The effects of concomitant In and N incorporation on the photoluminescence of GaInNAs

We investigated the effects of concomitant In- and N-incorporation on the photoluminescence (PL) of GaInNAs grown by molecular beam epitaxy. In comparison with the N-free GaInAs epilayer, the PL spectra of the GaInNAs epilayer exhibit an anomalous S-shape temperature dependence of dominant luminescence peak. Through further careful inspection, two PL peaks are clearly discerned and are associated with the interband excitonic recombinations and excitons bound to N-induced isoelectronic impurity states, respectively. By comparing the PL spectra of GaInNAs/ GaAs quantum wells (QWs) with those of In-free GaNAs/GaAs QWs grown under similar conditions, it is found that the concomitant In- and N-incorporation reduces the density of impurities and has an effect to improve the intrinsic optical transition of GaInNAs, but also enhance the N-induced clustering effects. At last, we found that rapid thermal annealing can significantly reduce the density of N-induced impurities. (C) 2002 Elsevier Science B.V. All rights reserved.

Dependence of optical properties on the structure of multi-layer self-organized InAs quantum dots emitting near 1.3 mu m

Self-organized InAs quantum dots (QDs) have been fabricated by molecular beam epitaxy and characterized by photoluminescence (PL). For both single- and multi-layer QDs, PL intensity of the first excited state is larger than that of the ground state at 15 K. Conversely, at room temperature (RT), PL intensity of the first excited state is smaller than that of the ground state. This result is explained by the phonon bottleneck effect. To the ground state, the PL intensities of the multi-layer QDs are larger than that of the single-layer QDs at 15 K, while the intensities are smaller than that of the single-layer QDs at RT. This is due to the defects in the multi-layer QD samples acting as the nonradiative recombination centers. The inter-diffusion of Ga and In atoms in the growth process of multi-layer QDs results in the PL blueshift of the ground state and broadening of the full-width at half-maximum (FWHM), which can be avoided by decreasing the spacers' growth temperature. At the spacers' growth temperature of 520degreesC, we have prepared the 5-layer QDs which emit near 1.3 mum with a FWHM of 31.7 meV at RT, and 27.9 meV at 77 K. (C) 2002 Published by Elsevier Science B.V.

Proof of InAs/GaAs self-organized quantum dot lasing and the experimental determination of local Strain effect on the band structures

Confirmation of quantum dot lasing have been given by photoluminescence and electro-luminescence spectra. Energy levels of QD laser are distinctively resolved due to band filling effect, and the lasing energy of quantum dot laser is much lower than quantum well laser. The energy barrier at InAs/GaAs interface due to the built-in strain in self-organized system has been determined experimentally by deep level transient spectroscopy (DLTS). Such barrier has been predicted by previous theories and can be explained by the apexes appeared in the interface between InAs and GaAs caused by strain.

Electrolyte electroreflectance spectroscopy studies on the interfacial behavior of the near-surface In0.15Ga0.85As/GaAs quantum well electrode vertical bar non-aqueous electrolyte

Electrolyte electroreflectance spectra of the near-surface strained-layer In0.15Ga0.85As/GaAs double single-quantum-well electrode have been studied at different biases in non-aqueous solutions of ferrocene and acetylferrocene. The optical transitions, the Franz-Keldysh oscillations (FKOs) and the quantum confined Stark effects (QCSE) of In0.15Ga0.85As/GaAs quantum well electrodes are analyzed. Electric field strengths at the In0.15Ga0.85As/GaAs interface are calculated in both solutions by a fast Fourier transform analysis of FKOs. A dip is exhibited in the electric field strength versus bias (from 0 to 1.2 V) curve in ferrocene solution. A model concerning the interfacial tunneling transfer of electrons is used to explain the behavior of the electric field. (C) 2001 Elsevier Science B.V. All rights reserved.

