Functional alkali tantalate 2D structures for microelectronics and related applications

Alkali tantalates and niobates, including K(Ta / Nb)O3, Li(Ta / Nb)O3 and Na(Ta / Nb)O3, are a very promising ferroic family of lead-free compounds with perovskite-like structures. Their versatile properties make them potentially interesting for current and future application in microelectronics, photocatalysis, energy and biomedics. Among them potassium tantalate, KTaO3 (KTO), has been raising interest as an alternative for the well-known strontium titanate, SrTiO3 (STO). KTO is a perovskite oxide with a quantum paraelectric behaviour when electrically stimulated and a highly polarizable lattice, giving opportunity to tailor its properties via external or internal stimuli. However problems related with the fabrication of either bulk or 2D nanostructures makes KTO not yet a viable alternative to STO. Within this context and to contribute scientifically to the leverage tantalate based compounds applications, the main goals of this thesis are: i) to produce and characterise thin films of alkali tantalates by chemical solution deposition on rigid Si based substrates, at reduced temperatures to be compatible with Si technology, ii) to fulfil scientific knowledge gaps in these relevant functional materials related to their energetics and ii) to exploit alternative applications for alkali tantalates, as photocatalysis. In what concerns the synthesis attention was given to the understanding of the phase formation in potassium tantalate synthesized via distinct routes, to control the crystallization of desired perovskite structure and to avoid low temperature pyrochlore or K-deficient phases. The phase formation process in alkali tantalates is far from being deeply analysed, as in the case of Pb-containing perovskites, therefore the work was initially focused on the process-phase relationship to identify the driving forces responsible to regulate the synthesis. Comparison of phase formation paths in conventional solid-state reaction and sol-gel method was conducted. The structural analyses revealed that intermediate pyrochlore K2Ta2O6 structure is not formed at any stage of the reaction using conventional solid-state reaction. On the other hand in the solution based processes, as alkoxide-based route, the crystallization of the perovskite occurs through the intermediate pyrochlore phase; at low temperatures pyrochlore is dominant and it is transformed to perovskite at >800 °C. The kinetic analysis carried out by using Johnson-MehlAvrami-Kolmogorow model and quantitative X-ray diffraction (XRD) demonstrated that in sol-gel derived powders the crystallization occurs in two stages: i) at early stage of the reaction dominated by primary nucleation, the mechanism is phase-boundary controlled, and ii) at the second stage the low value of Avrami exponent, n ~ 0.3, does not follow any reported category, thus not permitting an easy identification of the mechanism. Then, in collaboration with Prof. Alexandra Navrotsky group from the University of California at Davis (USA), thermodynamic studies were conducted, using high temperature oxide melt solution calorimetry. The enthalpies of formation of three structures: pyrochlore, perovskite and tetragonal tungsten bronze K6Ta10.8O30 (TTB) were calculated. The enthalpies of formation from corresponding oxides, ∆Hfox, for KTaO3, KTa2.2O6 and K6Ta10.8O30 are -203.63 ± 2.84 kJ/mol, - 358.02 ± 3.74 kJ/mol, and -1252.34 ± 10.10 kJ/mol, respectively, whereas from elements, ∆Hfel, for KTaO3, KTa2.2O6 and K6Ta10.8O30 are -1408.96 ± 3.73 kJ/mol, -2790.82 ± 6.06 kJ/mol, and -13393.04 ± 31.15 kJ/mol, respectively. The possible decomposition reactions of K-deficient KTa2.2O6 pyrochlore to KTaO3 perovskite and Ta2O5 (reaction 1) or to TTB K6Ta10.8O30 and Ta2O5 (reaction 2) were proposed, and the enthalpies were calculated to be 308.79 ± 4.41 kJ/mol and 895.79 ± 8.64 kJ/mol for reaction 1 and reaction 2, respectively. The reactions are strongly endothermic, indicating that these decompositions are energetically unfavourable, since it is unlikely that any entropy term could override such a large positive enthalpy. The energetic studies prove that pyrochlore is energetically more stable phase than perovskite at low temperature. Thus, the local order of the amorphous precipitates drives the crystallization into the most favourable structure