Spray combustion synthesis of nanocrystalline Y2O3 and its thermodynamical and morphological study

Nano Y2O3 particles with a spherical shape and narrow size distribution have been prepared by a novel spray combustion method. The experimental procedure is briefly described and the thermodynamical process of the post-heat treatment is investigated in this paper. The precursor fully crystallized when treated at as low as 400 degrees C. Prepared particles showed spherical shape and well dispersibility under different treating conditions. Narrow size distribution of particles was achieved even when the precursor was treated at 1373 K. (C) 2007 Elsevier B.V. All rights reserved.

Effect of natural dissolved humic material on bioavailability and acute toxicity of fenpropathrin to the grass carp, Ctenopharyngodon idellus

The effects of aquatic humic acids on the bioconcentration and acute toxicity of fenpropathrin were evaluated using grass carp, Ctenopharyngodan idellus, in laboratory freshwater systems. The results demonstrated that both bioavailability and acute toxicity decreased in the presence of aquatic humic acid 5 and 10 mg/liter. In addition, the extent of influence increased with increasing concentration of aquatic humic acid, (C) 1999 Academic Press.

Peculiarity of constant photocurrent method for silicon films with mixed amorphous-nanocrystalline structure

The results of conductivity, photoconductivity and constant photocurrent method absorption measurements by DC and AC methods in hydrogenated silicon films with mixed amorphous-nanocrystalline structure are presented. A series of diphasic silicon films was deposited by very high frequency plasma enhanced chemical vapor deposition technique, using different hydrogen dilution ratios of silane. The increase of hydrogen dilution ratio results in five orders of magnitude increase of conductivity and a sharp increase of grain volume fraction. The comparison of the absorption spectra obtained by DC and AC methods showed that they are similar for silicon films with the predominantly amorphous structure and films with high grain volume fraction. However we found a dramatic discrepancy between the absorption spectra obtained by DC and AC constant photocurrent methods in silicon films deposited in the regime of the structure transition from amorphous to nanocrystalline state. AC constant photocurrent method gives higher absorption coefficient than DC constant photocurrent method in the photon energy range of 1.2-1.7 eV. This result indicates the possibility of crystalline grains contribution to absorption spectra measured by AC constant photocurrent method in silicon films with intermediate crystalline grain volume fraction. (c) 2008 Published by Elsevier B.V.

The influence of growth temperature and input V/III ratio on the initial nucleation and material properties of InN on GaN by MOCVD

The effects of growth temperature and V/III ratio on the InN initial nucleation of islands on the GaN (0 0 0 1) surface were investigated. It is found that InN nuclei density increases with decreasing growth temperature between 375 and 525 degrees C. At lower growth temperatures, InN thin films take the form of small and closely packed islands with diameters of less than 100 nm, whereas at elevated temperatures the InN islands can grow larger and well separated, approaching an equilibrium hexagonal shape due to enhanced surface diffusion of adatoms. At a given growth temperature of 500 degrees C, a controllable density and size of separated InN islands can be achieved by adjusting the V/III ratio. The larger islands lead to fewer defects when they are coalesced. Comparatively, the electrical properties of the films grown under higher V/III ratio are improved.

Photoluminescence characterization of nanocrystalline ZnO array

High-density and uniform well-aligned ZnO sub-micron rods are synthesized on the silicon substrate over a large area. The morphology, and structure of the ZnO sub-micron rods are investigated by x-ray diffraction, transmission electron microscopy and Raman spectra. It is found that the ZnO sub-micron rods are of high crystal quality with the diameter in the range of 400-600 nm and the length of several micrometres long. The optical properties were studied bill photoluminescence spectra. The results show that the intensity of the ultraviolet emission at 3.3 eV is rather high, meanwhile the deep level transition centred at about 2.38 eV is weak. The free exciton emission could also be observed at low, temperature, which implies the high optical quality of the ZnO sub-micron rods. This growth technique provides one effective way to fabricate the high crystal quality ZnO nanowires array, which is very important for potential applications in the new-type optoelectronic nanodevices.

Preferred growth of nanocrystalline silicon in boron-doped nc-Si : H Films

Preferred growth of nanocrystalline silicon (nc-Si) was first found in boron-doped hydrogenated nanocrystalline (nc-Si:H) films prepared using plasma-enhanced chemical vapor deposition system. The films were characterized by high-resolution transmission electron microscope, X-ray diffraction (XRD) spectrum and Raman Scattering spectrum. The results showed that the diffraction peaks in XRD spectrum were at 2theta approximate to 47degrees and the exponent of crystalline plane of nc-Si in the film was (220). A considerable reason was electric field derived from dc bias made the bonds of Si-Si array according to a certain orient. The size and crystalline volume fraction of nc-Si in boron-doped films were intensively depended on the deposited parameters: diborane (B2H6) doping ratio in silane (SiH4), silane dilution ratio in hydrogen (H-2), rf power density, substrate's temperature and reactive pressure, respectively. But preferred growth of nc-Si in the boron-doped nc-Si:H films cannot be obtained by changing these parameters. (C) 2004 Elsevier Ltd. All rights reserved.