Influence of dual incorporation of In and N on the luminescence of GaInNAs/GaAs single quantum wells

The optical properties of above- and below-band-edge transitions have been investigated by incorporating In atoms into GaNAs/GaAs single quantum wells. The experimental results show that with increasing In concentration the interband luminescence is improved and the luminescence intensity below the band edge in GaInNAs/GaAs decreases significantly. An interpretation is given that N atoms are preferable to form a covalent bond with In than with Ga atoms in a GaInNAs alloy, due to the compensation of the atomic-size difference between In and N atoms on the GaAs substrate. The photoreflectance spectra of the GaInNAs/GaAs single quantum well support the assignment of an intrinsic mechanism to the high-energy luminescence peak. (C) 2000 American Institute of Physics. [S0003- 6951(00)01752-6].

Effects of interdiffusion on the luminescence of InAs/GaAs quantum dots covered by InGaAs overgrowth layer

We have studied the effects of postgrowth rapid thermal annealing on the optical properties of 3-nm-height InAs/GaAs quantum dots covered by 3-nm-thick InxGa1-xAs (x = 0, 0.1, and 0.2) overgrowth layer. At higher annealing temperature (T greater than or equal to 750 degreesC), the photoluminescence peak of InGaAs layer has been observed at lower-energy side of the InAs quantum-dot peak. In addition, the blueshift in photoluminescence (PL) emission energy is found to he similar for all samples with increasing the annealing temperature from 650 to 850 degreesC. However, the trend of narrowing of photoluminescence linewidth is significantly different for InAs quantum dots with different In mole fractions in InGaAs overgrowth layer. These results suggest that the intermixing in the lateral direction plays an important role in helping to understand the modification of optical properties induced by rapid thermal annealing. (C) 2000 Elsevier Science B.V. All rights reserved.

Effects of seed layer on the realization of larger self-assembled coherent InAs/GaAs quantum dots

The size and shape evolution of self-assembled InAs quantum dots (QDs) influenced by 2.0 ML InAs seed layer has been systematically investigated for 2.0, 2.5, and 2.9 ML deposition on GaAs(100) substrate. Based on comparisons with the formation of large incoherent InAs islands on single-layer samples at late growth stage, the larger coherent InAs quantum dots at 2.9 ML deposition has been observed on the second InAs layer. A simple model analysis accounting for the surface strain distribution influenced by buried islands gives a stronger increment of critical QD diameter for dislocation nucleation on the second layer in comparison with the single-layer samples. Additionally, the inhibition of dislocation nucleation in InGaAs/GaAs large islands can also be explained by our theoretical results. (C) 2000 American Institute of Physics. [S0021-8979(00)08922-2].

Annealing effect on the surface morphology and photoluminescence of InGaAs/GaAs quantum dots grown by molecular beam epitaxy

Postgrowth rapid thermal annealing was performed on InGaAs/GaAs quantum dots grown by molecular beam epitaxy. The blue shift of the emission peak and the narrowing of the luminescence line width are observed at lower annealing temperature. However, when the annealing temperature is increased to 850 degrees C, the emission line width becomes larger. The TEM image of this sample shows that the surface becomes rough, and some large clusters are formed, which is due to the interdiffusion of In, Ga atoms at the InGaAs/GaAs interface and to the strain relaxation. The material is found to degrade dramatically when the annealing temperature is further increased to 900 degrees C, while emission from quantum dots can still be detected, along with the appearance of the emission from excited state. (C) 2000 Elsevier Science B.V. All rights reserved.

The effect of dopant Si on the uniformity of self-organized InAs quantum dots

The photoluminescence in directly si-doped self-organized InAs quantum dots was systematically studied. With doping, a decrease in linewidth and a little blue shift in peak were observed by PL measurement. The results show that direct doping when growing InAs layer may be helpful to the formation of uniform small quantum dots. The work will be meaningful for the fabrication of self-organized InAs quantum dots semiconductor device.

