Comparison of dentin root canal permeability and morphology after irradiation with Nd:YAG, Er:YAG, and diode lasers

The aim of this study was to compare the effects of Nd:YAG, Er:YAG, and diode lasers on the morphology and permeability of root canal walls. The three laser wavelengths mentioned interact differently with dentin and therefore it is possible that the permeability changes caused will determine different indications during endodontic treatment. Twenty-eight human single-rooted teeth were instrumented up to ISO 40 and divided into four groups: group C, control (GC), non-laser irradiated; group N (GN), irradiated with Nd:YAG laser; group E (GE), with Er:YAG laser and group D (GD) with diode laser. After that, the roots were filled with a 2% methylene blue dye, divided into two halves and then photographed. The images were analyzed using Image J software and the percentage of dye penetration in the cervical, middle, and apical root thirds were calculated. Additional scanning electron microscopy (SEM) analyses were also performed. The analysis of variance (ANOVA) showed significant permeability differences between all groups in the middle and cervical thirds (p < 0.05). The Tukey test showed that in the cervical third, GN presented means of dye penetration statistically significantly lower than all of the other groups. In the middle third, GE and GD showed statistically higher dye penetration means than GC and GN. SEM analysis showed melted surfaces for GN, clean wall surfaces with open dentinal tubules for GE, and mostly obliterated dentinal tubules for GD. Er:YAG (2,094 nm) laser and diode laser (808 nm) root canal irradiation increase dentinal permeability and Nd:YAG (1,064 nm) laser decreases dentin permeability, within the studied parameters.

Effect of argon purity on mechanical properties, microstructure and fracture mode of commercially pure (cp) Ti and Ti-6Al-4V alloys for ceramometal dental prostheses

Provision of an inert gas atmosphere with high-purity argon gas is recommended for preventing titanium castings from contamination although the effects of the level of argon purity on the mechanical properties and the clinical performance of Ti castings have not yet been investigated. The purpose of this study was to evaluate the effect of argon purity on the mechanical properties and microstructure of commercially pure (cp) Ti and Ti-6Al-4V alloys. The castings were made using either high-purity and/or industrial argon gas. The ultimate tensile strength (UTS), proportional limit (PL), elongation (EL) and microhardness (VHN) at different depths were evaluated. The microstructure of the alloys was also revealed and the fracture mode was analyzed by scanning electron microscopy. The data from the mechanical tests and hardness were subjected to a two-and three-way ANOVA and Tukey`s test (alpha = 0.05). The mean values of mechanical properties were not affected by the argon gas purity. Higher UTS, PL and VHN, and lower EL were observed for Ti-6Al-4V. The microhardness was not influenced by the argon gas purity. The industrial argon gas can be used to cast cp Ti and Ti-6Al-4V.

Effect of processing induced particle alignment on the fracture toughness and fracture behavior of multiphase dental ceramics

Objective. To investigate the processing induced particle alignment on fracture behavior of four multiphase dental ceramics (one porcelain, two glass-ceramics and a glass-infiltrated-alumina composite). Methods. Disks (empty set12mm x 1.1 mm-thick) and bars (3 mm x 4 mm x 20 mm) of each material were processed according to manufacturer instructions, machined and polished. Fracture toughness (K(IC)) was determined by the indentation strength method using 3-point bending and biaxial flexure fixtures for the fracture of bars and disks, respectively. Microstructural and fractographic analyses were performed with scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction. Results. The isotropic microstructure of the porcelain and the leucite-based glass-ceramic resulted in similar fracture toughness values regardless of the specimen geometry. On the other hand, materials containing second-phase particles with high aspect ratio (lithium disilicate glass-ceramic and glass-infiltrated-alumina composite) showed lower fracture toughness for disk specimens compared to bars. For the lithium disilicate glass-ceramic disks, it was demonstrated that the occurrence of particle alignment during the heat-pressing procedure resulted in an unfavorable pattern that created weak microstructural paths during the biaxial test. For the glass-infiltrated-alumina composite, the microstructural analysis showed that the large alumina platelets tended to align their large surfaces perpendicularly to the direction of particle deposition during slip casting of green preforms. Significance. The fracture toughness of dental ceramics with anisotropic microstructure should be determined by means of biaxial testing, since it results in lower values. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Durability of Enamel Bonding Using One-step Self-etch Systems on Ground and Unground Enamel

