Safe fabrication of sharp gold tips for light emission in scanning tunnelling microscopy

Gold is the optimal tip metal for light emission in scanning tunnelling microscopy (LESTM) under ambient conditions. Sharp Au-tips of similar to 10nm radius were produced reliably using a safe, two-step etching method in 20% (w/w) CaCl2 solution. Previous CaCl2-based methods have tended to produce blunter tips, while other etching techniques that do produce sharp Au-tips, do so with the use of toxic or hazardous electrolytes. The tips are characterised using scanning electron microscopy and their efficacy in LESTM is evidenced by high-resolution, simultaneous topographic and photon mapping of Au(1 1 1)- and polycrystalline Au-surfaces. Spectra of the optical emission exhibit only one or two peaks with etched tips in contrast to the more complex spectra typical of cut tips; this feature, together with the highly symmetric geometry of the tips, facilitates a definitive analysis of the light emission process. (c) 2007 Elsevier B. V.. All rights reserved.

The tip-sample water bridge and light emission from scanning tunnelling microscopy

The light emission spectrum from a scanning tunnelling microscope (LESTM) is investigated as a function of relative humidity and shown to provide a novel and sensitive means for probing the growth and properties of a water meniscus on the nanometre scale. An empirical model of the light emission process is formulated and applied successfully to replicate the decay in light intensity and spectral changes observed with increasing relative humidity. The modelling indicates a progressive water filling of the tip-sample junction with increasing humidity or, more pertinently, of the volume of the localized surface plasmons responsible for light emission; it also accounts for the effect of asymmetry in structuring of the water molecules with respect to the polarity of the applied bias. This is juxtaposed with the case of a non-polar liquid in the tip-sample nanocavity where no polarity dependence of the light emission is observed. In contrast to the discrete detection of the presence/absence of a water bridge in other scanning probe experiments through measurement of the feedback parameter for instrument control, LESTM offers a means of continuously monitoring the development of the water bridge with sub-nanometre sensitivity. The results are relevant to applications such as dip-pen nanolithography and electrochemical scanning probe microscopy.

SrTiO3(001)(2x1) reconstructions: First-principles calculations of surface energy and atomic structure compared with scanning tunneling microscopy images

(1x1) and (2x1) reconstructions of the (001) SrTiO3 surface were studied using the first-principles full-potential linear muffin-tin orbital method. Surface energies were calculated as a function of TiO2 chemical potential, oxygen partial pressure and temperature. The (1x1) unreconstructed surfaces were found to be energetically stable for many of the conditions considered. Under conditions of very low oxygen partial pressure the (2x1) Ti2O3 reconstruction [Martin R. Castell, Surf. Sci. 505, 1 (2002)] is stable. The question as to why STM images of the (1x1) surfaces have not been obtained was addressed by calculating charge densities for each surface. These suggest that the (2x1) reconstructions would be easier to image than the (1x1) surfaces. The possibility that the presence of oxygen vacancies would destabilise the (1x1) surfaces was also investigated. If the (1x1) surfaces are unstable then there exists the further possibility that the (2x1) DL-TiO2 reconstruction [Natasha Erdman Nature (London) 419, 55 (2002)] is stable in a TiO2-rich environment and for p(O2)>10(-18) atm.

Surface plasmon polariton propagation length: A direct comparison using photon scanning tunneling microscopy and attenuated total reflection

The propagation of surface plasmon polaritons (SPP's) is studied using a photon scanning tunneling microscope (PSTM) and conventional attenuated total reflection (ATR). The PSTM experiment uses localized (focused beam) launching or SPP's at a wavelength of 632.8 nm. Propagation of the SPP is observed as an exponentially decaying tail beyond the launch site acid the 1/e propagation length is measured directly for a series of Ag films of different thicknesses. The ATR measurements are used to characterize the thin film optical and thickness parameters, revealing, notably, the presence of a contaminating adlayer of Ag2S of typical dielectric function, 8.7 + i2.7, and thickness 1-2 nm. Values of the SPP propagation length, based on the ATR- derived film parameters used in the four-media implicit SPP dispersion relation, show very good agreement with those based on the PSTM images for the case of undercoupled or optimally coupled SPP modes. The observed propagation lengths are quantitatively analyzed taking explicit account of additional intrinsic damping due to the growth of the Ag2S layer and of reradiation of the SPP back into the prism outside the launch site. Finally, the PSTM images show excellent SPP beam confinement in the original propagation direction.

