Photoinduced spin alignment of the magnetic ions in (Ga,Mn)As

Time-resolved Kerr rotation measurement in the (Ga,Mn)As diluted magnetic semiconductor allows direct observation of the dynamical properties of the spin system of the magnetic ions and the spin-polarized holes. Experimental results show that the magnetic ions can be aligned by the polarized holes, and the time scales of spin alignment and relaxation take place in tens and hundreds of picoseconds, respectively. The Larmor frequency and effective g factor obtained in the Voigt geometry show an unusual temperature dependence in the vicinity of the Curie temperature due to the exchange coupling between the photoexcited holes and magnetic ions. Such a spin coherent precession can be amplified or destructed by two sequential excitation pulses with circularly copolarized or oppositely polarized helicity, respectively. (c) 2006 American Institute of Physics.

Raman scattering study on vibrational modes in Ga1-xMnxN prepared by Mn-ion implantation

Raman scattering measurements have been carried out on ferromagnetic semiconductor Ga1-xMnxN prepared by Mn-ion implantation and post annealing. The Raman results obtained from the annealed and un-annealed Ga1-xMnxN demonstrate that crystalline quality has been improved in Ga1-xMnxN after annealing. Some new vibrational modes in addition to GaN-like modes are found in the Raman spectra measured from the Ga1-xMnxN where the GaN-like modes are found to be shifted in the higher frequency side than those measured from the bulk GaN. A new vibrational mode observed is assigned to MnN-like mode. Other new phonon modes observed are assigned to disorder-activated modes and Mn-related vibrational modes caused by Mn-ion implantation and post-annealing. (c) 2006 Elsevier Ltd. All rights reserved.

Investigation of Mn-doped Si films prepared by magnetron cosputtering

Mn-doped Si films were prepared on Si(001) substrates by magnetron cosputtering and post-annealing process. The structural, morphological and magnetic properties of the films have been investigated. X-ray diffraction results show that the as-prepared film is amorphous. By annealing at 800 degrees C, however, the film is crystallized. There is no secondary phase found except Si in the two films. Chemical mapping shows that no segregation of the Mn atoms appears in the annealed film. Atomic force microscopy images of the films indicate that the annealed film has a granular feature that covers uniformly the film surface while there is no such kind of characteristic in the as-prepared film. The field dependence of magnetization was measured using an alternating gradient magnetometer, and it has been indicated that the annealed film shows room-temperature ferromagnetism. (c) 2006 Elsevier B.V. All rights reserved.

Growth and properties of magnetron cosputtering grown Mn(x)Ge(1-x)on Si(001)

We have grown MnxGe1-x films (x=0, 0.06, 0.1) on Si (001) substrates by magnetron cosputtering, and have explored the resulting structural, morphological, electrical and magnetic properties. X-ray diffraction results show there is no secondary phase except Ge in the Mn0.06Ge0.94 film while new phase appears in the Mn0.1Ge0.9 film. Nanocrystals are formed in the Mn0.06Ge0.94 film, determined by field-emission scanning electron microscopy. Hall measurement indicates that the Mn0.06Ge0.94 film is p-type semiconductor and hole carrier concentration is 6.07 X 10(19) cm(-3) while the MnxGe1-x films with x=0 has n-type carriers. The field dependence of magnetization was measured using alternating gradient magnetometer, and it has been indicated that the Mn0.06Ge0.94 film is ferromagnetic at room temperature. (c) 2005 Elsevier Ltd. All rights reserved.

Pressure dependence of Mn2+ luminescence in differently sized ZnS : Mn nanoparticles

The pressure behavior of Mn2+ emission in the 10-, 4.5-, 3.5-, 3-, and 1-nm-sized ZnS:Mn2+ nanoparticles is investigated. The emission shifts to lower energies with increasing pressure, and the shift rate (the absolute value of the pressure coefficient) is larger in the ZnS:Mn2+ nanoparticles than in bulk. The pressure coefficient increases with the decrease in particle size with the 1-nm-sized particles as an exception. Pressure coefficient calculations based on the crystal field theory are in agreement with the experimental results. The pressure dependence of the emission intensity is also size dependent. For nanoparticles 1 and 3 nm in size, the luminescence intensity of Mn2+ decreases dramatically with increasing pressure, while, for bulk and particles with average sizes of 3.5, 4.5, and 10 nm, the luminescence intensity of Mn2+ is virtually unchanged at different pressures. The bandwidth increases faster with increasing pressure for smaller particles. This is perhaps due to the fact that there are more Mn2+ ions at the near-surface sites and because the phonon frequency is greater for smaller particles. These new phenomena provide some insight into the luminescence behavior of Mn2+ in ZnS:Mn2+ nanoparticles.

The micro-magnetic structures of Mn+ ion-implanted GaSb

The micro-magnetic structures of Mn+ ion-implanted GaSb are studied using a magnetic force microscope (MFM). MFM images reveal that there are many magnetic domains with different magnetization directions in our samples. The magnetic domain structures and the magnetization direction of typical MFM patterns are analyzed by numeric simulation.

(Ga,Mn,N) compounds growth with mass-analyzed low energy dual ion beam deposition

The (Ga,Mn,N) samples were grown by the implantation of low-energy Mn ions into GaN/Al2O3 substrate at different elevated substrate temperatures with mass-analyzed low-energy dual ion beam deposition system. Auger electron spectroscopy depth profile of samples grown at different substrate temperatures indicates that the Mn ions reach deeper in samples with higher substrate temperatures. Clear X-ray diffraction peak from (Ga,Mn)N is observed in samples grown at the higher substrate temperature. It indicates that under optimized substrate temperature and annealing conditions the solid solution (Ga,Mn)N phase in samples was formed with the same lattice structure as GaN and different lattice constant. (C) 2003 Elsevier Science B.V. All rights reserved.

