for T-bar clasps; CP Ti showed the lowest retention force values when compared to Co-Cr alloy in each undercut, but with significant difference only for the 0.50-mm undercut; and both materials maintained the retentive capacity during the simulation test.

Comparative study of chemical and mechanical retentive systems for bonding of indirect composite resin to commercially pure titanium

This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (a=5%). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.

A quantitative and qualitative evaluation of reports of clinical trials published in six Brazilian dental journals indexed in the Scientific Electronic Library Online (SciELO)

INTRODUCTION: Open access publishing is becoming increasingly popular within the biomedical sciences. SciELO, the Scientific Electronic Library Online, is a digital library covering a selected collection of Brazilian scientific journals many of which provide open access to full-text articles.This library includes a number of dental journals some of which may include reports of clinical trials in English, Portuguese and/or Spanish. Thus, SciELO could play an important role as a source of evidence for dental healthcare interventions especially if it yields a sizeable number of high quality reports. OBJECTIVE: The aim of this study was to identify reports of clinical trials by handsearching of dental journals that are accessible through SciELO, and to assess the overall quality of these reports. MATERIAL AND METHODS: Electronic versions of six Brazilian dental Journals indexed in SciELO were handsearched at www.scielo.br in September 2008. Reports of clinical trials were identified and classified as controlled clinical trials (CCTs - prospective, experimental studies comparing 2 or more healthcare interventions in human beings) or randomized controlled trials (RCTs - a random allocation method is clearly reported), according to Cochrane eligibility criteria. CRITERIA TO ASSESS METHODOLOGICAL QUALITY INCLUDED: method of randomization, concealment of treatment allocation, blinded outcome assessment, handling of withdrawals and losses and whether an intention-to-treat analysis had been carried out. RESULTS: The search retrieved 33 CCTs and 43 RCTs. A majority of the reports provided no description of either the method of randomization (75.3%) or concealment of the allocation sequence (84.2%). Participants and outcome assessors were reported as blinded in only 31.2% of the reports. Withdrawals and losses were only clearly described in 6.5% of the reports and none mentioned an intention-to-treat analysis or any similar procedure. CONCLUSIONS: The results of this study indicate that a substantial number of reports of trials and systematic reviews are available in the dental journals listed in SciELO, and that these could provide valuable evidence for clinical decision making. However, it is clear that the quality of a number of these reports is of some concern and that improvement in the conduct and reporting of these trials could be achieved if authors adhered to internationally accepted guidelines, e.g. the CONSORT statement.

Surface and subsurface erosion of primary enamel by acid beverages over time

This study evaluated the influence of a cola-type soft drink and a soy-based orange juice on the surface and subsurface erosion of primary enamel, as a function of the exposure time. Seventy-five primary incisors were divided for microhardness test (n=45) or scanning electron microscopy (SEM) analysis (n=30). The specimens were randomly assigned to 3 groups: 1 - artificial saliva (control); 2 - cola-type soft drink; and 3 - soy-based orange juice. Immersion cycles in the beverages were undertaken under agitation for 5 min, 3 times a day, during 60 days. Surface microhardness was measured at 7, 15, 30, 45 and 60 days. After 60 days, specimens were bisected and subsurface microhardness was measured at 30, 60, 90, 120, 150 and 200 µm from the surface exposed. Data were analyzed by ANOVA and Tukey’s test (a=0.05). Groups 2 and 3 presented similar decrease of surface microhardness. Regarding subsurface microhardness, group 2 presented the lowest values. SEM images revealed that after 60 days the surfaces clearly exhibited structural loss, unlike those immersed in artificial saliva. It may be concluded that erosion of the surfaces exposed to the cola-type soft drink was more accentuated and directly proportional to the exposure time.

