Synthesis, characterization and catalytic evaluation of cubic ordered mesoporous iron-silicon oxides

Iron was successfully incorporated in FDU-1 type cubic ordered mesoporous silica by a simple direct synthesis route. The (Fe/FDU-1) samples were characterized by Rutherford back-scattering spectrometry (RBS), small angle X-ray scattering (SAXS). N(2) sorption isotherm, X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). The resulting material presented an iron content of about 5%. Prepared at the usual acid pH of -0.3, the composite was mostly formed by amorphous silica and hematite with a quantity of Fe(2+) present in the structure. The samples prepared with adjusted pH values (2 and 3.5) were amorphous. The samples` average pore diameter was around 12.0 nm and BET specific surface area was of 680 m(2) g(-1). Although the iron-incorporated material presented larger lattice parameter, about 25 nm compared to pure FDU-1, the Fe/FDU-1 composite still maintained its cubic ordered fcc mesoporous structure before and after the template removal at 540 degrees C. The catalytic performance of Fe/FDU-1 was investigated in the catalytic oxidation of Black Remazol B dye using a catalytic ozonation process. The results indicated that Fe/FDU-1 prepared at the usual acid pH exhibited high catalytic activity in the mineralization of this pollutant when compared to the pure FDU-1. Fe(2)O(3) and Fe/FDU-1 prepared with higher pH of 2 and 3.5. (C) 2010 Elsevier B.V. All rights reserved.

Statistical analysis of the Doppler broadening coincidence spectrum of electron-positron annihilation radiation in silicon

We report a statistical analysis of Doppler broadening coincidence data of electron-positron annihilation radiation in silicon using a (22)Na source. The Doppler broadening coincidence spectrum was fit using a model function that included positron annihilation at rest with 1s, 2s, 2p, and valence band electrons. In-flight positron annihilation was also fit. The response functions of the detectors accounted for backscattering, combinations of Compton effects, pileup, ballistic deficit, and pulse-shaping problems. The procedure allows the quantitative determination of positron annihilation with core and valence electron intensities as well as their standard deviations directly from the experimental spectrum. The results obtained for the core and valence band electron annihilation intensities were 2.56(9)% and 97.44(9)%, respectively. These intensities are consistent with published experimental data treated by conventional analysis methods. This new procedure has the advantage of allowing one to distinguish additional effects from those associated with the detection system response function. (C) 2009 Elsevier B.V. All rights reserved.

Chemical bonding and composition of silicon nitride films prepared by inductively coupled plasma chemical vapor deposition

Thin silicon nitride films were prepared at 350 degrees C by inductively coupled plasma chemical vapor deposition on Si(100) substrates under different NH(3)/SiH(4) or N(2)/SiH(4) gas mixture. The chemical composition and bonding structure of the deposited films were investigated as a function of the process parameters, such as the gas flow ratio NH(3)/SiH(4) or N(2)/SiH(4) and the RF power, using X-ray photoelectron spectroscopy (XPS). The gas flow ratio was 1.4, 4.3, 7.2 or 9.5 and the RF power, 50 or 100 W. Decomposition results of Si 2p XPS spectra indicated the presence of bulk Si, under-stoichiometric nitride, stoichiometric nitride Si(3)N(4), oxynitride SiN(x)O(y), and stoichiometric oxide SiO(2), and the amounts of these compounds were strongly influenced by the two process parameters. These results were consistent with those obtained from N 1s XPS spectra. The chemical composition ratio N/Si in the film increased with increasing the gas flow ratio until the gas flow ratio reached 4.3, reflecting the high reactivity of nitrogen, and stayed almost constant for further increase in gas flow ratio, the excess nitrogen being rejected from the growing film. A considerable and unexpected incorporation of contaminant oxygen and carbon into the depositing film was observed and attributed to their high chemical reactivity. (C) 2010 Elsevier B.V. All rights reserved.

Oxygen-mediated electron transport through hybrid silicon-organic interfaces

We investigate from first principles the electronic and transport properties of hybrid organic/silicon interfaces of relevance to molecular electronics. We focus on conjugated molecules bonded to hydrogenated Si through hydroxyl or thiol groups. The electronic structure of the systems is addressed within density functional theory, and the electron transport across the interface is directly evaluated within the Landauer approach. The microscopic effects of molecule-substrate bonding on the transport efficiency are explicitly analyzed, and the oxygen-bonded interface is identified as a candidate system when preferential hole transfer is needed.