that is the pyrochlore one with similar local organization; the distance between nearest neighbours in the amorphous or short-range ordered phase is very close to that in pyrochlore. Taking into account the stoichiometric deviation in KTO system, the selection of the most appropriate fabrication / deposition technique in thin films technology is a key issue, especially concerning complex ferroelectric oxides. Chemical solution deposition has been widely reported as a processing method to growth KTO thin films, but classical alkoxide route allows to crystallize perovskite phase at temperatures >800 °C, while the temperature endurance of platinized Si wafers is ~700 °C. Therefore, alternative diol-based routes, with distinct potassium carboxylate precursors, was developed aiming to stabilize the precursor solution, to avoid using toxic solvents and to decrease the crystallization temperature of the perovskite phase. Studies on powders revealed that in the case of KTOac (solution based on potassium acetate), a mixture of perovskite and pyrochlore phases is detected at temperature as low as 450 °C, and gradual transformation into monophasic perovskite structure occurs as temperature increases up to 750 °C, however the desired monophasic KTaO3 perovskite phase is not achieved. In the case of KTOacac (solution with potassium acetylacetonate), a broad peak is detected at temperatures <650 °C, characteristic of amorphous structures, while at higher temperatures diffraction lines from pyrochlore and perovskite phases are visible and a monophasic perovskite KTaO3 is formed at >700 °C. Infrared analysis indicated that the differences are due to a strong deformation of the carbonate-based structures upon heating. A series of thin films of alkali tantalates were spin-coated onto Si-based substrates using diol-based routes. Interestingly, monophasic perovskite KTaO3 films deposited using KTOacac solution were obtained at temperature as low as 650 °C; films were annealed in rapid thermal furnace in oxygen atmosphere for 5 min with heating rate 30 °C/sec. Other compositions of the tantalum based system as LiTaO3 (LTO) and NaTaO3 (NTO), were successfully derived as well, onto Si substrates at 650 °C as well. The ferroelectric character of LTO at room temperature was proved. Some of dielectric properties of KTO could not be measured in parallel capacitor configuration due to either substrate-film or filmelectrode interfaces. Thus, further studies have to be conducted to overcome this issue. Application-oriented studies have also been conducted; two case studies: i) photocatalytic activity of alkali tantalates and niobates for decomposition of pollutant, and ii) bioactivity of alkali tantalate ferroelectric films as functional coatings for bone regeneration. Much attention has been recently paid to develop new type of photocatalytic materials, and tantalum and niobium oxide based compositions have demonstrated to be active photocatalysts for water splitting due to high potential of the conduction bands. Thus, various powders of alkali tantalates and niobates families were tested as catalysts for methylene blue degradation. Results showed promising activities for some of the tested compounds, and KNbO3 is the most active among them, reaching over 50 % degradation of the dye after 7 h under UVA exposure. However further modifications of powders can improve the performance. In the context of bone regeneration, it is important to have platforms that with appropriate stimuli can support the attachment and direct the growth, proliferation and differentiation of the cells. In lieu of this here we exploited an alternative strategy for bone implants or repairs, based on charged mediating signals for bone regeneration. This strategy includes coating metallic 316L-type stainless steel (316L-SST) substrates with charged, functionalized via electrical charging or UV-light irradiation, ferroelectric LiTaO3 layers. It was demonstrated that the formation of surface calcium phosphates and protein adsorption is considerably enhanced for 316L-SST functionalized ferroelectric coatings. Our approach can be viewed as a set of guidelines for the development of platforms electrically functionalized that can stimulate tissue regeneration promoting direct integration of the implant in the host tissue by bone ingrowth and, hence contributing ultimately to reduce implant failure.

