Gas permeability and permselectivity of polyimides prepared from phenylenediamines with methyl substitution at the ortho position

Polyimides were prepared from diamines: 2,4,6-trimethyl-1,3-phenylenediamine (3MPDA) and 2,3,4,5-tetramethyl-1,4-phenylenediamine (4MPDA). 1,4-Bis(3,4-dicarboxyphenoxy)benzene dianhydride (HQDPA), 3,3',4,4'-benzophenone tetracarboxylic dianhydride (BTDA), 3,3'-4,4'-diphenylsulphone tetracarboxylic dianhydride (SO(2)PDA), 3,3',4,4'-diphenylsulphide tetracarboxylic dianhydride (SPDA), pyromellitic dianhydride (PMDA), and 2,2'-bis(3,4-dicarboxyphenyl)hexa-fluoroisopropane dianhydride (6FDA) were used as dianhydride. The gas permeabilities of H-2, O-2 and N-2 through the polyimides were measured at temperatures from 30 degrees C to 90 degrees C. The results show that as methyl and trifluoromethyl substitution groups densities increase from 7.73 x 10(-3) molcm(-3) to 13.50 x 10(-3)molcm(-3), the peameability of H-2 increases 10-fold at 60% loss of permselectivity of H-2/N-2 however, the permeability of O-2 increases 20-fold at 20% loss of permselectivity of O-2/N-2. For O-2/N-2 separation, PMDA-3MPDA has similar performance to 6FDA-3MPDA and 6FDA-4MPDA; all have higher permeabilities for O-2 than normal polyimides, and the P(O-2)/alpha(O-2/N-2) trade-off relationships lie on the upper bound line for polymers. (C) 1999 Society of Chemical Industry.