Confinement and surface effects in B and P doping of silicon nanowires

Several experimental groups have achieved effective n- and p-type doping of silicon nanowires (SiNWs). However, theoretical analyses on ultrathin SiNWs suggest that dopants tend to segregate to their surfaces, where they would combine with defects such as dangling bonds (DB), becoming electronically inactive. Using fully ab initio calculations, we show that the differences in formation energies among surface and core substitutional sites decrease rapidly as the diameters of the wires increase, indicating that the dopants will be uniformly distributed. Moreover, occurrence of the electronically inactive impurity/DB complex rapidly becomes less frequent for NWs of larger diameters. We also show that the high confinement in the ultrathin SiNWs causes the impurity levels to be deeper than in the silicon bulk, but our results indicate that for NWs of diameters larger than approximately 3 nm the impurity levels recover bulk characteristics. Finally, we show that different surfaces will lead to different dopant properties in the gap.

Energy States of Phosphorous Donor in Silicon in Fields up to 18 T

The evolution of the energy states of the phosphorous donor in silicon with magnetic field has been the subject of previous experimental and theoretical studies to fields of 10 T. We now present experimental optical absorption data to 18 T in combination with theoretical data to the same field. We observe features that are not revealed in the earlier work, including additional interactions and anti-crossings between the different final states. For example, according to the theory, for the ""1s -> 2p (+)"" transition, there are anti-crossings at about 5, 10, 14, 16, and 18 T. In the experiments, we resolve at least the 5, 10, and 14 T anti-crossings, and our data at 16 and 18 T are consistent with the calculations.

Structural-electronic aspects related to the near-infrared light emission of Fe-doped silicon films

The need of efficient (fast and low consumption) optoelectronic devices has always been the driving force behind the investigation of materials with new or improved properties. To be commercially attractive, however, these materials should be compatible with our current micro-electronics industry and/or telecommunications system. Silicon-based compounds, with their matured processing technology and natural abundance, partially comply with such requirements-as long as they emit light. Motivated by these issues, this work reports on the optical properties of amorphous Si films doped with Fe. The films were prepared by sputtering a Si+Fe target and were investigated by different spectroscopic techniques. According to the experimental results, both the Fe concentration and the thermal annealing of the samples induce changes in their atomic structure and optical-electronic properties. In fact, after thermal annealing at similar to 750 degrees C, the samples partially crystallize with the development of Si and/or beta-FeSi(2) crystallites. In such a case, certain samples present light emission at similar to 1500 nm that depends on the presence of beta-FeSi(2) crystallites and is very sensitive to the annealing conditions. The most likely reasons for the light emission (or absence of it) in the considered Fe-doped Si samples are presented and discussed in view of their main structural-electronic characteristics. (C) 2011 Elsevier Ltd. All rights reserved.

Fano resonance in heavily doped porous silicon

Unexpectedly, the Fano resonance caused by the interference of continuum electron excitations with the longitudinal optical (LO) phonons was observed in random porous Si by Raman scattering. The analysis of the experimental data shows that the electron states trapped at the Si-SiO(2) interface dominate in the observed Raman scattering. The gap energy associated with the interface states was determined. Copyright (C) 2011 John Wiley & Sons, Ltd.

Characterization of anodic silicon oxide films grown in room temperature ionic liquids

The electroformation of silicon oxide was performed in two room temperature ionic liquids (RTIL), 1-butyl-3-methyl-imidazolium bis(trifluoromethane sulfonyl) imide (BMITFSI) and N-n-butyl-N-methylpiperidinium bis(trifluoromethane sulfonyl) imide (BMPTFSI). This phenomenon was studied by electrochemical techniques and it was observed that the oxide growth follows a high-field mechanism. X-ray Photoelectron Spectroscopy experiments have shown that a non-stoichiometric oxide film was formed, related to the low water content present in both RTILs (< 30 ppm). The roughness values obtained by using AFM technique of the silicon surface after etching with HF was 1.5 nm (RMS). The electrochemical impedance spectroscopy at low frequencies range was interpreted as a resistance in parallel with a CPE element, the capacitance obtained was associated with the dielectric nature of the oxide formed and the resistance was interpreted considering the chemical dissolution of the oxide by the presence of the TFSI anion. The CPE element was associated with the surface roughness and the very thin oxide film obtained. (C) 2007 Elsevier Ltd. All rights reserved.

