Microtwins and twin inclusions in the 3C-SiC epilayers grown on Si(001) by APCVD

Microtwins in the 3C-SiC films grown on Si(001) by APCVD were analyzed in detail using an X-ray four-circle diffractometer. The empty set scan shows that 3C-SiC films can grow on Si substrates epitaxially and the epitaxial relationship is revealed as (001)(3C-SiC)//(001)(Si), [111](3C-SiC)//[111](Si). Other diffractions emerged in the pole figures of the (111) 3C-SiC. We performed the (10 (1) over bar0) h-SiC and the reciprocal space mapping of the (002) plane of twins for the first time, finding that the diffractions at chi = 15.8 degrees result from not hexagonal SiC but microtwins of 3C-SiC, and twin inclusions are estimated to be 1%.

Multiplicity factor and diffraction geometry factor for single crystal X-ray diffraction analysis and measurement of phase content in cubic GaN/GaAs(001) epilayers

On the basis of integrated intensity of rocking curves, the multiplicity factor and the diffraction geometry factor for single crystal X-ray diffraction (XRD) analysis were proposed and a general formula for calculating the content of mixed phases was obtained. With a multifunction four-circle X-ray double-crystal diffractometer, pole figures of cubic (002), {111} and hexagonal {1010} and reciprocal space mapping were measured to investigate the distributive character of mixed phases and to obtain their multiplicity factors and diffraction geometry factors. The contents of cubic twins and hexagonal inclusions were calculated by the integrated intensities of rocking curves of cubic (002), cubic twin {111}, hexagonal {1010} and {1011}.

Experimental measurement of microwave-induced electron spin-flip time

The electron spin resonance (ESR) is optically detected by monitoring the microwave-induced changes in the circular polarization of the neutral exciton (X) and the negatively charged exciton (X-) emission in CdTe quantum wells with low density of excess electrons. We find that the circular polarization of the X and X- emission is a mapping of the spin polarization of excess electrons. By analyzing the ESR-induced decrease in the circular polarization degree of the X emission, we deduce the microwave-induced electron spin-flip time >0.1 mus, which is much longer than the recombination time of X and X-. This demonstrates that the optically detected ESR in type I quantum wells with low density of excess electrons does not obey the prerequisite for the conventional optically detected magnetic resonance. (C) 2001 American Institute of Physics.

Polishing-related optical anisotropy of semi-insulating GaAs studied by reflectance difference spectroscopy

The strong in-plane optical anisotropy of (001) semi-insulating GaAs, which comes from the submicron region under the surface, has been observed by reflectance difference spectroscopy. The optical anisotropy can be explained by the anisotropic strain that is introduced by the asymmetric distribution of 60 degrees dislocations during surface polishing. The simulated spectra reproduce the line shape of the experimental ones. The simulations show that the anisotropic strain is typically about 2.3x10(-4). (C) 2000 American Institute of Physics. [S0021-8979(00)01315-3].

The content calculation of hexagonal phase inclusions in cubic GaN films on GaAs(001) substrates grown by metalorganic chemical vapor deposition

Cubic GaN(c-GaN) films are grown on GaAs(001) substrates by metalorganic chemical vapor deposition (MOCVD). Two GaN samples were grown with different buffer layer, the deposition time of each was 1 and 3 min, respectively. 4-circle X-ray double crystal diffraction (XRDCD) was used to study the secondary crystallographic phases presented in the c-GaN films. The phase composition of the epilayers was determined by X-ray reciprocal space mapping. The intensities of the c-GaN(002) and h-GaN(10 (1) over bar 1) planes detected in the mapping were investigated by omega scans. The content of the hexagonal phase inclusions in the c-GaN films was calculated to about 1.6 and 7.9%, respectively. The thicker buffer layer is not preferable for growing high quality pure c-GaN films. (C) 2000 Elsevier Science S.A. All rights reserved.

Semi-insulating GaAs grown in outer space

A semi-insulating GaAs single crystal ingot was grown in a recoverable satellite, within a specially designed pyrolytic boron nitride crucible, in a power-traveling furnace under microgravity. The characteristics of a compound semiconductor single crystal depends fundamentally on its stoichiometry, i.e. the ration of two types of atoms in the crystal. a practical technique for nondestructive and quantitative measuring stoichiometry in GaAs single crystal was used to analyze the space-grown GaAs single crystal. The distribution of stoichiometry in a GaAs wafer was measured for the first time. The electrical, optical and structural properties of the space-grown GaAs crystal were studied systematically, Device fabricating experiments prove that the quality of field effect transistors fabricated from direct ion-implantation in semi-insulating GaAs wafers has a close correlation with the crystal's stoichiometry. (C) 2000 Elsevier Science S.A. All rights reserved.

