Electrical instability in vanadyl-phthalocyanine thin-film transistors

We investigated the electrical instability of vanadyl-phthalocyanine (VOPc) thin-film transistors (TFTs) at various temperatures. The results demonstrate a slow threshold voltage shift in the bias stress process and a rapid recovery after the removal of bias stress, which indicates that a slower degradation process occurs in the on state while a faster removal in the off state of VOPc TFTs. The shift of threshold voltage comes from traps generated at the organic/dielectrics interface. Additionally, a relaxation time of 10(7) s was obtained at room temperature according to the stretched exponential model, which is comparable to a-Si: H TFTs. Therefore, VOPc TFTs are suitable to be applied in flat panel displays.

Very low hysteresis organic thin-film transistors

Very low hysteresis vanadyl-phthalocyanine/para-sexiphenyl thin-film transistors (TFTs) have been fabricated using benzocyclobutenone (BCBO) derivatives/tantalum pentoxide (Ta2O5)/BCBO triple gate dielectrics. The field effect mobility, on/off current ratio and threshold voltage of organic TFTs are 0.45 cm(2) V-1 s(-1), 3.5 x 10(4) and -6.8 V, respectively. To clarify the mechanism of hysteresis, devices with different dielectrics have been studied. It is found that the bottom BCBO derivatives (contact with a gate electrode) block the electron injection from a gate electrode to dielectrics.