Objective: To examine the morphological, early and long-term microtensile bond strengths (mu TBS) of one-step self-etch systems to unground and ground enamel. Materials and Methods: Resin composite (Filtek Z250) buildups were bonded to the buccal and lingual enamel surfaces (unground, bur-cut or SiC-roughened enamel) of third molars after adhesive application using the following adhesives: Clearfil S(3) Bond (CS3); Adper Prompt L-Pop (ADP); iBond (iB) and, as the control, Clearfil SE Bond (CSE). Six tooth halves were assigned for each condition. After storage in water (24 hours/37 degrees C), the bonded specimens were sectioned into beams (0.8 mm(2)) and subjected to pTBS (0.5 mm/min) either immediately (IM) or after six (6M) or 12 months (12M) of water storage. The data were analyzed by three-way repeated measures ANOVA and Tukey`s test (alpha=0.05). Surface conditioning was observed under scanning electron microscopy (SEM). Results: The mu TBS in the Si-C paper and diamond bur groups were similar and higher than the unground group. No significant difference was observed among the different storage periods, except for CS3, which showed an increase in the pTBS after 12M. The etching pattern was more retentive on ground enamel. Conclusions: One-step self-etch adhesives showed higher bond strengths on ground enamel and no reductions in resin-enamel bonds were observed after 12M of water storage.

Adhesive Temperature: Effects on Adhesive Properties and Resin-Dentin Bond Strength

Objectives: To evaluate the effect of adhesive temperature on the resin-dentin bond strength (mu TBS), nanoleakage (NL), adhesive layer thickness (AL), and degree of conversion (DC) of ethanol/water- (SB) and acetone-based (PB) etch-and-rinse adhesive systems. Methods: The bottles of the two adhesives were kept at each temperature (5 degrees C, 20 degrees C, 37 degrees C, and 50 degrees C) for 2 hours before application to demineralized dentin surfaces of 40 molars. Specimens were prepared for mu TBS testing. Bonded sticks (0.8 mm(2)) were tested under tension (0.5 mm/min). Three bonded sticks from each tooth were immersed in silver nitrate and analyzed by scanning electron microscopy. The DC of the adhesives was evaluated by Fourier transformed infrared spectroscopy. Results: Lower mu TBS was observed for PB at 50 degrees C. For SB, the mu TBS values were similar for all temperatures. DC was higher at 50 degrees C for PB. Higher NL and thicker AL were observed for both adhesives in the 5 degrees C and 20 degrees C groups compared to the 37 degrees C and 50 degrees C groups. The higher temperatures (37 degrees C or 50 degrees C) reduced the number of pores within the adhesive layer of both adhesive systems. Conclusions: It could be useful to use an ethanol/water-based adhesive at 37 degrees C or 50 degrees C and an acetone-based adhesive at 37 degrees C to improve adhesive performance.

Effect of prolonged erosive pH cycling on different restorative materials

This in vitro study evaluated the effect of a prolonged erosive pH cycling on the superficial microhardness change (SMHC) and the erosive wear of different restorative materials. Eighty enamel specimens with prepared cavities of 1.5 x 1.5 mm were randomly divided into eight groups according to the restorative materials used for the fillings (RMGI - resin-modified glass-ionomer, CGI - conventional glass-ionomer, CR- composite resin, A - amalgam) and immersion media used (ERO - erosive medium or SAL - artificial saliva). During 35 days, half of the specimens were immersed in a cola drink (ERO), for 5 min, three times a day, and they remained in SAL between the erosive cycles. The other half of the specimens was immersed in SAL only, for the entire experimental period (control). Data were tested for significant differences by anova and Tukey`s tests (P < 0.05). Scanning electron microscopy images were made to illustrate the enamel erosive wear and restorative materials alterations. The mean SMHC (%) and mean erosive wear (mu m) of the materials were: RMGI-ERO (30/0.5); CGI-ERO (37/0.5); CR-ERO (-0.3/0.3); A-ERO (-4/0.3); RMGI-SAL (4/0.4); CGI-SAL (-6/0.4); CR-SAL (-3/0.2) and A-SAL (2/0.4). Scanning electron microscopy images showed pronounced enamel erosive wear on groups submitted to erosive pH cycling when compared with groups maintained in saliva. In conclusion, the prolonged pH cycling promoted significantly higher alterations (SMHC and erosive wear) on the glass-ionomer cements than the CR and amalgam.

