Pressure behavior of Te isoelectronic centers in S-rich ZnS1-xTex alloy

The photoluminescence from ZnS1-xTex alloy with 0 < x < 0.3 was investigated under hydrostatic pressure up to 7 GPa. Two peaks were observed in the alloys with x < 0.01, which are related to excitons bound to isolated Te isoelectronic impurities (Te-1 centers) and Te pairs (Te-2 centers), respectively. Only the Te-2 related emissions were observed in the alloys with 0.01 < x < 0.03. The emissions in the alloys with 0.03 < x < 0.3 are attributed to the excitons bound to the Te-n (n greater than or equal to 3) cluster centers. The pressure coefficient of the Te-1 related peak is 89(4) meV/GPa, about 40% larger than that of the band gap of ZnS. On the other hand, the pressure coefficient of the Te-2 related emissions is only 52(4) meV/GPa, about 15% smaller than that of the ZnS band gap. A simple Koster-Slater model has been used to explain the different pressure behavior of the Te-1 and Te-2 centers. The pressure coefficient of the Te-3 centers is 62(2) meV/GPa. Then the pressure coefficients of the Te-n centers decrease rapidly with further increasing Te composition.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Pressure behavior of Te isoelectronic centers in S-rich ZnS1-xTex alloy

The photoluminescence from ZnS1-xTex alloy with 0 < x < 0.3 was investigated under hydrostatic pressure up to 7 GPa. Two peaks were observed in the alloys with x < 0.01, which are related to excitons bound to isolated Te isoelectronic impurities (Te-1 centers) and Te pairs (Te-2 centers), respectively. Only the Te-2 related emissions were observed in the alloys with 0.01 < x < 0.03. The emissions in the alloys with 0.03 < x < 0.3 are attributed to the excitons bound to the Te-n (n greater than or equal to 3) cluster centers. The pressure coefficient of the Te-1 related peak is 89(4) meV/GPa, about 40% larger than that of the band gap of ZnS. On the other hand, the pressure coefficient of the Te-2 related emissions is only 52(4) meV/GPa, about 15% smaller than that of the ZnS band gap. A simple Koster-Slater model has been used to explain the different pressure behavior of the Te-1 and Te-2 centers. The pressure coefficient of the Te-3 centers is 62(2) meV/GPa. Then the pressure coefficients of the Te-n centers decrease rapidly with further increasing Te composition.

Pressure behavior of deep centers in ZnSxTe1-x alloys

We have measured photoluminescence of ZnSxTe1-x alloys (x > 0.7) at 300 K and under hydrostatic pressure up to 7 GPa. The spectra contain only a broad emission band under excitation of the 406.7 nm line. Its pressure coefficients are 47, 62 and 45 meV/GPa for x = 0.98, 0.92 and 0.79 samples, which are about 26%, 7% and 38% smaller than that of the band gap in the corresponding alloys. The Stokes shifts between emission and absorption of the bands were calculated by fitting the pressure dependence of the emission intensity, being 0.29, 0.48 and 0.13 eV for the three samples, respectively. The small pressure coefficient and large Stokes shift indicate that the emission band observed in our samples may correspond to the Te isoelectronic center in the ZnSxTe1-x alloy.

Luminescence centers and valence change of Eu2+ in KCaF3

The nature of the emission centers and the valence change of Eu2+ in KCaF3:Eu2+ depends strongly on preparation conditions. Experimental results show that there are two different d-->f emission bands, located at 425 and 510 nm, respectively. Their origin, relationship, and the effect of doping concentration on them are discussed. A Eu2+-Eu3+ valence change process is proposed. (C) 2000 Elsevier Science Ltd. All rights reserved.

Luminescent centers of EU2+ in BaMgAl10O17 phosphor

Two kinds of luminescent centers an observed in BaMgAl10O17:Eu2+ phosphor. Influence of flux on luminescence of Eu2+ in the phosphor is discussed in detail. There exists Eu2+ (F-) center (a luminescent center with 277 nm excitation band and 386 nm emission band) due to the substitution of F- ions for O2- ions, Effective energy transfer from Eu2+ (F-) to Eu2+ (O2-) (a luminescent center with 334 nm excitation band and 450 nm emission band) is observed. The quenching concentration of Eu2+ in BaMgAl10O17 is raised by 0.20 mole per mole host due to forming of new luminescent center Eu2+ (F-). (C) 2001 Elsevier Science Ltd. All rights reserved.

A rule to design high spin molecules with hetero-spin centers

The series of biradicals with m-phenylene coupling unit and hetero-spin centers were calculated compared with those possessing home-spin centers using AM1-CI method. A simple rule was proposed to design high spin molecules with ferromagnetic coupling unit and hetero-spin centers. Two neutral (or charged) hetero-spin centers resulted in high spin ground state, one neutral and another charged hetero-spin centers correspond to low spin ground state. The latter was ascribed to the huge splitting of two partially occupied molecular orbitals.

Studies on the electron transfer centers of amino oxidase immobilized on self-assembly monolayer using electrochemical methods

The direct electron transfer of amino oxidase on electrode surface based on self-assembly technique occurs at 505 mW(vs. Ag/AgCl), indicating that copper atoms are the electron transfer centers and catalytic centers of amino oxidase.