Study of La2-xCaxCuO4 perovskites for the low temperature water gas shift reaction

The effects of small fractions of calcium (x = 0, 0.05, 0.1, 0.15, and 0.20) on the structure and the catalytic properties of La2-xCaxCuO4 peroviskites have been investigated. The samples have been synthesized using the co-precipitation method. Perovskite-type oxides were characterized by XRD, TPR, XPS, XANES, SEM, and TEM. Catalytic tests for the water gas shift reaction (WGSR) were carried out in a tubular reactor at 290 degrees C. All samples showed a well-defined perovskite structure with surface areas between 6 and 18 m(2) g(-1). The partial substitution of La by Ca enhanced the stability of the perovskites and increased their reduction temperature. All catalysts were actives for WGSR, and the best catalytic performance was obtained for the La1.85Ca0.15CuO4 catalyst, but the samples with 5 and 10% of Ca had the best TOF values for reaction. These results can be associated to promoter effect of calcium, the high surface area, and the reducible species Cu-0 and Cu1+. (C) 2011 Elsevier B.V. All rights reserved.

Fe valence fluctuations and magnetoelastic coupling in Pb-based multiferroics perovskites

Lead-based multiferroics perovskites with nominal compositions Pb(Fe1/2Nb1/2)O3 and Pb(Fe2/3W1/3)O3 were synthesized following a two-stage method. Magnetic proprieties were investigated and correlated to anelastic proprieties, measured by the conventional pulse-echo method. The discussions are focused in the region around 250 K, where magnetoelectroelastic instabilities have been observed. X-ray absorption nearedge structure (XANES) study further indicates that the edge position varies with temperature revealing a fluctuation on the valence of iron ions with the temperature, which can be related to a variation in anelastic and magnetic proprieties.