Effect of repeated disinfections by microwave energy on the physical and mechanical properties of denture base acrylic resins

The present study evaluated the effect of repeated simulated microwave disinfection on physical and mechanical properties of Clássico, Onda-Cryl and QC-20 denture base acrylic resins. Aluminum patterns were included in metallic or plastic flasks with dental stone following the traditional packing method. The powder/liquid mixing ratio was established according to the manufacturer's instructions. After water-bath polymerization at 74ºC for 9 h, boiling water for 20 min or microwave energy at 900 W for 10 min, the specimens were deflasked after flask cooling and finished. Each specimen was immersed in 150 mL of distilled water and underwent 5 disinfection cycles in a microwave oven set at 650 W for 3 min. Non-disinfected and disinfected specimens were subjected to the following tets: Knoop hardness test was performed with 25 g load for 10 s, impact strength test was done using the Charpy system with 40 kpcm, and 3-point bending test (flexural strength) was performed at a crosshead speed of 0.5 mm/min until fracture. Data were analyzed statistically by ANOVA and Tukey's test (α= 0.05%). Repeated simulated microwave disinfections decreased the Knoop hardness of Clássico and Onda-Cryl resins and had no effect on the impact strength of QC-20. The flexural strength was similar for all tested resins.

Bond strength of a pit-and-fissure sealant associated to etch-and-rinse and self-etching adhesive systems to saliva-contaminated enamel: individual vs. simultaneous light curing

This study evaluated in vitro the shear bond strength (SBS) of a resin-based pit-and-fissure sealant [Fluroshield (F), Dentsply/Caulk] associated with either an etch-and-rinse [Adper Single Bond 2 (SB), 3M/ESPE] or a self-etching adhesive system [Clearfil S3 Bond (S3), Kuraray Co., Ltd.] to saliva-contaminated enamel, comparing two curing protocols: individual light curing of the adhesive system and the sealant or simultaneous curing of both materials. Mesial and distal enamel surfaces from 45 sound third molars were randomly assigned to 6 groups (n=15), according to the bonding technique: I - F was applied to 37% phosphoric acid etched enamel. The other groups were contaminated with fresh human saliva (0.01 mL; 10 s) after acid etching: II - SB and F were light cured separately; III - SB and F were light cured together; IV - S3 and F were light cured separately; V - S3 and F were light cured simultaneously; VI - F was applied to saliva-contaminated, acid-etched enamel without an intermediate bonding agent layer. SBS was tested to failure in a universal testing machine at 0.5 mm/min. Data were analyzed by one-way ANOVA and Fisher's test (α=0.05).The debonded specimens were examined with a stereomicroscope to assess the failure modes. Three representative specimens from each group were observed under scanning electron microscopy for a qualitative analysis. Mean SBS in MPa were: I-12.28 (±4.29); II-8.57 (±3.19); III-7.97 (±2.16); IV-12.56 (±3.11); V-11.45 (±3.77); and VI-7.47 (±1.99). In conclusion, individual or simultaneous curing of the intermediate bonding agent layer and the resin sealant did not seem to affect bond strength to saliva-contaminated enamel. S3/F presented significantly higher SBS than the that of the groups treated with SB etch-and-rinse adhesive system and similar SBS to that of the control group, in which the sealant was applied under ideal dry, noncontaminated conditions.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1% NaOCl/17% EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% EDTA produced similar bond strength to that of untreated dentin.

Effect of eugenol-based endodontic sealer on the adhesion of intraradicular posts cemented after different periods

OBJECTIVE: This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. MATERIAL AND METHODS: Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pullout test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (α=0.001) RESULTS: There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement. CONCLUSIONS: It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation.

Adhesion of an endodontic sealer to dentin and gutta-percha: shear and push-out bond strength measurements and SEM analysis