Obtaining and characterization of single crystals and ceramics of PZT

É conhecido que as propriedades electromecânicas do zirconato titanato de chumbo, PbZrxTi1-xO3 (PZT), alcançam um máximo na região morfotrópica. Este trabalho foi desenvolvido na tentativa de explicar as causas deste máximo e a sua dependência com a microestrutura. Para conhecer essas causas, que provocam o aparecimento de um máximo nas propriedades electromecânicas foi necessário estudar cerâmicos com composições próximas da zona morfotrópica. Os cerâmicos foram caracterizados do ponto de vista dieléctrico e estrutural e o máximo da constante dieléctrica na região morfotrópica foi confirmado, assim como a sua dependência do tamanho do grão. A posição do máximo de permitividade está relacionada com o ponto onde ocorre a transição de fase da estrutura romboédrica para tetragonal. Para conhecer as propriedades intrínsecas do PZT surgiu a necessidade de produzir monocristais destes compostos com dimensões e qualidade adequadas à medição das suas propriedades. No presente trabalho, fizeramse crescer monocristais de PZT com boa qualidade e dimensões relativamente elevadas, usando um método de solução a alta temperatura, com um fluxo de [PbO-KF-PbCl2]-B2O3, numa razão molar de 60/40 entre PZT e fluxo. Primeiro, optimizaram-se as condições de processamento, testando-se diferentes perfis de temperatura e percentagem de fluxo para promover o crescimento e melhorar a qualidade dos cristais de PZT. As condições identificadas como óptimas foram usadas para depois fazer crescer cristais de PZT. Os cristais obtidos evidenciaram uma morfologia cúbica com dimensões típicas de - 3 x 3 x 3 mm3.

