Role of edge dislocation and Si impurity in linking the blue luminescence and yellow luminescence in n-type GaN films

A close relationship is found between the blue and yellow luminescence bands in n-type GaN films, which are grown without intentional acceptor doping. The intensity ratio of blue luminescence to yellow luminescence (I-BL/I-YL) decreases with the increase in edge dislocation densities as demonstrated by the (102) full width at half maximum of x-ray diffraction. In addition, the I-BL/I-YL ratio decreases with the increase in Si doping. It is suggested that the edge dislocation and Si impurity play important roles in linking the blue and yellow luminescence.

Enhancement of conductivity and transmittance of ZnO films by post hydrogen plasma treatment

We studied the effects of hydrogen plasma treatment on the electrical and optical properties of ZnO films deposited by radio frequency magnetron sputtering. It is found that the ZnO H film is highly transparent with the average transmittance of 92% in the visible range. Both carrier concentration and mobility are increased after hydrogen plasma treatment, correspondingly, the resistivity of the ZnO H films achieves the order of 10(-3) cm. We suggest that the incorporated hydrogen not only passivates most of the defects and/or acceptors present, but also introduces shallow donor states such as the V-O-H complex and the interstitial hydrogen H-i. Moreover, the annealing data indicate that H-i is unstable in ZnO, while the V-O-H complex remains stable on the whole at 400 degrees C, and the latter diffuses out when the annealing temperature increases to 500 degrees C. These results make ZnO H more attractive for future applications as transparent conducting electrodes.

Curvature Correction of FWHM in the X-Ray Rocking Curve of Bent Heteroepitaxial Films

A method for accurate determination of the curvature radius of semiconductor thin films is proposed. The curvature-induced broadening of the x-ray rocking curve (XRC) of a heteroepitaxially grown layer can be determined if the dependence of the full width at half maximum (FWHM) of XRC is measured as a function of the width of incident x-ray beam. It is found that the curvature radii of two GaN films grown on a sapphire wafer are different when they are grown under similar MOCVD conditions but have different values of layer thickness. At the same time, the dislocation-induced broadening of XRC and thus the dislocation density of the epitaxial film can be well calculated after the curvature correction.

Suppression of indium droplet formation by adding CCl4 during metalorganic chemical vapor deposition growth of InN films

In this work, the influences of CCl4 on the metalorganic chemical vapor deposition (MOCVD) growth of InN were studied for the first time. It was found that the addition of CCl4 can effectively suppress the formation of metal indium (In) droplets during InN growth, which was ascribed to the etching effect of Cl to In. However, with increasing of CCl4 flow, the InN growth rate decreased but the lateral growth of InN islands was enhanced. This provides a possibility of promoting islands coalescence toward a smooth surface of the InN film by MOCVD. The influence of addition of CCl4 on the electrical properties was also investigated.

Optical properties of aluminum-, gallium-, and indium-doped Bi4Ti3O12 thin films

Undoped and Al-, Ga-, and In-doped Bi4Ti3O12 thin films were prepared on fused quartz substrates by chemical solution deposition. Their microstructures and optical properties were investigated by x-ray diffraction and UV-visible-NIR spectrophotometer, respectively. The optical band-gap energies, Urbach energies, and linear refractive indices of all the films are derived from the transmittance spectrum. Following the single oscillator model, the dispersion parameters such as the average oscillator energy (E-0) and dispersion energy (E-d) are achieved. The energy band gap and refractive indices are found to decrease with introducing the dopants of Al, Ga, and In, which is useful for the band-gap engineering and optical waveguide devices. The refractive index dispersion parameter (E-0/S-0) increases and the chemical bonding quantity (beta) decreases in all the films compared with those of bulk. It is supposed to be caused by the nanosize grains in films. (c) 2009 American Institute of Physics. [DOI 10.1063/1.3138813]

Growth behavior of AlInGaN films

The structural and surface properties of AlInGaN quaternary films grown at different temperatures on GaN templates by metalorganic chemical vapor deposition are investigated. Formation of two quaternary layers is confirmed and the difference between them is pronounced when the growth temperature is increased. The surface is featured with V-shaped pits and cracks, whose characteristics are further found to be strongly dependent on the growth temperature of AlInGaN layers. The two-layer structure is interpreted by taking into account of the strain status in AlInGaN layers. (C) 2008 Elsevier B.V. All rights reserved.

Al composition variations in AlGaN films grown on low-temperature GaN buffer layer by metalorganic chemical vapor deposition

We have investigated the optical properties of AlGaN grown on sapphire. It is found that two main luminescence peaks occur in the cathodoluminescence (CL) spectra of AlGaN films, and their energy separation increases with the increase of Al source flux during the growth. Spatially resolved CL investigations have shown that the line splitting is a result of variation of AlN mole fraction within the layer. The Al composition varies in both lateral and vertical direction. It is suggested that the difference in the surface mobility of Al and Ga atoms, especially, its strong influence on the initial island coalescence process and the formation of island-like regions on the uneven film surface, is responsible for the Al composition inhomogeneity. (C) 2008 Elsevier B.V. All rights reserved.

