Syntheses and properties of novel polyimides derived from 2-(4-aminophenyl)-5-aminopyrimidine

2-(4-Aminophenyl)-5-aminopyrimidine (4) is synthesized via a condensation reaction of vinamidium salts and amidine chloride salts, followed by hydrazine palladium catalyzed reduction. A series of novel homo- and copolyimides containing pyrimidine unit are prepared from the diamine and 1,4-phenylenediamine (PDA) with pyromellitic dianhydride (PMDA) or 3,3',4,4'-biphenyl tertracarboxylic dianhydride (BPDA) via a conventional two-step thermal imidization method. The poly(amic acid) precursors had inherent viscosities of 0.97-4.38 dL/g (c = 0.5 g/dL, in DMAc, 30 degrees C) and all of them could be cast and thermally converted into flexible and tough polyimide films. All of the polyimides showed excellent thermal stability and mechanical properties. The glass transition temperatures of the resulting polyimides are in the range of 307-434 degrees C and the 10% weight loss temperature is in the range of 556-609 degrees C under air. The polyimide films possess strength at break in the range of 185-271 MPa, elongations at break in the range of 6.8-51%, and tensile modulus in the range of 3.5-6.46 GPa. The polymer films are insoluble in common organic solvents, exhibiting high chemical resistance.

Syntheses of biphenyl polyimides via nickel-catalyzed coupling polymerization of bis(chlorophthalimide)s

A facile method for the synthesis of biphenyl polyimides, which involves the nickel-catalyzed coupling of aromatic dichlorides containing imide structure in the presence of zinc and triphenylphosphine, has been developed. The polymerizations proceeded smoothly under mild conditions and produced biphenyl polyimides with inherent viscosities of 0.13-0.98 dL/g. The polymerizations of bis(4-chlorophthalimide)s with bulky side substituents gave high molecular weight polymers. Low molecular weight polymers from bis(4-chlorophthalimide)s containing rigid diamine moieties and bis(3-chlorophthalimide)s were obtained because of the formations of polymer precipitate and cyclic oligoimides, respectively. The effects of various factors, such as amount of catalyst, solvent volume, ligand, reaction temperature, and time, on the polymerization were studied. The random copolymerization of two bis(chlorophthalimide)s in varying proportions produced medium molecular weight material. The TgS of prepared polyimides were observed at 245-311 degreesC, and the thermogravimetry of polymers showed 10% weight loss in nitrogen at 470-530 degreesC.

Polyimides from isomeric oxydiphthalic anhydrides

2,2',3,3'-Oxydiphthalic dianhydride (2,2',3,3'-ODPA) and 2,3,3',4'-ODPA were synthesized from 3-chlorophthalic anhydride with 2,3-xylenol and 3,4-xylenol, respectively. Their structures were determined via single-crystal X-ray diffraction. A series of polyimides derived from isomeric ODPAs with several diamines were prepared in dimethylacetamide (DMAc) with the conventional two-step method. Matrix-assisted laser desorption/ionization time-of-flight spectra showed that the polymerization of 2,2',3,3'-ODPA with 4,4'-oxydianiline (ODA) has a greater trend to form cyclic oligomers than that of 2,3,3',4'-ODPA. Both 2,2',3,3'-ODPA and 2,3,3',4'-ODPA based polyimides have good solubility in polar aprotic solvents such as DMAc, dimethylformamide, and N-methylpyrrolidone. The 5% weight-loss temperatures of all polyimides were obtained near 500 degreesC in air. Their glass-transition temperatures measured by dynamic mechanical thermal analysis or differential scanning calorimetry decreased according to the order of polyimides on the basis of 2,2',3,3'-ODPA, 2,3,3',4'-ODPA, and 3,3',4,4'-ODPA. The wide-angle X-ray diffraction of all polyimide films from isomeric ODPAs and ODA showed some certain extent of crystallization after stretching. Rheological properties revealed that polyimide (2,3,3',4'-ODPA/ODA) has a comparatively lower melt viscosity than its isomers, which indicated its better melt processability.

