Microstructure and grain boundary microanalysis of X70 pipeline steel

Grain boundaries (GBs), particularly ferrite: ferrite GBs, of X70 pipeline steel were characterized using analytical electron microscopy (AEM) in order to understand its intergranular stress corrosion cracking (IGSCC) mechanism(s). The microstructure consisted of ferrite (alpha), carbides at ferrite GBs, some pearlite and some small precipitates inside the ferrite grains. The precipitates containing Ti, Nb, V and N were identified as complex carbo-nitrides and designated as (Ti, Nb, WC, N). The GB carbides occurred (1) as carbides along ferrite GBs, (2) at triple points, and (3) at triple points and extending along the three ferrite GBs. The GB carbides were Mn rich, were sometimes also Si rich, contained no micro-alloying elements (Ti, Nb, V) and also contained no N. It was not possible to measure the GB carbon concentration due to surface hydrocarbon contamination despite plasma cleaning and glove bag transfer from the plasma cleaner to the electron microscope. Furthermore, there may not be enough X-ray signal from the small amount of carbon at the GBs to enable measurement using AEM. However, the microstructure does indicate that carbon does segregate to alpha : alpha GBs during microstructure development. This is particularly significant in relation to the strong evidence in the literature linking the segregation of carbon at GBs to IGSCC. It was possible to measure all other elements of interest. There was no segregation at alpha : alpha GBs, in particular no S, P and N, and also no segregation of the micro-alloying elements, Ti, Nb and V. (C) 2003 Kluwer Academic Publishers.

Atom probe field ion microscope measurements of carbon segregation at an a:a grain boundary and service failures by intergranular stress corrosion cracking

This work reports on a critical measurement to understand the intergranular stress corrosion cracking (IGSCC) of pipeline steels: the atom probe field ion microscope (APFIM) measurement of the carbon concentration at a grain boundary (GB). The APFIM measurement was related to the microstructure and to IGSCC observations. The APFIM indicated that the GB carbon concentration of X70 was similar to 10 at% or less, which correlated with a high resistance to IGSCC for X70. (C) 2005 Elsevier Ltd. All rights reserved.

The effect of iron on liquid film migration and sintering of an Al-Cu-Mg alloy

Analytical transmission electron microscopy indicates that liquid film migration occurs during sintering of an Al-Cu-Mg alloy, that intragranular liquid pools develop from migrating films and that iron segregates to these pools. It is suggested that a high localised iron concentration retards the liquid film migration rate by reducing the coherency strain in the retreating grain, causing a region of the film to detach from the boundary, thus forming an intragranular pool in the advancing grain. Alloys with low iron levels develop few intragranular pools and have high sintered densities. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Microanalysis of epitaxially grown diamond tip array

Electron backscattering diffraction has been applied on polycrystalline diamond films grown using microwave plasma assisted chemical vapour deposition on silicon substrate, in order to provide a map of the individual diamond grains, grain boundary, and the crystal orientation of discrete crystallites. The nucleation rate and orientation are strongly affected by using a voltage bias on the substrate to influence and enhance the nucleation process, the bias enhanced nucleation process. In this work, the diamond surface is mapped using electron backscattering diffraction, then a layer of a few microns is ion milled away exposing a lower layer for analysis and so on. This then permits a three dimensions reconstruction of the film texture.

Stress corrosion cracking and hydrogen embrittlement of an Al-Zn-Mg-Cu alloy

The age hardening, stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of an Al-Zn-Mg-Cu 7175 alloy were investigated experimentally. There were two peak-aged states during ageing. For ageing at 413 K, the strength of the second peak-aged state was slightly higher than that of the first one, whereas the SCC susceptibility was lower, indicating that it is possible to heat treat 7175 to high strength and simultaneously to have high SCC resistance. The SCC susceptibility increased with increasing Mg segregation at the grain boundaries. Hydrogen embrittlement (HE) increased with increased hydrogen charging and decreased with increasing ageing time for the same hydrogen charging conditions. Computer simulations were carried out of (a) the Mg grain boundary segregation using the embedded atom method and (b) the effect of Mg and H segregation on the grain boundary strength using a quasi-chemical approach. The simulations showed that (a) Mg grain boundary segregation in Al-Zn-Mg-Cu alloys is spontaneous, (b) Mg segregation decreases the grain boundary strength, and (c) H embrittles the grain boundary more seriously than does Mg. Therefore, the SCC mechanism of Al-Zn-Mg Cu alloys is attributed to the combination of HE and Mg segregation induced grain boundary embrittlement. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

On the nonlinear Neumann problem involving the critical Sobolev exponent on the boundary

in this paper we investigate the solvability of the Neumann problem (1.1) involving the critical Sobolev exponents on the right-hand side of the equation and in the boundary condition. It is assumed that the coefficients Q and P are smooth. We examine the common effect of the mean curvature of the boundary a deltaOhm and the shape of the graph of the coefficients Q and P on the existence of solutions of problem (1.1). (C) 2003 Published by Elsevier Inc.