Bottom up strategies for the morphology control of BaTiO3 particulates

As propriedades funcionais dos materiais ferroeléctricos tais como a polarização reversível, piroelectricidade, piezoelectricidade, elevada actividade óptica não linear e comportamento dieléctrico não linear são fundamentais para a sua aplicação em sensores, microactuadores, detectores de infravermelhos, filtros de fase de microondas e memórias não-voláteis. Nos últimos anos, motivado pelas necessidades industriais de redução do tamanho dos dispositivos microelectrónicos, aumentando a eficiência volumétrica, tem sido feito um grande esforço ao nível da investigação para desenvolver estruturas ferroeléctricas à escala micro- e nano- métrica. É sabido que a redução de tamanho em materiais ferroeléctricos afecta significamente as suas propriedades. Neste sentido e considerando que foi previsto teoreticamente por cálculos ab initio que estruturas do tipo nanocilindros e nanodiscos apresentariam um novo tipo de ordem ferroeléctrica e, na expectativa de alcançar conhecimento para o desenvolvimento de uma nova geração de dispositivos microelectróncos, existe um grande interesse em desenvolver métodos de fabrico de nanoestruturas ferroeléctricas unidimensionais (1D) tais como nanocilindros e nanotubos. As estratégias de fabrico de nanoestruturas 1D até agora descritas na literatura indicam claramente as dificuldades inerentes à sua preparação. Existem duas grandes vias de síntese destas nanoestruturas: i) o método “topdown” que consiste na redução de tamanho de um dado material até à obtenção duma estrutura 1D; e ii) o método “bottom-up” em que átomos, iões e moléculas são agrupados para formar um material 1D. O método “top down” envolve em geral técnicas de desgaste, como o uso do feixe de electrões, que apesar de permitirem elevada precisão no posicionamento e no controlo do tamanho, falham em termos de resolução, exigem muito tempo e causam facilmente defeitos que deterioram as propriedades físicas destes materiais. Na metodologia “bottom up” a utilização de moléculas ou estruturas “molde” tem sido a mais explorada. As estructuras 1D podem também ser preparadas sem recorrer a “moldes”. Neste caso a agregação orientada é promovida pelo recurso a aditivos que controlam o crescimento dos cristais em direcções preferenciais. Neste contexto, neste trabalho utilizaram-se duas estratégias “bottom up” de baixo custo para a preparação de nanopartículas de titanato de bário (BaTiO3) com morfologia controlada: 1) síntese química (em solução e em fase vapor) com utilização de nanotubos de titanato TiNTs) como “moldes” e precursores de titânio 2) síntese química em solução com presença de aditivos. Os nanotubos de titanato de sódio foram preparados por síntese hidrotermal. Como existiam muitas dúvidas acerca da natureza estrutural e do mecanismo de formação dos NTs, a parte inicial do trabalho foi dedicada à realização de um estudo sistemático dos parâmetros intervenientes na síntese e à caracterização da sua estrutura e microestrutura. Foi demonstrado que os NTs têm a fórmula geral A2Ti2O5 (A = H+ or Na+), e não TiO2 (anátase) com defendido por vários autores na literatura, e podem ser preparados por método hidrotermal em meio fortemente alcalino usando como fonte de titânio TiO2 comercial na forma de anátase ou rútilo. A menor reactividade do rútilo exige temperaturas de síntese superiores ou tempos de reacção mais longos. A forma tubular resulta do tratamento hidrotermal e não de processos de lavagem e neutralização subsequentes. Se os NTs forem tratados após a síntese hidrotérmica em água a 200 ºC, transformam-se em nanocilindros. Uma das partes principais desta tese consistiu na investigação do papel dos NTs de titanato no crescimento anisotrópico de BaTiO3. O potencial funcionamento dos NTs como “moldes” para além de precursores foi testado em reacção com hidróxido de bário em síntese em solução e por reacção com um precursor orgânico de bário em fase vapor. Tendo por base os estudos cinéticos realizados, bem como as alterações estruturais e morfológicas das amostras, é possível concluir que a formação do BaTiO3 a partir de NTs de titanato de sódio, ocorre por dois mecanismos dependendo da temperatura e tempo de reacção. Assim, a baixa temperatura e curto tempo de reacção verifica-se que se formam partículas dendríticas de BaTiO3 cuja superfície é bastante irregular (“wild”) e que apresentam estrutura pseudo-cúbica. Estas partículas formam-se por reacção topotáctica na fronteira dos nanotubos de titanato de sódio. A temperaturas mais altas e/ou reacções mais longas, a reacção é controlada por um mecanismo de dissolução e precipitação com formação de dendrites de BaTiO3 tetragonais com superfície mais regular (“seaweed”). A microscopia de força piezoeléctrica mostrou que as dendrites “seaweeds“ possuem actividade piezoeléctrica superior à das dendrites “wild”, o que confirma o papel desempenhado pela estrutura e pela concentração de defeitos na rede na coerência e ordem ferroeléctrica de nanoestruturas. Os nossos resultados confirmam que os NTs de titanato não actuam facilmente como “moldes” na síntese em solução de BaTiO3 já que a velocidade de dissolução dos NTs em condições alcalinas é superior à velocidade de formação do BaTiO3. Assumindo que a velocidade de reacção dos NTs com o precursor de bário é superior em fase vapor, efectuou-se a deposição de um precursor orgânico de bário por deposição química de vapor sobre um filme de NTs de titnato de sódio depositados por deposição electroforética. Estudou-se a estabilidade dos NTs nas diferentes condições do reactor. Quando os NTs são tratados a temperaturas superiores a 700 ºC, ocorre a transformação dos NTs em nanocilindros de anatase por um mecanismo de agregação orientada. Quando se faz a deposição do precursor de bário, seguida de calcinação a 700 ºC em atmosfera oxidante de O2, verifica-se que a superficie dos NTs fica coberta com nanocristais de BaTiO3 independentemente da concentração de bário. O papel dos NTs de titanato no crescimento anisotrópico de BaTiO3 em fase vapor é assim descrito pela primeira vez. Em relação à metodologias de crescimento de partículas na ausência de “moldes” mas com aditivos fez-se um estudo sistemático utilizando 5 aditivos de natureza differente. As diferenças entre aditivos foram sistematizadas tendo em conta as diferenças estruturais e morfológicas verificadas. Está provado que os aditivos podem funcionar como modificadores de crescimento cristalino por alteração do seu padrão de crescimento ou por alteração da cinética de crescimento das faces cristalográficas do cristal. Entre os aditivos testados verificou-se que o ácido poliacrilíco adsorve em faces específicas do BaTiO3 alterando a cinética de crescimento e induzindo a agregação orientada das partículas. O polivinilpirrolidona, o docecilsulfato de sódio e hidroxipropilmetilcelulose actuam mais como inibidores de crescimento do que como modificadores do tipo de crescimento. A D-frutose aumenta a energia de activação da etapa de nucleação não ocorrendo formação de BaTiO3 para as mesmas condições dos outros aditivos. Esta tese clarifica o papel dos NTs de titanato de sódio enquanto precursores e “moldes” no crescimento anisotrópico de BaTiO3 em solução e em fase vapor. É feita também a abordagem do controlo morfológico do BaTiO3 através do uso de aditivos. As estratégias de preparação de BaTiO3 propostas são de baixo custo, reprodutíveis e fáceis de efectuar. Os resultados contribuem para uma melhor compreensão da relação tamanho – morfologia – propriedade em materiais ferroeléctricos nanométricos com vista à sua potencial aplicação.