Radiation hardness improvement of separation-by-implantation-of-oxygen/silicon-on-insulator material by nitrogen ion implantation

In our work, nitrogen ions were implanted into separation-by-implantation-of-oxygen (SIMOX) wafers to improve the radiation hardness of the SIMOX material. The experiments of secondary ion mass spectroscopy (SIMS) analysis showed that some nitrogen ions were distributed in the buried oxide layers and some others were collected at the Si/SiO2 interface after annealing. The results of electron paramagnetic resonance (EPR) suggested the density of the defects in the nitrided samples changed with different nitrogen ion implantation energies. Semiconductor-insulator-semiconductor (SIS) capacitors were made on the materials, and capacitance-voltage (C-V) measurements were carried out to confirm the results. The super total dose radiation tolerance of the materials was verified by the small increase of the drain leakage current of the metal-oxide-semiconductor field effect transistor with n-channel (NMOSFETs) fabricated on the materials before and after total dose irradiation. The optimum implantation energy was also determined.

Photoluminescence and transmission spectra of nanocrystalline GaAs1-xSbx embedded in silica films

The composite films of the nanocrystalline GaAs1-xSbx-SiO2 have been successfully deposited on glass and GaSb substrates by radio frequency magnetron co-sputtering. The 10K photoluminescence (PL) properties of the nanocrystalline GaAs1-xSbx indicated that the PL peaks of the GaAs1-xSbx nanocrystals follow the quantum confinement model very closely. Optical transmittance spectra showed that there is a large blue shift of optical absorption edge in nanocrystalline GaAs1-xSbx-SiO2 composite films, as compared with that of the corresponding bulk semiconductor, which is due to the quantum confinement effect.

Impact of hydrogen dilution on microstructure and optoelectronic properties of silicon films deposited using tirisilane

We explored the deposition of hydrogenated amorphous silicon (a-Si: H) using trisilane (Si3H8) as a gas precursor in a radiofrequency plasma enhanced chemical vapour deposition process and studied the suitability of this material for photovoltaic applications. The impact of hydrogen dilution on the deposition rate and microstructure of the films is systematically examined. Materials deposited using trisilane are compared with that using disilane (Si2H6). It is found that when using Si3H8 as the gas precursor the deposition rate increases by a factor of similar to 1.5 for the same hydrogen dilution (R = [H-2]/[Si3H8] or [H-2]/[Si2H6])- Moreover, the structural transition from amorphous to nanocrystalline occurs at a higher hydrogen dilution level for Si3H8 and the transition is more gradual as compared with Si2H6 deposited films. Single-junction n-i-p a-Si: H solar cells were prepared with intrinsic layers deposited using Si3H8 or Si2H6. The dependence of open circuit voltage (V-oc) on hydrogen dilution was investigated. V-oc greater than 1 V can be obtained when the i-layers are deposited at a hydrogen dilution of 180 and 100 using Si3H8 and Si2H6, respectively.

Fabrication of arrayed waveguide grating based on SOI material

An arrayed waveguide grating based on SOI material was fabricated by inductive coupled plasma (ICP) etching technology. The central wavelength of the device was designed at 1.5509 mu m and the channel spacing was 200 GHz. Comparing with the values of the design, the differences of the central wavelength and the channel spacing in the test were 0.28 nm and 0.02 nm, respectively. The adjacent channel crosstalk was about 10 dB, and the uniformity of the five channels' insertion loss was only 0.7 dB. The results show that the device can be used as a demultiplexer.

Photonic crystal vertical-cavity surface-emitting laser based on GaAs material

A photonic crystal vertical-cavity-surface-emitting laser ( PC-VCSEL) with a wavelength of about 850 nm was realized. The direct-current electrically-driven PC-VCSELs with a minimum threshold current of 2 mA and a maximum threshold current of 13.5 mA were obtained. We fabricated a series of PC-VCSEL chips whose lattice constants are in the range from 0.5 to 3 mu m with different filling factors, and found that the laser characterization depends on the lattice constant, the filling factor, the size of cavity, etc.

Thermally induced Fe atom transition from substitutional to interstitial sites in InP and its influence on material property

As-grown Fe-doped semi-insulating InP single crystal has been converted into n-type low-resistance material after high temperature annealing. Defects in the InP materials have been studied by conventional Hall effect measurement, thermally stimulated current spectroscopy, deep level transient spectroscopy and X-ray diffraction respectively. The results indicate that Fe atoms in the InP material change from the substitutional to the interstitial sites under thermal activation. Consequently, the InP material loses its deep compensation centers which results in the change in types of conduction. The mechanism and cause of the phenomena have been analyzed through comparison of the sites of Fe atom occupation and activation in doping, diffusion and ion implantation processes of InP.

Material growth and device fabrication of highly strained InGaAs/InGaAsP long wavelength distributed feedback lasers

1.6-1.7 mu m highly strained InGaAs/InGaAsP distributed feedback lasers was grown and fabricated by low pressure mentalorganic chemical vapor deposition. High quality highly strained InGaAs/InP materials were obtained by using strain buffer layer. Four pairs of highly strained quantum wells were used in the devices and carrier blocking layer was used to improve the temperature characteristics of the devices. The uncoated 1.66 mu m and 1.74 mu m lasers with ridge wave guide 3 mu m wide have low threshold current (< 15mA) and high output power (> 14mW at 100mA). In the temperature range from 10 degrees C to 40 degrees C, the characteristic temperature T-0 of the 1.74 mu m laser is 57K, which is comparable to that of the 1.55 mu m-wavelength InGaAsP/InP-DFB laser.