Full S matrix calculation via a single real-symmetric Lanczos recursion: The Lanczos artificial boundary inhomogeneity method

We present an efficient and robust method for the calculation of all S matrix elements (elastic, inelastic, and reactive) over an arbitrary energy range from a single real-symmetric Lanczos recursion. Our new method transforms the fundamental equations associated with Light's artificial boundary inhomogeneity approach [J. Chem. Phys. 102, 3262 (1995)] from the primary representation (original grid or basis representation of the Hamiltonian or its function) into a single tridiagonal Lanczos representation, thereby affording an iterative version of the original algorithm with greatly superior scaling properties. The method has important advantages over existing iterative quantum dynamical scattering methods: (a) the numerically intensive matrix propagation proceeds with real symmetric algebra, which is inherently more stable than its complex symmetric counterpart; (b) no complex absorbing potential or real damping operator is required, saving much of the exterior grid space which is commonly needed to support these operators and also removing the associated parameter dependence. Test calculations are presented for the collinear H+H-2 reaction, revealing excellent performance characteristics. (C) 2004 American Institute of Physics.

Feeding strategies for grain-fed cattle in a hot environment

Six Bos taurus (Hereford) steers (body weight 324 22 kg) were used in a 45-day study with a replicated 3 x 3 Latin-square design. Three treatments [ad libitum feeding (ADLIB); limit feeding, 85% of ad libitum (LIMIT); bunk management feeding where steers were only given access to feed from 1600 to 0800 hours the following day (BUNK)] were imposed over 3 periods, with 2 steers assigned to each treatment in each period. Cattle were managed in a temperature-controlled metabolism unit and were exposed to both thermoneutral (17.7degreesC-26.1degreesC) and hot (16.7degreesC-32.9degreesC) environmental conditions. By design, during the thermoneutral period, the ADLIB cattle displayed greater intake (P < 0.05) than the LIMIT group, with the BUNK group being intermediate. However, during the hot period, both the LIMIT and BUNK treatment groups increased feed intake 4-5%, whereas feed intake of the ADLIB treatment group declined nearly 2%. During both periods respiration rate (RR, breath/min) followed the same pattern that was observed for feed intake, with the greatest (P < 0.05) RR found in the ADLIB treatment group (81.09 and 109.55, thermoneutral and hot, respectively) and lowest (P < 0.05) RR in the LIMIT treatment group (74.47 and 102.76, thermoneutral and hot, respectively). Rectal temperature (RT) did not differ among treatments during the thermoneutral period or the first hot day, although during the thermoneutral period the ADLIB treatment group did tend to display a lower RT, possibly as a result of other physiological processes (pulse rate and RR) aiding to keep RT lower. During the hot period, differences in RT were found on Day 5, with the LIMIT cattle having lower (P < 0.10) RT (38.92degreesC) than the ADLIB (39.18degreesC) cattle, with BUNK cattle RT (39.14degreesC) being intermediate. However, when hourly data were examined, the ADLIB cattle had greater(P < 0.05) RT than the BUNK and LIMIT at 1800 hours and greater RT (P < 0.05) than the LIMIT group at 1400, 1500, and 1600 hours. Clearly, a change in diurnal RT pattern was obtained by using the LIMIT and BUNK feeding regimen. Both of these groups displayed a peak RT during the hot conditions, between 2100 and 2200 hours, whereas the ADLIB group displayed a peak RT between 1400 and 1500 hours, a time very close to when peak climatic stress occurs. Based on these results it is apparent that feedlot managers could alleviate the effects of adverse hot weather on cattle by utilising either a limit-feeding regimen or altering bunk management practices to prevent feed from being consumed several hours prior to the hottest portion of the day.