Temperature behaviour of the orange and blue emissions in ZnS : Mn nanoparticles

The temperature dependences of the orange and blue emissions in 10, 4.5, and 3 nm ZnS:Mn nanoparticles were investigated. The orange emission is from the T-4(1)-(6)A(1) transition of Mn2+ ions and the blue emission is related to the donor-acceptor recombination in the ZnS host. With increasing temperature, the blue emission has a red-shift. On the other hand, the peak energy of the orange emission is only weakly dependent on temperature. The luminescence intensity of the orange emission decreases rapidly from 110 to 300 K for the 10 nm sample but increases obviously for the 3 nm sample, whereas the emission intensity is nearly, independent of temperature for the 4.5 nm sample. A thermally activated carrier-transfer model has been proposed to explain the observed abnormal temperature behaviour of the orange emission in ZnS:Mn nanoparticles.

(Ga,Mn,As) compounds grown on semi-insulating GaAs with mass-analyzed low energy dual ion beam depositionw

The (Ga,Mn,As) compounds were obtained by the implantation of Mn ions into semi-insulating GaAs substrate with mass-analyzed low energy dual ion beam deposition technique. Auger electron spectroscopy depth profile of a typical sample grown at the substrate temperature of 250degreesC showed that the Mn ions were successfully implanted into GaAs substrate with the implantation depth of 160 nm. X-ray diffraction was employed for the structural analyses of all samples. The experimental results were greatly affected by the substrate temperature. Ga5.2Mn was obtained in the sample grown at the substrate temperature of 250degreesC. Ga5.2Mn, Ga5Mn8 and Mn3Ga were obtained in the sample grown at the substrate temperature of 400degreesC. However, there is no new phase in the sample grown at the substrate temperature of 200degreesC. The sample grown at 400degreesC was annealed at 840degreesC. In this annealed sample Mn3Ga disappeared, Ga5Mn8 tended to disappear,Ga5.2Mn crystallized better and a new phase of Mn2As was generated. (C) 2002 Elsevier Science B,V. All rights reserved.

Mechanical alloying of Fe-Mn and Fe-Mn-Si

The ball milling of Fe-24Mn and Fe-24Mn-6Si mixed powders has been performed by the high energy ball milling technique. By employing X-ray diffraction and Mossbauer measurements, the composition evolution during the milling process has been investigated. The results indicate the formation of paramagnetic Fe-Mn or Fe-Mn-Si alloys with a metastable fee phase as final products, which imply that the Fe and Mn proceed a co-diffusion mechanism through the surface of fragmented powders. The thermal stability and composition evolution of the as-milled alloys were discussed comparing with the bulk alloy. (C) 1999 Published by Elsevier Science S.A. All rights reserved.

Tunneling magnetoresistance in (Ga,Mn)As/Al-O/CoFeB hybrid structures

Tunneling magnetoresistance (TMR) in Ga(0.9)2Mn(0.08)As/Al-O/Co40Fe40B20 trilayer hybrid structure as a function of temperature from 10 to 50 K with magnetic field vertical bar H vertical bar <= 2000 Oe has been studied. TMR ratio of 1.6% at low fields at 10 K was achieved with the applied current of 1 mu A. The behavior of junction resistance was well explained by the tunneling resistance across the barrier. Strong bias dependences of magnetoresistance and junction resistance were presented. (C) 2009 American Institute of Physics. [DOI: 10.1063/1.3068418]

Raman scattering study on diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation

Raman scattering measurements have been performed in diluted magnetic semiconductor Ga1-xMnxAs prepared by Mn-ion implantation, deposition, and post-annealing technique. It is found that the Raman spectrum measured from the implanted surface of the sample shows some new weak modes in addition to the GaAs-like modes which are observed from the unimplanted surface. The new vibrational modes observed are assigned to MnAs-like modes. The coupled LO-phonon plasmon mode, and Mn and As related vibrational modes caused by Mn-ion implantation, deposition, and post-annealing are also observed. Furthermore, the GaAs-like modes are found to be shifted by approximately 4 cm(-1) in the lower frequency side, compared with those observed from the unimplanted surface.

Raman scattering study on vibrational modes in Ga1-xMnxN prepared by Mn-ion implantation

Raman scattering measurements have been carried out on ferromagnetic semiconductor Ga1-xMnxN prepared by Mn-ion implantation and post annealing. The Raman results obtained from the annealed and un-annealed Ga1-xMnxN demonstrate that crystalline quality has been improved in Ga1-xMnxN after annealing. Some new vibrational modes in addition to GaN-like modes are found in the Raman spectra measured from the Ga1-xMnxN where the GaN-like modes are found to be shifted in the higher frequency side than those measured from the bulk GaN. A new vibrational mode observed is assigned to MnN-like mode. Other new phonon modes observed are assigned to disorder-activated modes and Mn-related vibrational modes caused by Mn-ion implantation and post-annealing. (c) 2006 Elsevier Ltd. All rights reserved.

Optical properties of Mn+ doped GaAs

The above work was supported by the national Basic Research Program of China (2006cb604904, 2006cb604908), the hi-tech R & D program of China (2006aa03z0408, 2006aa03z0404), the scientific research Fund of Central South University of Forstry and Technology.