Long-Wavelength Emission InAs Quantum Dots Grown on InGaAs Metamorphic Buffers

In this work, InAs quantum dots (QDs) grown on a linear graded InGaAs metamorphic buffer layer by molecular beam epitaxy have been investigated. The growth of the metamorphic buffer layers was carefully optimized, yielding a smooth surface with a minimum root mean square of roughness of less than 0.98 nm as measured by atomic force microscopy (AFM). InAs QDs were then grown on the buffer layers, and their emission wavelength at room-temperature is 1.49 mu m as measured by photoluminescence (PL). The effects of post-growth rapid thermal annealing (RTA) on the optical properties of the InAs QDs were investigated. After the RTA, the PL peak of the QDs was blue-shifted and the full width at half maximum decreased.

GaAs Based InAs/GaSb Superlattice Short Wavelength Infrared Detectors Grown by Molecular Beam Epitaxy

InAs/GaSb superlattice (SL) short wavelength infrared photoconduction detectors are grown by molecular beam epitaxy on GaAs(001) semi-insulating substrates. An interfacial misfit mode AlSb quantum dot layer and a thick GaSb layer are grown as buffer layers. The detectors containing a 200-period 2ML/8ML InAs/GaSb SL active layer are fabricated with a pixel area of 800 x 800 mu m(2) without using passivation or antireflection coatings. Corresponding to the 50% cutoff wavelengths of 2.05 mu m at 77K and 2.25 mu m at 300 K, the peak detectivities of the detectors are 4 x 10(9) cm.Hz(1/2)/W at 77K and 2 x 10(8) cm.Hz(1/2)/W at 300 K, respectively.

Optical matching layer structures in evanescent coupling photodiodes at a wavelength of 1.55 mu m: physics, design and simulation

We have studied the optical matching layers (OMLs) and external quantum efficiency in the evanescent coupling photodiodes (ECPDs) integrating a diluted waveguide as a fibre-to-waveguide coupler, by using the semi-vectorial beam propagation method (BPM). The physical basis of OML has been identified, thereby a general designing rule of OML is developed in such a kind of photodiode. In addition, the external quantum efficiency and the polarization sensitivity versus the absorption and coupling length are analysed. With an optical matching layer, the absorption medium with a length of 30 mu m could absorb 90% of the incident light at 1.55 mu m wavelength, thus the total absorption increases more than 7 times over that of the photodiode without any optical matching layer.

Control of the lasing wavelength by a sampled grating in a complex-coupled DFB laser

The lasing wavelength of a complex-coupled DFB laser is controlled by a sampled grating. The key concepts of the approach are to utilize the -1st order (negative first order) reflection of a sampled grating for laser single mode operation, and use conventional holographic exposure combined with the usual photolithography to fabricate the sampled grating. The typical threshold current of the sampled grating based DFB laser is 32 mA, and the optical output is about 10 mW at an injected current of 100 mA. The lasing wavelength of the device is 1.5356 mu m, which is the -1st order wavelength of the sampled grating.

Effects of waveguide length and pump power on the efficiency of wavelength conversion in silicon nanowire waveguides

We point out the use of a wrong definition for conversion efficiency in the literature and analyze the effects of the waveguide length and pump power on conversion efficiency according to the correct definition. The existence of the locally optimal waveguide length and pump power is demonstrated theoretically and experimentally. Further analysis shows that the extremum of conversion efficiency can be achieved by global optimization of the waveguide length and pump power simultaneously, which is limited by just the linear propagation loss and the effective carrier lifetime. (C) 2009 Optical Society of America

Long-wavelength SiGe/Si MQW resonant-cavity-enhanced photodiodes (RCE-PD)

Si1-xGex/Si optoelectronic devices are promising for the monolithic integration with silicon-based microelectronics. SiGe/Si MQW RCE-PD (Resonant-Cavity-Enhanced photodiodes) with different structures were investigated in this work. Design and fabrication of top- and bottom-incident RCE-PD, such as growth of SiGe MQW (Multiple Quantum Wells) on Si and SOI (Si on insulator) wafers, bonding between SiGe epitaxial wafer and SOR (Surface Optical Reflector) consisting Of SiO2/Si DBR (Distributed Bragg Reflector) films on Si, and performances of RCE-PD, were presented. The responsivity of 44mA/W at 1.314 mum and the FWHM of 6nm were obtained at bias of 10V. The highest external quantum efficiency measured in the investigation is 4.2%.

Photoluminescence from self-assembled long-wavelength InAs/GaAs quantum dots under pressure

The photoluminescence from self-assembled long-wavelength InAs/GaAs quantum dots was investigated at 15 K under hydrostatic pressure up to 9 GPa. Photoemission from both the ground and the first excited states in large InAs dots was observed. The pressure coefficients of the two emissions were 69 and 72 meV/GPa, respectively. A nonlinear elasticity theory was used to interpret the significantly small pressure coefficients of the large dots. The sequential quenching of the ground and the excited state emissions with increasing pressure suggests that the excited state emissions originate from the optical transitions between the first excited electron states and the first excited hole states. (C) 2004 American Institute of Physics.