Compromised Bond Strength after Root Dentin Deproteinization Reversed with Ascorbic Acid

Introduction: The present study evaluated the effect of a reducing agent on the bond strength of deproteinized root canal dentin surfaces when using a self-adhesive versus dual-cured cement. Regional differences were also evaluated. Methods: A total of 45 bovine incisor roots were divided into 3 groups: irrigation with physiologic solution (control), 10-minute deproteinization with 5% NaOCl, and 10-minute deproteinization with 5% NaOCl followed by 10 minutes of 10% ascorbic acid. Fiber posts were cemented with either RelyX 0100 or RelyX ARC (with SingleBond 2 or Clearfil SE Bond). The push-out bond strength was evaluated after 24 hours of storage. Data were submitted to three-way analyses of variance and Dunnett 13 tests (alpha = 0.05). Results: No differences between cements were observed within the testing conditions, regardless of the adhesive (P < .05). Deproteinization reduced bond strengths. Subsequent treatment with ascorbic acid was capable of reversing bond strength value changes to levels similar to those of controls. Regional radicular differences were also found, where coronal > middle > apical. Conclusions: The reducing agent was capable. of reversing the effect of dentin deproteinization, and RelyX U100 behaved similarly to RelyX ARC. (J Endod 2010;36:130-134)

SEM observation of the bond integrity of fiber-reinforced composite posts cemented into root canals

Objectives. To test the null hypothesis that continuity of resin cement/dentin interfaces is not affected by location along the root canal walls or water storage for 3 months when bonding fiber posts into root canals. Methods. Fiber posts were luted to bovine incisors using four resinous luting systems: Multilink, Variolink II, Enforce Dual and Enforce PV. After cementation, roots were longitudinally sectioned and epoxy resin replicas were prepared for SEM analysis (baseline). The original halves were immersed in solvent, replicated and evaluated. After 3 months water storage and a second solvent immersion, a new set of replicas were made and analyzed. The ratio (%) between the length (mm) of available bonding interface and the actual extension of bonded cement/dentin interface was calculated. Results. Significant lower percent values of bond integrity were found for Multilink (8.25%) and Variolink 11 (10.08%) when compared to Enforce Dual (25.11%) and Enforce PV (27.0%) at baseline analysis. The same trend was observed after immersion in solvent, with no significant changes. However, bond integrity was significantly reduced after 3 months water storage and a second solvent immersion to values below 5% (Multilink = 3.31%, Variolink=1.87%, Enforce Dual=1.20%, and Enforce PV=0.75%). The majority of gaps were depicted at the apical and middle thirds at baseline and after immersion in solvent. After 3 months, gaps were also detected at the cervical third. Significance. Bond integrity at the cement/dentin interface was surprisingly low after cementation of fiber posts to root canals with all resin cements. That was not significantly altered after immersion in solvent, but was further compromised after 3 months water storage. Gaps were mainly seen at middle and apical thirds throughout the experiment and extended to the cervical third after water storage for 3 months. Bond integrity of fiber posts luted to root canals was affected both by location and water storage. (C) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical Testing of Indirect Composite Materials Directly Applied on Implant Abutments

Purpose: To test the strength to failure and fracture mode of three indirect composite materials directly applied onto Ti-6Al-4V implant abutments vs cemented standard porcelain-fused-to-metal (PFM) crowns. Materials and Methods: Sixty-four locking taper abutments were randomly allocated to four groups and were cleaned in ethanol in an ultrasonic bath for 5 min. After drying under ambient conditions, the abutments were grit blasted and a custom 4-cusp molar crown mold was utilized to produce identical crowns (n = 16 per group) of Tescera (Bisco), Ceramage (Shofu), and Diamond Crown (DRM) according to the manufacturer`s instructions. The porcelain-fused-to-metal crowns were fabricated by conventional means involving the construction and a wax pattern and casting of a metallic coping followed by sintering of increasing layers of porcelain. All crowns were loaded to failure by an indenter placed at one of the cusp tips at a 1 mm/min rate. Subsequently, fracture analysis was performed by means of stereomicroscopy and scanning electron microscopy. One-way ANOVA at 95% level of significance was utilized for statistical analysis. Results: The single load to failure (+/- SD) results were: Tescera (1130 +/- 239 N), Ceramage (1099 +/- 257 N), Diamond Crown (1155 +/- 284 N), and PFM (1081 +/- 243 N). Stereomicroscopy analysis showed two distinct failure modes, where the loaded cusp failed either with or without abutment/metallic coping exposure. SEM analysis of the fractures showed multiple crack propagation towards the cervical region of the crown below a region of plastic deformation at the indenter contact region. Conclusion: The three indirect composites and PFM systems fractured at loads higher than those typically associated with normal occlusal function. Although each material had a different composition and handling technique, no significant differences were found concerning their single load to fracture resistance among composite systems and PFM.

