Composites of poly(ε-caprolactone) and Mo6S3I6 Nanowires

Composites of poly(e-caprolactone) (PCL) and molybdenum sulfur iodine (MoSI) nanowires were prepared using twin-screw extrusion. Extensive microscopic examination of the composites revealed the nanowires were well dispersed in the PCL matrix, although bundles of Mo6S3I6 ropes were evident at higher loadings. Secondary electron imaging (SEI) showed the nanowires had formed an extensive network throughout the PCL matrix, resulting in increased electrical conductivity of PCL, by eight orders of magnitude, and an electrical percolation threshold of 6.5T10S3vol%. Thermal analysis (DSC), WAXD, and hot stage polarized optical microscopy (HSPOM) experiments revealed Mo6S3I6 addition altered PCL crystallization kinetics, nucleation density, and crystalline content. A greater number of smaller spherulites were formed via heterogeneous nucleation. The onset of thermal decomposition (TGA) of PCL decreased by 70-C, a consequence of the thermal degradation of Mo6S3I6 to MoO3, which in turn accelerates the formation of volatile gases during the first stage of PCL decomposition.

Catalytic Mo2C coatings for the water gas shift reaction: Electrosynthesis in molten salts

Electrosynthesis methods using molten salts are suggested for obtaining a new catalytic system based on the Mo2C/Mo composition for the water gas shift reaction. The coatings obtained by the discharge of the carbonate ion on a molybdenum substrate and by the simultaneous reduction of the electroactive species MoO42 and CO32- are catalytically more active than bulk Mo2C or the commercial catalyst Cu-ZnO-Al2O3 by one and three orders of magnitude, respectively.

Electrochemical synthesis of Mo2C catalytical coatings for the water-gas shift reaction

The electroreduction of CO32- ions on a molybdenum cathode in a NaCl-KCl-Li2CO3 melt was studied by cyclic voltarnmetry. The electrochemical synthesis of Mo2C on molybdenum substrates has been performed at It 23 K for 7 h with a cathodic current density of 5 mA cm(-2). If molybdenum carbide is present as a thin (ca. 500 nm) film on a molybdenum substrate (Mo2C/Mo), its catalytic activity in the water gas-shift reaction is enhanced by at least an order of magnitude compared to that of the bulk Mo2C phase.

Hydrothermal synthesis of a continuous zeolite Beta layer by optimization of time, temperature and heating rate of the precursor mixture

Highly crystalline zeolite Beta coatings in a range of Si/Al ratios of 12-23 were synthesized on a surface-modified molybdenum substrate by hydrothermal synthesis. The average thickness of the coatings was ca. 2 mu m corresponding to a coverage of 2.5 gm(-2). The coatings were obtained from a viscous Na, K, and TEAOH containing aluminosilicate precursor mixture with silica sol as reactive silicon source. A mechanism for the in situ growth of zeolite Beta coatings is proposed. According to this mechanism, the deposition of an amorphous gel layer on the substrate surface in the initial stage of the synthesis is an important step for the crystallization of continuous zeolite Beta coatings. The heating rate of the precursor mixture and the synthesis temperature were optimized to control the level of supersaturation and to stimulate the initial formation of a gel layer. At a Si/Al ratio of 23, fast heating and a temperature of 150 degrees C are required to obtain high coverage, while at a Si/Al ratio of 15, hydrothermal synthesis has to be performed with a slow initial heating rate at 140 degrees C. (c) 2007 Elsevier Inc. All rights reserved.

Synthesis of protective Mo-Si-B coatings in molten salts and their oxidation behavior in an air-water mixture

The formation of various phases during boronizing of silicided molybdenum substrates (MoSi2/Mo) was investigated. Boronizing treatments were conducted in molten salts under an inert gas atmosphere in the 700-1000 degrees C temperature range for 3-7 h. Depending on the process type (non-current or electrochemical) and molten salt temperature, the formation of different boride phases (MoB, Mo2B5, MoB2, MoB4) was observed. At the same time, substantial oxidation of the bulk molybdenum disilicide phase (MoSi2) to the Mo5Si3 phase was observed in non-current boronizing. The oxidation resistance of the coatings was investigated by the weight change in an air-water (2.3 vol.%) mixture at a temperature of 500 degrees C for a period up to 700 h. Results indicated that a two-phase microstructure consisting of the MoSi2, matrix phase with 12-15 wt.% of the MoB4 phase greatly improved the oxidation resistance of the molybdenum substrates. The weight gain rate observed was 6.5 center dot 10(-4) mg/cm(2) h. (c) 2006 Elsevier B.V. All rights reserved.