The use of an adequate method for evaluation of the adhesion of root canal filling materials provides more reliable results to allow comparison of the materials and substantiate their clinical choice. The aims of this study were to compare the shear bond strength (SBS) test and push-out test for evaluation of the adhesion of an epoxy-based endodontic sealer (AH Plus) to dentin and gutta-percha, and to assess the failure modes on the debonded surfaces by means of scanning electron microscopy (SEM). Three groups were established (n=7): in group 1, root cylinders obtained from human canines were embedded in acrylic resin and had their canals prepared and filled with sealer; in group 2, longitudinal sections of dentin cylinders were embedded in resin with the canal surface smoothed and turned upwards; in group 3, gutta-percha cylinders were embedded in resin. Polyethylene tubes filled with sealer were positioned on the polished surface of the specimens (groups 2 and 3). The push-out test (group 1) and the SBS test (groups 2 and 3) were performed in an Instron universal testing machine running at crosshead speed of 1 mm/min. Means (±SD) in MPa were: G1 (8.8±1.13), G2 (5.9±1.05) and G3 (3.8±0.55). Statistical analysis by ANOVA and Student's t-test (a=0.05) revealed statistically significant differences (p<0.01) among the groups. SEM analysis showed a predominance of adhesive and mixed failures of AH Plus sealer. The tested surface affected significantly the results with the sealer reaching higher bond strength to dentin than to gutta-percha with the SBS test. The comparison of the employed methodologies showed that the SBS test produced significantly lower bond strength values than the push-out test, was skilful in determining the adhesion of AH Plus sealer to dentin and gutta-percha, and required specimens that could be easily prepared for SEM, presenting as a viable alternative for further experiments.

Clinical evaluation of desensitizing treatments for cervical dentin hypersensitivity

The aim of this study was to compare different treatments for dentin hypersensitivity in a 6-month follow-up. One hundred and one teeth exhibiting non carious cervical lesions were selected. The assessment method used to quantify sensitivity was the cold air syringe, recorded by the visual analogue scale (VAS), prior to treatment (baseline), immediately after topical treatment, after 1 week, 1, 3 and 6 months. Teeth were randomly assigned to five groups (n = 20): G1: Gluma Desensitizer (GD); G2: Seal&Protect (SP); G3: Oxa-gel (OG); G4: Fluoride (F); G5: Low intensity laser-LILT (660 nm/3.8 J/cm²/15 mW). Analysis was based on the non-parametric Kruskal-Wallis test that demonstrated statistical differences immediately after the treatment (p = 0.0165). To observe the individual effects of each treatment, data was submitted to Friedman test. It was observed that GD and SP showed immediate effect after application. Reduction in the pain level throughout the six-month follow-up was also observed. In contrast, LILT presented a gradual reduction of hypersensitivity. OG and F showed effects as of the first and third month respectively. It can be concluded that, after the 6-month clinical evaluation, all therapies showed lower VAS sensitivity values compared with baseline, independently of their different modes of action.

Effect of different polishing systems on the surface roughness of microhybrid composites

The use of composite resins in dentistry is well accepted for restoring anterior and posterior teeth. Many polishing protocols have been evaluated for their effect on the surface roughness of restorative materials. This study compared the effect of different polishing systems on the surface roughness of microhybrid composites. Thirty-six specimens were prepared for each composite $#91;Charisma® (Heraeus Kulzer), Fill Magic® (Vigodent), TPH Spectrum® (Dentsply), Z100® (3M/ESPE) and Z250® (3M/ESPE)] and submitted to surface treatment with Enhance® and PoGo® (Dentsply) points, sequential Sof-Lex XT® aluminum oxide disks (3M/ESPE), and felt disks (TDV) combined with Excel® diamond polishing paste (TDV). Average surface roughness (Ra) was measured with a mechanical roughness tester. The data were analyzed by two-way ANOVA with repetition of the factorial design and the Tukey-Kramer test (p<0.01). The F-test result for treatments and resins was high (p<0.0001 for both), indicating that the effect of the treatment applied to the specimen surface and the effect of the type of resin on surface roughness was highly significant. Regarding the interaction between polishing system and type of resin used, a p value of 0.0002 was obtained, indicating a statistically significant difference. A Ra of 1.3663 was obtained for the Sof-Lex/TPH Spectrum interaction. In contrast, the Ra for the felt disk+paste/Z250 interactions was 0.1846. In conclusion, Sof-Lex polishing system produced a higher surface roughness on TPH Spectrum resin when compared to the other interactions.