Ce：YAP晶体中的孪晶缺陷

The twin defects in Ce:YAP were investigated by using synchrotron radiation topography and etch figures. The results show that the twins are {101} and {121} types, and the exchange of neighboring lattice parameters is considered to be the intrinsic factor for twining. Based on such analysis, the twin structure model was established. Otherwise, the growth experiment results show that the abrupt change of growth rate during shoulder formation tends to cause twining.

Laser conditioning and multi-shot laser damage accumulation effects of HfO2/SiO2 antireflective coatings

Laser conditioning effects of the HfO2/SiO2 antireflective (AR) coatings at 1064 nm and the accumulation effects of multishot laser radiation were investigated. The HfO2/SiO2 AR coatings were prepared by E-beam evaporation (EBE). The singleshot and multi-shot laser induced damage threshold was detected following ISO standard 11254-1.2, and the laser conditioning was conducted by three-step raster scanning method. It was found that the single-shot LIDT and multi-shot LIDT was almost the same. The damage mostly > 80% occurred in the first shot under multi-shot laser radiation, and after that the damage occurring probability plummeted to < 5%. There was no obvious enhancement of the laser damage resistance for both the single-shot and multi-shot laser radiation of the AR coatings after laser conditioning. A Nomarski microscope was employed to map the damage morphology, and it found that the damage behavior is defect-initiated for both unconditioned and conditioned samples. © 2004 Elsevier B.V. All rights reserved.

Effects of CO2 laser conditioning of the antireflection Y2O3/SiO2 coatings at 351 nm

Y2O3/SiO2 coatings were deposited on fused silica by electron beam evaporation. A continuous wave CO2 laser was used to condition parts of the prepared samples at different scanning speeds in the air. LAMBDA 900 spectrometer was used to investigate the changes of the transmittance and residual reflection spectrum. A Nomarski microscope under dark field was used to examine the changes of the micro defect density. The changes of the surface roughness and the microstructure of the film before and after conditioning were investigated by AFM and X-ray diffraction, respectively. We found that laser-induced damage threshold (LIDT) of the films conditioning at 30 mm/s scanning speed was increased by more than a factor of 3 over the thresholds of the as-deposited films. The conditioning effect was correlated with an irradiation-induced decrease of the defect density and absorption of the films. (c) 2005 Elsevier B.V. All rights reserved.

Extended bidirectional reflectance distribution function for polarized light scattering from subsurface defects under a smooth surface

By introducing the scattering probability of a subsurface defect (SSD) and statistical distribution functions of SSD radius, refractive index, and position, we derive an extended bidirectional reflectance distribution function (BRDF) from the Jones scattering matrix. This function is applicable to the calculation for comparison with measurement of polarized light-scattering resulting from a SSD. A numerical calculation of the extended BRDF for the case of p-polarized incident light was performed by means of the Monte Carlo method. Our numerical results indicate that the extended BRDF strongly depends on the light incidence angle, the light scattering angle, and the out-of-plane azimuth angle. We observe a 180 degrees symmetry with respect to the azimuth angle. We further investigate the influence of the SSD density, the substrate refractive index, and the statistical distributions of the SSD radius and refractive index on the extended BRDF. For transparent substrates, we also find the dependence of the extended BRDF on the SSD positions. (c) 2006 Optical Society of America.

离子束溅射法薄膜生长中结瘤微缺陷的生长机理

用离子束溅射法制备了锆单层薄膜．用设计新型夹具和预置种子方法，对薄膜中结瘤微缺陷的生长过程进行了研究．在高分辨率光学显微镜和扫描电子显微镜下观察发现，结瘤在其生长初期呈现出分形的特征．用分子动力学和薄膜生长的扩散限制聚集模型，薄膜中结瘤微缺陷成核时的分形现象得到了很好的解释．

应用离子后处理技术提高薄膜激光损伤阈值

利用电子束热蒸发方法在K9玻璃基底上沉积氧化锆薄膜,并对其中一些样品用低能O2^+进行了后处理.采用表面热透镜技术测量薄膜样品表面弱吸收,采用显微镜观察样品离子后处理前后的显微缺陷密度.测试结果表明:经离子后处理样品表面的缺陷密度从18.6/mm^2降低到6.2/mm^2,且其激光损伤阈值从15.9 J/cm^2提高到23.1 J/cm^2,样品的平均吸收率从处理前的1.147×10^-4降低到处理后的9.56×10^-5.通过对处理前后样品的表面微缺陷密度、吸收率及损伤形貌等的分析发现:离子后处理可以降

Subsurface damage in optical substrates

The origin, character, analysis and treatment of subsurface damage (SSD) were summarized in this paper. SSD, which was introduced to substrates by manufacture processes, may bring about the decrease of laser-induced damage threshold (LIDT) of substrates and thin films. Nondestructive evaluation (NDE) methods for the measurement of SSD were used extensively because of their conveniences and reliabilities. The principle, experimental setup and some other technological details were given for total internal reflection microscopy (TIRM), high-frequency scanning acoustic microscopy (HFSAM) and laser-modulated scattering (LMS). However, the spatial resolution, probing depth and theoretic models of these NDE methods demanded further studies. Furthermore, effective surface treatments for minimizing or eliminating SSD were also presented in this paper. Both advantages and disadvantages of ion beam etching (IBE) and magnetorheological finishing (MRF) were discussed. Finally, the key problems and research directions of SSD were summarized. (c) 2005 Elsevier GmbH. All rights reserved.

