Structure and optical properties of ZnS thin films grown by glancing angle deposition

The glancing angle deposition (GLAD) technique was used to deposit ZnS films by electron beam evaporation method. The cross sectional scanning electron microscopy (SEM) image illustrated a highly orientated microstructure composed of slanted column. The atomic force microscopy (APM) analysis indicated that incident flux angle had significant effects on the nodule size and surface roughness. Under identical nominal thickness, the actual thickness of the GLAD films is related to the incident flux angle. The refractive index and in-plane birefringence of the GLAD ZnS films were discussed, and the maximum bireffingence Delta n = 0.036 was obtained at incident flux angle of alpha = 80 degrees. Therefore, the glancing angle deposition technique is a promising way to create a columnar structure with enhanced birefringent property. (c) 2005 Elsevier B.V. All rights reserved.

电子束蒸发氧化锆薄膜的粗糙度和光散射特性

利用电子束蒸发工艺，以Ag层为衬底，沉积了中心波长为632．8nm的氧化锆（ZrO2）薄膜，膜层厚度在80-480nm范围内变化．研究了不同厚度样品的粗糙度变化规律和表面散射特性．结果发现，随着膜层厚度的逐渐增加．其表面均方根（RMS）粗糙度和总积分散射（TIS）均呈现出先减小后增大的趋势．利用非相关表面粗糙度的散射模型对样品的TIS特性进行了理论计算，所得结果与测量结果相一致．

不同沉积参量下ZrO_2薄膜的微结构和激光损伤阈值

ZrO2采用X射线衍射(XRD)技术分析了不同充氧条件和沉积温度对ZrO2溥膜组成结构的影响，并对不同工艺下制备的薄膜的表面粗糙度和激光损伤阈值进行了测量。结果发现随着氧压的升高，ZrO2溥膜将由单斜相多晶态逐渐转变为非晶态结构，而随着基片温度的增加，溥膜将由非晶态逐渐转变为单斜相多晶态。同时发现随着氧压升高晶粒尺寸减小，而随着沉积温度增加，晶粒尺寸增大。氧压增加时工艺对表面粗糙度有一定程度的改善，而沉积温度升高，工艺对表面粗糙度的改善不明显。晶粒尺寸大小变化与表面粗糙度变化存在对应关系。激光损伤测量表明

Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

不同膜层数的Mo/Si多层膜的表界面粗糙度和软X射线反射率

用磁控溅射法制备了顶层分别是Mo膜层和Si膜层的两个系列的Mo/Si多层膜，它们的周期厚度相同但是膜层数各不相同。Mo/Si多层膜的周期厚度和界面粗糙度由小角X射线衍射（SAXRD）曲线拟和得到。用原子力显微镜测量了Mo/Si多层膜的表面粗糙度。在国家同步辐射实验室测量了Mo/Si多层膜的软X射线反射率。通过理论和试验研究，发现Mo/Si多层膜的软X射线反射率主要由周期数和界面粗糙度决定，表面粗糙度对Mo/Si多层膜的软X射线反射率影响较小。

薄膜材料对TiO2基薄膜激光损伤阈值的影响

abstract {The optical property, structure, surface properties (roughness and defect density) and laser-induced damage threshold (LIDT) of TiO₂ films deposited by electronic beam (EB) evaporation of TiO₂ (rutile), TiO₂ (anatase) and TiO₂ + Ta₂O₅ composite materials are comparatively studied. All films show the polycrystalline anatase TiO₂ structure. The loose sintering state and phase transformation during evaporating TiO₂ anatase slice lead to the high surface defect density, roughness and extinction coefficient, and low LIDT of films. The TiO₂ + Ta₂O₅ composite films have the lowest extinction coefficient and the highest LIDT among all samples investigated. Guidance of selecting materials for high LIDT laser mirrors is given.}

Comparison of TiO2 and ZrO2 films deposited by electron-beam evaporation and by sol-gel process

TiO2 and ZrO2 films are deposited by electron-beam (EB) evaporation and by sol-gel process. The film properties are characterized by visible and Fourier-transform infrared spectrometry, x-ray diffraction analysis, surface roughness measure, absorption and laser-induced damage threshold (LIDT) test. It is found that the sol-gel Elms have lower refractive index, packing density and roughness than EB deposited films due to their amorphous structure and high OH group concentration in the film. The high LIDT of sol-gel films is mainly due to their amorphous and porous structure, and low absorption. LIDT of EB deposited film is considerably affected by defects in the Elm, and LIDT of sol-gel deposited film is mainly effected by residual organic impurities and solvent trapped in the film.

