Effect of GaAS(100) 2 degrees surface misorientation on the formation and optical properties of MOCVD grown InAs quantum dots

The influence of GaAS(1 0 0)2 degrees substrate misorientation on the formation and optical properties of InAs quantum dots (QDs) has been studied in compare with dots on exact GaAs(1 0 0) substrates. It is shown that, while QDs on exact substrates have only one dominant size, dots on misoriented substrates are formed in lines with a clear bimodal size distribution. Room temperature photoluminescence measurements show that QDs on misoriented substrates have narrower FWHM, longer emission wavelength and much larger PL intensity relative to those of dots on exact substrates. However, our rapid thermal annealing (RTA) experiments indicate that annealing shows a stronger effect on dots with misoriented substrates by greatly accelerating the degradation of material quality. (c) 2005 Elsevier B.V All rights reserved.

Investigation of a chemically treated InP(100) surface during hydrophilic wafer bonding process

Surface micro-roughness, surface chemical properties, and surface wettability are three important aspects of wafer surfaces during a wafer cleaning process, which determine the bonding quality of ordinary direct wafer bonding. In this study, InP wafers are divided into four groups and treated by different chemical processes. Subsequently, the characteristics of the treated InP surfaces are carefully studied by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and contact angle measurements. The optimal wafer treatment method for wafer bonding is determined by comparing the results of the processes as a whole. This optimization is later evaluated by a scanning electronic microscope (SEM), and the ridge waveguide 1.55 mu m Si-based InP/InGaAsP multi-quantum-well laser chips are also fabricated. (c) 2005 Elsevier B.V. All rights reserved.

INVESTIGATION OF THE GROWN DIAMOND (100) SURFACE USING HIGH-RESOLUTION ELECTRON-ENERGY LOSS SPECTROSCOPY

The diamond (100) facets deposited at initial 1.0% CH4 have been investigated using high resolution electron energy loss spectroscopy (HREELS). The diamond (100) facets grown at 800-degrees-C are terminated by CH2 radicals, and there is no detectable frequency shift compared with the characteristic frequencies of molecular subgroup CH2. Beside the CH2 vibration loss, CH bend loss (at 140 meV) of locally monohydrogenated dimer is detected for the diamond (100) facets grown at 1000-degrees-C. Dosing the (100) facets grown at 800-degrees-C with atomic hydrogen at 1*10(-6) mbar, the loss peak at 140 meV appears. It is suggested that there are enough separately vacant sites and uniformly dispersed monohydrogenated dimers on (100) facets. This structure relaxes the steric repulsion between the adjacent hydrogen atoms during the diamond (100) surface growth.

ELECTRONIC SPECTROSCOPY STUDIES OF A P2S5NH4OH TREATED GAS(100) SURFACE

Microscopic characteristics of the GaAs(100) surface treated with P2S5/NH4OH solution has been investigated by using Auger-electron spectroscopy (AES) and x-ray photoemission spectroscopy (XPS). AES reveals that only phosphorus and sulfur, but not oxygen, are contained in the interface between passivation film and GaAs substrate. Using XPS it is found that both Ga2O3 and As2O3 are removed from the GaAs surface by the P2S5/NH4OH treatment; instead, gallium sulfide and arsenic sulfide are formed. The passivation film results in a reduction of the density of states of the surface electrons and an improvement of the electronic and optical properties of the GaAs surface.

New aspects of K promoted nitridation of the InP(100) surface

The effect of molecular nitrogen exposure on the InP(100) surface modified by the alkali metal K overlayer is investigated by core-level photoemission spectroscopy using synchrotron radiation. The alkali metal covered surface exhibits reasonable nitrogen uptake at room temperature, and results in the formation of a P3N5 nitride complex. Flash annealing at 400 degrees C greatly enhanced the formation of this kind of nitride complex. Above 500 degrees C, the nitride complex dissolved completely. (C) 1997 American Vacuum Society.

