The microstructure and its high-temperature annealing behaviours of a-Si : O : H film

The microstructure and its annealing behaviours of a-Si:O:H film prepared by PECVD are investigated in detail using micro-Raman spectroscopy, X-ray photoelectron spectroscopy and Infrared absorption spectroscopy. The results indicate that the as-deposited a-Si:O:H film is structural inhomogeneous, with Si-riched phases surrounded by O-riched phases. The Si-riched phases are found to be nonhydrogenated amorphous silicon (a-Si) clusters, and the O-riched phases SiOx:H (x approximate to 1. 35) are formed by random bonding of Si, O and H atoms. By high-temperature annealing at 1150 degreesC, the SiOx:H (x approximate to 1.35) matrix is shown to be transformed into SiO2 and SiOx ( x approximate to 0.64), during which all of the hydrogen atoms in the film escape and some of silicon atoms are separated from the SiOx:H ( x approximate to 1.35) matrix; The separated silicon atoms are found to be participated in the nucleation and growth processes of solid-phase crystallization of the a-Si clusters, nano-crystalline silicon (ne-Si) is then formed. The microstructure of the annealed film is thereby described with a multi-shell model, in which the ne-Si clusters are embedded in SiOx (x = 0.64) and SiO2. The former is located at the boundaries of the nc-Si clusters, with a thickness comparable with the scale of nc-Si clusters, and forms the transition oxide layer between the ne-Si and the SiO2 matrix.

Effects of annealing time and Si cap layer thickness on the Si/SiGe/Si heterostructures thermal stability

The effects of annealing time and Si cap layer thickness: on the thermal stability of the Si/SiGe/Si heterostructures deposited by disilane and solid-Ge molecule beam epitaxy were investigated. It is found that in the same strain state of the SiGe layers the annealing time decreases with increasing Si cap layer thickness. This effect is analyzed by a force-balance theory and an equation has been obtained to characterize the relation between the annealing time and the Si cap layer thickness. (C) 2001 Elsevier Science B.V. All rights reserved.

Effects of rapid thermal annealing and SiO2 encapsulation on GaNAs/GaAs single quantum wells grown by plasma-assisted molecular-beam epitaxy

Effects of rapid thermal annealing and SiO2 encapsulation on GaNAs/GaAs single quantum wells grown by plasma-assisted molecular-beam epitaxy were studied. Photoluminescence measurements on a series of samples with different well widths and N compositions were used to evaluate the effects. The intermixing of GaNAs and GaAs layers was clearly enhanced by the presence of a SiO2-cap layer. However, it was strongly dependent on the N composition. After annealing at 900 degreesC for 30 s, a blueshift up to 62 meV was observed for the SiO2-capped region of the sample with N composition of 1.5%, whereas only a small blueshift of 26 meV was exhibited for the bare region. For the sample with the N composition of 3.1%, nearly identical photoluminescence peak energy shift for both the SiO2-capped region and the bare region was observed. It is suggested that the enhanced intermixing is mainly dominated by SiO2-capped layer induced defects-assisted diffusion for the sample with smaller N composition, while with increasing N composition, the diffusion assisted by interior defects become predominant. (C) 2001 American Institute of Physics.

Annealing-induced evolution of defects in low-temperature-grown GaAs-related materials

Infrared absorption spectroscopy, optical transient current spectroscopy (OTCS), and photoluminescence (PL) spectroscopy are used to investigate the annealing induced evolution of defects in low-temperature (LT)-grown GaAs-related materials. Two LT samples of bulk GaAs (sample A) and GaAs/AlxGa1-xAs multiple-quantum-well. (MQW) structure (sample B) were grown at 220 and 320 degreesC on (001) GaAs substrates, respectively. A strong defect-related absorption band has been observed in both as-grown samples A and B. It becomes weaker in samples annealed at temperatures above 600 degreesC. In sample A, annealed in the range of 600-800 degreesC, a large negative decay signal of the optical transient current (OTC) is observed in a certain range of temperature, which distorts deep-level spectra measured by OTCS, making it difficult to identify any deep levels. At annealing temperatures of 600 and 700 degreesC, both As-Ga antisite and small As cluster-related deep levels are identified in sample B. It is found that compared to the As cluster, the As-Ga antisite has a larger activation energy and carrier capture rate. At an annealing temperature of 800 degreesC, the large negative decay signal of the OTC is also observed in sample B. It is argued that this negative decay signal of the OTC is related to large arsenic clusters. For sample B, transient PL spectra have also been measured to study the influence of the, defect evolution on optical properties of LT GaAs/AlxGa1-xAs MQW structures. Our results clearly identify a defect evolution from AS(Ga) antisites to arsenic clusters after annealing.

