Precursor scavenging of the resistive grain-boundary phase in 8 mol% yttria-stabilized zirconia: Effect of trace concentrations of SiO2

The influence that trace concentrations Of SiO2 have on improving grain-boundary conduction via precursor scavenging using additional heat treatment at 1200 degreesC for 40 h before sintering was investigated. At a SiO2-impurity level (SIL) less than or equal to 160 ppm by weight, the grain-boundary resistivity (p(gb)) decreased to 20% of its value, while no improvement in grain-boundary conduction was found at a SIL greater than or equal to 310 ppm. The correlation between the resistance per unit grain-boundary area, p(gb), and average grain size indicated that the inhomogeneous distribution of the siliceous phase in the sample with a SIL greater than or equal to 310 ppm. hampered the scavenging reaction.

Improvement of the electrolytic properties of Y2O3-based materials using a crystallographic index

Y2O3 is a c-type rare earth oxide with a fluorite-related structure. This material has been used to refractory because of its high thermal stability and excellent resistance to hydration. In this study, the effective index was suggested in order to improve the electrolytic properties of Y2O3-based oxide. (CexY1-x)(2)O3+delta (x = 0.25 and 0.3) and [LaaSrbCe0.25Y(1-a-b)](2)O3+delta (a = 0.05, 0.1 and 0.15, b = 0, 0.006 and 0.0125) were prepared as the examples with intermediate and high index, respectively. The specimens with high index value such as (La0.15Ce0.25Y0.60)(2)O-3.25 and (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.24 consisted of two phases such as c-type and fluorite, although (Ce0.25Y0.75)(2)O-3.25 with intermediate index value had a single phase of c-type rare earth oxide. Microanalysis indicates that a grain in the (La0.1Sr0.0125Ce0.25Y0.6375)(2)O-3.23(7) sintered body consists of c-type and fluorite phases. An interface between c-type and fluorite phases is coherent in a grain. This suggests that this effective index guides the crystal structure in the specimen to fluorite and the examined composition introduces the interface between c-type and fluorite in the microstructure. The electrochemical properties of specimens including Y2O3 were characterized on the basis of the suggested index. The electrical conductivity of Y2O3-based materials increased with an increase of the index. The apparent activation energy of Y2O3-based materials decreased with increasing index. The ionic transport number of oxygen of the specimens was improved by enhancement of the index, confirming validity of the index. The oxide ionic conductive region of (La0.1Sr0.0125Ce0.25Y0.(6375))(2)O-3.23(7) with high effective index extended up to P-O2 = 10(-18) atm at 800 degreesC, although the specimens with low or intermediate index showed p- or n-type semi-conduction in the same P-O2 region at 800 and 1000 degreesC. These results suggest that the interface between c-type and fluorite phases also contributes to improve the electrolytic properties in the grain. It is concluded that the improvement of electrolytic properties in Y2O3-based materials is attributable to the microstructure with interface between two phases in a grain and the fluorite structure guided by the suggested index. (C) 2001 Published by Elsevier Science B.V.

Elastic moduli of model random three-dimensional closed-cell cellular solids

Most cellular solids are random materials, while practically all theoretical structure-property results are for periodic models. To be able to generate theoretical results for random models, the finite element method (FEM) was used to study the elastic properties of solids with a closed-cell cellular structure. We have computed the density (rho) and microstructure dependence of the Young's modulus (E) and Poisson's ratio (PR) for several different isotropic random models based on Voronoi tessellations and level-cut Gaussian random fields. The effect of partially open cells is also considered. The results, which are best described by a power law E infinity rho (n) (1<n<2), show the influence of randomness and isotropy on the properties of closed-cell cellular materials, and are found to be in good agreement with experimental data. (C) 2001 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Thermal characterization of copolymers obtained by radiation grafting of styrene onto poly(tetrafluoroethyleneperfluoropropylvinylether) substrates: thermal decomposition, melting behavior and low-temperature transitions

Differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA) have been used to study the thermal decomposition, the melting behavior and low-temperature transitions of copolymers obtained by radiation-induced grafting of styrene onto poly (tetrafluoroethylene- perfluoropropylvinylether) (PFA) substrates. PFA with different contents of perfluoropropylvinylether (PPVE) as a comonomer have been investigated. A two step degradation pattern was observed from TGA thermograms of all the grafted copolymers, which was attributed to degradation of PSTY followed by the degradation of the PFA backbone at higher temperature. One broad melting peak can be identified for all copolymers, which has two components in the samples with higher PPVE content. The melting peak, crystal-crystal transition and the degree of crystallinity of the grafted copolymers increases with radiation grafting up to 50 kGy, followed by a decrease at higher doses. No such decrease was observed in the ungrafted PFA samples after irradiation. This indicated that the changes in the heats of transitions and crystallinity at low doses are due to the radiation effects on the microstructure of PFA (chain scission), whereas at higher doses the grafted PSTY is the driving force behind these changes. (C) 2001 Elsevier Science Ltd. All rights reserved.

