The Effect of Framework Design on Fracture Resistance of Metal-Ceramic Implant-Supported Single Crowns

This study evaluated the effect of framework design on the fracture resistance of metal-ceramic implant-supported crowns. Screw-retained molar crowns with a screw access hole composed of metal or porcelain were compared to a cement-retained crown (control). For each group (n = 10), five crowns were subjected to dynamic loading (1,200,000 x 100 N x 2 Hz at 37 degrees C). Afterward, all specimens were loaded to failure using a universal testing machine. Significant differences could be established between the cement-and screw-retained groups (P <= .05), but no difference was found between the screw-retained groups and the specimens subjected to dynamic loading. Occlusal discontinuity of screw-retained crowns affects their resistance, and the metallic support on the screw access hole did not reinforce the crowns. Int J Prosthodont 2010;23:350-352.

Reliability and Failure Modes of Implant-Supported Y-TZP and MCR Three-Unit Bridges

Purpose: Chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (yttria-tetragonal zirconia polycrystals [Y-TZP]) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus palladium-silver alloy (PdAg) three-unit bridges. Materials and Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n = 21 each), were fabricated, veneered, cemented (n = 3 each), and Hertzian contact-tested to obtain ultimate failure load. In each framework group, 18 specimens were distributed across three step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (two-sided at 90% confidence intervals) for a ""mission"" of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft, Tucson, AZ, USA). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusions: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300 N. Failure modes differed between materials.

Implant Abutment Deformation During Prosthetic Cylinder Screw Tightening: An In Vitro Study

Purpose: Nonpassive fit frameworks are believed to lead to implant overload and consequently loss of osseointegration. This is one of the most commonly reported failures of implant prostheses. In an ideal situation of passive fit, when torque is applied to bring the abutment-cylinder interface together some amount of deformation can be expected, and it should be homogeneous along the periphery of the abutment. The aim of this study was to verify the amount of abutment deformation that can be expected when a free-standing cylinder is screwed into place. This could give insight into what should be accepted as passive fit. Materials and Methods: Strain gauges were bonded to the sides of five standard abutments that had machined palladium-silver cylinders or cobalt-chromium cast cylinders screwed into place. Measurements were taken to verify the deformation at each site. Results: Values of abutment deformation after abutment screw tightening ranged from -127.70 to -590.27 mu epsilon. The deformation recorded for palladium-silver prosthetic cylinder tightening ranged from 56.905 to -381.50 mu epsilon (mean: 173.298 mu epsilon) and from -5.62638 to -383.86 mu epsilon ( mean: 200.474 mu epsilon) for cobalt-chromium cylinders. There was no statistically significant difference among the two groups. Conclusion: Both abutment screw tightening and prosthetic cylinder screw tightening result in abutment deformation, which is compressive most of the time. Int J Prosthodont 2009; 22: 391-395.

Effect of cantilever length and framework alloy on the stress distribution of mandibular-cantilevered implant-supported prostheses

The purpose of this in vitro study was to analyze the stress distribution on components of a mandibular-cantilevered implant-supported prosthesis with frameworks cast in cobalt-chromium (Co-Cr) or palladium-silver (Pd-Ag) alloys, according to the cantilever length. Frameworks were fabricated on (Co-Cr) and (Pd-Ag) alloys and screwed into standard abutments positioned on a master-cast containing five implant replicas. Two linear strain gauges were fixed on the mesial and distal aspects of each abutment to capture deformation. A vertical static load of 100 N was applied to the cantilever arm at the distances of 10, 15, and 20 mm from the center of the distal abutment and the absolute values of specific deformation were recorded. Different patterns of abutment deformation were observed according to the framework alloy. The Co-Cr alloy framework resulted in higher levels of abutment deformation than the silver-palladium alloy framework. Abutment deformation was higher with longer cantilever extensions. Physical properties of the alloys used for framework interfere with abutment deformations patterns. Excessively long cantilever extensions must be avoided. To cite this article:Jacques LB, Moura MS, Suedam V, Souza EAC, Rubo JH. Effect of cantilever length and framework alloy on the stress distribution of mandibular-cantilevered implant-supported prostheses.Clin. Oral Impl. Res. 20, 2009; 737-741.doi: 10.1111/j.1600-0501.2009.01712.x.

