Metallization and crystallization of semiconducting amorphous Ga20Te80 alloy under high pressure

Pressure and temperature dependence of the electrical resistivity of amorphous Ga20Te80 alloy is reported for the first time. The alloy undergoes a pressure induced amorphous semiconductor-to-crystalline metal phase transition at 6.5 ± 0.5 GPa. The high pressure crystalline phase is a mixture of Te and GaTe3 phases.

Effect of Post-Metallization Hydrogen Annealing on C-V Characteristic of Zirconia Grown Using Atomic Layer Deposition

Substantial amount of fixed charge present in most of the alternative gate dielectrics gives rise to large shifts in the flat-band voltage (VFB) and charge trapping and de-trapping causes hysterectic changes on voltage cycling. Both phenomena affect stable and reliable transistor operation. In this paper we have studied for the first time the effect of post-metallization hydrogen annealing on the C-V curve of MOS capacitors employing zirconia, one of the most promising gate dielectric. Samples were annealed in hydrogen ambient for up to 30 minutes at different temperatures ranging from room temperature to 400°C. C-V measurements were done after annealing at each temperature and the hysteresis width was calculated from the C-V curves. A minimum hysteresis width of ∼35 mV was observed on annealing the sample at 200°C confirming the excellent suitability of this dielectric

Evidence for double valence fluctuation in metallic oxides of lead

The possible role of double valence fluctuation in both lead and oxide ions with reference to metallization in oxides of lead is examined by x-ray-photoemission spectroscopy, ultraviolet-photoemission spectroscopy (UPS), and 207Pb NMR studies. The double valence fluctuations may be viewed as Pb4++2O2-⇄Pb2+O22-. While the insulating oxides PbO, Pb3O4, and Sr2PbO4 show a single oxide ion, O2- characterized by O(1s) at 529.7 eV, the insulating peroxide BaO2 is characterized by the ion O22- with a single O(1s) at 533 eV. The metallic PbO2, BaPbO3, BaBiPbO3, and SrPbO3 showed the occurrence of both O2- and O22- ions. The valence band in these compounds has also been studied by UPS, and clear evidence for the coexistence of O2- and O22- is seen in PbO2. A simultaneous study of 207Pb NMR suggests that the Pb ion could also exist in mixed-valence states. Qualitative arguments are presented to rationalize the existence of such mixed valences of the anion in metal oxides in general and their role in superconductivity.

Interdiffusion studies in bulk Au-Ti system

The performance of the contacts, where Au/Ti layers are used in the metallization scheme, largely depends on the product phases grown by interdiffusion at the interface. It is found that four intermetallic compounds grow with narrow homogeneity range and wavy interfaces in the interdiffusion zone. The presence of wavy interfaces is the indication of high anisotropy in diffusion of the product phases. This also reflects in the deviation of parabolic growth from the average. Further, we have determined the relevant diffusion parameters, such as interdiffusion coefficient in the penetrated region of the end members and integrated diffusion coefficients of the intermetallic compounds.

Effect of High Pressure on the Electrical Conductivity of TlInX2 (X = Se, Te) Layered Semiconductors

The dc electrical conductivity of TlInX2 (X = Se, Te) single crystals, parallel and perpendicular to the (001) c-axis is studied under high quasi-hydrostatic pressure up to 7.0 GPa, at room temperature. Conductivity measurements parallel to the c-axis are carried out at high pressures and down to liquid nitrogen temperatures. These materials show continuous metallization under pressure. Both compounds have almost the same pressure coefficient of the electrical activation energy parallel to the c-axis, d(ΔE∥)/dP = −2.9 × 10−10 eV/Pa, which results from the narrowing of the band gap under pressure. The results are discussed in the light of the band structure of these compounds.

High-pressure studies on the critical composition in Ge—As—Te glasses

High-pressure resistivity measurements have been performed on G37.5AsxTe92.5-x (x = 20, 40, 45, 50 and 55) and Ge10AsxTe90-x (x = 15, 20, 35, 40, 45 and 50) glasses. The glasses show reversible metallization behaviour under pressure. The pressure derivative of the logarithm of the resistivity of the glasses is a minimum at glass compositions corresponding to the average coordination number [r] = 2.60. This behaviour is interpreted on the basis of the existence of a critical composition in glasses with a layered structure.