Eutectic solidification in hypoeutectic Al-Si alloys: electron backscatter diffraction analysis

Nucleation and growth of the eutectic, in hypoeutectic Al-Si foundry alloys has been investigated by the electron backscatter diffraction (EBSD) mapping technique using a scanning electron microscope (SEM). Sample preparation procedures for optimizing mapping have been developed. To obtain a sufficiently smooth surface from a cast Al-Si eutectic microstructure for EBSD mapping, an appropriate preparation technique by ion milling was developed and applied instead of conventional electropolishing. By comparing the orientation of the aluminum in the eutectic to that of the surrounding primary aluminum dendrites, the growth mechanism of the eutectic can be determined. Two different results were found, in isolation or sometimes together, but distinct for different strontium contents: (1) crystallographic orientations of aluminum in eutectic and surrounding primary dendrites are identical, and (2) wide variation in orientations of the aluminum in the eutectic. (C) 2001 Elsevier Science Inc. All rights reserved.

Freeform fabrication of aluminum metal-matrix composites

A series of metal-matrix composites were formed by extrusion freeform, fabrication of a sinterable aluminum alloy in combination with silicon carbide particles and whiskers, carbon fibers, alumina particles, and hollow flyash cenospheres. Silicon carbide particles were most successful in that the composites retained high density with up to 20 vol% of reinforcement and the strength approximately doubles over the strength of the metal matrix alone. Comparison with simple models suggests that this unexpectedly high degree of reinforcement can be attributed to the concentration of small silicon carbide particles around the larger metal powder. This fabrication method also allows composites to be formed with hollow spheres that cannot be formed by other powder or melt methods.

A practical method for identifying intermetallic phase particles in aluminium alloys by electron probe microanalysis

Aluminium alloys that contain Si, Mg, Fe, Mn and/or Cu usually contain one or more types of intermetallic phases that are not readily distinguishable in the microstructure by conventional microscopy methods. It has thus been a challenge to develop a method that will unambiguously identify them. A practical approach has been developed that is based on an inherent linear relationship revealed for the overall distribution of any two elements in a precipitate/matrix geometry and the first-order approximation of electron probe microanalysis (EPMA) results. Application of this approach to a direct chill cast 6082 alloy is demonstrated, and its major limitations are discussed.

Precipitation hardening of Cu-Fe-Cr alloys - Part II - Microstructural characterisation

This research is part of a project whose scope was to investigate the engineering properties of new non-commercial alloy formulations based on the Cu rich corner of the Cu-Fe-Cr ternary system with the primary aim of exploring the development of a new cost-effective high-strength, high-conductivity copper alloy. Promising properties have been measured for the following alloys: Cu-0.7wt%Cr-0.3wt%Fe and Cu-0.7wt%Cr-2.0wt%Fe. This paper reports on the microstructural characterisation of these alloys and discusses the mechanical and electrical properties of these alloys in terms of their microstructure, particularly the formation of precipitates. These alloys have evinced properties that warrant further investigation. Cost modelling has shown that Cu-0.7wt%Cr-0.3wt%Fe is approximately 25% cheaper to produce than commercial Cu-1%Cr. It has also been shown to be more cost efficient on a yield stress and % IACS per dollar basis. The reason for the cost saving is that the Cu-0.7%Cr-0.3%Fe alloy can be made with low carbon ferro-chrome additions as the source of chromium rather than the more expensive Cu-Cr master-alloy. For applications in which cost is one of the primary materials selection criteria, it is envisaged that there would be numerous applications in both cast and wrought form, where the Cu-0.7%Cr-0.3%Fe alloy would be more suitable than Cu-1%Cr. (C) 2001 Kluwer Academic Publishers.

Influence of nano-structure on electrolytic properties in CeO2 based system

Doped ceria (CeO2) compounds are fluorite type oxides that show oxygen ionic conductivity higher than yttria stabilized zirconia, in oxidizing atmosphere. In order to improve the conductivity, the effective index was suggested to maximize the oxygen ionic conductivity in doped CeO2 based oxides. In addition, the true microstructure of doped CeO2 was observed at atomic scale for conclusion of conduction mechanism. Doped CeO2 had small domains (10-50 nm) with ordered structure in a grain. It is found that the electrolytic properties strongly depended on the nano-structural feature at atomic scale in doped CeO2 electrolyte.

Precursor scavenging of resistive grain-boundary phase in 8 mol % ytterbia-stabilized zirconia

The grain-boundary conduction of 8 mol % ytterbia-stabilized zirconia (8YbSZ) was improved markedly by precursor scavenging via the two-stage sintering process. The most significant increase in the grain-boundary conductivity was found when the sample, whose conductivity was higher than that via Al2O3-derived scavenging, was heat-treated at 1250degreesC for greater than or equal to 20 h. The formation of a stable Si-containing phase such as ZrSiO4 during the first-stage heat-treatment was suggested as one probable scavenging route from the optimal heat-treatment temperature (HTT), long duration time (>20 h) at HTT, and the stability of the formed phase up to sintering temperatures (1500degrees C). (C) 2002 The Electrochemical Society.