Progressive recovery of osseoperception as a function of the combination of implant-supported prostheses

The extraction of teeth involves the elimination of extremely sensitive periodontal mechanoreceptors, which play an important role in oral sensory perception. Objectives: The aim of this study was to evaluate the recovery of interocclusal sensory perception for micro-thickness in individuals with different types of implant-supported prostheses. Materials and Methods: Wearers of complete dentures (CDs) comprised the negative control group (group A, n=17). The experimental group consisted of wearers of prostheses supported by osseointegrated implants (Group B, n=29), which was subsequently divided into 4 subgroups: B(1) (n=5) - implant supported overdentures (ISO) occluding with CD; B(2) (n=6) - implant-supported fixed prostheses (ISFP) occluding with CD; B3 (n=8) - wearers of maxillary and mandibular ISFP, and B(4) (n=10) - ISFP occluding with natural dentition (ND). Individuals with ND represented the positive control group (Group C, n=24). Aluminum foils measuring 10 mu m, 24 mu m, 30 mu m, 50 mu m, 80 mu m, and 104 mu m thickness were placed within the premolar area, adding up to 120 tests for each individual. Results: The mean tactile thresholds of groups A, B(1), B(2), B(3), B(4), and C were 92 mu m, 27 mu m, 27 mu m, 14 mu m, 10 mu m, and 10 mu m, respectively. [Correction added after publication online 18 April 2008: in the preceding sentence 92 mu m, 27 mu m, 14 mu m, 10 mu m and 10 mu m, was corrected to 92 mu m, 27 mu m, 27 mu m, 14 mu m, 10 mu m and 10 mu m.] The Kruskal-Wallis test revealed significant difference among groups (P < 0.05). The Dunn test revealed that group A was statistically different from groups C, B(3), and B(4), and that B(1) and B(2) were statistically different from group C. Conclusion: Progressive recovery of osseoperception as a function of the combination of implant-supported prostheses could be observed. Moreover, ISO and/or ISFP combinations may similarly maximize the recovery of osseoperception.

Survival of Dental Implants in the Cleft Area-A Retrospective Study

Objective To evaluate the survival rate of dental implants placed in the cleft area Design Retrospective study Setting Hospital for Rehabilitation of Craniofacial Anomalies, Brazil Institutional Tertiary Healthcare Center Patients 120 patients who received dental implants in the grafted cleft area in the years 1999 to 2005 Interventions Clinical data were evaluated from the records of 120 patients according to the following criteria placement grafted, cleft area, and age at surgery, age at placement of dental implants, site and dimension of implants, interval between placement of implants and the last clinical follow-up, and interval between placement and removal or indication for removal of implants Main Outcome Measures Percentage of survival rate of implants Results Mean age at placement of the bone graft was 17 6 years and 21 years at placement of implants A total of 123 cleft areas received secondary bone graft and bone graft to install implants (regraft) The mean survival rate was 34 months since placement of the implant to the last clinical follow-up and 26 months since placement of the prosthesis Seven dental implants were removed The survival rate since placement to the last clinical follow-up was 94 3% Conclusion Rehabilitation of the cleft area with dental implants is a viable and secure alternative, with good prognosis

Mechanical Testing of Indirect Composite Materials Directly Applied on Implant Abutments

Purpose: To test the strength to failure and fracture mode of three indirect composite materials directly applied onto Ti-6Al-4V implant abutments vs cemented standard porcelain-fused-to-metal (PFM) crowns. Materials and Methods: Sixty-four locking taper abutments were randomly allocated to four groups and were cleaned in ethanol in an ultrasonic bath for 5 min. After drying under ambient conditions, the abutments were grit blasted and a custom 4-cusp molar crown mold was utilized to produce identical crowns (n = 16 per group) of Tescera (Bisco), Ceramage (Shofu), and Diamond Crown (DRM) according to the manufacturer`s instructions. The porcelain-fused-to-metal crowns were fabricated by conventional means involving the construction and a wax pattern and casting of a metallic coping followed by sintering of increasing layers of porcelain. All crowns were loaded to failure by an indenter placed at one of the cusp tips at a 1 mm/min rate. Subsequently, fracture analysis was performed by means of stereomicroscopy and scanning electron microscopy. One-way ANOVA at 95% level of significance was utilized for statistical analysis. Results: The single load to failure (+/- SD) results were: Tescera (1130 +/- 239 N), Ceramage (1099 +/- 257 N), Diamond Crown (1155 +/- 284 N), and PFM (1081 +/- 243 N). Stereomicroscopy analysis showed two distinct failure modes, where the loaded cusp failed either with or without abutment/metallic coping exposure. SEM analysis of the fractures showed multiple crack propagation towards the cervical region of the crown below a region of plastic deformation at the indenter contact region. Conclusion: The three indirect composites and PFM systems fractured at loads higher than those typically associated with normal occlusal function. Although each material had a different composition and handling technique, no significant differences were found concerning their single load to fracture resistance among composite systems and PFM.