Influence of indium composition on the surface morphology of self-organized InxGa1-xAs quantum dots on GaAs substrates

InxGa1-xAs self-organized quantum dots with x=1.0, 0.5, and 0.35 have been grown by molecular beam epitaxy. The areal density, distribution, and shapes have been found to be dependent on x. The dot shape changes from a round shape for x=1.0 to an elliptical shape for x less than or equal to 0.5. The major axis and minor axis of the elliptical InxGa1-xAs dots are along the [(1) over bar 10] and [110] directions, respectively. The ordering phenomenon is also discussed. It is suggested that the dot-dot interaction may play important roles in the self-organization process. (C) 2000 American Institute of Physics. [S0021-8979(00)10701-7].

Effects of rapid thermal annealing on the optical properties of GaNxAs1-x/GaAs single quantum well structure grown by molecular beam epitaxy

The effect of rapid thermal annealing (RTA) on the optical properties of GaNxAs1-x/GaAs strained single quantum well (SQW) was studied by low-temperature photoluminescence (PL). The GaNxAs1-x/GaAs SQW structures were prepared by dc active nitrogen plasma assisted molecular beam epitaxy. PL measurements on a series of samples with different well widths and nitrogen compositions were used to evaluate the effects of RTA. The annealing temperature and time were varied from 650 to 850 degrees C and 30 s to 15 min, respectively. Remarkable improvements of the optical properties of the samples were observed after RTA under optimum conditions. The interdiffusion constants have been calculated by taking into account error function diffusion and solving the Schrodinger equation. The estimated interdiffusion constants D are 10(-17)-10(-16) cm(2)/s for the earlier annealing conditions. Activation energies of 6-7 eV are obtained by fitting the temperature dependence of the interdiffusion constants. (C) 2000 American Institute of Physics. [S0021-8979(00)10401-3].

Strain effect on the band structure of InAs/GaAs quantum dots

The strain effect on the band structure of InAs/GaAs quantum dots has been investigated. 1 mu m thick InGaAs cap layer was added onto the InAs quantum dot layer to modify the strain in the quantum dots. The exciton energies of InAs quantum dots before and after the relaxation of the cap layer were determined by photoluminescence. When the epilayer was lifted off from the substrate by etching away the sacrifice layer (AlAs) by HF solution, the energy of exciton in the quantum dots decreases due to band gap narrowing resulted from the strain relaxation. This method can be used to obtain much longer emission wavelength from InAs quantum dots.

Indium composition dependence of the size uniformity of InGaAs quantum dots on (311)B GaAs grown by molecular beam epitaxy

The deposition of InxGa1-xAs (0.2 less than or equal to x less than or equal to 0.5) on (311)B GaAs surfaces using solid source molecular beam epitaxy (MBE) has been studied. Both AFM and photoluminescence emission showed that homogeneous quantum dots could be formed on (311)B GaAs surface when indium composition was around 0.4. Indium composition had a strong influence on the size uniformity and the lateral alignment of quantum dots. Compared with other surface orientation, (100) and (n11) A/B (n=1,2,3), photoluminescence measurement confirmed that (311)B surface is the most advantageous in fabricating uniform and dense quantum dots.

Morphology and photoluminescence of GeSi self-assembled quantum dot on Si(113)

Morphology of self-assembled GeSi quantum dot grown on Si(113) by Si molecular beam epitaxy has been studied by transmission electron microscopy and atomic force microscopy. Photoluminescence from the as-grown sample and annealed sample was studied. The results were analyzed and explained.

Effect of dopant on the uniformity of InAs self-organized quantum dots

Low-temperature photoluminescence studies have been performed on Si-doped and Be-doped self-organized InAs/GaAs quantum dot (QD) samples to investigate the effect of doping. When Si or Be is doped into the sample, a remarkable decrease in line-width is observed. We relate this phenomenon to a model that takes the Si or Be atoms as the nucleation centers for the formation of QDs. When Si or Be is doped, more small uniform quantum dots are formed. The result will be of significance for the application of self-organized InAs quantum dots in semiconductor devices.