A Low-Voltage Silicon Light Emitting Device in Standard Salicide CMOS Technology

National Natural Science Foundation of China 60536030 60776024 60877035 90820002 National High-Technology Research and Development Program of China 2007AA04Z329 2007AA04Z254

Role of Bi3+ ions for Er3+ ions efficient 1.54 mu m light emission in Er/Bi codoped SiO2 thin film prepared by sol-gel method

Er/Bi codoped SiO2 thin films were prepared by sol-gel method and spin-on technology with subsequent annealing process. The bismuth silicate crystal phase appeared at low annealing temperature while vanished as annealing temperature exceeded 1000 degrees C, characterized by X-ray diffraction, and Rutherford backscattering measurements well explained the structure change of the films, which was due to the decrease of bismuth concentration. Fine structures of the Er3+-related 1.54 mu m light emission (line width less than 7 nm) at room temperature was observed by photoluminescence (PL) measurement. The PL intensity at 1.54 gm reached maximum at 800 degrees C and decreased dramatically at 1000 degrees C. The PL dependent annealing temperature was studied and suggested a clear link with bismuth silicate phase. Excitation spectrum measurements further reveal the role of Bi3+ ions for Er3+ ions near infrared light emission. Through sol-gel method and thermal treatment, Bi3+ ions can provide a perfect environment for Er3+ ion light emission by forming Er-Bi-Si-O complex. Furthermore, energy transfer from Bi3+ ions to Er3+ ions is evidenced and found to be a more efficient way for Er3+ ions near infrared emission. This makes the Bi3+ ions doped material a promising application for future erbium-doped waveguide amplifier and infrared LED

Transparent and Light-Emitting Epoxy Super-Nanocomposites Containing ZnO-QDs/SiO2 Nanocomposite Particles as Encapsulating Materials for Solid-State Lighting

In this article, the ZnO quantum dots-SiO2 (Z-S) nanocomposite particles were first synthesized. Transparent Z-S/epoxy super-nanocomposites were then prepared by introducing calcined Z-S nanocomposite particles with a proper ratio of ZnO to SiO2 into a transparent epoxy matrix in terms of the filler-matrix refractive index matching principle. It was shown that the epoxy super-nanocomposites displayed intense luminescence with broad emission spectra. Moreover, the epoxy super-nanocomposites showed the interesting afterglow phenomenon with a long phosphorescence lifetime that was not observed for ZnO-QDs/epoxy nanocomposites. Finally, the transparent and light-emitting Z-S/epoxy super-nanocomposites were successfully employed as encapsulating materials for synthesis of highly bright LED lamps.

High transmission of slow light in the photonic crystal waveguide bends

We present the research on the transmission characteristic of slow-light-mode in the photonic crystal line-defect waveguide bends on SOL After optimizing the structure parameters in the vicinity of the bends, the normalized transmission efficiency of slow-light-mode through the photonic crystal 60 degree and 120 degree waveguide bends are as high as 80% and 60% respectively, which are 10 times higher than that in the undeformed case. To slow down light further, we design novel coupled cavity waveguide bend structures with high quality-factor. High normalized transmission efficiency of 75% and low group velocity of c/170 ( c is the light velocity in vacuum) are realized. These results are beneficial to enhance the slow light effect of photonic crystal structures and improve the miniaturization and integration of photonic crystal slow light devices.

Flexible Control of Light Propagation Using a Novel Photonic Crystal Hetero-Waveguide Based on Silicon-on-Insulator Slab

We demonstrate a photonic crystal hetero-waveguide based on silicon-on-insulator (SOI) slab, consisting of two serially connected width-reduced photonic crystal waveguides with different radii of the air holes adjacent to the waveguide. We show theoretically that the transmission window of the structure corresponds to the transmission range common to both waveguides and it is in inverse proportion to the discrepancy between the two waveguides. Also the group velocity of guided mode can be changed from low to high or high to low, depending on which port of the structure the signal is input from just in the same device, and the variation is proportional to the discrepancy between the two waveguides. Using this novel structure, we realize flexible control of transmission window and group velocity of guided mode simultaneously.

Realization of MMI power splitter by UV-light imprinting technique using hybrid sol-gel SiO2 materials

An efficient fabrication scheme of buried ridge waveguide devices is demonstrated by UV-light imprinting technique using organic-in organic hybrid sol-gel Zr-doped SiO2 materials. The refractive indices of a guiding layer and a cladding layer for the buried ridge waveguide structure are 1.537 and 1.492 measured at 1550 nm, respectively. The tested results show more circular mode profiles clue to existence of the cladding layer. A buried ridge single-mode waveguide operating at 1550 nm has a low propagation loss (0.088 dB/cm) and the 1 x 2 MMI power splitter exhibits uniform outputs, with a very low splitting loss of 0.029 dB at 1549 nm.