PASSIVATION OF THE INP(100) SURFACE USING (NH4)(2)S-X

InP(100) surface treated with (NH4)(2)S-x has been investigated by using photoluminescence(PL), Auger electron spectroscopy and X-ray photoelectron spectroscopy. It is found that PL intensity increased by a factor of 3.3 after (NH4)(2)S-x passivation and the sulfur remained on the surface only bonded to indium, not to phosphorus. This suggests that the sulfur atoms replace the phosphorus atoms on the surface and occupy the phosphorus vacancies.

PHOTOEMISSION-STUDIES OF K-PROMOTED NITRIDATION AND OXIDATION OF THE INP(100) SURFACE USING SYNCHROTRON-RADIATION

The effect of a potassium overlayer on nitridation and oxidation of the InP(100) surface is investigated by core-level and valence-band photoemission spectroscopy using synchrotron radiation. In comparison with the K-promoted nitridation of the InP(110) surface obtained by cleavage in situ, we found that the promotive effect for the InP(100) surface cleaned by ions bombardment is much stronger and that the nitridation products consist of two kinds of complexes: InPNx and InPNx+y. The results confirmed that surface defects play an important part in the promotive effect. Furthermore, in contrast with K-promoted oxidation of InP(100) where bonding is observed between indium and oxygen, indium atoms did not react directly with nitrogen atoms during the K-promoted nitridation of InP(100). (C) 1995 American Vacuum Society.

PHOTOEMISSION-STUDIES OF K-PROMOTED NITRIDATION OF INP(100) SURFACE USING SYNCHROTRON-RADIATION

The effect of molecular nitrogen exposure on the surfaces of InP(100) modified by potassium overlayers is investigated by core-level and valence-band photoemission spectroscopy using Synchrotron radiation. In comparison with InP(110) surface, we found the promotion is much stronger for InP(100) surface due to the central role of surface defects in the promotion; furthermore, in contrast with K-promoted oxidation of InP(100) where the bonding is observed between indium and oxygen, indium atoms did not react directly with nitrogen atoms during the K-promoted nitridation of InP(100).

Evidence for perimeter sites over SmOx-modified Rh(100) surface by CO chemisorption

SmOx modified Rh(l 0 0) surfaces have been in-situ prepared by depositing metallic Sin and subsequently oxidizing under controlled conditions, and the interaction between the lanthanide oxide and transition metal has been characterized by means of X-ray photoelectron spectroscopy (XPS) and high-resolution electron-energy-loss spectroscopy (HREELS) as well as thermal desorption spectroscopy (TDS). As evidenced, the adsorption of CO on the modified surfaces shows some different features to the original surface of Rh(l 00). The covering of SmOx blocks some sites on the surface and consequently suppresses adsorption of the typical CO species with an uptake at about 500 K, while a novel desorption peak centered at 260 K emerges in the CO TDS. Correspondingly, the XP spectrum exhibits a new C Is peak at 287.9 eV and 0 Is peak at 532.6 eV. The intensity of the low temperature peak varies with the coverage of SmOx, which shows an actual correlation to the perimeter sites of SmOx particles on the surface. (C) 2004 Elsevier B.V. All rights reserved.

Addition reaction of nitrones on the reconstructed Si(100)-2 x 1 surface

The reaction of nitrone, N-methyl nitrone, and their hydroxylamine tautomers (vinyl-hydroxylamine and N-methyl vinyl-hydroxylamine) on the reconstructed Si(100)-2 x 1 surface has been investigated by means of hybrid density functional theory (B3LYP) and Moller-Plesset second-order perturbation (MP2) methods. The calculations predicted that both of the nitrones should react with the surface dimer via facile concerted 1,3-dipolar cycloaddition leading to 5-member-ring compounds. The reaction of hydroxylamine tautomers on the Si(100) surface follows pi-complex (intermediate) mechanism. For the reaction of N-methyl vinyl-hydroxylamine, the pi-complex intermediate undergoes [2+2] cycloaddition leading to a 4-member-ring compound. But in the reaction of vinyl-hydroxylamine, the intermediate undergoes H-migration reaction ("ene" reaction) resulting in the oxime-terminated Si surface. All the surface reactions result in the hydroxyl-terminated silicon surfaces, which are very useful for the further modification of the semiconductor.