Growth of high quality semi-insulating InP single crystal by suppression of compensation defects

Deep level defects in as-grown and annealed SI-InP samples were investigated by thermally stimulated current spectroscopy. Correlations between electrical property, compensation ratio, thermal stability and deep defect concentration in SI-InP were revealed. An optimized crystal growth condition for high quality SI-InP was demonstrated based on the experimental results.

Improvement of the electrical property of semi-insulating InP by suppression of compensation defects

Semi-insulating (SI) InP obtained by iron phosphide ambient annealing has very low concentration of deep level defects and better electrical property than SI-InP annealed in phosphorus ambient. The defect suppression phenomenon correlates with Fe diffusion and substitution in the annealing process. Analysis of the experimental result suggests that a high activation ratio of incorporated Fe in InP has an effect of defect suppression in Fe-doped and Fe-diffused SI-InP.

PASSIVATION OF COPPER BY LITHIUM IN P-TYPE GAAS

We report the passivation of two deep copper-related acceptor levels in Cu-diffused p-type GaAs by the group-I element lithium. The deep-level-transient-spectroscopy (DLTS) signals of the well-known Cu-related levels with apparent activation energies 0.15 eV and 0.40 eV disappear in Cu-diffused samples when they are diffused with Li, but can be reactivated by annealing. Photoluminescence measurements show a corresponding disappearance and reappearance of the copper-related luminescence at 1.36 eV. Also we observe with DLT'S an energy level at E(V) + 0.32 eV in the Cu-Li-diff-used samples. The level is neither present in the Cu-diffused samples before Li diffusion nor in Cu-Li-diffused samples after annealing. As the level is not observed in starting materials or solely Li-diffused samples we suggest that it is related to a Cu-Li complex.

OXYGEN IN INXGA1-XASYP1-Y GROWN ON GAAS

The measurement of DLTS on the alloy InxGa1-xAsyP1-y (0 less-than-or-equal-to y less-than-or-equal-to 0.3; 0.5 greater-than-or-equal-to x greater-than-or-equal-to 0.35) shows a new signal, labeled as E2, with an activation energy of E(c) - 0.61 eV and the SIMS signals show a large number of oxygen. To clarify is further, the energy of the deep level E2 is quantitatively calculated by using Vogl's tight-binding theory and Hjalmarson's deep level theory. As a result, the deep A1-symmetric level associated with an oxygen on the anion site of InxGa1-xAsyP1-y locates deeply in the band gap. Thus, the level E2 is considered to be induced by the oxygen impurity.

ON THE FORMATION OF THE SBGA HETEROANTISITE IN METALORGANIC VAPOR-PHASE EPITAXIAL GAAS-SB

Metalorganic vapor-phase epitaxial growth of GaAs doped with isovalent Sb is reported. By increasing the trimethylantimony concentration during growth the total Sb concentration was varied between 1 X 10(17)-1 X 10(19) cm-3. A new deep level defect with an activation energy of the thermal emission rates of E(c) - 0.54 eV is observed. The defect concentration increases with increasing As partial pressure and with increasing Sb doping. It is also found that the EL2 concentration decreases with increasing Sb doping. The new energy level is suggested to be the 0/ + transition of the Sb(Ga) heteroantisite defect. No photocapacitance quenching effect, reflecting a metastable state as seen for EL2 (As(Ga)), is observed for Sb(Ga).

ELECTRICAL CHARACTERS OF OXYGEN DEFECTS IN SILICON SUBJECTED TO INTRINSIC GETTERING TREATMENT

The influence of oxygen defects on the resistivity and mobility of silicon wafers is discussed. Grinding processes were performed on the surfaces of samples in order to obtain the information on interior defects of the samples. Spreading resistivity and Hall measurements prove that SiO(x) complexes alone result in resistivity increase and mobility decrease. Deep level transient spectroscopy experiments prove that SiO(x) complexes alone are electrically active. A mechanism of carrier scattering by electrically active SiO(x) complex is proposed to explain the changes of resistivity and mobility.

IDENTIFICATION OF THE ENERGY-LEVELS OF SI-RH

Two thermostable levels E(0.31) and E(0.58) related to Rh in Si were observed using deep level transient spectroscopy and double correlation deep level transient spectroscopy techniques. By means of thermal annealing and electron irradiation, the microscopic natures of these levels were identified for the first time. The levels E(0.31) and E(0.58) arise from by the same impurity center but have different charge states. Their microstructures are not related to a pure substitutional Rh atom, but correspond to a complex. This result is compared to our self-consistent theoretical calculation.