Wetting and the physiological responses of grain-fed cattle in a heated environment

A controlled crossover experimental design was used to determine the effect of altered water sprinkling duration on heifers subjected to heat stress conditions. Heifers were subjected to 3 days of thermoneutral conditions followed by 3 days of hot conditions accompanied by water sprinkling between 1300 and 1500 h (HOT1-3). Then on the following 2 days (HOT4-5), environmental conditions remained similar, but 3 heifers were sprinkled between 1200 and 1600 h ( WET) and 3 were not sprinkled (NONWET). This was followed by a 1-day period (HOT6) in which environmental conditions and sprinkling regimen were similar to HOT1-3. Rectal temperature (RT) was collected hourly, and respiration rate (RR) was monitored every 2 h on HOT Days 2, 4, 5, and 6. Dry matter intake and rate of eating were also determined. Sprinkling reduced RR and RT (P < 0.01) of all heifers during HOT1-3. During HOT4-5, WET heifers had lower (P < 0.05) RT than NONWET from 1300 to 700 h and lower RR from 1400 to 2000 h. Dry matter intake of NONWET heifers was reduced by 30.6% (P < 0.05) during HOT4-5 and by 51.2% on HOT6. On HOT4-5 the dry matter intakes of WET heifers were similar to intakes under thermoneutral conditions. During HOT6, RT was again reduced following sprinkling in all heifers. Comparison of RT and RR of NONWET and WET heifers on HOT1-3 v. HOT6 revealed that under similar environmental conditions, NONWET heifers had increased RT, partially due to carry-over from HOT4-5. However, NONWET heifers had 40% lower feed intake but tended to have lower RR on HOT6 v. HOT1-3. Only RR of WET heifers was greater on HOT6, possibly a result of switching from a 4-h back to a 2-h sprinkling period, while maintaining a 62% greater intake (5.80 v. 3.58 kg/day) than NONWET heifers during this time. Results suggest that inconsistent cooling regimens may increase the susceptibility of cattle to heat stress and elicit different physiological and metabolic responses.

Hormonal growth-promotant effects on grain-fed cattle maintained under different environments

Six steers (3/4 Charolaisx1/4 Brahman) (mean body weight 314 +/- 27 kg) and six spayed heifers (3/5 Shorthornx2/5 Red Angus) (mean body weight 478 +/- 30 kg) were used to determine the effects of climatic conditions and hormone growth promotants (HGP) on respiration rate (RR; breaths/min), pulse rate (beats/min), rectal temperature (RT; degrees C), and heat production (HP; kJ). Cattle were exposed to the following climatic conditions prior to implantation with a HGP and then again 12 days after implantation: 2 days of thermoneutral conditions (TNL) [21.9 +/- 0.9 degrees C ambient temperature (T-A) and 61.7 +/- 22.1% relative humidity (RH)] then 2 days of hot conditions [HOT; 29.2 +/- 4 degrees C (T-A) and 78.3 +/- 13.2% (RH)], then TNL for 3 days and then 2 days of cold conditions [COLD; 17.6 +/- 0.9 degrees C (T-A) and 63.4 +/- 1.8% (RH); cattle were wet during this treatment]. The HGP implants used were: estrogenic implant (E), trenbolone acetate implant (TBA), or both (ET). Both prior to and following administration of HGP, RRs were lower (P < 0.05) on cold days and greater (P < 0.05) on hot days compared to TNL. On hot days, RTs, were 0.62 degrees C higher after compared to before implanting. Across all conditions, RTs were > 0.5 degrees C greater (P < 0.05) for E cattle than for TBA or ET cattle. On cold days, RTs of steers were > 0.8 degrees C higher than for the heifers, while under TNL and HOT, RTs of steers were 0.2-0.35 degrees C higher than those of heifers. Prior to implantation, HP per hour and per unit of metabolic body weight was higher (P < 0.05) for cattle exposed to hot conditions, when compared to HP on cold days. After implantation, HP was greater (P < 0.05) on hot days than on cold days. Under TNL, ET cattle had the lowest HP and greatest feed intake. On hot days, E cattle had the lowest HP, and the highest RT; therefore, if the potential exists for cattle death from heat episodes, the use of either TBA or ET may be preferred. Under cold conditions HP was similar among implant groups.

