The fabrication of TiO2-supported zeolite with core/shell heterostructure for ethanol dehydration to ethylene

The TiO2-supported zeolite with core/shell heterostructure was fabricated by coating aluminosilicate zeolite (ASZ) on the TiO2 inoculating seed via in situ hydrothermal synthesis. The catalysts were characterized by transmission electron microscope (TEM), X-ray diffraction (XRD), nitrogen physisorption (BET), and Fourier transform infrared spectroscopy (FT-IR). The surface acidity of the catalysts was measured by pyridine-TPD method. The catalytic performance of the catalysts for ethanol dehydration to ethylene was also investigated. The results show that the TiO2-supported zeolite composite catalyst with core/shell heterostructure exhibits prominent conversion efficiency for ethanol dehydration to ethylene.

Partial oxidation reforming of biomass fuel gas over nickel-based monolithic catalyst with naphthalene as model compound

With naphthalene as biomass tar model compound, partial oxidation reforming (with addition of O-2) and dry reforming of biomass fuel gas were investigated over nickel-based monoliths at the same conditions. The results showed that both processes had excellent performance in upgrading biomass raw fuel gas. Above 99% of naphthalene was converted into synthesis gases (H-2+CO). About 2.8 wt% of coke deposition was detected on the catalyst surface for dry reforming process at 750 degrees C during 108 h lifetime test. However, no Coke deposition was detected for partial oxidation reforming process, which indicated that addition of O-2 can effectively prohibit the coke formation. O-2 Can also increase the CH4 conversion and H-2/CO ratio of the producer gas. The average conversion of CH4 in dry and partial oxidation reforming process was 92% and 95%, respectively. The average H-2/CO ratio increased from 0.95 to 1.1 with the addition of O-2, which was suitable to be used as synthesis gas for dimethyl ether (DME) synthesis.

Fabrication of microstructured polymer optical fiber preform

SPIE

Research on micro-optical lenses fabrication technology

We present a detail investigation on the development of a series of gradient index (GRIN) optical glass microlens and polymer microlens and microlens arrays in our laboratory in recent years. The special glass material GRIN lenses have been fabricated mainly by using ion-exchange technology, which are applied to construct micro-optic devices and other applications. On one hand, we demonstrated the light propagation and imaging properties of GRIN lenses and the results analyzed. On the other hand, we have explored a drop-on-demand ink-jet printing method to produce microlens array using nano-scale polymer droplets involved with a uniform ultraviolet light and heat solidifying process. The experimental setup for manufacturing polymer microlens array and the performance of refractive microlens elements are also given in this paper. (C) 2006 Elsevier GmbH. All rights reserved.

Liquid-filled microstructured polymer fibers as monolithic liquid-core array fibers

Liquid-filled microstructured polymer optical fibers (MPOFs) as monolithic liquid-core array fiber are proposed and prepared by injecting high-refractive-index liquid into the holes array of the MPOFs. One example for potential applications is demonstrated as a new kind of coherent imaging fiber. It provides great potential for applications in chemical sensing, biosensors, and endoscopy, particularly in bifunctional detection. (C) 2009 Optical Society of America

Composition Optimization of Tellurite Glass for Low-Loss and Robust Fiber Fabrication

低损耗高强度碲酸盐玻璃光纤用光学材料的优化方案

The fabrication of GaN-based nanopillar light-emitting diodes

InGaN/GaN multiple quantum well-based light-emitting diode (LED) nanopillar arrays were fabricated using Ni self-assembled nanodots as etching mask. The Ni nanodots were fabricated with a density of 6 x 10(8)-1.5 x 10(9) cm(-2) and a dimension of 100-250 nm with varying Ni thickness and annealing duration time. Then LED nanopillar arrays with diameter of approximately 250 nm and height of 700 nm were fabricated by inductively coupled plasma etching. In comparison to the as-grown LED sample an enhancement by a factor of four of photoluminescence (PL) intensity is achieved for the nanopillars and a blueshift as well as a decrease in full width at half maximum of the PL peak are also observed. The method of additional chemical etching was used to remove the etching-induced damage. Then nano-LED devices were further completed using a planarization approach to deposit p-type electrode on the tips of nanopillars. The current-voltage curves of both nanopillars and planar LED devices are measured for comparison.