Structural and optical properties of ZnO films on SrTiO3 substrates by MOCVD

ZnO films have been fabricated on (0 0 1), (0 1 1) and (1 1 1) SrTiO3 (STO) substrates by metal-organic chemical vapour deposition (MOCVD). It is interesting that the ZnO films on (0 0 1) and (0 1 1) STO substrates show polar and semipolar orientations, which are different from previous reports, while the same growing direction of polar ZnO with previous results is found on (1 1 1) STO. For the atomic arrangements, two orthogonal domains and a single domain are observed on (0 0 1) and (1 1 1) STO, respectively. Photoluminescence spectra show that every sample has a sharp near-band-edge emission peak at about 3.28 eV without any deep-level emission band between 1.5 and 2.8 eV, implying a high optical quality. A violet emission around 3.0 eV is observed only in ZnO films on (0 0 1) and (0 1 1) STO substrates grown at 600 degrees C, which is discussed briefly. Additionally, the semipolar ZnO does not weaken the emission efficiency along with the reduction in the polarization effect compared with polar ZnO. These results show that high-quality polar and semipolar ZnO films can be grown on STO substrates by MOCVD.

Effect of Nitridation on Morphology, Structural Properties and Stress of AIN Films

We investigate effects of nitridation on AIN morphology, structural properties and stress. It is found that 3 min nitridation can prominently improve AIN crystal structure, and slightly smooth the surface morphology. However, 10 min nitridation degrades out-of-plane crystal structure and surface morphology instead. Additionally, 3-min nitridation introduces more tensile stress (1.5 GPa) in AIN films, which can be attributed to the weaker islands 2D coalescent. Nitridation for 10 min can introduce more defects, or even forms polycrystallinity interlayer, which relaxes the stress. Thus, the stress in AIN with 10 min nitridation decreases to -0.2 GPa compressive stress.

Growth of crack-free GaN films on Si(111) substrate by using Al-rich AlN buffer layer

GaN epilayers were grown on Si(111) substrate by metalorganic chemical vapor deposition. By using the Al-rich AlN buffer which contains Al beyond stoichiometry, crack-free GaN epilayers with 1 mum thickness were obtained. Through x-ray diffraction (XRD) and secondary ion mass spectroscopy analyses, it was found that a lot of Al atoms have diffused into the under part of the GaN epilayer from the Al-rich AlN buffer, which results in the formation of an AlxGa1-xN layer at least with 300 nm thickness in the 1 mum thick GaN epilayer. The Al fraction x was estimated by XRD to be about 2.5%. X-ray photoelectron spectroscopy depth analysis was also applied to investigate the stoichiometry in the Al-rich buffer before GaN growth. It is suggested that the underlayer AlxGa1-xN originated from Al diffusion probably provides a compressive stress to the upper part of the GaN epilayer, which counterbalances a part of tensile stress in the GaN epilayer during cooling down and consequently reduces the cracks of the film effectively. The method using the Al diffusion effect to form a thick AlGaN layer is really feasible to achieve the crack-free GaN films and obtain a high crystal quality simultaneously. (C) 2004 American Institute of Physics.

Impacts of hydrogen dilution on growth and optical properties of a-SiC : H films

Hydrogenated amorphous silicon-carbon (a-SiC:H) films were deposited by plasma enhanced chemical vapor deposition (PECVD) with a fixed methane to silane ratio ([CH4]/[SiH4]) of 1.2 and a wide range of hydrogen dilution (R-H=[H-2]/[SiH4 + CH4]) values of 12, 22, 33, 102 and 135. The impacts of RH on the structural and optical properties of the films were investigated by using UV-VIS transmission, Fourier transform infrared (FTIR) absorption, Raman scattering and photoluminescence (PL) measurements. The effects of high temperature annealing on the films were also probed. It is found that with increasing hydrogen dilution, the optical band gap increases, and the PL peak blueshifts from similar to1.43 to 1.62 eV. In annealed state, the room temperature PL peak for the low R-H samples disappears, while the PL peak for the high R-H samples appears at similar to 2.08 eV, which is attributed to nanocrystalline Si particles confined by Si-C and Si-O bonds.