Powder forging of a sintered Al-3.8Cu-1Mg-0.8Si-O.1Sn alloy

The forging characteristics of an Al-Cu-Mg-Si-Sn alloy are examined using it new testing strategy which incorporates a double truncated cone specimen and finite element modelling. This sample geometry produces controlled strain distributions within a single specimen and can readily identify the specific strain required to achieve a specific microstructural event by matching the metallographic data with the strain profiles calculated from finite element software, The friction conditions were determined using the conventional friction ring test, which was evaluated using finite element software. The rheological properties of the alloy, evaluated from compression testing of right cylinders, are similar to the properties of conventional aluminium forgings. A hoop strain develops at the outer diameter of the truncated cones and this leads to pore opening at the outer few millimetres. The porosity is effectively removed when the total strain equals the net compressive strain. The strain profiles that develop in the truncated cones are largely independent of the processing temperature and the strain rate although the strain required for pore closure increases as the forging temperature is reduced. This suggests that the microstructure and the strain rate sensitivity may also be important factors controlling pore behaviour. (C) 2002 Elsevier Science B.V. All rights reserved.

The essential work of fracture through the wall of uPVC pipe

The specific essential work of fracture, w(e), has been measured for a relatively thick walled uPVC pipe as a function of position through the wall of the pipe. w(e) was highest at the surface of the pipe and decreased significantly at the centre of the pipe wall. The variation in w(e) through the wall of the pipe correlated with the processing level of the uPVC material as measured by the critical temperature, T-c. The variability in the measured values of w(e) was substantially higher in the centre of the pipe where the processing levels were lower. This was likely to be a result of the variability in the microstructure of the material where poor processing had introduced regions of poor fusion of primary PVC particles. (C) 2002 Kluwer Academic Publishers.

Columnar to equiaxed transition of eutectic in hypoeutectic aluminium-silicon alloys

Directional solidification of unmodified and strontium modified binary, high-purity aluminium-7 wt% silicon and commercial A356 alloys has been carried out to investigate the mechanism of eutectic solidification. The microstructure of the eutectic growth inter-face was investigated with optical microscopy and Electron Backscattering Diffraction (EBSD). In the commercial alloys, the eutectic solidification inter-face extends in the growth direction and creates a eutectic mushy zone. A planar eutectic growth front is observed in the high-purity alloys. The eutectic aluminium has mainly the same crystallographic orientation as the dendrites in the unmodified alloys and the strontium modified high-purity alloy. A more complex eutectic grain structure is found in the strontium modified commercial alloy. A mechanism involving constitutional undercooling and a columnar to equiaxed transition explains the differences between pure and commercial alloys. It is probably caused by the segregation of iron and magnesium and the activation of nucleants in the commercial alloy. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

An age hardening model for Al-7Si-Mg casting alloys

Yield strength (YS) ageing curves have been modelled for A356 and A357 aluminium casting alloys below the solvus temperature of the main hardening precipitate. Predictions are based on the Shercliff and Ashby methodology (Acta MetaH. Mater. 38 (1990) 1789) for wrought alloys. Differences between strengthening in wrought and cast Al-Si-Mg alloys are considered. A Brinell hardness to YS conversion incorporating strain hardening has been established to enable YS ageing curves to be predicted with reduced experimental effort. (C) 2002 Elsevier Science B.V. All rights reserved.

An atomistic simulation of solid state sintering using Monte Carlo methods

This paper presents results on the simulation of the solid state sintering of copper wires using Monte Carlo techniques based on elements of lattice theory and cellular automata. The initial structure is superimposed onto a triangular, two-dimensional lattice, where each lattice site corresponds to either an atom or vacancy. The number of vacancies varies with the simulation temperature, while a cluster of vacancies is a pore. To simulate sintering, lattice sites are picked at random and reoriented in terms of an atomistic model governing mass transport. The probability that an atom has sufficient energy to jump to a vacant lattice site is related to the jump frequency, and hence the diffusion coefficient, while the probability that an atomic jump will be accepted is related to the change in energy of the system as a result of the jump, as determined by the change in the number of nearest neighbours. The jump frequency is also used to relate model time, measured in Monte Carlo Steps, to the actual sintering time. The model incorporates bulk, grain boundary and surface diffusion terms and includes vacancy annihilation on the grain boundaries. The predictions of the model were found to be consistent with experimental data, both in terms of the microstructural evolution and in terms of the sintering time. (C) 2002 Elsevier Science B.V. All rights reserved.