Monensin supplementation of lactating cows fed tropical grasses and cane molasses or grain

Effects of monensin (Mon) on performance of Holstein-Friesian cows fed tropical grasses and cane molasses (M) or cereal grain were examined in three experiments. In experiment I (incomplete 4 x 4 Latin square), three rumen-fistulated cows [188 I I days in milk (DIM)] were fed mixed diets based on rhodes grass (Chloris gayana cv. Callide) bay where M was substituted for wheat grain (W) at rates of 0 (MO), 125 (M 125) or 250 (M250) g/kg dry matter (DM). A fourth diet contained M250 plus 0.02 g Mon/kg DM (M250 + Mon). Substituting M for W tended (P < 0.10) to decrease the ratio of rumen molar proportions of acetate+butyrate (Bu):propionate (Pr) (4.3 versus 3.8 and 4.0 for M0, M125 and M250, respectively). There were no treatment effects (P> 0.10) on intake, organic matter digestibility, milk production or liveweight (LW) change. In experiment 2, 48 cows (173 &PLUSMN; 28.3 DIM) grazing kikuyu (Pennisetum clandestinum cv. common) pastures and supplemented with maize silage and a grain-based concentrate were offered either M (2.6 kg DM/(cow day)) or barley grain (B) (2.7 kg DM/(cow day)). Within each supplement type, half were fed 0 or 320 mg of Mon/(cow day). There were Mon x supplement interactions (Mon x S; P < 0.05) on the rumen molar proportion of Pr and Bu at 15:00 h, with B + Mon having the highest value for Pr (0.259 mmol/mmol) and lowest value for Bu (0.121 mmol/mmol). A Mon x S effect (P < 0.05) on milk fat content was noted with Mon causing a lower value regardless of energy source (31 and 36 g/l versus 40 and 38 g/l for B + Mon, M + Mon, B - Mon and M - Mon, respectively). As a main effect, M as opposed to B, reduced yields of milk (P < 0.05; 16.21/(cow day) versus 18.01/(cow day)) and protein (P < 0.05; 479 g/(cow day) versus 538 g/(cow day)). Monensin reduced milk fat yield (P < 0.05; 669 g/(cow day) versus 562 g/(cow day)), raised milk protein concentration (P < 0.05; 31 g/l versus 29 g/l) and caused LW gain rather than loss (P < 0.05; +0.06 kg/(cow day) versus -0.30 kg/(cow day)). No treatment effects on pasture intake were noted. In experiment 3, 48 cows (91 &PLUSMN; 16.1 DIM) grazing kikuyu pasture and supplemented with grain-based concentrate, sugar cane silage and 2.7 kg DM(cow day) of M were supplemented with either 0 or 320 mg Mon/(cow day). Monensin reduced (P < 0.05) milk fat content (33 g/l versus 30 g/l) and tended (P < 0.10) to reduce milk protein content (29 g/l versus 28 g/l). No effects of Mon on other milk production parameters, LW change or pasture intake were noted. Feeding monensin to mid-lactation Holstein-Friesian cows offered diets based on tropical grasses, and cane molasses or grain, improves rumen fermentation efficiency, thereby improving energy efficiency resulting in higher LW gain. Monensin had no effect on milk yield, but reduced milk fat concentration.

Sharp Sobolev inequality involving a critical nonlinearity on a boundary

We consider the solvability of the Neumann problem for the equation -Delta u + lambda u = 0, partial derivative u/partial derivative v = Q(x)vertical bar u vertical bar(q-2)u on partial derivative Omega, where Q is a positive and continuous coefficient on partial derivative Omega, lambda is a parameter and q = 2(N - 1)/(N - 2) is a critical Sobolev exponent for the trace embedding of H-1(Omega) into L-q(partial derivative Omega). We investigate the joint effect of the mean curvature of partial derivative Omega and the shape of the graph of Q on the existence of solutions. As a by product we establish a sharp Sobolev inequality for the trace embedding. In Section 6 we establish the existence of solutions when a parameter lambda interferes with the spectrum of -Delta with the Neumann boundary conditions. We apply a min-max principle based on the topological linking.

Microstructures and electrolytic properties of yttrium-doped ceria electrolytes: Dopant concentration and grain size dependences

The microstructures and electrolytic properties of YxCe1-xO2-x/2 (x = 0.10-0.25) electrolytes with average grain size in the range 90 nm-1.7 mu m were systematically investigated. Through detailed transmission electron microscopy characterization, nanosized domains were observed. The relationship of the domains, the doping level and grain sizes were determined, and their impacts on the electrolytic properties were systematically studied. It was found that the formation of domains has a negative impact on the electrolytic properties, so that electrolytic properties can be adjusted through careful control of domain formation, doping level and grain size. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.