Enhanced infrared emission from colloidal HgTe nanocrystal quantum dots on silicon-on-insulator photonic crystals

A two dimensional silicon-on-insulator based photonic crystal structure is used to enhance the emission from colloidal HgTe nanocrystal quantum dots embedded in a thin polymer film. The enhancement is resonant to the leaky eigenmodes of the photonic crystals due to coherent scattering effects. Transmittance and photoluminescence experiments are presented to map the leaky mode dispersion and the angle dependence of the emission enhancement factor, which reaches values up to 80 (650) for vertical (oblique) emission in the telecommunication wavelength range.

Origin of the blueshift in the infrared absorbance of intersubband transitions in AlxGa1-x/GaN multiple quantum wells

A self-consistent calculation of the subband energy levels of n-doped quantum wells is studied. A comparison is made between theoretical results and experimental data. In order to account for the deviations between them, the ground-state electron-electron exchange interactions, the ground-state direct Coulomb interactions, the depolarization effect, and the exciton-like effect are considered in the simulations. The agreement between theory and experiment is greatly improved when all these aspects are taken into account. The ground-to-excited-state energy difference increases by 8 meV from its self-consistent value if one considers the depolarization effect and the exciton-like effect only. It appears that the electron-electron exchange interactions account for most of the observed residual blueshift for the infrared intersubband absorbance in AlxGa1-xN/GaN multiple quantum wells. It seems that electrons on the surface of the k-space Fermi gas make the main contribution to the electron-electron exchange interactions, while for electrons further inside the Fermi gas it is difficult to exchange their positions. (C) 2004 Elsevier B.V. All rights reserved.

Quantum measurement characteristics of a double-dot single electron transistor

Owing to a few unique advantages, the double-dot single electron transistor has been proposed as an alternative detector for charge states. In this work, we present a further study for its signal-to-noise property, based on a full analysis of the setup configuration symmetry. It is found that the effectiveness of the double-dot detector can approach that of an ideal detector, if the symmetric capacitive coupling is taken into account. The quantum measurement efficiency is also analyzed by comparing the measurement time with the measurement-induced dephasing time.

Effects of seed dot layer and thin GaAs spacer layer on the structure and optical properties of upper In(Ga)As quantum dots

The structure and optical properties of In(Ga)As with the introduction of InGaAlAs or InAlAs seed dot layers are investigated. The area density and size homogeneity of the upper InGaAs dots are efficiently improved by the introduction of a buried layer of high-density dots. Our explanation for the realization of high density and size homogeneity dots is presented. When the GaAs spacer layer is too thin to cover the seed dots, the upper dots exhibit some optical properties like those of a quantum well. By analyzing the growth dynamics, we refer to this kind of dot as an empty-core dot. (C) 2003 American Institute of Physics.

InxGa1-xAs/AlyGa1-yAs/AlzGa1-zAs asymmetric step quantum-well middle wavelength infrared detectors

InxGa1-xAs/AlyGa1-yAs/AlzGa1-zAs asymmetric step quantum-well middle wavelength (3-5 mum) infrared detectors are fabricated. The components display photovoltaic-type photocurrent response as well as the bias-controlled modulation of the peak wavelength of the main response, which is ascribed to the Stark shifts of the intersubband transitions from the local ground states to the extended first excited states in the quantum wells, at the 3-5.3 mum infrared atmospheric transmission window. The blackbody detectivity (D-bb*) of the detectors reaches to about 1.0x10(10) cm Hz(1/2)/W at 77 K under bias of +/-7 V. By expanding the electron wave function in terms of normalized plane wave basis within the framework of the effective-mass envelope-function theory, the linear Stark effects of the intersubband transitions between the ground and first excited states in the asymmetric step well are calculated. The obtained results agree well with the corresponding experimental measurements. (C) 2001 American Institute of Physics.

Linewidth of the infrared absorption spectra due to bound-to-continuum transition in GaAs/AlxGa1-xAs multiple quantum well structures

We have observed an extremely narrow absorption spectrum due to bound-to-continuum transition in GaAs/AlxGa1-xAs multiple quantum wells (MQWs). Its linewidth is only about one tenth of the values reported previously. Our calculation indicates that the broadening of the excited state in the continuum has little contribution to the absorption linewidth. We have grown a sample whose MQW region contains two kinds of wells with a minor thickness inhomogeneity. Its resultant absorption linewidth is six times as large as that of homogeneous well sample, which is in good agreement with our theoretical analysis. Thus we can suggest that the wider absorption spectra reported by many authors may be due to the well width inhomogeneity. (C) 1998 American Institute of Physics. [S0003-6951(98)03430-5]

INFRARED-ABSORPTION DUE TO 2-DIMENSIONAL-ELECTRON-GAS COLLECTIVE EXCITATION IN GAAS/ALXGA1-XAS MULTIPLE-QUANTUM-WELL STRUCTURES

Infrared absorption due to a collective excitation of a two-dimensional electronic gas was observed in GaAs/AlxGa1-xAs multiple-quantum wells when the incident light is polarized parallel to the quantum-well plane. We attribute this phenomenon to a plasma oscillation in the quantum wells. The measured wavelength of the absorption peak due to the plasma oscillation agrees with our theoretical analysis. In addition, in this study the plasma-phonon coupling effect is also fitted to the experimental result. We show that the absorption is not related to the intersubband transitions but to the intrasubband transition, which originates from a plasma oscillation.