Chemical vapour deposition of vanadium oxide thermochromic thin films

Thermochromic materials change optical properties, such as transmittance or reflectance, with a variation in temperature. An ideal intelligent (smart) material will allow solar radiation in through a window in cold conditions, but reflect that radiation in warmer conditions. The variation in the properties is often associated with a phase change, which takes place at a definite temperature, and is normally reversible. Such materials are usually applied to window glass as thin films. This thesis presents the work on the development of thermochromic vanadium (IV) oxide (VO2) thin films – both undoped and doped with tungsten, niobium and gold nanoparticles – which could be employed as solar control coatings. The films were deposited using Chemical Vapour Deposition (CVD), using improved Atmospheric Pressure (APCVD), novel Aerosol Assisted (AACVD) and novel hybrid AP/AACVD techniques. The effects of dopants on the metalto- semiconductor transition temperature and transmittance/reflectance characteristics were also investigated. This work significantly increased the understanding of the mechanisms behind thermochromic behaviour, and resulted in thermochromic materials based on VO2 with greatly improved properties.

Catalytic routes to convert saccharides to furanic aldehydes

The conversion of plant biomass-derived carbohydrates (preferably non-edible) into added-value products is envisaged to be at the core of the future biorefineries. Carbohydrates are the most abundant natural organic polymers on Earth. This work deals with the chemical valorisation of plant biomass, focusing on the acid-catalysed conversion of carbohydrates (mono and polysaccharides) to furanic aldehydes, namely 2-furaldehyde (Fur) and 5-hydroxymethyl-2-furaldehyde (Hmf), which are valuable platform chemicals that have the potential to replace a variety of oil derived chemicals and materials. The investigated reaction systems can be divided into two types depending on the solvent used to dissolve the carbohydrates in the reaction medium: water or ionic liquid-based systems. The reaction temperatures were greater than 150 ºC when the solvent was water, and lower than 150 º C in the cases of the ionic liquid-based catalytic systems. As alternatives to liquid acids (typically used in the industrial production of Fur), solid acid catalysts were investigated in these reaction systems. Aiming at the identification of (soluble and insoluble) reaction products, complementary characterisation techniques were used namely, FT-IR spectroscopy, liquid and solid state NMR spectroscopy, TGA, DSC and GC´GC-ToFMS analyses. Complex mixtures of soluble reaction products were obtained and different types of side reactions may occur. The requirements to be put on the catalysts for these reaction systems partly depend on the type of carbohydrates to be converted and the reaction conditions used. The thermal stability is important due to the fact that formation of humins and catalyst coking phenomena are characteristically inherent to these types of reactions systems leading to the need to regenerate the catalyst which can be effectively accomplished by calcination. Special attention was given to fully inorganic nanoporous solid acids, amorphous or crystalline, and consisting of nano to micro-size particles. The investigated catalysts were silicoaluminophosphates, aluminosilicates and zirconium-tungsten mixed oxides which are versatile catalysts in that their physicochemical properties can be fine-tuned to improve the catalytic performances in the conversion of different substrates (e.g. introduction of mesoporosity and modification of the acid properties). The catalytic systems consisting of aluminosilicates as solid acids and water as solvent seem to be more effective in converting pentoses and related polysaccharides into Fur, than hexoses and related polysaccharides into Hmf. The investigated solid acids exhibited fairly good hydrothermal stabilities. On the other hand, ionic liquid-based catalytic systems can allow reaching simultaneously high Fur and Hmf yields, particularly when Hmf is obtained from D-fructose and related polysaccharides; however, catalyst deactivation occurs and the catalytic reactions take place in homogeneous phase. As pointed out in a review of the state of the art on this topic, the development of truly heterogeneous ionic liquid-based catalytic systems for producing Fur and Hmf in high yields remains a challenge.

Laser assisted directional solidification of zirconia-based eutectics

Directionally solidified zirconia-based eutectic (DSE) fibres were obtained using the laser floating zone (LFZ) method. Two systems were investigated: zirconia-barium zirconate and zirconia-mullite. The purpose was to take advantage of zirconia properties, particularly as an ionic conductor and a mechanical rein-forcement phase. The influence of processing conditions in the structural and microstructural characteristics and their consequences on the electrical and mechanical behaviour were the focus of this thesis. The novel zirconia-barium zirconate eutectic materials were developed in order to combine oxygen ionic conduction through zirconia with protonic conduction from barium zirconate, promoting mixed ionic conduction behaviour. The mi-crostructure of the fibres comprises two alternated regions: bands having coarser zirconia-rich microstructure; and inter-band regions changing from a homogeneous coupled eutectic, at the lowest pulling rate, to columnar colony microstructure, for the faster grown fibres. The bands inter-distance increases with the growth rate and, at 300 mm/h, zirconia dendrites develop enclosed in a fine-interpenetrated network of 50 vol.% ZrO2-50 vol.% BaZrO3. Both phases display contiguity without interphase boundaries, according to impedance spec-troscopy data. Yttria-rich compositions were considered in order to promote the yttrium incorporation in both phases, as revealed by Raman spectroscopy and corroborated by the elemental chemical analysis in energy dispersive spectros-copy. This is a mandatory condition to attain simultaneous contribution to the mixed ionic conduction. Such results are supported by impedance spectrosco-py measurements, which clearly disclose an increase of total ionic conduction for lower temperatures in wet/reduction atmospheres (activation energies of 35 kJ/mol in N2+H2 and 48 kJ/mol in air, in the range of 320-500 ºC) compared to the dry/oxidizing conditions (attaining values close to 90 kJ/mol, above 500 ºC). At high temperatures, the proton incorporation into the barium zirconate is un-favourable, so oxygen ion conduction through zirconia prevails, in dry and oxi-dizing environments, reaching a maximum of 1.3x10-2 S/cm in dry air, at ~1000 ºC. The ionic conduction of zirconia was alternatively combined with another high temperature oxygen ion conductor, as mullite, in order to obtain a broad elec-trolytic domain. The growth rate has a huge influence in the amount of phases and microstructure of the directionally solidified zirconia-mullite fibres. Their microstructure changes from planar coupled eutectic to dendritic eutectic mor-phology, when the growth rate rises from 1 to 500 mm/h, along with an incre-ment of tetragonal zirconia content. Furthermore, high growth rates lead to the development of Al-Si-Y glassy phase, and thus less mullite amount, which is found to considerably reduce the total ionic conduction of as-grown fibres. The reduction of the glassy phase content after annealing (10h; 1400 ºC) promotes an increase of the total ionic conduction (≥0.01 S/cm at 1370 °C), raising the mullite and tetragonal zirconia contents and leading to microstructural differ-ences, namely the distribution and size of the zirconia constituent. This has important consequences in conductivity by improving the percolation pathways. A notable increase in hardness is observed from 11.3 GPa for the 10 mm/h pulled fibre to 21.2 GPa for the fibre grown at 500 mm/h. The ultra-fine eutectic morphology of the 500 mm/h fibres results in a maximum value of 534 MPa for room temperature bending strength, which decreases to about one-fourth of this value at high temperature testing (1400 ºC) due to the soft nature of the glassy-matrix.

