Effect of counterpart on the tribological behavior and tribo-induced phase transformation of Si

The tribological behaviors and phase transformation of single crystal silicon against Si3N4, Ruby and steel were investigated in this study. It was found that the strong chemical action between silicon and Fe was the key factor to the tribological behavior of silicon as slid against steel. SEM and Raman spectroscopy indicated that phase transformation of single crystal silicon occurred during the running-in period at low sliding velocity as slid against Si3N4 and Ruby. and gave birth to single or a mixture phase of Si-III, Si-XII and amorphous silicon. The high hardness of counterpart and the absence of chemical action between silicon and counterpart facilitated the phase transformation of single crystal silicon. (C) 2008 Elsevier Ltd. All rights reserved.

Cathodoluminescence and Raman research of V-shape inverted pyramid in HVPE grown GaN film

Thick GaN films with high quality have been grown on (0001) sapphire substrate in a home-made vertical HVPE reactor. Micron-size hexagonal pits with inverted pyramid shape appear on the film surface, which have six triangular {10-11} facets. These I {10-11} facets show strong luminescence emission and are characteristic of doped n-type materials. Broad red emission is suppressed in {10-11} facets and is only found at the flat region out of the pit, which is related with the decreasing defects on {10-11} facets. Low CL emission intensity is observed at the apex of V-shape pits due to the enhanced nonradiative recombination. Raman spectra show that there are higher carrier concentration and low strain in the pit in comparison to the flat region out of the pit. The strain relaxation may be the main mechanism of the V-shape pits formation on the GaN film surface. (c) 2006 Elsevier B.V. All rights reserved.

Magnetism and photoluminescence in manganese-gallium oxide nanowires with monoclinic and spinel structures

Manganese-gallium oxide nanowires were synthesized via in situ Mn doping during nanowire growth using a vapor phase evaporation method. The microstructure and composition of the products were characterized via transmission electron microscopy (TEM), field emission scanning electron microscopy (SEM), X-ray diffraction (XRD) and Raman spectroscopy. The field and temperature dependence of the magnetization reveal the obvious hysteresis loop and large magnitude of Curie-Weiss temperature. The photoluminescence of the manganese-gallium oxide nanowires were studied in a temperature range between 10 and 300 K. A broad green emission band was observed which is attributed to the T-4(1)-(6)A(1) transition in Mn2+ (3d(5)) ions. (c) 2005 Elsevier B.V. All rights reserved.

Structural properties and Raman measurement of AlN films grown on Si (111) by NH3-GSMBE

Epitaxial growth of AlN has been performed by molecular beam epitaxy (MBE) with ammonia. The structural properties of materials were studied by cross-sectional transmission electron microscopy (TEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). XRD and TEM diffraction pattern confirm the AlN is single crystalline 2H-polytype with the epitaxial relationship of (0001)AlNparallel to(111)Si, [11 (2) over bar0](AlN)parallel to[110](Si), [10 (1) over bar0](AlN)parallel to[11 (2) over bar](Si). Micro-Raman scattering measurement shows that the E-2 (high) and A(1) (LO) phonon mode shift 9 cm(-1) toward the low frequency, which shows the existence of large tensile strain in the AlN films. Furthermore, the appearance of forbidden A, (TO) mode and its anomalous shift toward high frequency was found and explained. (C) 2002 Elsevier Science B.V. All rights reserved.

Photoluminescence and Raman scattering of silicon nanocrystals prepared by silicon ion implantion into SiO2 films

Photoluminescence (PL) and Raman spectra of silicon nanocrystals prepared by Si ion implantion into SiO2 layers on Si substrate have been measured at room temperature. Their dependence on annealing temperature was investigated in detail. The PL peaks observed in the as-implanted sample originate from the defects in SiO2 layers caused by ion implantation. They actually disappear after thermal annealing at 800 degrees C. The PL peak from silicon nanocrystals was observed when thermal annealing temperatures are higher than 900 degrees C. The PL peak is redshifted to 1.7 eV and the intensity reaches maximum at the thermal annealing temperature of 1100 degrees C. The characterized Raman scattering peak of silicon nanocrystals was observed by using a right angle scattering configuration. The Raman signal related to the silicon nanocrystals appears only in the samples annealed at temperature above 900 degrees C. It further proves the formation of silicon nanocrystals in these samples. (C) 2000 American Institute of Physics. [S0021-8979(00)00215-2].

Photovoltage and photoreflectance spectroscopy of InAs/GaAs self-organized quantum dots

We present a detailed study of the interband excitonic transitions of InAs/GaAs self-organized quantum dots (QDs) based on photovoltage (PV) photoreflectance (PR) and photoluminescence (PL) spectroscopy. At room temperature, the interband absorption transitions of QDs have been observed by using PV spectrum, which clearly exhibits four well-resolved excitonic absorption peaks. The absorption line shape is Gaussian-like. Furthermore, the corresponding excitonic transitions are also observed in PR experiment at 77 K. The first derivative of a Gaussian profile can fit the experimental data well. (C) 1998 American Institute of Physics. [S0003-6951(98)00743-8]

Characterization of self-organized InAs/GaAs quantum dots under strain-induced and temperature-controlled nucleation mechanisms by atomic force microscopy and photoluminescence spectroscopy

Atomic force microscopy and photoluminescence spectroscopy (PL) has been used to study asymmetric bilayer InAs quantum dot (QD) structures grow by molecular-beam epitaxy on GaAs (001) substrates. The two InAs layers were separated by a 7-nm-thick GaAs spacer layer and were grown at different substrate temperature. We took advantage of the intrinsic nonuniformity of the molecular beams to grow the seed layer with an average InAs coverage of 2.0 ML. Then the seed layer thickness could be divided into three areas: below, around and above the critical thickness of the 2D-3D transition along the 11101 direction of the substrate. Correspondingly, the nucleation mechanisms of the upper InAs layer (UIL) could be also divided into three areas: temperature-controlled, competition between temperature-controlled and strain-induced, and strain-induced (template-controlled) nucleation. Small quantum dots (QDs) with a large density around 5 x 10(10) cm(-2) are found in the temperature-controlled nucleation area. The QD size distributions undergo a bimodal to a unimodal transition with decreasing QD densities in the strain-induced nucleation area, where the QD densities vary following that of the seed layer (templating effect). The optimum QD density with the UIL thickness fixed at 2.4 ML is shown to be around 1.5 x 10(10) cm(-2), for which the QD size distribution is unimodal and PL emission peaks at the longest wavelength. The QDs in the in-between area exhibit a broad size distribution with small QDs and strain-induced large QDs coexisting.

Absorption and Raman spectra of Se-8-ring clusters in zeolite 5A

Samples with different weight ratio of Se to zeolite 5A (Se composition) have been prepared by loading Se into the cages of zeolite 5A and the measurements of the absorption and Raman spectra have been carried out for the prepared samples. The measured absorption edges of the samples close and blue shifted to the value for monoclinic Se containing Se-8-ring, suggesting the formation of Se-8-ring clusters dagger in the cages. The continuous and broadening features of the absorption spectra are interpreted by the strong electron-phonon coupling in Se-8-ring clusters. The sample with high Se composition has a red shift of the absorption band edge relative to the samples with less Se composition. It is tentatively attributed to the reason that with different Se composition, single Se-8-ring clusters and double Se-8-ring clusters are formed in the cages of zeolite 5A. A single broad band at about 262 cm(-1) is observed in the Raman spectra, that gives the further support of the formation of Se-8-ring clusters. Copyright (C) 1996 Elsevier Science Ltd