Characterisation of additional mental foramina through cone beam computed tomography

Variations in jaw bone neurovascularisation must be identified to decrease the potential risk for haemorrhages and neural disturbances during surgical procedures such as implant placement and orthognatic surgeries. The aim of this study is to characterise additional mental foramina (AMF) through cone beam computed tomography (CBCT) images, by describing their frequency, size, location and direction of their associated bony canals, as well as to assess their corresponding ipsilateral and contralateral mental foramina (MF). CBCT images from 285 patients were analysed. Prevalence of AMF was 9.4%. From 0 to 2 AMF were observed, with two bilateral cases. Two cases of unilateral absence of MF were registered. Patients presenting AMF did not differ significantly from those without AMF regarding gender, age or ethnicity. Diameters of AMF and their corresponding ipsilateral and contralateral MF were 1.9 mm (+/- 0.7 mm), 3.8 mm (+/- 0.6 mm) and 4.1 mm (+/- 0.6 mm), respectively. Ratios between diameters of AMF and corresponding ipsilateral MF ranged between 0.24 and 0.99. Location of AMF was variable, with most cases located posteriorly, posterior-inferiorly, posterior-superiorly or anterior-superiorly to their respective MF. Significant anatomical variability regarding neurovascularisation was observed among patients and CBCT examinations presented as a valuable tool for individually assessing these anatomical features.

Cleft Palate Obturation With Branemark Protocol Implant-Supported Fixed Denture and Removable Obturator

A 41-year-old man with cleft palate presented with a wide dehiscence and missing teeth. Six implants had been placed for fabrication of an overdenture, which was unsatisfactory. A bar was waxed and cast for connection to the implants; precision attachments were placed laterally for retention. A fixed partial denture was fabricated, and milled crowns were fabricated at the molar region to provide a guiding plane for insertion of a removable palatal obturator. Good swallowing and speech outcomes were achieved. This technique provided functional and esthetic benefits, enhanced oral hygiene, and improved the psychological condition of the patient.

Morphometric evaluation of the repair of critical-size defects using demineralized bovine bone and autogenous bone grafts in rat calvaria

Objective: To evaluate the repair of critical-size bone defects in rats treated with demineralized bovine bone (DBB) compared with autogenous bone (AB). Material and method: A bone defect of 8 mm in diameter was created in the calvaria of 50 Rattus norvegicus, treated either with DBB or AB. Sub-groups of five rats of each group were killed at 7, 14, 21, 30 and 90 days post-operatively, and the skulls were removed and processed histologically. Histological sections were stained with hematoxylin and eosin. Result: Histological analysis showed complete closure of the defects with new bone at 90 days in group AB, and substitution of the biomaterial by fibrotic connective tissue in the DBB group at 21 days. Morphometric analysis showed that DBB was rapidly absorbed at 14 days, with its volume density decreasing from 47%+/- 0.8% at 7 days to 1.2%+/- 0.41% at 14 days. Subsequently, volume densities of the connective tissue and neoformed bone increased from 51.1%+/- 11.17% to 86.8%+/- 7.92% and from 1.9%+/- 1.13% to 12%+/- 8.02%, respectively, for the same time interval. The volume density of AB particles did not change throughout the experimental periods, but the amount of new bone increased markedly between 7 and 90 days, from 4.5%+/- 1.57% to 53.5%+/- 6.42% (P < 0.05). Conclusion: DBB did not provide complete repair of the defects, with significantly less new bone formation than in the AB group.