Sulfur forming an isoelectronic center in zinc telluride thin films

ZnTe1-xSx epitaxial layers grown on GaAs by molecular-beam epitaxy were studied by photoluminescence (PL) as a function of temperatures, excitation powers, and hydrostatic pressures. A sulfur-related emission peak, labeled as P-2, is identified as a deep-level emission by hydrostatic-pressure PL measurement. This indicates that sulfur atoms form isoelectronic centers in a ZnTe matrix. The results qualitatively agree with the theoretical prediction and show experimental evidence of isoelectronic S in ZnTe. A model is proposed to explain the emission mechanisms in the ZnTe1-xSx system with small x values.

Temperature-stimulated abnormal annealing of neutron-induced damage in high-resistivity silicon detectors

Neutron-irradiated high-resistivity silicon detectors have been subjected to elevated temperature annealing (ETA). It has been found that both detector full depletion voltage and leakage current exhibit abnormal annealing (or ''reverse annealing'') behaviour for highly irradiated detectors: increase with ETA. Laser induced current measurements indicate a net increase of acceptor type space charges associated with the full depletion voltage increase after ETA. Current deep level transient spectroscopy (I-DLTS) and thermally stimulated current (TSC) data show that the dominant effect is the increase of a level at 0.39 eV below the conduction band (E(c) - 0.39 eV) or a level above the valence band (E(v) + 0.39 eV). Candidates tentatively identified for this level are the singly charged double vacancy (V-V-) level at E(c) - 0.39 eV, the carbon interstitial-oxygen interstitial (C-i-O-i) level at E(v) + 0.36 eV, and/or the tri-vacancy-oxygen center (V3O) at E(v) + 0.40 eV.

Characterization of recombination centres in n-type Hg1-xCdxTe

The defect levels in Hg1-xCdxTe P+N junction photodiodes (x = 0.4) were first studied using deep-level transient spectroscopy. Two electron traps, E(1)(0.06) and E(2)(0.15), and two hole traps, H-1(0.075) and H-2(0.29), were obtained, Characteristic parameters-the minority lifetime of the devices and the dynamic resistance-area product at zero bias-are estimated according to these levels. Results show that these two minority levels may be important in controlling lifetime. We have studied the recombination mechanism of the hole trap H-2(0.29) further. It has a large activation energy and satisfies the formula sigma(T) = sigma(x) exp(-E(F)/E(T)). This reflects the fact that its recombination mechanism is multiphonon nonradiative recombination, which is rarely reported in narrow-bandgap materials.

High efficiency AlxGa1-xAs/GaAs solar cells: Fabrication, irradiation and annealing effect

High efficiency AlxGa1-xAs/GaAs heteroface solar cells have been fabricated by an improved multi-wafer squeezing graphite boat liquid phase epitaxy (LPE) technique, which enables simultaneous growth of twenty 2.3 X 2.3cm(2) epilayers in one run. A total area conversion efficiency of 17.33% is exhibited (1sun, AM0, 2.0 x 2.0cm(2)). The shallow junction cell shows more resistance to 1 MeV electron radiation than the deep one. After isochronal or isothermal annealing the density and the number of deep level traps induced by irradiation are reduced effectively for the solar cells with deep junction and bombardment under high electron fluences.

Characterization and improvement of GaAs layers grown on Si using an ultrathin a-Si film as a buffer layer

GaAs epilayers grown on Si by metalorganic chemical vapor deposition (MOCVD) using an ultrathin a-Si buffer layer were characterized by deep-level transient spectroscopy (DLTS). Six electron traps with activation energies of 0.79, 0.67, 0.61, 0.55, 0.53 and 0.32 eV below the conduction band were determined by fitting the experimental spectra. Two of the levels, C (0.61 eV) and F (0.32 eV), were first detected in GaAs epilayers on Si and identified as the metastable defects M3 and M4, respectively. In order to improve the quality of GaAs/Si epilayers, another GaAs layer was grown on the GaAs/Si epilayers grown using MOCVD. The deep levels in this regrown GaAs epilayer were also studied using DLTS. Only the EL2 level was found in the regrown GaAs epilayers. These results show that the quality of the GaAs epilayer was greatly improved by applying this growth process.