Multilayered micro/nanocrystalline CVD diamond coatings for biotribology

In the present work multilayered micro/nanocrystalline (MCD/NCD) diamond coatings were developed by Hot Filament Chemical Vapour Deposition (HFCVD). The aim was to minimize the surface roughness with a top NCD layer, to maximize adhesion onto the Si3N4 ceramic substrates with a starting MCD coating and to improve the mechanical resistance by the presence of MCD/NCD interfaces in these composite coatings. This set of features assures high wear resistance and low friction coefficients which, combined to diamond biocompatibility, set this material as ideal for biotribological applications. The deposition parameters of MCD were optimized using the Taguchi method, and two varieties of NCD were used: NCD-1, grown in a methane rich gas phase, and NCD-2 where a third gas, Argon, was added to the gas mixture. The best combination of surface pre-treatments in the Si3N4 substrates is obtained by polishing the substrates with a 15 μm diamond slurry, further dry etching with CF4 plasma for 10 minutes and final ultrasonic seeding in a diamond powder suspension in ethanol for 1 hour. The interfaces of the multilayered CVD diamond films were characterized with high detail using HRTEM, STEM-EDX and EELS. The results show that at the transition from MCD to NCD a thin precursor graphitic film is formed. On the contrary, the transition of the NCD to MCD grade is free of carbon structures other than diamond, as a result of the richer atomic hydrogen content and of the higher substrate temperature for MCD deposition. At those transitions, WC nanoparticles were found due to contamination from the filament, being also present at the first interface of the MCD layer with the silicon nitride substrate. In order to study the adhesion and mechanical resistance of the diamond coatings, indentation and particle jet blasting tests were conducted, as well as tribological experiments with homologous pairs. Indentation tests proved the superior behaviour of the multilayered coatings that attained a load of 800 N without delamination, when compared to the mono and bilayered ones. The multilayered diamond coatings also reveal the best solid particle erosion resistance, due to the MCD/NCD interfaces that act as crack deflectors. These results were confirmed by an analytical model on the stress field distribution based on the von Mises criterion. Regarding the tribological testing under dry sliding, multilayered coatings also exhibit the highest critical load values (200N for Multilayers with NCD-2). Low friction coefficient values in the range μ=0.02- 0.09 and wear coefficient values in the order of ~10-7 mm3 N-1 m-1 were obtained for the ball and flat specimens indicating a mild wear regime. Under lubrication with physiological fluids (HBSS e FBS), lower wear coefficient values ~10-9-10-8 mm3 N-1 m-1) were achieved, governed by the initial surface roughness and the effective contact pressure.

Electromechanical properties of engineered lead free potassium sodium niobate based materials