Tuning of detection wavelength in a resonant-cavity-enhanced quantum-dot-embedded photodiode by changing detection angle

We have fabricated a resonant-cavity-enhanced photodiode (RCE-PD) with InGaAs quantum dots (QDs) as an active medium. This sort of QD-embedded RCE-PD is capable of a peak external quantum efficiency of 32% and responsivity of 0.27A/W at 1.058 mu m with a full width at half maximum (FWHM) of 5 nm. Angle-resolved photocurrent response eventually proves that with the detection angle changing from 0 degrees to 60 degrees, the peak-current wavelength shifts towards the short wavelength side by 37 nm, while the quantum efficiency remains larger than 15%.

Demonstration of low-cost Si-based tunable long-wavelength resonant-cavity-enhanced photodetectors

A simple process for fabricating low-cost Si-based continuously tunable long-wavelength resonant-cavity-enhanced (RCE) photodetectors has been investigated. High-contrast SiO2/Si(Deltan similar to2) was employed as mirrors to eliminate the need to grow thick epitaxial distributed Bragg reflectors. Such high-reflectivity SiO2/Si mirrors were deposited on the as-grown InGaAs epitaxy layers, and then were bonded to silicon substrates at a low temperature of 350 C without any special treatment on bonding surfaces, employing silicate gel as the bonding medium. The cost is thus decreased. A thermally tunable Si-based InGaAs RCE photodetector operating at 1.3-1.6 mum was obtained, with a quantum efficiency of about 44% at the resonant wavelength of 1476 nm and a tuning range of 14.5 nm. It demonstrates a great potential for industry processes. (C) 2005 American Institute of Physics.

Gain measurement and anomalous decrease of peak gain at long wavelength for InAs/GaAs quantum-dot lasers

Mode gain spectrum is measured by the Fourier series expansion method for InAs/GaAs quantum-dot (QD) lasers with seven stacks of QDs at different injection currents. Gain spectra with distinctive peaks are observed at the short and long wavelengths of about 1210 nm and 1300 nm. For a QD laser with the cavity length of 1060 mu m, the peak gain of the long wavelength first increases slowly or even decreases with the injection current as the peak gain of the short wavelength increases quickly, and finally increases quickly before approaching the saturated values as the injection current further increases.

Fabrication of ultra-low density and long-wavelength emission InAs quantum dots

By optimizing the molecular beam epitaxy growth conditions of self-organized InAs/GaAs quantum dots (QDs), we obtained an ultra-low density system of InAs QDs (4 x 10(6)cm(-2)). Photoluminescence (PL) spectroscopy reveals the emission wavelength at room temperature to be longer than 1300 nm with a GaAs capping layer. (c) 2007 Elsevier B.V. All rights reserved.

Unselective regrowth buried heterostructure long-wavelength superluminescent diode realized with MOVPE

A novel unselective regrowth buried heterostructure (BH) long-wavelength superluminescent diode (SLD), which has a grade-strained bulk InGaAs active region, was developed by metalorganic vapor-phase epitaxy (MOVPE). The 3 dB emission spectrum bandwidth of the SLD is about 65 nm with the range from 1596 to 1661 nm at 90 mA and front 1585 to 1650 nm at 150 mA. An output power of 3.5 mW is obtained at 200 mA injection current under CW operation at room temperature. (c) 2006 Elsevier B.V. All rights reserved.

MBE InAs quantum dots grown on metamorphic InGaAs for long wavelength emitting

GaAs-based InAs quantum dots using InGaAs composition-graded metamorphic layers have been investigated by molecular beam epitaxy. Emission with the wavelength similar to 1.5 mu m from the dots was obtained at room temperature with the relatively large full width at half maximum. The emission wavelength is relatively stable when subjected to fast annealing. The number density of dots reached similar to 6 x 10(10) cm(-2). Undulated morphology was observed on the surface of the sample, which has some influence on the dot size and distribution. In epilayers, misfit dislocations were confined within the step-graded InGaAs metamorphic buffer layer. (c) 2006 Elsevier B.V. All rights reserved.

Material growth and device fabrication of highly strained InGaAs/InGaAsP long wavelength distributed feedback lasers

1.6-1.7 mu m highly strained InGaAs/InGaAsP distributed feedback lasers was grown and fabricated by low pressure mentalorganic chemical vapor deposition. High quality highly strained InGaAs/InP materials were obtained by using strain buffer layer. Four pairs of highly strained quantum wells were used in the devices and carrier blocking layer was used to improve the temperature characteristics of the devices. The uncoated 1.66 mu m and 1.74 mu m lasers with ridge wave guide 3 mu m wide have low threshold current (< 15mA) and high output power (> 14mW at 100mA). In the temperature range from 10 degrees C to 40 degrees C, the characteristic temperature T-0 of the 1.74 mu m laser is 57K, which is comparable to that of the 1.55 mu m-wavelength InGaAsP/InP-DFB laser.

A two-dimensional photonic crystal slab mirror with silicon on insulator for wavelength 1.3 mu m

A concrete two-dimensional photonic crystal slab with triangular lattice used as a mirror for the light at wavelength 1.3 mu m with a silicon-on-insulator (Sol) substrate is designed by the three-dimensional plane wave expansion method. For TE-like modes, the bandgap in the F-K direction is from 1087nm to 1559nm. The central wavelength in the bandgap is about 1.3 mu m, hence the incident light at wavelength 1.3 mu m will be strongly reflected. Experimentally, such a photonic crystal slab is fabricated on an SOI substrate by the combination of EBL and ICP etching. The measurement of its transmission characteristics shows the bandgap edge in a longer wavelength is about 1540mn. The little discrepancy between the experimental data and the theoretical values is mainly due to the size discrepancy of the fabricated air holes.