Microwave Irradiation for the Facile Synthesis of Transition-Metal Nanoparticles (NPs) in Ionic Liquids (ILs) from Metal-Carbonyl Precursors and Ru-, Rh-, and Ir-NP/IL Dispersions as Biphasic Liquid-Liquid Hydrogenation Nanocatalysts for Cyclohexene

Stable chromium, molybdenum, tungsten, manganese, rhenium, ruthenium, osmium, cobalt, rhodium, and iridium metal nanoparticles (MNPs) have been reproducibly obtained by facile, rapid (3 min), and energysaving 10 W microwave irradiation (MWI) under an argon atmosphere from their metal–carbonyl precursors [Mx(CO)y] in the ionic liquid (IL) 1-butyl-3-methylimidazolium tetrafluoroborate ([BMIm][BF4]). This MWI synthesis is compared to UV-photolytic (1000 W, 15 min) or conventional thermal decomposition (180–2508C, 6–12 h) of [Mx(CO)y] in ILs. The MWIobtained nanoparticles have a very small (<5 nm) and uniform size and are prepared without any additional stabilizers or capping molecules as long-term stable M-NP/IL dispersions (characterization by transmission electron microscopy (TEM), transmission electron diffraction (TED), and dynamic light scattering (DLS)). The ruthenium, rhodium, or iridium nanoparticle/IL dispersions are highly active
and easily recyclable catalysts for the biphasic liquid–liquid hydrogenation of cyclohexene to cyclohexane with activities of up to 522 (mol product)(mol Ru)1h1 and 884 (mol product)(molRh)1h1 and give almost quantitative conversion within 2 h at 10 bar H2 and 908C. Catalyst poisoning experiments with CS2 (0.05 equiv per Ru) suggest a heterogeneous surface catalysis of RuNPs.

Profiling the ionome of rice and its use in discriminating geographical origins at the regional scale, China

Element profile was investigated for their use to trace the geographical origin of rice (Oryza sativa L.) samples. The concentrations of 13 elements (calcium (Ca), potassium (K), magnesium (Mg), phosphorus (P), boron (B), manganese (Mn), iron (Fe), nickel (Ni), copper (Cu), arsenic (As), selenium (Se), molybdenum (Mo), and cadmium (Cd)) were determined in the rice samples by inductively coupled plasma optical emission and mass spectrometry. Most of the essential elements for human health in rice were within normal ranges except for Mo and Se. Mo concentrations were twice as high as those in rice from Vietnam and Spain. Meanwhile, Se concentrations were three times lower in the whole province compared to the Chinese average level of 0.088 mg/kg. About 12% of the rice samples failed the Chinese national food safety standard of 0.2 mg/kg for Cd. Combined with the multi-elemental profile in rice, the principal component analysis (PCA), discriminant function analysis (DFA) and Fibonacci index analysis (FIA) were applied to discriminate geographical origins of the samples. Results indicated that the FIA method could achieve a more effective geographical origin classification compared with PCA and DFA, due to its efficiency in making the grouping even when the elemental variability was so high that PCA and DFA showed little discriminatory power. Furthermore, some elements were identified as the most powerful indicators of geographical origin: Ca, Ni, Fe and Cd. This suggests that the newly established methodology of FIA based on the ionome profile can be applied to determine the geographical origin of rice.

Interpretation of electrochemical measurements made during micro-scale abrasion-corrosion

This paper brings together and analyzes recent work based on the interpretation of the electrochemical measurements made on a modified micro-abrasion-corrosion tester used in several research programmes. These programmes investigated the role of abradant size, test solution pH in abrasion-corrosion of biomaterials, the abrasion-corrosion performance of sintered and thermally sprayed tungsten carbide surfaces under downhole drilling environments and the abrasion-corrosion of UNS S32205 duplex stainless steel. Various abrasion tests were conducted under two-body grooving, three-body rolling and mixed grooving-rolling abrasion conditions, with and without abrasives, on cast F75 cobalt-chromium-molybdenum (CoCrMo) alloy in simulated body fluids, 2205 in chloride containing solutions as well as sprayed and sintered tungsten carbide surfaces in simulated downhole fluids. Pre- and post-test inspections based on optical and scanning electron microscopy analysis are used to help interpret the electrochemical response and current noise measurements made in situ during micro-abrasion-corrosion tests. The complex wear and corrosion mechanisms and their dependence on the microstructure and surface composition as a function of the pH, abrasive concentration, size and type are detailed and linked to the electrochemical signals. The electrochemical versus mechanical processes are plotted for different test parameters and this new approach is used to interpret tribo-corrosion test data to give greater insights into different tribo-corrosion systems. Thus new approaches to interpreting in-situ electrochemical responses to surfaces under different abrasive wear rates, different abrasives and liquid environments (pH and NaCl levels) are made. This representation is directly related to the mechano-electrochemical processes on the surface and avoids quantification of numerous synergistic, antagonistic and additive terms associated with repeat experiments. (C) 2010 Elsevier Ltd. All rights reserved.

Genetic mapping of the rice ionome in leaves and grain:Identification of QTLs for 17 elements including arsenic, cadmium, iron and selenium

Research into the composition of cereal grains is motivated by increased interest in food quality. Here multi-element analysis is conducted on leaves and grain of the Bala x Azucena rice mapping population grown in the field. Quantitative trait loci (QTLs) for the concentration of 17 elements were detected, revealing 36 QTLs for leaves and 41 for grains. Epistasis was detected for most elements. There was very little correlation between leaf and grain element concentrations. For selenium, lead, phosphorus and magnesium QTLs were detected in the same location for both tissues. In general, there were no major QTL clusters, suggesting separate regulation of each element. QTLs for grain iron, zinc, molybdenum and selenium are potential targets for marker assisted selection to improve seed nutritional quality. An epistatic interaction for grain arsenic also looks promising to decrease the concentration of this carcinogenic element. © Springer Science+Business Media B.V. 2009.