K0.5Na0.5NbO3 (KNN), is the most promising lead free material for substituting lead zirconate titanate (PZT) which is still the market leader used for sensors and actuators. To make KNN a real competitor, it is necessary to understand and to improve its properties. This goal is pursued in the present work via different approaches aiming to study KNN intrinsic properties and then to identify appropriate strategies like doping and texturing for designing better KNN materials for an intended application. Hence, polycrystalline KNN ceramics (undoped, non-stoichiometric; NST and doped), high-quality KNN single crystals and textured KNN based ceramics were successfully synthesized and characterized in this work. Polycrystalline undoped, non-stoichiometric (NST) and Mn doped KNN ceramics were prepared by conventional ceramic processing. Structure, microstructure and electrical properties were measured. It was observed that the window for mono-phasic compositions was very narrow for both NST ceramics and Mn doped ceramics. For NST ceramics the variation of A/B ratio influenced the polarization (P-E) hysteresis loop and better piezoelectric and dielectric responses could be found for small stoichiometry deviations (A/B = 0.97). Regarding Mn doping, as compared to undoped KNN which showed leaky polarization (P-E) hysteresis loops, B-site Mn doped ceramics showed a well saturated, less-leaky hysteresis loop and a significant properties improvement. Impedance spectroscopy was used to assess the role of Mn and a relation between charge transport – defects and ferroelectric response in K0.5Na0.5NbO3 (KNN) and Mn doped KNN ceramics could be established. At room temperature the conduction in KNN which is associated with holes transport is suppressed by Mn doping. Hence Mn addition increases the resistivity of the ceramic, which proved to be very helpful for improving the saturation of the P-E loop. At high temperatures the conduction is dominated by the motion of ionized oxygen vacancies whose concentration increases with Mn doping. Single crystals of potassium sodium niobate (KNN) were grown by a modified high temperature flux method. A boron-modified flux was used to obtain the crystals at a relatively low temperature. XRD, EDS and ICP analysis proved the chemical and crystallographic quality of the crystals. The grown KNN crystals exhibit higher dielectric permittivity (29,100) at the tetragonal-to-cubic phase transition temperature, higher remnant polarization (19.4 μC/cm2) and piezoelectric coefficient (160 pC/N) when compared with the standard KNN ceramics. KNN single crystals domain structure was characterized for the first time by piezoforce response microscopy. It could be observed that <001> - oriented potassium sodium niobate (KNN) single crystals reveal a long range ordered domain pattern of parallel 180° domains with zig-zag 90° domains. From the comparison of KNN Single crystals to ceramics, It is argued that the presence in KNN single crystal (and absence in KNN ceramics) of such a long range order specific domain pattern that is its fingerprint accounts for the improved properties of single crystals. These results have broad implications for the expanded use of KNN materials, by establishing a relation between the domain patterns and the dielectric and ferroelectric response of single crystals and ceramics and by indicating ways of achieving maximised properties in KNN materials. Polarized Raman analysis of ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3 (KNN) single crystals was performed. For the first time, an evidence is provided that supports the assignment of KNN single crystals structure to the monoclinic symmetry at room temperature. Intensities of A′, A″ and mixed A′+A″ phonons have been theoretically calculated and compared with the experimental data in dependence of crystal rotation, which allowed the precise determination of the Raman tensor coefficients for (non-leaking) modes in monoclinic KNN. In relation to the previous literature, this study clarifies that assigning monoclinic phase is more suitable than the orthorhombic one. In addition, this study is the basis for non-destructive assessments of domain distribution by Raman spectroscopy in KNN-based lead-free ferroelectrics with complex structures. Searching a deeper understanding of the electrical behaviour of both KNN single crystal and polycrystalline materials for the sake of designing optimized KNN materials, a comparative study at the level of charge transport and point defects was carried out by impedance spectroscopy. KNN single crystals showed lower conductivity than polycrystals from room temperature up to 200 ºC, but above this temperature polycrystalline KNN displays lower conductivity. The low temperature (T < 200 ºC) behaviour reflects the different processing conditions of both ceramics and single crystals, which account for less defects prone to charge transport in the case of single crystals. As temperature increases (T > 200 ºC) single crystals become more conductive than polycrystalline samples, in which grain boundaries act as barriers to charge transport. For even higher temperatures the conductivity difference between both is increased due to the contribution of ionic conduction in single crystals. Indeed the values of activation energy calculated to the high temperature range (T > 300 ºC) were 1.60 and 0.97 eV, confirming the charge transport due to ionic conduction and ionized oxygen vacancies in single crystals and polycrystalline KNN, respectively. It is suggested that single crystals with low defects content and improved electromechanical properties could be a better choice for room temperature applications, though at high temperatures less conductive ceramics may be the choice, depending on the targeted use. Aiming at engineering the properties of KNN polycrystals towards the performance of single crystals, the preparation and properties study of (001) – oriented (K0.5Na0.5)0.98Li0.02NbO3 (KNNL) ceramics obtained by templated grain growth (TGG) using KNN single crystals as templates was undertaken. The choice of KNN single crystals templates is related with their better properties and to their unique domain structure which were envisaged as a tool for templating better properties in KNN ceramics too. X-ray diffraction analysis revealed for the templated ceramics a monoclinic structure at room temperature and a Lotgering factor (f) of 40% which confirmed texture development. These textured ceramics exhibit a long range ordered domain pattern consisting of 90º and 180º domains, similar to the one observed in the single crystals. Enhanced dielectric (13017 at TC), ferroelectric (2Pr = 42.8 μC/cm2) and piezoelectric (d33 = 280 pC/N) properties are observed for textured KNNL ceramics as compared to the randomly oriented ones. This behaviour is suggested to be due to the long range ordered domain patterns observed in the textured ceramics. The obtained results as compared with the data previously reported on texture KNN based ceramics confirm that superior properties were found due to ordered repeated domain pattern. This study provides an useful approach towards properties improvement of KNN-based piezoelectric ceramics. Overall, the present results bring a significant contribution to the pool of knowledge on the properties of sodium potassium niobate materials: a relation between the domain patterns and di-, ferro-, and piezo-electric response of single crystals and ceramics was demonstrated and ways of engineering maximised properties in KNN materials, for example by texturing were established. This contribution is envisaged to have broad implications for the expanded use of KNN over the alternative lead-based materials.