用不同的Mo靶溅射功率制备Mo／Si多层膜

用磁控溅射法制备了周期厚度和周期数均相同的Mo／Si多层膜，用原子力显微镜和小角X射线衍射分别研究了Mo靶溅射功率不相同时，Mo／Si多层膜表面形貌和晶相的变化。随后在国家同步辐射实验室测量了Mo／Si多层膜的软X射线反射率。研究发现，随着Mo靶溅射功率的增大，Mo／Si多层膜的表面粗糙度增加，Mo的特征X射线衍射峰也增强，Mo／Si多层膜的软X射线峰值反射率先增大后减小。

Mo／Si软X射线多层膜的界面粗糙度研究

用磁控溅射法分别制备了以Mo膜层和Si膜层为顶层的Mo／Si多层膜系列，利用小角X射线衍射确定了各多层膜的周期厚度。以不同周期数的Mo／Si多层膜的新鲜表面近似等同于同一多层膜的内界面，通过原子力显微镜研究了多层膜界面粗糙度随膜层数的变化规律。并在国家同步辐射实验室测量了各多层膜的软X射线反射率。研究表明：随着膜层数的增加，Mo膜层和Si膜层的界面粗糙度先减小后增加然后再减小，多层膜的峰值反射率先增加后减小。

沉积温度对热舟蒸发MgF2薄膜性能的影响

采用热舟蒸发方法沉积了氟化镁（MgF2）材料的单层膜，沉积温度从200℃上升到350℃，间隔为50℃。测量了样品的透射率和反射率光谱曲线，进行了表面粗糙度的标定，并在此基础上进行了光学损耗及散射损耗的计算。同时对355nm波长处的激光诱导损伤阈值进行了测量。结果表明：随着沉积温度的升高，光学损耗增加;在短波长范围散射损耗在光学损耗中所占比例很小，光学损耗的增加主要由吸收损耗引起；在355nm波长处的损伤阈值变化与吸收损耗的变化趋势相关，损伤机制主要是吸收起主导作用。样品的微缺陷密度也是影响损伤阈值的一个重要因素，损伤阈值随缺陷密度的增加而降低。

热舟蒸发LaF_3薄膜的紫外性能研究

研究了沉积温度对热舟蒸发氟化镧薄膜结构和光学性能的影响,沉积温度从200℃上升到350℃,间隔为50℃.采用分光光度计测量了样品的透射率和反射率光谱曲线,并在此基础上进行了光学损耗、光学常数以及带隙和截止波长的计算.采用表面轮廓仪进行了表面形貌和表面粗糙度的标定,采用X射线衍射(XRD)方法测量了不同沉积温度下样品的微结构.发现在短波长波段,随着沉积温度的升高,光学损耗增加,晶粒尺寸增大,表面粗糙度略有增加.不过散射损耗在光学损耗中所占比例均很小,光学损耗的增加主要由吸收损耗引起.随着沉积温度的升高,折射率与消光系数增大,带隙变小,相对应的截止波长向长波方向移动.

Influence of oxygen plasma treatment on properties of ZrO2 films prepared by e-beam evaporation techniques

Zirconia films were prepared by e-beam evaporation, and oxygen plasma treatment was used to modify film properties. Spectrophotometry, x-ray diffractometry (XRD), and atomic force microscopy were used to characterize refractive index, extinction coefficient, rnicrostructure, and surface roughness, respectively. The experimental results indicate that both refractive index and extinction coefficient of the films were reduced slightly after oxygen plasma treatment, with the decrease of intrinsic stress and surface roughness. From XRD spectra, the intensity decrease of the T(110) diffraction peak was clearly observed after the treatment, which was caused by the restructuring of the film atoms. (C) 2008 Elsevier Ltd. All rights reserved.

低损耗193nm反射膜的设计

采用1/4规整膜系,从电场强度、吸收损耗及散射损耗的分布几个方面,对影响193 nm反射膜性能的因素进行了分析。以分析结果为基础,对低损耗193 nm反射膜的设计进行了探讨。结果表明:在空气侧的外膜层中电场强度较大,随着层数向内过渡,电场强度迅速减小;高折射率材料膜层的吸收损耗明显高于低折射率材料膜层的吸收损耗,而且靠近空气侧最外层的高折射率膜层的吸收损耗最大;按由外层向内层过渡的方向,吸收损耗迅速减小,减小的速度与高低折射率材料折射率的比值相关;表面散射损耗与两种材料的折射率比值成正比,但折射率比值减小后只能通过增加膜层数来获得一定的反射率,而这样又会使表面粗糙度增加,并且引入其它的损耗。因此,选择折射率差值适当大一些的材料对降低散射损耗是有利的。设计了27层膜堆的193 nm反射膜,设计反射率在98%以上。

Growth and fabrication of AlGaN/GaN HEMT based on Si(111) substrates by MOCVD

AlGaN/GaN high electron mobility transistor (HEMT) hetero-structures were grown on the 2-in Si (1 1 1) substrate using metal-organic chemical vapor deposition (MOCVD). Low-temperature (LT) AlN layers were inserted to relieve the tension stress during the growth of GaN epilayers. The grown AlGaN/GaN HEMT samples exhibited a maximum crack-free area of 8 mm x 5 mm, XRD GaN (0 0 0 2) full-width at half-maximum (FWHM) of 661 arcsec and surface roughness of 0.377 nm. The device with a gate length of 1.4 mu m and a gate width of 60 mu m demonstrated maximum drain current density of 304 mA/mm, transconductance of 124 mS/mm and reverse gate leakage current of 0.76 mu A/mm at the gate voltage of -10 V. (C) 2008 Published by Elsevier Ltd.