Comparative histomorphometric and tomographic analysis of maxillary sinus floor augmentation in rabbits using autografts and xenografts

Our goal was to evaluate bone neoformation promoted by a bovine xenograft composite (XC) compared with autogenous graft for maxillary sinus augmentation in a rabbit model. The left maxillary sinus of 18 male rabbits was filled with 200 mg of cortical and cancellous autogenous bone and the right sinus was filled with 200 mg of a composite comprised organic and inorganic bovine matrices, pool of bBMPs and collagen. Postoperative implant intervals of 2, 4, and 8 weeks were analyzed. Differences in the bone optical density among the groups and experimental periods were evaluated by computed tomography analysis. The tissue response was evaluated by histomorphometric analysis of the newly formed bone, connective tissue and/or granulation tissue, residual material, and bone marrow. The tomographic analyses showed a maximum optical density in the 4-week period for both groups. Histologically, an inflammatory infiltrate was observed at 2 weeks in the XC group but exclusively around the organic particles of the biomaterial. Regarding to the amount of newly formed bone, no statistical differences (p > 0.05) were observed among the two treatments throughout the implant intervals. However, by the end of the 8 weeks, the quantity of bone marrow was two times greater (p < 0.05) in the control group than in the XC group. In conclusion, the xenograft composite promotes formation of new bone in a similar fashion to autogenous bone and could therefore be considered a biomaterial with potential applications as a bone substitute in maxillary sinus floor augmentation. (C) 2007 Wiley Periodicals, Inc.

COX-2 inhibition decreases VEGF expression and alveolar bone loss during the progression of experimental periodontitis in rats

Background: Vascular endothelial growth factor (VEGF) is a macromolecule of importance in inflammation that has been implicated in periodontitis. The aims of this study were to investigate VEGF expression during the progression of periodontal disease and to evaluate the effect of a preferential cyclooxygenase (COX)-2 inhibitor meloxicam on VEGF expression and alveolar bone loss in experimentally induced periodontitis. Methods: A total of 120 Wistar rats were randomly separated into groups 1 (control) and 2 (meloxicam, 3 mg/kg/day, intraperitoneally, for 3, 7, 14, or 30 days). Silk ligatures were placed at the gingival margin level of the lower right first molar of all rats. VEGF expression was assessed by reverse transcription-polymerase chain reaction (RT-PCR), Western blot (WB), and immunohistochemical (IHC) analyses. The hemiarcades were processed for histopathologic analysis. RT-PCR and WB results were submitted to analysis of variance, the Tukey test, and Pearson correlation analysis (P<0.05). Results: A reduction in alveolar bone resorption was observed in the meloxicam-treated group compared to the control group at all periods studied. There was a positive correlation between COX-2 mRNA and VEGF mRNA in the gingival tissues and periodontal disease (R = 0.80; P = 0.026). Meloxicam significantly reduced the increased mRNA VEGF expression in diseased tissues after 14 days of treatment (P = 0.023). Some alterations in VEGF receptor I mRNA expression were observed, but these were not statistically significant. VEGF protein expression in WB experiments was significantly higher in diseased sites compared to healthy sites (P<0.05). After 14 days of treatment with meloxicam, an important decrease in VEGF protein expression was detected in diseased tissues (P = 0.08). Qualitative IHC analysis revealed that VEGF protein expression was higher in diseased tissues and decreased in tissues from rats treated with meloxicam. Conclusions: The present data suggest an important role for VEGF in the progression of periodontal disease. Systemic therapy with meloxicam can modify the progression of experimentally induced periodontitis in rats by reducing VEGF expression and alveolar bone loss.

Bone cell responses to the composite of Ricinus communis polyurethane and alkaline phosphatase

The aim of this study was to evaluate the response of osteoblastic cells to the composite of Ricinus cominunis polyurethane (RCP) and alkaline phosphatase (ALP) incubated in synthetic body fluid (SBF). RCP pure (RCPp) and RCP blended with ALP 6 mg/mL polymer (RCP+ALP) were incubated in SBF for 17 days. Four groups of RCP were tested: RCPp, RCP+ALP, and RCPp and RCP+ALP incubated in SBF (RCPp/SBF and RCP+ALP/SBF). Stem cells from rat bone marrow were cultured in conditions that allowed osteoblastic differentiation on RCP discs and were evaluated: cell adhesion, culture growth, cell viability, total protein content, ALP activity, and bone-like nodule formation. Data were compared by ANOVA or Kruskal-Wallis test. The group RCP-A P was highly cytotoxic and, therefore, was not considered here. Cell adhesion (p = 0.14), culture growth (p = 0.39), viability (p = 0.46) and total protein content (p = 0.12) were not affected by either RCP composition or incubation in SBE ALP activity was affected (p = 0.0001) as follows: RCPp < RCPp/SBF < RCP+ALP/SBF. Bone-like nodule formation was not observed on all evaluated groups. The composite RCP+ALP prior to SBF incubation is cytotoxic and must not be considered as biomaterial, but the incorporation of ALP to the RCP followed by SBF incubation could be a useful alternative to improve the biological properties of the RCP. (c) 2007 Wiley Periodicals, Inc.