Cytotoxic Effects of Different Concentrations of a Carbamide Peroxide Bleaching Gel on Odontoblast-Like Cells MDPC-23

This study evaluated the cytotoxic effects of a carbamide peroxide (CP) bleaching gel at different concentrations on odontoblast-like cells. Immortalized cells of the MDPC-23 cell line (30,000 cells/cm(2)) were incubated for 48 h. The bleaching gel was diluted in DMEM culture medium originating extracts with different CP concentrations. The amount (mu g/mL) of hydrogen peroxide (H(2)O(2)) released from each extract was measured by the leukocrystal violet/horseradish peroxidase enzyme assay. Five groups (n = 10) were formed according to the CP concentration in the extracts: G1-DMEM (control); G2-0.0001 % CP (0.025 mu g/mL H(2)O(2)); G3-0.001% CP (0.43 mu g/mL H(2)O(2)); G4-0.01% CP (2.21 mu g/mL H(2)O(2)); and G5-0.1 % CP (29.74 mu g/mL H(2)O(2)). MDPC-23 cells were exposed to the bleaching gel extracts for 60 min and cell metabolism was evaluated by the NITT assay. Data were analyzed statistically by one-way ANOVA and Tukey`s test (alpha = 0.05). Cell morphology was examined by scanning electron microscopy. The percentages of viable cells were as follows: G1, 100%; G2, 89.41%; G3, 82.4%; G4, 61.5%; and G5, 23.0%. G2 and G3 did not differ significantly (p > 0.05) from G1. The most severe cytotoxic effects were observed in G3 and G4. In conclusion, even at low concentrations, the CP gel extracts presented cytotoxic effects. This cytotoxicity was dose-dependent, and the 0.1% CP concentration caused the most intense cytopathic effects to the MDPC-23 cells. (C) 2009 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 9013: 907-912, 2009

Effect of framework design on crown failure

This study evaluated the effect of core-design modification on the characteristic strength and failure modes of glass-infiltrated alumina (In-Ceram) (ICA) compared with porcelain fused to metal (PFM). Premolar crowns of a standard design (PFMs and ICAs) or with a modified framework design (PFMm and ICAm) were fabricated, cemented on dies, and loaded until failure. The crowns were loaded at 0.5 mm min(-1) using a 6.25 mm tungsten-carbide ball at the central fossa. Fracture load values were recorded and fracture analysis of representative samples were evaluated using scanning electron microscopy. Probability Weibull curves with two-sided 90% confidence limits were calculated for each group and a contour plot of the characteristic strength was obtained. Design modification showed an increase in the characteristic strength of the PFMm and ICAm groups, with PFM groups showing higher characteristic strength than ICA groups. The PFMm group showed the highest characteristic strength among all groups. Fracture modes of PFMs and of PFMm frequently reached the core interface at the lingual cusp, whereas ICA exhibited bulk fracture through the alumina core. Core-design modification significantly improved the characteristic strength for PFM and for ICA. The PFM groups demonstrated higher characteristic strength than both ICA groups combined.

Physicochemical Properties of Methacrylate Resin-based Root Canal Sealers

Introduction: This study assessed in vitro the physicochemical properties of 2 methacrylate resin-based sealers (Epiphany SE and Hybrid Root SEAL), comparing the results with a well-established epoxy resin-based sealer (AH Plus). Methods: Five samples of each material were used for each test (setting time, flow, radiopacity, dimensional change after setting, and solubility) according to American National Standards Institute/American Dental Association (ANSI/ADA) Specification 57. The samples were assigned to 3 groups: I, AH Plus; II, Epiphany SE; and III, Hybrid Root SEAL. The distilled and deionized water used at the solubility test was submitted to atomic absorption spectrometry to observe the presence of Ca2+, K+, Ni2+, and Zn2+ ions. In addition, the surface morphology of the specimens was analyzed by means of scanning electron microscopy (SEM). Statistical analysis was performed by using one-way analysis of variance and Tukey-Kramer test (P < .05). Results: Flow, radiopacity, and solubility of all sealers were in accordance with ANSI/ADA. The setting time of Hybrid Root SEAL did not agree with ANSUADA requirements. The dimensional change of all sealers was greater than the values considered acceptable by ANSI/ADA. The spectrometry analysis showed significant Ca2+ ions release for AH Plus. In SEM analysis, Hybrid Root SEAL presented spherical monomers with inferior size than AH Plus and Epiphany SE. Conclusions: It might be concluded that physicochemical properties of the tested sealers conformed to ANSI/ADA (2000) standardization, except for the setting time of Hybrid Root SEAL and the dimensional change of all sealers, which did not fulfill the ANSI/ADA requirements. (J Endod 2010;36:1531-1536)