Light emission from scanning tunnelling microscope on polycrystalline Au films - what is happening at the single-grain level?

When operated with a metallic tip and sample the scanning tunnelling microscope constitutes a nanoscale, plasmonic light source yielding broadband emission up to a photon energy determined by the applied bias. The emission is due to tunnelling electron excitation and subsequent radiative decay of localized plasmon modes, which can be on the lateral scale of a single metal grain (similar to 25 nm) or less. For a Au-tip/Au-polycrystalline sample under ambient conditions it is found that the intensity and spectral content of the emitted light are not dependent on the lateral grain dimension, but are predominantly determined by the tip geometry. However, the intensity increases strongly with increasing film thickness (grain depth) up to 20-25 nm or approximately the skin depth of the Au film. Photon maps can show less emissive grains and two classes of this occurrence are distinguished. The first is geometrical in origin - a double-tip structure in this case - while the second is due to a contamination-induced lowering of the local work function that causes the tunnel gap to increase. It is suggested that differences in work-function lowering between grains presenting different crystalline facets, combined with an exponential decay in emitted light intensity with tip - sample distance, leads to grain contrast. These results are relevant to tip-enhanced Raman scattering and the fabrication of micro/nano-scale planar, light-emitting tunnel devices.

Monte Carlo simulation of cluster growth in surface defects induced by the tip of a scanning tunnelling microscope

First steps are taken to model the electrochemical deposition of metals in nanometer-sized cavities. In the present work, the electrochemical deposition of Cu atoms in nanometer-sized holes dug on Au(111) is investigated through Monte Carlo simulations using the embedded atom method to represent particle interactions. By sweeping the chemical potential of Cu, a cluster is allowed to grow within the hole rising four atomic layers above the surface. Its lateral extension remains confined to the area defined by the borders of the original defect. (C) 2004 Elsevier B.V. All rights reserved.

A combined experimental and theoretical study of the generation of palladium clusters on Au(111) with a scanning tunnelling microscope

Palladium clusters have been deposited on the surface of a Au(111) electrode with the tip of a scanning tunnelling microscope. The distance over which the tip was moved towards the surface has a decisive influence on the properties of the clusters: the larger this distance, the larger the generated clusters, and the more stable they are. These findings are supported by computer simulations, which further suggest that the larger clusters contain a sizable amount of gold, which enhances their stability. Dissolution of the clusters occurs from the edges rather than layer by layer.

Electronic structures and bonding properties of chlorine-treated nitrogenated carbon nanotubes: X-ray absorption and scanning photoelectron microscopy studies

The electronic and bonding properties of nitrogenated carbon nanotubes (N-CNTs) exposed to chlorine plasma were investigated using C and N K-edge x-ray absorption near-edge structure (XANES) and scanning photoelectron microscopy (SPEM). The C and N K-edge XANES spectra of chlorine-treated N-CNTs consistently reveal the formation of pyridinelike N-CNTs by the observation of 1s ->pi(*)(e(2u)) antibonding and 1s ->pi(*)(b(2g)) bonding states. The valence-band photoemission spectra obtained from SPEM images indicate that chlorination of the nanotubes enhances the C-N bonding. First-principles calculations of the partial densities of states in conjunction with C K-edge XANES data identify the presence of C-Cl bonding in chlorine treated N-CNTs. (C) 2007 American Institute of Physics.

Scanning electron microscopy study of microstructural evolution of electroless nickel-phosphorus deposits with heat treatment

This paper follows previous X-ray diffraction work on crystallisation and phase transformation of electroless nickel–phosphorus deposits, concentrating on microstructural changes. Amorphous or nanocrystalline coatings, depending on their phosphorus content, were heat treated at temperatures between 100 and 500 °C for 1 h. Changes in microstructure after the heat treatment were examined using high-resolution field emission scanning electron microscope. Crystallisation and grain growth effects are observed, as well as some inherent defect structures in the coatings and their changes. These are compared with the previous X-ray diffraction work and in general, good agreement is observed. The complementary strength and weakness of the different characterisation techniques are discussed.