Immobilization of Catalysts of Biological Interest on Porous Oxidized Silicon Surfaces

The present paper deals with the immobilization of redox mediators and proteins onto protected porous silicon surfaces to obtain their direct electrochemical reactions and to retain their bioactivities. This paper shows that MP-11 and viologens are able to establish chemical bonds with 3-aminopropyltriethoxylsilane-modified porous silicon surface. The functionalization of the surfaces have been fully characterized by energy dispersive X-ray analysis (EDX) and X-ray photoelectron spectroscopy (XPS) to examine the immobilization of these mediators onto the solid surface. Amperometric and open circuit potential measurements have shown the direct electron transfer between glucose oxidase and the electrode in the presence of the viologen mediator covalently linked to the 3-aminopropyltriethoxylsilane (APTES)-modified porous silicon surfaces.

Photocatalytic decomposition of methylene blue via Fenton mechanisms by silicon wafer doped with Au and Cu: a theoretical and experimental study

In this work, we studied the photocatalytic and the structural aspects of silicon wafers doped with Au and Cu submitted to thermal treatment. The materials were obtained by deposition of metals on Si using the sputtering method followed by fast heating method. The photocatalyst materials were characterized by synchrotron-grazing incidence X-ray fluorescence, ultraviolet-visible spectroscopy, X-ray diffraction, and assays of H(2)O(2) degradation. The doping process decreases the optical band gap of materials and the doping with Au causes structural changes. The best photocatalytic activity was found for thermally treated material doped with Au. Theoretical calculations at density functional theory level are in agreement with the experimental data.

Influence of sodium hypochlorite and edta on the microtensile bond strength of a self-etching adhesive system

Chemical substances used during biomechanical preparation of root canals can alter the composition of dentin surface and affect the interaction with restorative materials. OBJECTIVE: The purpose of this study was to evaluate the microtensile bond strength (µTBS) of a self-etching adhesive system to dentin irrigated with sodium hypochlorite (NaOCl) and ethylenediaminetetraacetic acid (EDTA). MATERIAL AND METHODS: Thirty human third molars were sectioned 3 mm below the occlusal surface, polished with 600- to 1200-grit silicon carbide papers, and randomly divided into 3 groups: G1 (control): no irrigating solution; G2: 1% NaOCl; and G3: 1% NaOCl followed by the application of 17% EDTA. The specimens received the self-etching adhesive system (XENO III - Dentsply), restored with microhybrid composite resin (Z250 - 3M ESPE), sectioned and trimmed to create 4 hourglass-shaped slabs of each tooth. The slabs were tested in microtensile strength in a universal testing machine (Emic DL 2000) at a crosshead speed of 0.5 mm/min until fracture. The results were analyzed statistically by ANOVA and Newman-Keuls test. RESULTS: Mean µTBS values and standard deviations in MPa were: G1 = 11.89 ± 4.22; G2 = 19.41 ± 5.32; G3 = 11.34 ± 4.73. 1% NaOCl increased the adhesive resistance significantly (p<0.001/F=22.5763). The application of 1% NaOCl/17% EDTA resulted in statistically similar µTBS to the control group. CONCLUSIONS: None of the irrigants affected negatively the µTBS of XENO III to dentin. The use of 1% NaOCl alone resulted in higher bond strength than the other treatments. The combination of 1% NaOCl and 17% EDTA produced similar bond strength to that of untreated dentin.