Diamond microelectrodes for corrosion studies

Este trabalho teve como objetivos a produção, caracterização e aplicação de microelétrodos (MEs) de diamante como sensores amperométricos e potenciométricos em sistemas de corrosão nos quais a agressividade do meio e a presença de produtos de corrosão, constituem obstáculos que podem diminuir o desempenho, ou inviabilizar a utilização, de outros tipos de sensores. Os microeléctrodos são baseados em filmes finos de diamante dopado com boro (BDD – Boron Doped Diamond) depositados sobre fios de tungsténio afiados, através do método de deposição química a partir da fase vapor, assistida por filamento quente (HFCVD – Hot Filament Chemical Vapor Deposition). A otimização das diversas etapas de fabricação dos MEs deu origem ao desenvolvimento de um novo sistema de afiamento eletroquímico para obtenção destes fios e a várias opções para a obtenção dos filmes de diamante condutor e seu isolamento com resinas para exposição apenas da ponta cilíndrica. A qualidade cristalina dos filmes de diamante foi avaliada por espectroscopia de Raman. Esta informação foi complementada com uma caracterização microestrutural dos filmes de diamante por microscopia eletrónica de varrimento (SEM), em que se fez a identificação da tipologia dos cristais como pertencendo às gamas de diamante nanocristalino ou microcristalino. Os filmes de BDD foram utilizados na sua forma não modificada, com terminações em hidrogénio e também com modificação da superfície através de tratamentos de plasma RF de CF4 e O2 indutores de terminações C-F no primeiro caso e de grupos C=O, C-O-C e C-OH no segundo, tal como determinado por XPS. A caracterização eletroquímica dos MEs não modificados revelou uma resposta voltamétrica com elevada razão sinal/ruído e baixa corrente capacitiva, numa gama de polarização quasi-ideal com extensão de 3 V a 4 V, dependente dos parâmetros de crescimento e pós-tratamentos de superfície. Estudou-se a reversibilidade de algumas reações heterogéneas com os pares redox Fe(CN)6 3-/4- e FcOH0/+ e verificou-se que a constante cinética, k0, é mais elevada em elétrodos com terminações em hidrogénio, nos quais não se procedeu a qualquer modificação da superfície. Estes MEs não modificados foram também testados na deteção de Zn2+ onde se observou, por voltametria cíclica, que a detecção da redução deste ião é linear numa escala log-log na gama de 10-5-10-2 M em 5 mM NaCl. Realizaram-se também estudos em sistemas de corrosão modelares, em que os microeléctrodos foram usados como sensores amperométricos para mapear a distribuição de oxigénio e Zn2+ sobre um par galvânico Zn-Fe, com recurso a um sistema SVET (Scanning Vibrating Electrode Technique). Foi possível detetar, com resolução lateral de 100 μm, um decréscimo da concentração de O2 junto a ambos os metais e produção de catiões de zinco no ânodo. Contudo verificou-se uma significativa deposição de zinco metálico na superfície dos ME utilizados. Os MEs com superfície modificada por plasma de CF4 foram testados como sensores de oxigénio dissolvido. A calibração dos microeléctrodos foi efetuada simultaneamente por voltametria cíclica e medição óptica através de um sensor de oxigénio comercial. Determinou-se uma sensibilidade de ~0.1422 nA/μM, com um limite de deteção de 0.63 μM. Os MEs modificados com CF4 foram também testados como sensores amperométricos com os quais se observou sensibilidade ao oxigénio dissolvido em solução, tendo sido igualmente utilizados durante a corrosão galvânica de pares Zn-Fe. Em alguns casos foi conseguida sensibilidade ao ião Zn2+ sem que o efeito da contaminação superficial com zinco metálico se fizesse sentir. Os microeléctrodos tratados em plasma de CF4 permitem uma boa deteção da distribuição de oxigénio, exibindo uma resposta mais rápida que os não tratados além de maior estabilidade de medição e durabilidade. Nos MEs em que a superfície foi modificada com plasma de O2 foi possível detetar, por cronopotenciometria a corrente nula, uma sensibilidade ao pH de ~51 mV/pH numa gama de pH 2 a pH 12. Este comportamento foi associado à contribuição determinante de grupos C-O e C=O, observados por XPS com uma razão O/C de 0,16. Estes MEs foram igualmente testados durante a corrosão galvânica do par Zn-Fe onde foi possível mapear a distribuição de pH associada ao desenvolvimento de regiões alcalinas causadas pela redução do oxigénio, acima da região catódica, e de regiões ácidas decorrentes da dissolução anódica do ânodo de zinco. Com o par galvânico imerso em 50 mM NaCl registou-se uma variação de pH aproximadamente entre 4,8 acima do ânodo de zinco a 9,3 sobre o cátodo de ferro. A utilização pioneira destes MEs como sensores de pH é uma alternativa promissora aos elétrodos baseados em membranas seletivas.