3μm GaInNAs/GasAs Quantum Well Resonant Cavity Enhanced Photodetector

A 1.3μm GaInNAs resonant cavity enhanced (RCE) photodetector (PD) has been grown by molecular beam epitaxy (MBE) monolithically on (100) GaAs substrate using a home-made ion-removed dc-plasma cell as nitrogen source. A transfer matrix method was used to optimize the device structure. The absorption region is composed of three GaInNAs quantum wells separated by GaAs layers. Devices were isolated by etching 130μm-diameter mesas and filling polyamide into grooves. The maximal quantum efficiency of the device is about 12% at 1.293μm. Full width at half maximum (FWHM) is 5.8nm and 3dB bandwidth is 304MHz. Dark current is 2 * 10~(-11) A at zero bias voltage. Further improvement of the performance of the RCE PD can be obtained by optimizing of the structure design and MBE growth conditions.

SiGe/Si quantum well resonant-cavity-enhanced photodetector

Resonant-cavity-enhanced photodetectors have been demonstrated to be able to improve the bandwidth-efficiency product. We report a novel SiGe/Si multiple quantum-well resonant-cavity-enhanced photodetector fabricated on a separation-by-implanted-oxygen wafer operating near 1300nm. The buried oxide layer in SIMOX is used as a bottom mirror to form a vertical cavity with silicon dioxide/silicon Bragg reflector deposited on the top surface. The quantum efficiency at the wavelength of 1300nm is measured with 3.5% at a reverse bias of 15V, which is enhanced by 10 folds compared with a conventional photodetector with the same absorption structures.

Near infrared light-emitting diodes based on composites of near infrared dye, CdSe/CdS quantum dots and polymer

Near infrared (NIR) light emitting diodes employing composites of an IR fluorescent dye, CdSe/CdScore/shell semiconductor quantum dots and poly( N-vinylcarbazole) (PVK) have been demonstrated. The device, with a configuration of indium-tin-oxide (ITO)//PEDOT:PSS//PVK:NIR Dye:CdSe/CdS//Al, had a turn-on voltage of 7 V, emitted the NIR light with a maximum at 890 nm and the irradiance intensity of 96 mu W. The electroluminescence efficiency of 0.02% was achieved at a current density of 13 mA cm(-2).

CRYSTAL-STRUCTURE AND INFRARED-SPECTRA OF A LANTHANUM COORDINATION COMPOUND WITH GLYCINE, ([LA(GLY)S-CENTER-DOT-2H2O]CENTER-DOT(CLO4)3)N

A lanthanum coordination compound with glycine {[La(Gly)3.2H2O].(ClO4)3}n (Gly = NH+ 3-CH2-COO-) was synthesized and obtained in the form of single crystals. Its X-ray crystal structure has been determined and the IR spectrum has been studied. Crystallo

Preparation And Optical Properties Of Cdte/Cdo Center Dot Nh(2)O Core/Shell Nano-Composites In Aqueous Solution

The deposition of CdO center dot nH(2)O On CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH similar to 8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited.

Preparation and optical properties of CdTe/CdO center dot nH(2)O core/shell nano-composites in aqueous solution

The deposition of CdO center dot nH(2)O On CdTe nanoparticles was studied in an aqueous phase. The CdTe nanocrystals (NCs) were prepared in aqueous solution through the reaction between Cd2+ and NaHTe in the presence of thioglycolic acid as a stabilizer. The molar ratio of the Cd2+ to Te2- in the precursory solution played an important role in the photoluminescence of the ultimate CdTe NCs. The strongest photoluminescence was obtained under 4.0 of [Cd2+]/[Te2-] at pH similar to 8.2. With the optimum dosage of Cd(II) hydrous oxide deposited on the CdTe NCs, the photoluminescence was enhanced greatly. The photoluminescence of these nanocomposites was kept constant in the pH range of 8.0-10.0, but dramatically decreased with an obvious blue-shifted peak while the pH was below 8.0. In addition, the photochemical oxidation of CdTe NCs with cadmium hydrous oxide deposition was markedly inhibited.