Effect of silicate fertilization on soil and on palisade grass plants under grazing intensities

Application of calcium silicate (SiCa) as soil acidity corrective was evaluated in a Rhodic Hapludox soil with palisade grass conducted under pasture rotation system with different grazing intensities. Experimental design was complete randomized blocks with four grazing intensities - grazing intensities were imposed by forage supply (50, 100, 150 and 200 kg t-1 of DM per LW) - in experimental plots with four replicates and, in the subplots, with seven doses of calcium silicate combined with lime: 0+0, 2+0, 4+0, 6+0, 2+4, 4+2 and 0+6 t ha-1, respectively. In the soil, it was evaluated the effect of four levels of calcium silicate (0, 2, 4 and 6 t ha-1) at 45, 90, and 365 days at three depths (0-10, 10-20 and 20-40 cm) and at 365 days, it was included one level of lime (6 t ha-1). For determination of leaf chemical composition and silicate content in the soil, four levels of calcium silicate (0, 2, 4 and 6 t ha-1) were evaluated at 45 and 365 days and at 45 days only for leaf silicate, whereas for dry matter production, all corrective treatments applied were evaluated in evaluation seasons. Application of calcium silicate was positive for soil chemical traits related to acidity correction (pH(CaCl2), Ca, Mg, K, H+Al and V), but the limestone promoted better results at 365 days. Leaf mineral contents were not influenced by application of calcium silicate, but there was an increase on silicate contents in leaves and in the soil. Dry matter yield and chemical composition of palisade grass improved with the application of correctives.

Efeito residual da silicatagem no solo e na produtividade do capim-marandu sob pastejo

A escória siderúrgica é uma alternativa para a correção da acidez dos solos e é constituída de silicato de cálcio. Neste estudo, avaliaram-se os efeitos residuais da aplicação de silicato de cálcio nos atributos químicos do solo e da planta em Latossolo Vermelho distroférrico típico com capim-Marandu (Brachiaria brizantha cv. Marandu), sob intensidades de pastejo em lotação rotacionada. O delineamento experimental foi de blocos ao acaso, com intensidades de pastejo avaliadas pelas ofertas diárias de forragem de 50, 100, 150 e 200 kg t-1 de MS por PV nas parcelas experimentais, enquanto a aplicação superficial de silicato de cálcio combinado com calcário dolomítico, respectivamente, nas doses 0 + 0; 2 + 0; 4 + 0; 6 + 0; 2 + 4; 4 + 2 e 0 + 6 t ha- 1 nas subparcelas com quatro repetições, duas épocas (verão e inverno) e avaliação em três profundidades do solo (0-10, 10-20 e 20-40 cm). Os atributos químicos do solo pH em CaCl2, Ca, Mg, K, H + Al e V, avaliados 720 dias após a aplicação, apresentaram resultados favoráveis do poder residual do silicato de Ca e do calcário. A oferta de forragem 200 kg t-1 e o tratamento somente com calcário dolomítico (0 + 6 t ha-1) elevaram o valor de pH em CaCl2 e o V, principalmente na camada de 0-10 cm. Os teores de Si no solo foram influenciados pelas doses aplicadas de silicato de Ca, apesar de não terem causado alterações significativas nos teores foliares de Si. A composição químico-bromatológica foi afetada somente pelas ofertas e épocas. As ofertas, épocas e a interação época x oferta resultaram em efeitos na produção de matéria seca no pré-pastejo, com maiores produções para a oferta 200 kg t-1 e menores para a de 50 kg t-1 nas duas épocas. O resíduo (pós-pastejo) foi influenciado pelas ofertas e épocas. As ofertas 50 e 100 kg t-1 e o tratamento com 2 t ha-1 de silicato de Ca promoveram as maiores taxas de acúmulo de matéria seca.

Filmes ultrafinos de ésteres de celulose: preparo, caracterização e imobilização de proteínas

In this study cellulose acetate butyrate (CAB) and carboxymehtylcellulose acetate butyrate (CMCAB) films adsorbed onto silicon wafers were characterized by means of ellipsometry, atomic force microscopy (AFM), sum frequency generation spectroscopy (SFG) and contact angle measurements. The adsorption behavior of lysozyme (LIS) or bovine serum albumin (BSA) onto CAB and CMCAB films was investigated. The amounts of adsorbed LIS or BSA onto CMCAB films were more pronounced than those onto CAB films due to the presence of carboxymethyl group in the CMCAB structure. Besides, the adsorption of BSA molecules on CMCAB films was more favored than that of LIS molecules. Antimicrobial effect of LIS bound to CAB or CMCAB layers was evaluated using Micrococcus luteus as substrate.