In situ annealing treatment and In-doping of GaN epilayers grown by MOVPE

The effects of in situ annealing treatment in the initial growth stage and In-doping during growth of the GaN on the material properties were investigated. GaN was grown by LP-MOVPE. In situ annealing reduced the full-width at half-maximum (FWHM) of X-ray rocking curves and reduced etch pit density of GaN films. It improved the optical properties of the epilayer. Undoped and In-doped GaN films of initial growth stage were investigated. It was found that morphology and optical properties were improved in In-doped samples. (C) 2000 Elsevier Science B.V. All rights reserved.

Light and annealing induced changes in Si-H bonds in undoped a-Si : H

Light and annealing induced changes in Si-H bonds in undoped a-Si:H have been investigated by a differential infrared spectroscopy method. The light-induced changes in Si-H bonds are not monotonic, quite different from the usual Staebler-Wronski effect in electronic properties, and involve more complicated physics. The magnitude of the light-induced changes in Si-H bonds is proportional to the hydrogen content in the film. There may exist more than one microscopic process which determine the light-induced changes in Si-H bonds. Almost the whole a-Si:H network is affected when a-Si:H is subjected to Light-soaking or to annealing. The light-induced changes in Si-H bonds may be an independent light-induced phenomenon or an auxiliary process of the metastable SWE defect creation. (C) 2000 Elsevier Science Ltd. All rights reserved.

Modeling the dynamics of Si wafer bonding during annealing

The bonding behavior of silicon wafers depends on activation energy for the formation of siloxane bonds. In this article we developed a quantitative model on the dynamics of silicon wafer bonding during annealing. Based on this model, a significant difference in the bonding behaviors is compared quantitatively between the native oxide bonding interface and the thermal oxide bonding interface. The results indicate that the bonding strength of the native oxide interface increases with temperature much more rapidly than that of the thermal oxide interface. (C) 2000 American Institute of Physics. [S0021-8979(00)05520-1].

Effect of rapid thermal annealing on GaInNAs/GaAs quantum wells grown by plasma-assisted molecular-beam epitaxy

We have studied the effect of rapid thermal annealing (RTA) on GaInNAs/GaAs quantum wells (QWs) grown by molecular-beam epitaxy using a dc plasma as the N source. It was found that RTA at low temperature (LT, 650 degrees C) and high temperature (HT, 900 degrees C) could both improve the QW quality significantly. To clarify the mechanism of quality improvement by RTA, a magnetic field perpendicular to the path of the N plasma flux was applied during the growth of the GaInNAs layers for the sake of comparison. It was found that LT-RTA mainly removed dislocations at interfaces related to the ion bombardment, whereas, HT-RTA further removed dislocations originating from the growth. LT-RTA caused only a slight blueshift of photoluminescence peak wavelength, probably due to defect-assisted interdiffusion of In-Ga at the QW interfaces. The blueshift caused by HT-RTA, on the other hand, was much larger. It is suggested that this is due to the fast defect-assisted diffusion of N-As at the QW interfaces. As defects are removed by annealing, the diffusion of In-Ga at interfaces would be predominant. (C) 2000 American Institute of Physics. [S0003- 6951(00)01535-7].

Polycrystalline silicon films prepared by improved pulsed rapid thermal annealing

An improved pulsed rapid thermal annealing (PRTA) has been used for the solid-phase crystallization (SPC) of a-Si films prepared by PECVD. The SPC can be completed with time-temperature budgets such as 10 cycles of 60-s 550 degrees C thermal bias/1-s 850 degrees C thermal pulse. The microstructure and surface morphology of the crystallized films are investigated by X-ray diffraction (XRD). The results indicate that this PRTA is a suitable post-crystallization technique for fabricating large-area poly-Si films on low-cost substrate. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of rapid thermal annealing on InGaAs/GaAs quantum wells

We have studied the effect of rapid thermal annealing (RTA) on highly strained InGaAs/GaAs quantum wells by using photoluminescence (PL) and double-crystal X-ray diffraction (DCXRD) measurements. It is found that a distinct additional PL emission peak can be observed for the annealed samples. This PL emission possesses features similar to the PL emission from InGaAs/GaAs quantum dots (QDs) with the same indium content. It is proposed that this emission stems from QDs, which were formed during the annealing process. This formation is attributed to the favorable diffusion due to the inhomogeneous strain distribution in the InGaAs layer intersurface. The DCXRD measurements also confirm that the dominant relaxation is strain enhanced diffusion under the low annealing temperatures. (C) 2000 Elsevier Science B.V. All rights reserved.