Push-out strength of methacrylate resin-based sealers to root canal walls

P>Aim To assess the push-out strength of Epiphany SE, Epiphany and Hybrid Root SEAL to the dentine walls of root canals. Methodology Sixty roots of canines were prepared and distributed to six groups (n = 10) according to the filling material: GI - Epiphany SE, GII - Epiphany primer and sealer, GIII - Epiphany primer, sealer and resinous solvent, GIV - Clearfil DC Bond and Epiphany sealer, GV - Clearfil, Epiphany sealer and solvent and GVI - Hybrid Root SEAL. Resilon cones were used in all groups. Roots were sectioned transversally to obtain three slices from each third. One slice was subjected to the push-out test (MPa), and results were analysed by anova and Tukey`s test (P < 0.05). The other two slices were prepared for scanning electron microscopy (SEM). Failure mode was also analysed. Results A statistically significant difference (P < 0.05) occurred between Hybrid Root SEAL (5.27 +/- 2.07) and the other materials, GI (0.40 +/- 0.23), GII (0.78 +/- 0.45), GIII (0.57 +/- 0.28), GIV (0.40 +/- 0.24) and GV (0.50 +/- 0.41), which did not differ significantly from each other (P > 0.05). Adhesive failures predominated in groups I, II, IV and V, whilst mixed and cohesive failures were the most frequent in groups III and VI, respectively. There were gaps in the adhesive interface of GI and GII, continuity areas of the filling material with dentine in GIV and GV and good adaptation of the interface of GVI. Conclusion Hybrid Root SEAL had greater push-out strength to root canal dentine than Epiphany SE and Epiphany. The use of primer, solvent and adhesive system did not influence the adhesion of Epiphany.

Influence of the irradiation distance and the use of cooling to increase enamel-acid resistance with Er:YAG laser

Objectives: The aim of this study was to assess the influence of irradiation distance and the use of cooling in the Er:YAG laser efficacy in preventing enamel demineralization. Methods: 84 enamel blocks were randomly assigned to seven groups (n = 12): G1: control group - no treatment, G2-G7: experimental groups treated with Er:YAG laser (80 mJ/2 Hz) at different irradiation distances with or without cooling: G2: 4 mm/2 mL; G3: 4 mm/no cooling; G4: 8 mm/2 mL; G5: 8 mm/no cooling; G6: 16 mm/2 mL; G7: 16 mm/no cooling. The samples were submitted to an in vitro pH cycles for 14 days. Next, the specimens were sectioned in sections of 80-100 mu m in thickness and the demineralization patterns of prepared slices were assessed using a polarized light microscope. Three samples from each group were analyzed with scanning electronic microscopy. Analysis of variance and the Fisher test were performed for the statistical analysis of the data obtained from the caries-lesion-depth measurements (CLDM) (alpha = 5%). Results: The control group (CLDM = 0.67 mm) was statistically different from group 2 (CLDM = 0.42 mm), which presented a smaller lesion depth, and group 6 (0.91 mm), which presented a greater lesion depth. The results of groups 3 (CLDM = 0.74 mm), 4 (CLDM = 0.70 mm), 5 (CLDM = 0.67 mm) and 7 (CLDM = 0.89 mm) presented statistical similarity. The scanning electronic microscopy analysis showed ablation areas in the samples from groups 4, 5, 6 and 7, and a slightly demineralized area in group 2. Conclusions: It was possible to conclude that Er:YAG laser was efficient in preventing enamel demineralization at a 4-mm irradiation distance using cooling. (C) 2010 Elsevier Ltd. All rights reserved.

Composite filling removal with erbium:yttrium-aluminum-garnet laser: morphological analyses

Considering the increase in esthetic restorative materials and need for improvement in unsatisfactory restoration substitution with minimal inadvertent removal of healthy tissues, this study assessed the efficacy of erbium:yttrium-aluminum-garnet (Er:YAG) laser for composite resin removal and the influence of pulse repetition rate on the morphological analyses of the cavity by scanning electron microscope. Composite resin fillings were placed in cavities (1.0 mm deep) prepared in bovine teeth, and the 75 specimens were randomly assigned to five groups according to the technique used for composite filling removal (high-speed diamond bur, group I, as a control, and Er:YAG laser, 250 mJ output energy and 80 J/cm(2) energy density, using different pulse repetition rates: group II, 2 Hz; group III, 4 Hz; group IV, 6 Hz; group V, 10 Hz). After the removal, the specimens were split in the middle, and we analyzed the surrounding and deep walls to check for the presence of restorative material. The estimation was qualitative. The surfaces were examined with a scanning electron microscope. The results revealed that the experimental groups presented bigger amounts of remaining restorative material. The scanning electron microscopy (SEM) analyses showed irregularities of the resultant cavities of the experimental groups that increased proportionally with increase in repetition rate.