Polyimides from isomeric biphenyltetracarboxylic dianhydrides and the effects of chemical structure on solubility

A series of homopolyimides and copolyimides was synthesized by the solution condensation of biphenyltetracarboxylic dianhydride (BPDA) isomers and various diamines followed by chemical imidization. These polyimides had intermediate to high molecular weights with inherent viscosities of 0.34-1.01 dL/g for homopolyimides and 0.48-1.02 dL/g for copolyimides. Thermogravimetric analysis indicated that the aromatic polyimides were stable up to 500degreesC, and the 5% weight loss temperatures were recorded in the range of 506-597degreesC in an air atmosphere and in the range of 517-601degreesC in a nitrogen atmosphere, depending on the diamines used. The glass transition temperatures of aromatic homopolyimides were above 271degreesC, while the glass transition temperatures of the copolyimides increased with an increase in the 2, 2', 3, 3'-BPDA-component. The effects of the chemical structure of the polymer chain on the solubility were investigated. It was found that the solubility of BPDA-based polyimides could be improved by the introduction of flexible units, nonlinear and non-coplanar units, and copolymerization. The polyimides with nonlinear and non-coplanar units derived from 2, 2', 3, 3'-BPDA appeared to have prominently enhanced solubility in polar aprotic solvents and polychlorocarbons when compared with the homopolyimide derived from 3, 3', 4, 4'-BPDA.

Aromatic poly(ester imide)s and poly(amide imide)s having 1,1 '-binaphthyl-2,2 '-diyls in the main chain

Full Paper: Two new 1,1'-binaphthyl-2,2'-diyl-based dianhydrides, i.e., 2,2'-bis(3,4-dicarboxybenzamido)-1,1'-binaphthyl dianhydride (BNDADA) and 2,2'-bis(3,4-dicarboxybenzoyloxy)-1,1'-binaphthyl dianhydride (BNDEDA), were synthesized and polymerized with various aromatic diamines to afford polyimides through the traditional two-step method. The polyimides with inherent viscosities ranging from 0.27 to 0.70 dl . g(-1) showed excellent solubilities in polar solvents such as DMAc, DMSO and NMP etc., except of the poly(ester imide) prepared from BNDEDA and benzidine. Poly(ester imide)s based on BNDEDA can also be readily dissolved in weakly polar solvents such as THF, CH2Cl2 and CHCl3. The glass transition temperatures of these polyimides are in the range of 210-310 degrees C; the 5% weight loss temperatures are in the range of 390-465 degrees C in nitrogen and 384-447 degrees c in air. These polymers from light yellow, tough films that were transparent above 365 nm. The effects of different flexible units attached in the 2- and 2'-positions, i.e., amide, ester and ether, on the properties of the polyimides obtained are discussed.

Tuning the aggregation of polyimide thin films by modification of their molecular interactions

Thin films of an organo-soluble polyimide based on 1,4-(3,4-dicarboxyphenoxy)benzene dianhydride (HQDPA) and 2,2'-dimethyl-4,4'-methylene dianiline (DMMDA) have been studied. A prism coupler was used to measure the refractive indices. The average refractive indices of thin films prepared by annealing at different temperatures and times were chosen to characterize the condensation states of thin films. Thin films annealed at 200 degrees C show irreversible changes in physical properties, eg solubility. FTIR spectroscopy showed that the chain structures of the above thin films remained unchanged. It is proposed that specific molecular interactions induce the irreversible changes revealed by fluorescence spectroscopy. (C) 2000 Society of Chemical Industry.