Anomalous photogalvanic effect of circularly polarized light incident on the two-dimensional electron gas in AlxGa1-xN/GaN heterostructures at room temperature

Under normal incidence of circularly polarized light at room temperature, a charge current with swirly distribution has been observed in the two-dimensional electron gas in Al0.25Ga0.75N/GaN heterostructures. We believe that this anomalous charge current is produced by a radial spin current via the reciprocal spin Hall effect. It suggests a new way to research the reciprocal spin Hall effect and spin current on the macroscopic scale and at room temperature.

Improved light extraction of GaN-based LEDs with nano-roughened p-GaN surfaces

p-GaN surfaces are nano-roughened by plasma etching to improve the optical performance of GaN-based light emitting diodes (LEDs). The nano-roughened GaN present a relaxation of stress. The light extraction of the LEDs with nano-roughened surfaces is greatly improved when compared with that of the conventional LEDs without nano-roughening. PL-mapping intensities of the nano-roughened LED epi-wafers for different roughening times present two to ten orders of enhancement. The light output powers are also higher for the nano-roughened LED devices. This improvement is attributed to that nano-roughened surfaces can provide photons multiple chances to escape from the LED surfaces.

Fabrication and optical characterization of GaN-based nanopillar light emitting diodes

InGaN/GaN-multiple-quantum-well-based light emitting diode ( LED) nanopillar arrays with a diameter of approximately 200nm and a height of 700nm are fabricated by inductively coupled plasma etching using Ni self-assembled nanodots as etching mask. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence ( PL) intensity is achieved after the fabrication of nanopillars, and a blue shift and a decrease of full width at half maximum of the PL peak are observed. The method of additional wet etching with different chemical solutions is used to remove the etch-induced damage. The result shows that the dilute HCl ( HCl:H2O=1:1) treatment is the most effective. The PL intensity of nanopillar LEDs after such a treatment is about 3.5 times stronger than that before treatment.

A GaN photodetector integrated structure for wavelength characterization of ultraviolet light

An interesting GaN photodetector structure, which can be used for characterizing the wavelength of incident ultraviolet light, is proposed. It is composed of two back-to-back integrated diodes, i.e. p-n and p-i-n GaN ultraviolet photodiodes with different spectral response. The wavelength of monochromatic ultraviolet light could be identified by measuring the photocurrent ratio value through a simple electronic circuit.

The performance enhancement in organic light-emitting diode using a semicrystalline composite for hole injection

A semicrystalline composite, 3, 4, 9, 10 perylenetetracarboxylic dianhydride (PTCDA) doped N,N'-di(1-naphthyl)-N,N'-diphenylbenzidine (NPB), has been fabricated and characterized. An organic light-emitting diode using such a composite in hole injection exhibits the improved performance as compared with the reference device using neat NPB in hole injection. For example, at a luminance of 2000 cd/m(2), the former device gives a current efficiency of 2.0cd/A, higher than 1.6cd/A obtained from the latter device. Furthermore, the semicrystalline composite has been shown thermally to be more stable than the neat NPB thin film, which is useful for making organic light emitting diodes with a prolonged lifetime.

Realization of extremely broadband quantum-dot superluminescent light-emitting diodes by rapid thermal-annealing process

The first demonstration, to our knowledge, of the creation of ultrabroadband superluminescent light-emitting diodes using multiple quantum-dot layer structure by rapid thermal-annealing process is reported. The device exhibits a 3 dB emission bandwidth of 146 nm centered at 984 mm with cw output power as high as 15 mW at room temperature corresponding to an extremely small coherence length of 6.6 mu m. (C) 2008 Optical Society of America.

Enhanced modulation bandwidth of a Fabry-Perot semiconductor laser subject to light injection from another Fabry-Perot laser

Variations in optical spectrum and modulation band-width of a modulated Fabry-Perot (FP) semiconductor laser subject to the external light injection from another FP Laser is investigated in this paper. Optimal wavelength matching conditions for two FP lasers are discussed. A series of experiments show that two FP lasers should have a central wavelength overlapping and a mode spacing difference of several gigahertz. Under these conditions both the magnitude and phase frequency responses can be improved significantly.

Organic light emitting diodes using magnesium doped organic acceptor as electron injection layer and silver as cathode

Organic light emitting diodes employing magnesium doped electron acceptor 3, 4, 9, 10 perylenetetracarboxylic dianhydride (Mg: PTCDA) as electron injection layer and silver as cathode were demonstrated. As compared to Mg: Ag cathode, the combination of the Mg: PTCDA layer and silver provided enhanced electron injection into tris (8-quinolinolato) aluminium. The device with 1: 2 Mg: PTCDA and Ag showed an increase of about 12% in the maximum current efficiency, mainly due to the improved hole-electron balance, and an increase of about 28% in the maximum power efficiency, as compared to the control device using Mg: Ag cathode. The properties of Mg: PTCDA composites were studied as well.

Long-wavelength light emission from self-assembled heterojunction quantum dots

The authors report the optical characteristics of GaSb/InAs/GaAs self-assembled heterojunction quantum dots (QDs). With increasing GaSb deposition, the room temperature emission wavelength can be extended to 1.56 mu m. The photoluminescence mechanism is considered to be a type-II transition with electrons confined in InAs and holes in GaSb.(C) 2008 American Institute of Physics.