Investigation on the N-eff reverse annealing effect using TSC/I-DLTS: Relationship between neutron induced microscopic defects and silicon detector electrical degradations

Neutron induced defect levels in high resistivity silicon detectors have been studied using a current-based macroscopic defect analysis system: thermally stimulated current (TSC) and current deep level transient spectroscopy (I-DLTS). These studies have been correlated to the traditional C-V, I-V, and transient current and charge techniques (TCT/TChT) after neutron radiation and subsequent thermal anneals. It has been found that the increases of the space charge density, N-eff, in irradiated detectors after thermal anneals (N-eff reverse anneal) correspond to the increases of deep levels in the silicon bandgap. In particular, increases of the double vacancy center (V-V and V-V-- -) and/or C-i-O-i level have good correlations with the N-eff reverse anneal. It has also been observed that the leakage current of highly irradiated (Phi(n) > 10(13) n/cm(2)) detectors increases after thermal anneals, which is different from the leakage current annealing behavior of slightly irradiated (Phi(n) < 10(13) n/cm(2)) detectors. It is apparent that V-V center and/or C-i-O-i level play important roles in both N-eff and leakage current degradations for highly irradiated high resistivity silicon detectors.

Microscopic analysis of defects in a high resistivity silicon detector irradiated to 1.7x10(15)n/cm(2)

Current-based microscopic defect analysis methods with optical filling techniques, namely current deep level transient spectroscopy (I-DLTS) and thermally stimulated current (TSC), have been used to study defect levels in a high resistivity silicon detector (p(+)-n-n(+)) induced by very high fluence neutron (VHFN) irradiation (1.7x10(15) n/cm(2)). As many as fourteen deep levels have been detected by I-DLTS. Arrhenius plots of the I-DLTS data have shown defects with energy levels ranging from 0.03 eV to 0.5 eV in the energy band gap. Defect concentrations of relatively shallow levels (E(t) < 0.33 eV) are in the order of 10(13)cm(-3), while those for relatively deep levels (E(t) > 0.33 eV) are in the order of 10(14) cm(-3). TSC data have shown similar defect spectra. A full depletion voltage of about 27,000 volts has been estimated by C-V measurements for the as-irradiated detector, which corresponds to an effective space charge density (N-eff) in the order of 2x10(14) cm(-3). Both detector leakage current and full depletion voltage have been observed to increase with elevated temperature annealing (ETA). The increase of the full depletion voltage corresponds to the increase of some deep levels, especially the 0.39 eV level. Results of positron annihilation spectroscopy have shown a decrease of total concentration of vacancy related defects including vacancy clusters with ETA, suggesting the breaking up of vacancy clusters as possible source of vacancies for the formation of single defects during the reverse anneal.

DEVELOPMENT OF CURRENT-BASED MICROSCOPIC DEFECT ANALYSIS-METHODS AND ASSOCIATED OPTICAL FILLING TECHNIQUES FOR THE INVESTIGATION ON HIGHLY IRRADIATED HIGH-RESISTIVITY SILICON DETECTORS

Current based microscopic defect analysis methods such as current deep level transient spectroscopy (I-DLTS) and thermally stimulated current (TSC) have been further developed in accordance with the need for the defect analysis of highly irradiated (Phi(n) > 10(13) n/cm(2)) high resistivity silicon detectors. The new I-DLTS/TSC system has a temperature range of 8 K less than or equal to T less than or equal to 450 K and a high sensitivity that can detect a defect concentration of less than 10(10)/cm(3) (background noise as low as 10 fA). A new filling method using different wavelength laser illumination has been applied, which is more efficient and suitable than the traditional voltage pulse filling. It has been found that the filling of a defect level depends on such factors as the total concentration of free carriers generated or injected, the penetration length of the laser (laser wavelength), the temperature at which the filling is taking place, as well as the decay time after the filling (but before the measurement). The mechanism of the defect filling can be explained by the competition between trapping and detrapping of defect levels, possible capture cross section temperature dependence, and interaction among various defect levels in terms of charge transferring. Optimum defect filling conditions have been suggested for highly irradiated high resistivity silicon detectors.