Study of infrared luminescence from Er-implanted GaN films

In this study, we report the dependences of infrared luminescence properties of Er-implanted GaN thin films (GaN:Er) on the kinds of substrates used to grow GaN, the growth techniques of GaN, the implantation parameters and annealing procedures. The experimental results showed that the photoluminescence (PL) intensity at 1.54 mum was severely influenced by different kinds of substrates. The integrated PL peak intensity from GaN:Er /Al2O3 (00001) was three and five times stronger than that from GaN:Er /Si (111) grown by molecular beam epitaxy (MBE) and by metalorganic chemical vapor deposition (MOCVD), respectively. The PL spectra observed from GaN:Er/Al2O3 (0001) grown by MOCVD and by MBE displayed a similar feature, but those samples grown by MOCVD exhibited a stronger 1.54 mum PL. It was also found that there was a strong correlation between the PL intensity with ion implantation parameters and annealing procedures. Ion implantation induced damage in host material could be only partly recovered by an appropriate annealing temperature procedure. The thermal quenching of PL from 15 to 300 K was also estimated. In comparison with the integrated PL intensity at 15 K, it is reduced by only about 30 % when going up to 300 K for GaN:Er/Al2O3 sample grown by MOCVD. Our results also show that the strongest PL intensity comes from GaN:Er grown on Al2O3 substrate by MOCVD. (C) 2004 Elsevier B.V. All rights reserved.

Preferred growth of nanocrystalline silicon in boron-doped nc-Si : H Films

Preferred growth of nanocrystalline silicon (nc-Si) was first found in boron-doped hydrogenated nanocrystalline (nc-Si:H) films prepared using plasma-enhanced chemical vapor deposition system. The films were characterized by high-resolution transmission electron microscope, X-ray diffraction (XRD) spectrum and Raman Scattering spectrum. The results showed that the diffraction peaks in XRD spectrum were at 2theta approximate to 47degrees and the exponent of crystalline plane of nc-Si in the film was (220). A considerable reason was electric field derived from dc bias made the bonds of Si-Si array according to a certain orient. The size and crystalline volume fraction of nc-Si in boron-doped films were intensively depended on the deposited parameters: diborane (B2H6) doping ratio in silane (SiH4), silane dilution ratio in hydrogen (H-2), rf power density, substrate's temperature and reactive pressure, respectively. But preferred growth of nc-Si in the boron-doped nc-Si:H films cannot be obtained by changing these parameters. (C) 2004 Elsevier Ltd. All rights reserved.

Effects of crystalline quality on the phase stability of cubic boron nitride thin films under medium-energy ion irradiation

To investigate the effect of radiation damage on the stability and the compressive stress of cubic boron nitride (c-BN) thin films, c-BN films with various crystalline qualities prepared by dual beam ion assisted deposition were irradiated at room temperature with 300 keV Ar+ ions over a large fluence range up to 2 x 10(16) cm(-2). Fourier transform infrared spectroscopy (FTIR) data were taken before and after each irradiation step. The results show that the c-BN films with high crystallinity are significantly more resistant against medium-energy bombardment than those of lower crystalline quality. However, even for pure c-BN films without any sp(2)-bonded BN, there is a mechanism present, which causes the transformation from pure c-BN to h-BN or to an amorphous BN phase. Additional high resolution transmission electron microscopy (HRTEM) results support the conclusion from the FTIR data. For c-BN films with thickness smaller than the projected range of the bombarding Ar ions, complete stress relaxation was found for ion fluences approaching 4 x 10(15) cm(-2). This relaxation is accompanied, however, by a significant increase of the width of c-BN FTIR TO-line. This observation points to a build-up of disorder and/or a decreasing average grain size due to the bombardment. (c) 2005 Elsevier B.V. All rights reserved.

Impact of hydrogen dilution on microstructure and optoelectronic properties of silicon films deposited using tirisilane

We explored the deposition of hydrogenated amorphous silicon (a-Si: H) using trisilane (Si3H8) as a gas precursor in a radiofrequency plasma enhanced chemical vapour deposition process and studied the suitability of this material for photovoltaic applications. The impact of hydrogen dilution on the deposition rate and microstructure of the films is systematically examined. Materials deposited using trisilane are compared with that using disilane (Si2H6). It is found that when using Si3H8 as the gas precursor the deposition rate increases by a factor of similar to 1.5 for the same hydrogen dilution (R = [H-2]/[Si3H8] or [H-2]/[Si2H6])- Moreover, the structural transition from amorphous to nanocrystalline occurs at a higher hydrogen dilution level for Si3H8 and the transition is more gradual as compared with Si2H6 deposited films. Single-junction n-i-p a-Si: H solar cells were prepared with intrinsic layers deposited using Si3H8 or Si2H6. The dependence of open circuit voltage (V-oc) on hydrogen dilution was investigated. V-oc greater than 1 V can be obtained when the i-layers are deposited at a hydrogen dilution of 180 and 100 using Si3H8 and Si2H6, respectively.