Gas permeability and permselectivity of polyimides prepared from phenylenediamines with methyl substitution at the ortho position

Polyimides were prepared from diamines: 2,4,6-trimethyl-1,3-phenylenediamine (3MPDA) and 2,3,4,5-tetramethyl-1,4-phenylenediamine (4MPDA). 1,4-Bis(3,4-dicarboxyphenoxy)benzene dianhydride (HQDPA), 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA), 3,3'-4,4'-diphenylsulphone tetracarboxylic dianhydride (SO(2)PDA), 3,3',4,4'-diphenylsulphide tetracarboxylic dianhydride (SPDA), pyromellitic dianhydride (PMDA), and 2,2'-bis(3,4-dicarboxyphenyl)hexa-fluoroisopropane dianhydride (6FDA) were used as dianhydride. The gas permeabilities of H-2, O-2 and N-2 through the polyimides were measured at temperatures from 30 degrees C to 90 degrees C. The results show that as methyl and trifluoromethyl substitution groups densities increase from 7.73 x 10(-3) molcm(-3) to 13.50 x 10(-3)molcm(-3), the peameability of H-2 increases 10-fold at 60% loss of permselectivity of H-2/N-2 however, the permeability of O-2 increases 20-fold at 20% loss of permselectivity of O-2/N-2. For O-2/N-2 separation, PMDA-3MPDA has similar performance to 6FDA-3MPDA and 6FDA-4MPDA; all have higher permeabilities for O-2 than normal polyimides, and the P(O-2)/alpha(O-2/N-2) trade-off relationships lie on the upper bound line for polymers. (C) 1999 Society of Chemical Industry.

Optically active poly(amide-imide)s containing axially dissymmetric 1,1 '-binaphthyl moieties

Novel optically active aromatic poly(amide-imide)s (PAIs) were prepared from newly synthesized 2,2'-bis(3,4-dicarboxybenzamido)-1,1'-binaphyl dianhydride ((+/-)-, (S)-, and (R)-BNDADA). PAIs based on dianhydride monomers with different ee % were investigated with respect to their structures and chiroptical properties. These polymers were highly soluble in polar aprotic solvents such as N,N-dimethylacetamide, N-methyl-2-pyrrolidone, pyridine, etc., and showed high glas s transition temperatures of 287-290 degrees C and 5% weight loss temperatures of 450-465 degrees C in nitrogen. Optically active PAIs exhibited high specific rotations, excellent optical stabilities, and a dependence of optical activities on temperature. Investigations on chiroptical properties indicated that chiral conformation was possessed by optically active PAIs. (C) 1999 John Wiley & Sons, Inc.

Effect of crosslinking distribution on gas permeability and permselectivity of crosslinked polyimides

Crosslinking modification of polyimide, prepared from 3,3'4,4'-benzophenone tetracarboxyl dianhydride (BTDA) and 2,3,5,6-tetramethyl-1,4-diphenylenediamine (4MPDA), was performed by two methods, putting the polyimide in ambient environment for 4 months, and under UV irradiation for 2 or 8 h. The gas permeation properties of the crosslinked polyimides were investigated. The crosslinked polyimides induced by UV irradiation, in which crosslinking occurs in the surface layer, are of much higher gas permselectivity of hydrogen to nitrogen than that induced by the ambient environment, in which crosslinking takes place in the whole matrix, but their gas permeabilities for hydrogen are similar. (C) 1999 Elsevier Science Ltd. All rights reserved.

Gas permeability and permselectivity of photochemically crosslinked copolyimides

A series of copolyimides were prepared from 2,4,6-trimethyl-1,3-phenylenediamines (3MPDA), 3,3',4,4'-benzophenone tetracarboxyl dianhydride (BTDA), and pyromellitic dianhydride (PMDA). Modification of the copolyimides by ultraviolet irradiation were carried out. Gas permeabilities of H-2, O-2, and N-2 through the copolyimides and photochemically crosslinked copolyimides were measured at temperatures from 30 to 90 degrees C. The relationships between gas permeabilities and temperature are in agreement with the Arrhenius equation. The structure of photochemically crosslinked copolyimides were characterized by Fourier transform infrared and gel measurement methods. Linear relationships between both log P and E-p and the volume fraction of PMDA-3MPDA exist. Photochemically crosslinking modification result in a decrease in gas permeability and an increase in E-p and alpha(H-2/N-2) for all the copolyimides. For H-2/N-2 separation, photochemically crosslinked copolyimides are of higher gas permeabilities and permselectivities simultaneously than normal polyimides. (C) 1999 John Wiley & Sons, Inc.