High pressure electrical measurements on Ge-Te-Se glasses

Electrical resistivity measurements have been carried out on bulk Ge-Te-Se glasses in a Bridgman anvil System. The resistivity of the Ge-Te-Se samples is found to decrease continuously with increasing pressure, with the metallization occurring around 8 GPa. Ge20TexSe80-x glasses (10 less than or equal to x less than or equal to 50) with the mean co-ordination number Z(av) = 2.4 exhibit a plateau in resistivity up to about 4 GPa pressure, followed by a continuous decrease to metallic values. On the other hand, Ge10TexSe90-x glasses (10 less than or equal to x less than or equal to 40) having Z(av) = 2.2, exhibit a smaller plateau (only up to 1 GPa), followed by a decrease in resistivity with pressure. This subtle difference in the high pressure resistivity of Ge-Te-Se glasses with Z(av) < 2.4 and Z(av) greater than or equal to 2.4 can be associated with the changes in the local structure of the chalcogenide glasses with composition.

Incorporation of Interfacial Intermetallic Morphology in Fracture Mechanism Map for Sn-Ag-Cu Solder Joints

A fracture mechanism map (FMM) is a powerful tool which correlates the fracture behavior of a material to its microstructural characteristics in an explicit and convenient way. In the FMM for solder joints, an effective thickness of the interfacial intermetallic compound (IMC) layer (t (eff)) and the solder yield strength (sigma (ys,eff)) are used as abscissa and ordinate axes, respectively, as these two predominantly affect the fracture behavior of solder joints. Earlier, a definition of t (eff), based on the uniform thickness of IMC (t (u)) and the average height of the IMC scallops (t (s)), was proposed and shown to aptly explain the fracture behavior of solder joints on Cu. This paper presents a more general definition of t (eff) that is more widely applicable to a range of metallizations, including Cu and electroless nickel immersion gold (ENIG). Using this new definition of t (eff), mode I FMM for SAC387/Cu joints has been updated and its validity was confirmed. A preliminary FMM for SAC387/Cu joints with ENIG metallization is also presented.

Influence of O-2 flow rate on HfO2 gate dielectrics for back-gated graphene transistors

HfO2 thin films deposited on Si substrate using electron beam evaporation, are evaluated for back-gated graphene transistors. The amount of O-2 flow rate, during vaporation is optimized for 35 nm thick HfO2 films, to achieve the best optical, chemical and electrical properties. It has been observed that with increasing oxygen flow rate, thickness of the films increased and refractive index decreased due to increase in porosity resulting from the scattering of the evaporant. The films deposited at low O-2 flow rates (1 and 3 SCCM) show better optical and compositional properties. The effects of post-deposition annealing and post-metallization annealing in forming gas ambience (FGA) on the optical and electrical properties of the films have been analyzed. The film deposited at 3 SCCM O-2 flow rate shows the best properties as measured on MOS capacitors. To evaluate the performance of device properties, back-gated bilayer graphene transistors on HfO2 films deposited at two O-2 flow rates of 3 and 20 SCCM have been fabricated and characterized. The transistor with HfO2 film deposited at 3 SCCM O-2 flow rate shows better electrical properties consistent with the observations on MOS capacitor structures. This suggests that an optimum oxygen pressure is necessary to get good quality films for high performance devices.