Laser conditioning of ZrO2 : Y2O3/SiO2 mirror coatings prepared by E-beam evaporation

Laser conditioning effects of the dielectric mirror coatings with different designs were investigated. Simple quarter-wave ZrO2:Y2O3/SiO2 mirrors and half-wave SiO2 over-coated ZrO2:Y2O3/SiO2 mirror coatings were fabricated by E-beam evaporation (EBE). The absorbance of the samples before and after laser conditioning was measured by surface thermal lensing (STL) technology and the defects density was detected under Nomarski microscope. The enhancement of the laser damage resistance was found after laser conditioning. The dependence of the laser conditioning on the coating design was also observed and the over-coated sample obtained greatest enhancement, whereas the absorbance of the samples did not change obviously. During the sub-threshold fluence raster scanning, the minor damage about defects size was found and the assumption of pre-damage mechanism, based on the functional damage concept, was put forward. The improvement of the laser induced damage threshold (LIDT) was attributed to the benign damage of the defects and the dependence on the coating design owed to the damage growth behavior of different coating designs. (C) 2004 Elsevier B.V. All rights reserved.

Structure and UV emission of nanocrystal ZnO films by thermal oxidation of ZnS films

ZnO films prepared by the thermal oxidation of the ZnS films through thermal evaporation are reported. The as-deposited ZnS films have transformed to ZnO films completely at 400 degrees C. The 400-700 degrees C annealed films with a preferential c-axis (002) orientation have a hexagonal wurtzite structure. The band gap of ZnO films shifts towards longer wavelength with the increase of the annealing temperature. The relationship between the band gap energy of ZnO films and the grain size is discussed. The shift of the band gap energy can be ascribed to the quantum confinement effect in nanocrystal ZnO films. The photoluminescence spectra of ZnO films show a dominant ultraviolet emission and no deep level or trap state defect emission in the green region. It confirms the absence of interstitial zinc or oxygen vacancies in ZnO films. These results indicate that ZnO film prepared by this simple thermal oxidation method is a promising candidate for optoelectronic devices and UV laser. (c) 2005 Elsevier BN. All rights reserved.

Surface morphology and properties of zirconia thin films prepared at different deposition rates

ZrO2 thin films were prepared on BK7 glass substrates by electron beam evaporation deposition method. The influence of deposition rate varying from 1.2 to 6.3 nm s(-1) on surface morphology and other properties of ZrO2 films were examined. With increasing deposition rate, the surface defect density increased. The decrease in half width at full maximum in X-ray diffraction pattern with deposition rate indicates an increase in crystal dimension with increasing deposition rate. Electron beam deposited ZrO2 films are known to be inhomogeneous. From the change of the peak transmittance value, it can be deduced that the inhomogeneity of ZrO2 films strengthened gradually with increasing deposition rate. The type of surface defects changed from nodules to craters when the deposition rate was high enough.

Damage on HfO2/SiO2 high-reflecting coatings under single and multiple Nd:YAG laser pulse irradiation

The single- and multi-shot damage behaviors of HfO2/SiO2 high-reflecting (HR) coatings under Nd:YAG laser exposure were investigated. Fundamental aspects of multi-shot laser damage, such as the instability due to pulse-to-pulse accumulation of absorption defect and structural defect effect, and the mechanism of laser induced defect generation, are considered. It was found in multi-shot damage, the main factors influencing laser-induced damage threshold (LIDT) are accumulation of irreversible changes of structural defects and thermal stress that induced by thermal density fluctuations.

脉冲激光辐照光学薄膜的缺陷损伤模型

建立了缺陷吸收升温致薄膜激光损伤模型，该模型从热传导方程出发，考虑了缺陷内部的温度分布以及向薄膜的传导过程，通过引入散射系数简化了Mie散射理论得出的吸收截面．对电子束蒸发沉积的ZrO2：Y2O3单层膜进行了激光破坏实验，薄膜样品的损伤是缺陷引起的，通过辉光放电质谱法对薄膜制备材料的纯度分析发现材料中的主要杂质元素为铂，其含量为0．9％．利用缺陷损伤模型对损伤过程进行了模拟，理论模型和实验结果取得了较好的一致性．

薄膜材料对TiO2基薄膜激光损伤阈值的影响

abstract {The optical property, structure, surface properties (roughness and defect density) and laser-induced damage threshold (LIDT) of TiO₂ films deposited by electronic beam (EB) evaporation of TiO₂ (rutile), TiO₂ (anatase) and TiO₂ + Ta₂O₅ composite materials are comparatively studied. All films show the polycrystalline anatase TiO₂ structure. The loose sintering state and phase transformation during evaporating TiO₂ anatase slice lead to the high surface defect density, roughness and extinction coefficient, and low LIDT of films. The TiO₂ + Ta₂O₅ composite films have the lowest extinction coefficient and the highest LIDT among all samples investigated. Guidance of selecting materials for high LIDT laser mirrors is given.}