In vitro osteogenesis induced by cells derived from sites submitted to sinus grafting with anorganic bovine bone

Objectives: This study evaluated key parameters of the in vitro osteogenesis induced by osteoblastic cells obtained from sites submitted to sinus grafting with anorganic bovine bone (ABB) in comparison with cells derived from bone sites of the same patients. Materials and methods: In three patients, the augmentation of maxillary sinus was carried out using ABB (Bio-Oss (R)). After at least 6 months, during the surgical intervention for titanium implants placement, biopsies were taken from these areas using trephine burs (grafted group). Bone fragments, of the same patients, from sites that had not received graft were also obtained with trephine burs and used as a control group. Osteoblastic cells were obtained from grafted and control groups by enzymatic digestion and cultured under standard osteogenic condition until subconfluence. First passaged cells were cultured in 24-well culture plates. Cell adhesion was evaluated at 24 h. For proliferation and viability assay, cells were cultured for 1, 3, 7, and 10 days. Total protein content and alkaline phosphatase (ALP) activity were measured at 3, 7, 10, 14, 17, and 21 days. Cultures were stained with Alizarin red S at 21 days, for detection of mineralized matrix. Data were compared by Student`s t-test. Results: Cell adhesion and viability were not affected by cell source (P>0.05). Total protein content was greater (P<0.05) for grafted group. Cell proliferation, ALP activity, and bone-like nodule formation were all greater (P<0.05) for the control group. Conclusions: Taken together, these results indicate that the in vivo long-term contact of cells with ABB downregulates the expression of osteoblast phenotype and consequently the in vitro osteogenesis.

Response of human alveolar bone-derived cells to a novel poly(vinylidene fluoride-trifluoroethylene)/barium titanate membrane

This study investigated the response of human alveolar bone-derived cells to a novel poly(vinylidene fluoride-trifluoroethylene)/barium titanate (P(VDF-TrFE)/BT) membrane. Osteoblastic cells were cultured in osteogenic conditions either on P(VDF-TrFE)/BT or polytetrafluoroethylene (PTFE) for up to 14 days. At 7 and 14 days, the mRNA expression of Runt-related transcription factor 2 (RUNX2), Type I collagen (COL I), Osteopontin (OPN), Alkaline phosphatase (ALP), Bone sialoprotein (BSP), and Osteocalcin (OC), key markers of the osteoblastic phenotype, and of Bcl2-associated X protein (Bax), B-cell CLL/lymphoma 2 (Bcl-2), and Survivin (SUR), associated with the control of the apoptotic cell death, was assayed by real-time PCR. In situ ALP activity was qualitatively evaluated by means of Fast red staining. Surface characterization was also qualitatively and quantitatively assayed in terms of topography, roughness, and wettability. Cells grown on P(VDF-TrFE)/BT exhibited a significantly higher mRNA expression for all markers compared to the ones on PTFE, except for Bcl-2, which was not detected for both groups. Additionally, Fast red staining was noticeably stronger in cultures on P(VDF-TrFE)/BT at 7 and 14 days. At micron-and submicron scale, SEM images and roughness analysis revealed that PTFE and P(VDF-TrFE)/BT exhibited a smooth topography and a similar roughness, respectively. PTFE membrane displayed higher contact angles compared with P(VDF-TrFE)/BT, as indicated by wettability assay. The novel P(VDF-TrFE)/BT membrane supports the acquisition of the osteoblastic phenotype in vitro, while up-regulating the expression of apoptotic markers. Further in vivo experiments should be carried out to confirm the capacity of P(VDF-TrFE)/BT membrane in promoting bone formation in guided bone regeneration.