Stress and resistivity controls on in situ boron doped LPCVD polysilicon films for high-Q MEMS applications

The simultaneous control of residual stress and resistivity of polysilicon thin films by adjusting the deposition parameters and annealing conditions is studied. In situ boron doped polysilicon thin films deposited at 520 ℃ by low pressure chemical vapor deposition (LPCVD) are amorphous with relatively large compressive residual stress and high resistivity. Annealing the amorphous films in a temperature range of 600-800 ℃ gives polysilicon films nearly zero-stress and relatively low resistivity. The low residual stress and low resistivity make the polysilicon films attractive for potential applications in micro-electro-mechanical-systems (MEMS) devices, especially in high resonance frequency (high-f) and high quality factor (high-Q MEMS resonators. In addition, polysilicon thin films deposited at 570 ℃ and those without the post annealing process have low resistivities of 2-5 mΩ·cm. These reported approaches avoid the high temperature annealing process (> 1000℃), and the promising properties of these films make them suitable for high-Q and high-f MEMS devices.

In situ doping of 3C-SiC grown on (0001) sapphire substrates by LPCVD

The heteroepitaxial growth of n-type and p-type 3C-SiC on (0001) sapphire substrates has been performed with a supply of SiH4+C2H4+H-2 system by introducing ammonia (NH3) and diborane (B2H6) precursors, respectively, into gas mixtures. Intentionally incorporated nitrogen impurity levels were affected by changing the Si/C ratio within the growth reactor. As an acceptor, boron can be added uniformly into the growing 3C-SiC epilayers. Nitrogen-doped 3C-SiC epilayers were n-type conduction, and boron-doped epilayers were p-type and probably heavily compensated.