Electron irradiation-induced defects in InP pre-annealed at high temperature

Electron irradiation-induced deep level defects have been studied in InP which has undergone high-temperature annealing in phosphorus and iron phosphide ambients, respectively. In contrast to a high concentration of irradiation-induced defects in as-grown and phosphorus ambient annealed InP, InP pre-annealed in iron phosphide ambient has a very low concentration of defects. The phenomenon has been explained in terms of a faster recombination of radiation-induced defects in the annealed InP. The radiation-induced defects in the annealed InP have been compared and studied. (c) 2006 Elsevier Ltd. All rights reserved.

Silicon nanowires grown on a pre-annealed Si substrate

Polycrystalline Si nanowires (poly SiNWS) were successfully synthesized by plasma-enhanced chemical vapor deposition (PECVD) at 440degreesC using silane as the Si source and Au as the catalyst. The diameters of Si nanowires range from 15 to 100nm. The growth process indicates that to fabricate SiNWS by PECVD, pre-annealing at high temperature is necessary. A few interesting nanowires with Au nanoclusters uniformly distributed in the body of the wire were also produced by this technique. (C) 2002 Elsevier Science B.V. All rights reserved.

The effects of pre-irradiation on the formation of Si1-xCx alloys

Carbon ions were implanted into crystal Si to a concentration of (0.6-1.5)at% at room temperature. Some samples were pre-irradiated with S-29(i)+ ions, while others were not pre-irradiated. Then the two kinds of samples were implanted with C-12(+) ions simultaneously, and Si1-xCx alloys were grown by solid phase epitaxy with high-temperature annealing. The effects of preirradiation on the formation of Si1-xCx alloys were studied. If the dose of implanted C ion was less than that for amorphizing Si crystals, the implanted C atoms would like to combine with defects produced during implantation, and then it was difficult for Si1-xCx alloys to form after annealine, at 950 degreesC. Pre-irradiation was advantageous for Si1-xCx alloy formation. With the increase of C ion dose, the damage produced by C ions increased. Pre-irradiation was unfavorable for Si1-xCx, alloy formation. If the implanted C concentration was higher than that for solid phase epitaxy solution, only part of the implanted C atoms form Si1-xCx alloys and the effects of pre-irradiation could be neglected. As the annealing temperature was increased to 1050 degreesC, Si1-xCx alloys in both pre-irradiated and unpreirradiated samples of low C concentration remained, whereas most part of Si1-xCx alloys in samples with high C concentration vanished.

Direct Wafer Bonding Technology employing vacuum-cavity pre-bonding

A novel low temperature direct wafer bonding technology employing vacuum-cavity pre-bonding is proposed and applied in bonding of InGaAs/Si couple wafers under 300 degrees C and InP/GaAs couple wafers under 350 degrees C. Aligning accuracy of 0.5 mu m is achieved. During wafer bonding process the pressure on the couple wafers is 10MPa. The interface energy is sufficiently high to allow thinning of the wafers down from 350um to about 100um. And the tensile strength test indicates the bonding energy of bonded samples is about equal to the bonded samples at 550 degrees C.

Electron irradiation-induced defects in InP pre-annealed at high temperature

Electron irradiation-induced deep level defects have been studied in InP which has undergone high-temperature annealing in phosphorus and iron phosphide ambients, respectively. In contrast to a high concentration of irradiation-induced defects in as-grown and phosphorus ambient annealed InP, InP pre-annealed in iron phosphide ambient has a very low concentration of defects. The phenomenon has been explained in terms of a faster recombination of radiation-induced defects in the annealed InP. The radiation-induced defects in the annealed InP have been compared and studied. (c) 2006 Elsevier Ltd. All rights reserved.

In-plane stray field induced spin-filtering in a two-dimensional electron gas under the modulation of surface ferromagnetic dual-gate

Based upon a hybrid ferromagnet/semiconductor structure consisting of two-dimensional electron gas and a pair of surface ferromagnetic stripes on top, we have theoretically investigated the effect of in-plane stray field omitted frequently in previous studies on the spin-dependent ballistic transport properties in hybrid structure. It is demonstrated here that, in combination with an external-controllable electrostatic modulation, the concerned structure shows a similar function as a lateral spin-polarized resonant tunneling device, where the strong spin-filtering effect occurs and nearly single-mode polarization is anticipated for the proper modulation. More importantly, the spin polarity of transmission electron can be easily transferred from one extreme to the other by switching the magnetization of stripes, showing the promising application as an efficient spin aligner in the developing semiconductor spintronics.

Measurement of the isospin-filtering dd → 4He K+K- reaction at Q = 39 MeV

The total cross-section for the dd → 4HeK+K− reaction has been measured at a beam momentum of 3.7GeV/c, corresponding to an excess energy of 39MeV, which is the maximum possible atthe Cooler Synchrotron COSY-Jülich. A deuterium cluster-jet target and the ANKE forward magnetic spectrometer, placed inside the storage ring, have been employed in this investigation. We find a total cross-section of σtot < 14 pb, which brings into question the viability of investigating the dd → 4He a0(980)reaction as a means of studying isospin violation.