氧分压对ZrO2薄膜激光损伤阈值的影响

在不同的氧分压下用电子束热蒸发的方法制备了ZrO2薄膜。分别通过X射线衍射、光学光谱、热透镜技术、抗激光辐照等测试，对所制备样品的微结构、折射率、吸收率及激光损伤阈值进行了测量。实验结果表明，薄膜中晶粒主要是四方相为主的多晶结构，并且随着氧分压的增加，结晶度、折射率以及弱吸收均逐渐降低。薄膜的激光损伤阈值开始随着氧分压增加从18．5J／cm^2逐渐增加，氧分压为9×10^-3Pa时达到最大，值为26．7J／cm^2，氧分压再增加时则又降低到17．5J／cm^2。由此可见，氧分压引起的薄膜微结构变化是ZrO

Design, simulation and testing of large area silicon drift detectors and detector array for X-ray spectroscopy

Large area (25 mm(2)) silicon drift detectors and detector arrays (5x5) have been designed, simulated, and fabricated for X-ray spectroscopy. On the anode side, the hexagonal drift detector was designed with self-biasing spiral cathode rings (p(+)) of fixed resistance between rings and with a grounded guard anode to separate surface current from the anode current. Two designs have been used for the P-side: symmetric self-biasing spiral cathode rings (p(+)) and a uniform backside p(+) implant. Only 3 to 5 electrodes are needed to bias the detector plus an anode for signal collection. With graded electrical potential, a sub-nanoamper anode current, and a very small anode capacitance, an initial FWHM of 1.3 keV, without optimization of all parameters, has been obtained for 5.9 keV Fe-55 X-ray at RT using a uniform backside detector.

Design, simulation and testing of large area silicon drift detectors and detector array for X-ray spectroscopy

Large area (25 mm(2)) silicon drift detectors and detector arrays (5x5) have been designed, simulated, and fabricated for X-ray spectroscopy. On the anode side, the hexagonal drift detector was designed with self-biasing spiral cathode rings (p(+)) of fixed resistance between rings and with a grounded guard anode to separate surface current from the anode current. Two designs have been used for the P-side: symmetric self-biasing spiral cathode rings (p(+)) and a uniform backside p(+) implant. Only 3 to 5 electrodes are needed to bias the detector plus an anode for signal collection. With graded electrical potential, a sub-nanoamper anode current, and a very small anode capacitance, an initial FWHM of 1.3 keV, without optimization of all parameters, has been obtained for 5.9 keV Fe-55 X-ray at RT using a uniform backside detector.