Barrier characteristics of PtSi/p-Si schottky diodes as determined from I-V-T measurements

The current-voltage-temperature characteristics of PtSi/p-Si Schottky barrier diodes were measured in the temperature range 60-115 K. Deviation of the ideality factor from unity below 80 K may be modelled using the so-called T-0 parameter with T-0 = 18 K. It is also shown that the curvature in the Richardson plots may be remedied by using the flatband rather than the zero-bias saturation current density. Physically, the departure from ideality is interpreted in terms of an inhomogeneous Schottky contact. Here we determine a mean barrier height at T = 0 K, phi(b)(-0) = 223 mV, with an (assumed) Gaussian distribution of standard deviation sigma(phi) = 12.5 mV. These data are correlated with the zero-bias barrier height, phi(j)(0) = 192 mV (at T = 90 K), the photoresponse barrier height, phi(ph) = 205 mV, and the flatband barrier height, phi(fb) = 214 mV. Finally, the temperature coefficient of the flatband barrier was found to be -0.121 mV K-1, which is approximately equal to 1/2(dE(g)(i)/dT), thus suggesting that the Fermi level at the interface is pinned to the middle of the band gap.

PHOTOSIGNAL ENHANCEMENT IN AL-GAAS DIODES DUE TO SURFACE-PLASMONS AND GUIDED-WAVE MODES

Light of wavelength 632.8 nm and p-polarization is incident on a prism-air gap (varied from 0.7 to 7 mum)-Al-GaAs arrangement. Both the photosignal generated by the Schottky diode and the reflectance are measured as a function of the internal angle of incidence in the prism. There is significant, well-defined enhancement of the photosignal, up to a factor of approximately 7.5, associated with two different types of enhanced absorption modes. For air gaps <1.5 mum there is photosignal enhancement due to an enhanced absorption feature (reflectance dip) that occurs at an angle of incidence just above critical angle in the prism; this feature corresponds to the excitation of a surface plasmon polariton at the Al-air interface. For air gaps > 1 mum there are between one and ten photoresponse peaks at input angles less than the critical angle. The corresponding enhanced absorption features are due to leaky guided wave modes set up in the air gap.

ANALYSIS OF SURFACE-PLASMON POLARITON ENHANCEMENT IN PHOTODETECTION BY AL-GAAS SCHOTTKY DIODES

The surface plasmon polariton mediated photoresponse from Al-GaAs diodes is examined in a prism-air gap-diode configuration as a function of both the wavelength of the incident light and thickness of the Al electrode. The experimental data shows a pronounced dip in reflectance as a function of internal angle of incidence in the prism, due to the excitation of the surface plasmon polariton at the Al-air interface, and a corresponding peak in device photosignal. Careful modelling of reflectance and quantum efficiency data shows that the bulk of the signal is generated by light which is re-radiated from this surface mode into the semiconductor substrate where it is absorbed by the creation of electron-hole pairs in the depletion region. This holds for all the wavelengths used here (all are shorter than the GaAs absorption edge) and across the thickness range of the Al electrodes (20-50 nm). Quantum efficiencies in the range 0.5-22% and enhancement factors of typically 7.5 were recorded in this investigation.

CHARACTERIZATION OF THE AU SURFACE-STRUCTURE OF AL-L-AU LIGHT-EMITTING TUNNEL-JUNCTIONS

Visible light is emitted from the Au-air interface of Al-I-Au thin-film tunnel junctions (deposited over a thin layer of CaF2 on glass) as a result of the decay of surface plasmon polaritons (SPPs). We show the surface topography of such a Au film and relate its large-scale features to the outcoupling of fast SPP's to photons. The absence of short-scale roughness features is explained by thier disappearance through surface diffusion. To confirm this a controlled sequence of 5-nm, 20-ms scanning tunneling microscope (STM) W tip crashes has been used to produce indentations 3 nm deep with a lateral dimension of 5-7 nm on a Au crystal in air at room temperature. Four sequences of indentations were drawn in the form of a square box. Right from the start, feature decay is observed and over a period of 2 h a succession of images shows that the structure disappears into the background as a result of surface diffusion. The surface diffusion constant is estimated to be 10(-18) cm2 s-1. The lack of light output via slow mode SPPs is an inevitable consequence of surface annealing.

Switching ‘on’ the Luminescence of One Metal Ion with Another: Selectivity Characteristics with Respect to the Emitting and Triggering Metal

Complexes 1a·EuIII and 1b·EuIII, but not 1a·TbIII and 1b·TbIII, display strong ‘off–on’ switching of delayed luminescence with alkali cations; the switching efficiency of 1b·EuIII is stronger with K+ rather than Na+.