Research on the band-gap of InN grown on siticon substrates

Photoluminescence (PL) and absorption experiments were carried out to examine the fundamental band-gap of InN films grown on silicon substrates. A strong PL peak at 0.78 eV was observed at room temperature, which is much lower than the commonly accepted value of 1.9 eV. The integrated PL intensity was found to depend linearly on the excitation laser intensity over a wide intensity range. These results strongly suggest that the observed PL is related to the emission of the fundamental inter-band transitions of InN rather than to deep defect or impurity levels. Due to the effect of band-filling with increasing free electron concentration, the absorption edge shifts to higher energy. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Photoluminescence (PL) and absorption experiments were carried out to examine the fundamental band-gap of InN films grown on silicon substrates. A strong PL peak at 0.78 eV was observed at room temperature, which is much lower than the commonly accepted value of 1.9 eV. The integrated PL intensity was found to depend linearly on the excitation laser intensity over a wide intensity range. These results strongly suggest that the observed PL is related to the emission of the fundamental inter-band transitions of InN rather than to deep defect or impurity levels. Due to the effect of band-filling with increasing free electron concentration, the absorption edge shifts to higher energy. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

zhangdi于2010-03-29批量导入

Made available in DSpace on 2010-03-29T06:06:19Z (GMT). No. of bitstreams: 1 2350.pdf: 168270 bytes, checksum: 3ff8d0dbd62ba0a58ce91e45b5aa053b (MD5) Previous issue date: 2006

Chinese Acad Sci, Inst Semicond, Beijing 100083, Peoples R China