Pressure-induced semiconducting to metallic transition in multilayered molybdenum disulphide

Molybdenum disulphide is a layered transition metal dichalcogenide that has recently raised considerable interest due to its unique semiconducting and opto-electronic properties. Although several theoretical studies have suggested an electronic phase transition in molybdenum disulphide, there has been a lack of experimental evidence. Here we report comprehensive studies on the pressure-dependent electronic, vibrational, optical and structural properties of multilayered molybdenum disulphide up to 35 GPa. Our experimental results reveal a structural lattice distortion followed by an electronic transition from a semiconducting to metallic state at similar to 19 GPa, which is confirmed by ab initio calculations. The metallization arises from the overlap of the valance and conduction bands owing to sulphur-sulphur interactions as the interlayer spacing reduces. The electronic transition affords modulation of the opto-electronic gain in molybdenum disulphide. This pressure-tuned behaviour can enable the development of novel devices with multiple phenomena involving the strong coupling of the mechanical, electrical and optical properties of layered nanomaterials.

Effects of Microstructure and Loading on Fracture of Sn-3.8Ag-0.7Cu Joints on Cu Substrates with ENIG Surface Finish

When dropped, electronic packages often undergo failure by propagation of an interfacial crack in solder joints under a combination of tensile and shear loading. Hence, it is crucial to understand and predict the fracture behavior of solder joints under mixed-mode high-rate loading conditions. In this work, the effects of the loading conditions (strain rate and loading angle) and microstructure interfacial intermetallic compound (IMC) morphology and solder yield strength] on the mixed-mode fracture toughness of Sn-3.8 wt.%Ag-0.7 wt.%Cu solder joints sandwiched between two Cu substrates with electroless nickel immersion gold (ENIG) metallization have been studied, and compared with the fracture behavior of joints attached to bare Cu. Irrespective of the surface finish, the fracture toughness of the solder joints decreased monotonically with strain rate and mode-mixity, both resulting in increased fracture proportion through the interfacial IMC layer. Furthermore, the proportion of crack propagation through the interfacial IMC layer increased with increase in the thickness and the roughness of the interfacial IMC layer and the yield strength of the solder, resulting in a decrease in the fracture toughness of the joint. However, under most conditions, solder joints with ENIG finish showed higher resistance to fracture than joints attached directly to Cu substrates without ENIG metallization. Based on the experimental observations, a fracture mechanism map is constructed correlating the yield strength of the solder, the morphology and thickness of the interfacial IMC, and the fracture mechanisms as well as the fracture toughness values for different solder joints under mode I loading.

Pressure-Dependent Optical and Vibrational Properties of Mono layer Molybdenum Disulfide

Controlling the band gap by tuning the lattice structure through pressure engineering is a relatively new route for tailoring the optoelectronic properties of two-dimensional (2D) materials. Here, we investigate the electronic structure and lattice vibrational dynamics of the distorted monolayer 1T-MoS2 (1T') and the monolayer 2H-MoS2 via a diamond anvil cell (DAC) and density functional theory (DFT) calculations. The direct optical band gap of the monolayer 2H-MoS2 increases by 11.7% from 1.85 to 2.08 eV, which is the highest reported for a 2D transition metal dichalcogenide (TMD) material. DFT calculations reveal a subsequent decrease in the band gap with eventual metallization of the monolayer 2H-MoS2, an overall complex structureproperty relation due to the rich band structure of MoS2. Remarkably, the metastable 1T'-MoS2 metallic state remains invariant with pressure, with the J(2), A(1g), and E(2)g modes becoming dominant at high pressures. This substantial reversible tunability of the electronic and vibrational properties of the MoS2 family can be extended to other 2D TMDs. These results present an important advance toward controlling the band structure and optoelectronic properties of monolayer MoS2 via pressure, which has vital implications for enhanced device applications.

Analysis of absorption characteristics of stacked patch arrays on moderately lossy dielectric layers

It is demonstrated that a square patch array on a moderately lossy dielectric can be transformed into a near-perfect absorber by the addition of a metallic square loop layer between the patch array and the metal back. In this configuration, the condition of perfect absorption can be easily obtained by modifying loop dimensions. The absorption properties of this configuration are analyzed theoretically using an equivalent circuit model and full-wave electromagnetic simulations. Experimental investigations included a bistatic radar cross-section measurement, which ensured that there are no scattered fields in other directions. An array structure built on a commercially available FR4 substrate with copper metallization is used to experimentally validate these results.