Effect of buffer layer growth conditions on the secondary hexagonal phase content in cubic GaN films on GaAs(001) substrates

In this letter, we investigated the effect of the buffer layer growth conditions on the secondary hexagonal phase content in cubic GaN films on GaAs(0 0 1) substrate. The reflection high-energy electron diffraction (RHEED) pattern of the low-temperature GaN buffer layers shows that both the deposition temperature and time are important in obtaining a smooth surface. Four-circle X-ray double-crystal diffraction (XRDCD) reciprocal space mapping was used to study the hexagonal phase inclusions in the cubic GaN (c-GaN) films grown on the buffer layers. The calculation of the volume contents of the hexagonal phase shows that higher temperature and longer time deposition of the buffer layer is not preferable for growing pure c-GaN film. Under optimized condition, 47 meV FWHM of near band gap emission of the c-GaN film was achieved. (C) 2000 Elsevier Science B.V. All rights reserved.

The investigations on semi-insulating GaAs by surface photovoltaic spectroscopy

The surface photovoltage (SPV) effect induced by the defect states in semi-insulating (SI) GaAs was studied. The PV response below the band edge was measured at room temperature with a de optical biasing. The spectra were found to be strongly dependent on the surface recombination and were attributed to formation of the carrier concentration gradient near the surface region, showing that SPV is a very sensitive and nondestructive technique for characterizing the surface quality of the SI-GaAs wafers.

Outer space grown semi-insulating GaAs and its applications

GaAs single crystal has been grown in recoverable satellite. Hall measurements indicate that the GaAs shows semi-insulating behavior. The structural properties of the crystal have been improved obviously, and their uniformity has been improved as well. The stoichiometry and its distribution in space-grown GaAs are improved greatly compared with the GaAs single crystal grown terrestrially. The properties of integrated circuits made by direct ion-implantation on space-grown GaAs are better than those made on ground-grown materials. These results show that the stoichiometry in semi-insulating GaAs seriously affects the properties of related devices.

Cubic-phase GaN light-emitting diodes

The feasibility of growing device-quality cubic GaN/GaAs(001) films by metal organic chemical vapor deposition has been demonstrated. The optical quality of the GaN films was characterized by room-temperature photoluminescence measurements, which shows a full width at half maximum of 46 meV. The structural quality of the films was investigated by transmission electron microscopy. There are submicron-size grains free from threading dislocations and stacking faults. More importantly, a cubic-phase GaN blue light-emitting diode has been fabricated. The device process, which is very simple and compatible with current GaAs technology, indicates a promising future for the blue light-emitting diode. (C) 1999 American Institute of Physics. [S0003-6951(99)01416-3].

Relationship between deep-level centers and stoichiometry in semi-insulating gallium arsenide

Experimental results have shown the fact that the deep-level centers in semi-insulating GaAs decrease with the improvement in stoichiometry. The electrical resistivity doubles when the concentration of EL2 centers decreases to a half. The microgravity-growth experiments also show that improved crystal stoichiometry results in a decrease of deep-level centers. (C) 1998 American Institute of Physics. [S0021-8979(98)04921-4].

Low Temperature Deposited Nano-structured Vanadium Oxide Thin Films for Uncooled Infrared Detectors

A novel process of room temperature ion beam sputtering deposition of vanadium oxide films and low temperature post annealing for uncooled infrared detectors was proposed in this work. VOx thin films with relatively low square resistance (70 K Omega / square) and large temperature coefficient of resistance (more than 3%/K) at room temperature were fabricated using this low temperature process which was very compatible with the process of uncooled infrared detectors based on micromachined technology. Furthermore, chemical composition and film surface have been characterized using X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) respectively. The results showed that the main composition of the processed thin films was V2O5 and the thin films were in the process of crystallization.

A Compact Direct Digital Frequency Synthesizer for System-on-chip

A compact direct digital frequency synthesizer (DDFS) for system-on-chip (SoC) is developed in this paper. For smaller chip size and lower power consumption, the phase to sine mapping data is compressed by using sine symmetry technique, sine-phase difference technique, quad line approximation (QLA) technique and quantization and error read only memory (QE-ROM) technique. The ROM size is reduced by 98 % using the techniques mentioned above. A compact DDFS chip with 32-bit phase storage depth and a 10-bit on-chip digital to analog converter(DAC) has been successfully implemented using standard 0.35um CMOS process. The core area of the DDFS is 1.6mm(2). It consumes 167 mW at 3.3V, and its spurious free dynamic range (SFDR) is 61dB.

A Novel Low-Power Digital Baseband Circuit for UHF RFID Tag with Sensors

A novel low-power digital baseband circuit for UHF RFID tag with sensors is presented in this paper. It proposes a novel baseband architecture and a new operating scheme to fulfill the sensor functions and to reduce power consumption. It is also compatible with the EPC C1G2 UHF RFID protocol. It adopts some advanced low power techniques for system design and circuit design: adaptive clock-gating, multi-clock domain and asynchronous circuit. The baseband circuit is implemented in 0.18um 1P3M standard CMOS process. ne chip area is 0.28 mm(2) excluding test pads. Its power consumption is 25uW under 1.1V power supply.