Room temperature mobility above 2100 cm2/Vs in Al0.3Ga0.7N/AIN/GaN heterostructures grown on sapphire substrates by MOCVD

Al0.3Ga0.7N/AlN/GaN HEMT structures with significantly high mobility have been grown by metalorganic chemical vapor deposition (MOCVD) on sapphire substrates. At room temperature (RT) a Hall mobility of 2104 cm(2)/Vs and a two-dimensional electron gas (2DEG) density of 1.1x10(13) cm(-2) are achieved, corresponding to a sheet resistance of 277.8 Omega/sq. The elimination of V-shaped defects were observed on Al0.3Ga0.7N/AlN/GaN HEMT structures and correlated with the increase of 2DEG mobility. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

Influence of Al content on electrical and structural properties of Si-doped AlxGa1-xN/GaN HEMT structures

Improved electrical properties of AlxGa1-xN/GaN high electron mobility transistor (HEMT) structures grown by metalorganic chemical vapor deposition (MOCVD) were achieved through increasing the Al mole fraction in the AlGaN barrier layers. An average sheet resistance of 326.6 Omega/sq and a good resistance uniformity of 98% were obtained for a 2-inch Al0.38Ga0 62N/GaN HEMT structure. The surface morphology of AlxGa1-xN/GaN HEMT structures strongly correlates with the Al content. More defects were formed with increasing Al content due to the increase of tensile strain, which limits further reduction of the sheet resistance. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

The difference of Si doping efficiency in GaN and AlGaN in GaN-based HBT structure

An AlGaN/GaN HBT structure was grown by low-pressure metalorganic chemical vapor deposition (MOCVD) on sapphire substrate. From the high-resolution x-ray diffraction and transmission electron microscopy (TEM) measurements, it was indicated that the structure is of good quality and the AlGaN/GaN interfaces are abrupt and smooth. In order to obtain the values of Si doping and electronic concentrations in the AlGaN emitter and GaN emitter cap layers, Secondary Ion Mass Spectroscopy (SIMS) and electrochemical CV measurements were carried out. The results showed that though the flow rate of silane (SiH4) in growing the AlGaN emitter was about a quarter of that in growing GaN emitter cap and subcollector layer, the Si sputtering yield in GaN cap layer was much smaller than that in the AlGaN emitter layer. The electronic concentration in GaN was about half of that in the AlGaN emitter layer. It is proposed that the Si, Al co-doping in growing the AlGaN emitter layer greatly enhances the Si dopant efficiency in the AlGaN alloy. (c) 2006 WILEY-VCH Verlag GmbH & Co KGaA, Weinheim.

Deep levels in high resistivity GaN epilayers grown by MOCVD

Undoped high resistivity (HR) GaN epilayers were grown on (0001) sapphire substrate by metalorganic chemical vapor deposition (MOCVD). Thermally stimulated current (TSC) and resistivity measurements have been carried out to investigate deep level traps. Deep levels with activation energies of 1.06eV and 0.85eV were measured in sample 1. Gaussian fitting of TSC spectra showed five deep levels in different samples. (c) 2006 WILEY VCH Vertag GmbH & Co. KGaA, Weinheim

Research on the band-gap of InN grown on siticon substrates

Photoluminescence (PL) and absorption experiments were carried out to examine the fundamental band-gap of InN films grown on silicon substrates. A strong PL peak at 0.78 eV was observed at room temperature, which is much lower than the commonly accepted value of 1.9 eV. The integrated PL intensity was found to depend linearly on the excitation laser intensity over a wide intensity range. These results strongly suggest that the observed PL is related to the emission of the fundamental inter-band transitions of InN rather than to deep defect or impurity levels. Due to the effect of band-filling with increasing free electron concentration, the absorption edge shifts to higher energy. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

1.3 mu m high indium content (42.5%) GaInNAs/GaAs quantum wells grown by molecular beam epitaxy

High structural and optical quality 1.3 mu m GaInNAs/GaAs quantum well (QW) samples with 42.5% indium content were successfully grown by molecular beam epitaxy. The growth of well layers was monitored by reflection high-energy electron diffraction (RHEED). Room temperature photoluminescence (PL) peak intensity of the GaIn0.425NAs/GaAs (6 nm / 20 nm) 3QW is higher than, and the full width at half maximum (FWHM) is comparable to, that of In0.425GaAs/GaAs 3QW, indicating improved optical quality due to strain compensation effects by introducing N to the high indium content InGaAs epilayer. The measured (004) X-ray rocking curve shows clear satellite peaks and Pendellosung fringes, suggesting high film uniformity and smooth interfaces. The cross sectional TEM measurements further reveal that there are no structural defects in such high indium content QWs. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

异质外延立方氮化硼薄膜的微结构研究

利用离子束辅助沉积技术在金刚石薄膜衬底上制备立方氮化硼薄膜,傅立叶变换红外谱的结果表明,在高度(001)织构金刚石薄膜衬底上沉积的立方氮化硼薄膜是纯的立方相,而在多晶金刚石薄膜衬底上制备的立方氮化硼薄膜中还含少量的六角氮化硼.高分辨透射电镜的分析表明,在金刚石晶粒上异质外延的c-BN直接成核于金刚石衬底,界面没有六角氮化硼过渡层;而在含有大量缺陷的晶粒边界,存在六角氮化硼的成核与生长.