Annealing effect on the surface morphology and photoluminescence of InGaAs/GaAs quantum dots grown by molecular beam epitaxy

Postgrowth rapid thermal annealing was performed on InGaAs/GaAs quantum dots grown by molecular beam epitaxy. The blue shift of the emission peak and the narrowing of the luminescence line width are observed at lower annealing temperature. However, when the annealing temperature is increased to 850 degrees C, the emission line width becomes larger. The TEM image of this sample shows that the surface becomes rough, and some large clusters are formed, which is due to the interdiffusion of In, Ga atoms at the InGaAs/GaAs interface and to the strain relaxation. The material is found to degrade dramatically when the annealing temperature is further increased to 900 degrees C, while emission from quantum dots can still be detected, along with the appearance of the emission from excited state. (C) 2000 Elsevier Science B.V. All rights reserved.

Effect of thermal annealing on hole trap levels in Mg-doped GaN grown by metalorganic vapor phase epitaxy

Deep trap levels in a Mg-doped GaN grown by metalorganic vapor phase epitaxy are studied with deep level transient spectroscopy (DLTS). The Mg concentration of the sample was 4.8 x 10(19) cm(-3), but the hole concentration was as low as 1.3x10(17) cm-3 at room temperature. The DLTS spectrum has a dominant peak D-1 with an activation energy of 0.41+/-0.05 eV, accompanied by two additional peaks with activation energies of 0.49+/-0.09 eV (D-2) and 0.59+/-0.05 eV (D-3). It was found that the dominant peak D-1 consists of five peaks, each of which has different activation energy and capture cross section. In order to investigate these deep levels further, we performed heat treatment on the same samples to observe the variations of activation energy, capture cross section, and amplitude of DLTS signals. It was found that the longer the heat treatment duration is, the lower the amplitude of DLTS peaks become. This suggests that the decrease of the DLTS signal originates from hydrogen atom outgoing from the film during the annealing process. The possible originality of multiple trap levels was discussed in terms of the Mg-N-H complex. (C) 2000 American Vacuum Society. [S0734-2101(00)01701-2].

Pulsed excimer laser annealing of Mg-doped cubic GaN

A KrF (248 nm) excimer laser with a 38 ns pulse width was used to study pulsed laser annealing (PLA) on Mg-doped cubic GaN alms. The laser-induced changes were monitored by photoluminescence (PL) measurement. It indicated that deep levels in as-grown cubic GaN : Mg films were neutralized by H and PLA treatment could break Mg-H-N complex. The evolution of emissions around 426 and 468 nm with different PLA conditions reflected the different activation of the involved deep levels. Rapid thermal annealing (RTA) in N-2 atmosphere reverts the luminescence of laser annealed samples to that of the pre-annealing state. The reason is that most H atoms still remained in the epilayers after PLA due to the short duration of the pulses and reoccupied the original locations during RTA. (C) 2000 Elsevier Science B.V. All rights reserved. PACS: 61.72.Vv; 61.72.Cc; 18.55. -m.

Effects of rapid thermal annealing on self-assembled InGaAs/GaAs quantum dots superlattice

Postgrowth rapid thermal annealing was used to study the relaxation mechanism and optical properties of InGaAs/GaAs self-assembled quantum dots superlattice grown by molecular beam epitaxy. It is found that a significant narrowing of the luminescence linewidth (from 80 to 42 meV) occurs together with about 86 meV blue shift at annealing temperature up to 950 degrees C. Double crystal X-ray diffraction measurements show that the intensity of the satellite diffraction peak, which corresponds to the quantum dots superlattice, decreased with the increasing annealing temperature and disappeared at 750 degrees C, but recovered and increased again at higher annealing temperatures. This behavior can be explained by two competing relaxation mechanisms; interdiffusion and favored migration. The study indicates that a suitable annealing treatment can improve the structural properties of the quantum dots superlattice. (C) 2000 Elsevier Science B.V. All rights reserved.

Effects of rapid thermal annealing on the optical properties of GaNxAs1-x/GaAs single quantum well structure grown by molecular beam epitaxy

The effect of rapid thermal annealing (RTA) on the optical properties of GaNxAs1-x/GaAs strained single quantum well (SQW) was studied by low-temperature photoluminescence (PL). The GaNxAs1-x/GaAs SQW structures were prepared by dc active nitrogen plasma assisted molecular beam epitaxy. PL measurements on a series of samples with different well widths and nitrogen compositions were used to evaluate the effects of RTA. The annealing temperature and time were varied from 650 to 850 degrees C and 30 s to 15 min, respectively. Remarkable improvements of the optical properties of the samples were observed after RTA under optimum conditions. The interdiffusion constants have been calculated by taking into account error function diffusion and solving the Schrodinger equation. The estimated interdiffusion constants D are 10(-17)-10(-16) cm(2)/s for the earlier annealing conditions. Activation energies of 6-7 eV are obtained by fitting the temperature dependence of the interdiffusion constants. (C) 2000 American Institute of Physics. [S0021-8979(00)10401-3].