Synthesis and properties of optically active poly(amide-imide)s containing axially dissymmetric 1,1 '-binaphthyl moieties

Novel optically active aromatic poly(amide-imide)s (PAIs) containing 1,1'-binaphthyl-2,2'-diyl units in the main chain were prepared by polycondensation reactions of newly synthesized dianhydride, 2,2'-bis(3,4-dicarboxylzenzamido)-1,1'-binaphthyl dianhydride[(S)-BN-DADA and (+/-)-BNDADA], with diamines, The properties of the resulted PAIs were fully characterized by a combination of investigations on inherent viscosity, thermal properties(DSC and TGA), specific rotation, CD and UV-Vis absorbance. These PAIs showed good solubilities, thermal properties and optical stabilities. Interesting UV-Vis absorption behavior of films casted from these PAIs was observed and analyzed.

Main-chain photosensitive polyamic acids using alkaline aqueous solution as developer

In order to develop photosensitive polyimides (PSPIs) imaged in alkaline aqueous solution, a photosensitive diamine and relevant polymer containing conjugated double bonds in the main chain have been synthesized. The photosensitive characteristics and thermal stability of the polymers were investigated. These polymers possess good thermal stability and sensitivity to UV irradiation, and could be used to form a PSPI resist using alkaline aqueous solution as developer. (C) 1999 Society of Chemical Industry.

Synthesis of aromatic polyimides in DMAc containing large amount of water and the properties thereof

A series of polyamic acids were prepared in N,N-dimethylactamide (DMAc) containing large amount of water, some of which contain the amount of water up to 25%. Their inherent viscosities decreased with the increase of water in DMAc, depending on the electronic properties of dianhydride and reaction condition. The molecular weights and mechanical properties of the polyimides thermally imidized from the polyamic acids were almost independent on the water content in solvent. The decomposition-resynthesis of polyamic acids during the curing was also investigated.

Synthesis and characterization of thermotropic liquid crystalline poly(ester imide)s

Two closely series of poly(ester imide)s had been synthesized by solution polycondensation of p-phenylenebis(trimellitate) dianhydride with aliphatic diamines. The differential scanning calorimetry (DSC) traces of the most poly(ester imide)s exhibited two endotherms representing the solid state to anisotropic phase transition (T-m1) and the anisotropic to isotropic melt transition (T-m2), respectively. Observation under polarizing microscope and wide-angle X-ray diffraction (WAXD) measurements suggested that the anisotropic phase formed above the melting paints (T-m1) had a smectic character. The thermogravimetric analyses (TGA) revealed that the thermal stabilities of the poly(ester imide)s were up to 350 degrees C. (C) 1999 John Wiley & Sons, Inc.

Chain conformation of a high-performance polyimide in organic solution

An organo-soluble polyimide based on 1,4-bis(3,4-dicarboxyphenoxy) benzene dianhydride (HQDPA) and 2,2'dimethyl-4,4'-methylene dianiline (DMMDA), was synthesized via two-step polycondensation accompanied by chemical imidization. Five fractions were prepared by fractionation. The dilute solutions of the fractions were studied by LLS (Laser Light Scattering) and the intrinsic viscosities of the fractions were measured. The unperturbed dimension was determined by the intrinsic viscosity with the Stockmayer-Fox equation. The results indicate that the polyimide in this study has a flexible chain conformation in chloroform and N,N-dimethyl acetamide (DMAc). However, the degree of chain expansion differs in different solvents. (C) 1998 Published by Elsevier Science Ltd. All rights reserved.