热舟蒸发LaF_3薄膜的紫外性能研究

研究了沉积温度对热舟蒸发氟化镧薄膜结构和光学性能的影响,沉积温度从200℃上升到350℃,间隔为50℃.采用分光光度计测量了样品的透射率和反射率光谱曲线,并在此基础上进行了光学损耗、光学常数以及带隙和截止波长的计算.采用表面轮廓仪进行了表面形貌和表面粗糙度的标定,采用X射线衍射(XRD)方法测量了不同沉积温度下样品的微结构.发现在短波长波段,随着沉积温度的升高,光学损耗增加,晶粒尺寸增大,表面粗糙度略有增加.不过散射损耗在光学损耗中所占比例均很小,光学损耗的增加主要由吸收损耗引起.随着沉积温度的升高,折射率与消光系数增大,带隙变小,相对应的截止波长向长波方向移动.

TN : TP ratio and planktivorous fish do not affect nutrient-chlorophyll relationships in shallow lakes

1. In previous work, phytoplankton regulation in freshwater lakes has been associated with many factors. Among these, the ratio of total nitrogen to total phosphorus (TN : TP) has been widely proposed as an index to identify whether phytoplankton are N- or P-limited. From another point of view, it has been suggested that planktivorous fish can be used to control phytoplankton. 2. Large-scale investigations of phytoplankton biomass [measured as chlorophyll a, (chl-a)] were carried out in 45 mid-lower Yangtze shallow lakes to test hypotheses concerning nutrient limitation (assessed with TN : TP ratios) and phytoplankton control by planktivorous fish. 3. Regression analyses indicated that TP was the primary regulating factor and TN the second regulating factor for both annual and summer phytoplankton chl-a. In separate nutrient-chl-a regression analyses for lakes of different TN : TP ratios, TP was also superior to TN in predicting chl-a at all particular TN : TP ranges and over the entire TN : TP spectrum. Further analyses found that chl-a : TP was not influenced by TN : TP, while chl-a : TN was positively and highly correlated to TP : TN. 4. Based on these results, and others in the literature, we argue that the TN : TP ratio is inappropriate as an index to identify limiting nutrients. It is almost impossible to specify a 'cut-off' TN : TP ratio to identify a limiting nutrient for a multi-species community because optimal N : P ratios vary greatly among phytoplankton species. 5. Lakes with yields of planktivorous fish (silver and bighead carp, the species native to China) > 100 kg ha(-1) had significantly higher chl-a and lower Secchi depth than those with yields < 100 kg ha(-1). TP-chl-a and TP-Secchi depth relationships are not significantly different between lakes with yields > 100 kg ha(-1) or < 100 kg ha(-1). These results indicate that the fish failed to decrease chl-a yield or enhance Z(SD). Therefore, silver carp and bighead carp are not recommended as a biotic agent for phytoplankton control in lake management if the goal is to control the entire phytoplankton and to enhance water quality.

Effects of solar UV radiation on germination of conchospores and morphogenesis of sporelings in Porphyra haitanensis (Rhodophyta)

The effects of ultraviolet radiation (UVR 280-400 nm) on the germination of Porphyra haitanensis conchospores and on the growth and morphogenesis of the subsequent sporelings were investigated by culturing the released conchospores under natural sunlight from 29 September to 6 October 2005. Germination increased with time and was faster when UV-B was excluded using cut-off filters. There were significant negative effects of UV-B radiation on growth and cell division of sporelings, with decreases up to 18% for thallus length, between 6 and 18% for thallus width, up to 29% for thallus area, and between 6 and 14% for cell size as compared to PAR-controls. UV-A had a significant positive effect on morphogenesis, enhancing the formation of sporelings with cells dividing transversely; on the other hand, UV-B delayed the formation of such sporelings. We also tested the effects of solar UVR on the growth of P. haitanensis juveniles and found no significant effects. Our results indicate that UV-A has an important role in the germination and morphogenesis of the species, but on the other hand, sporelings of P. haitanensis are more sensitive to UV-B radiation than juveniles.

The restoration of aquatic macrophytes for improving water quality in a hypertrophic shallow lake in Hubei Province, China

This paper deals with a case study of the restoration of submerged macrophytes for improving water quality in a hypertrophic shallow lake, Lake Donghu of Wuhan, Hubei Province, China. Macrophyte restoration experiments were conducted in large-scale enclosures established in three sublakes of different trophic status, and the effectiveness for water quality improvement was tested by using the enclosure experiment in the hypertrophic sublake. Water quality was remarkably improved after the reestablishment of aquatic macrophytes. It is suggested that the submerged vegetation of less polluted sublakes could be capable of recovering spontaneously once the stocking of herbivorous fishes has been ceased, and the K-selected plants such as Potamogeton maackianus should be introduced into these sublakes to enhance the stability of aquatic vegetation. However, it may not be possible and economical to restore the submerged macrophytes in severely polluted basins unless external pollution has been cut off and internal nutrient loadings considerably reduced. In this case, the r-selected submerged plants should be used as the pioneer species for macrophyte recovery. (C) 2001 Elsevier Science B.V. All rights reserved.

High-performance 2 mm gate width GaNHEMTs on 6H-SiC with output power of 22.4 W @ 8 GHz

Optimized AlGaN/AlN/GaN high electron mobility transistors (HEMTs) structures were grown on 2-in semi-insulating (SI) 6H-SiC substrate by metal-organic chemical vapor deposition (MOCVD). The 2-in. HEMT wafer exhibited a low average sheet resistance of 305.3 Omega/sq with a uniformity of 3.85%. The fabricated large periphery device with a dimension of 0.35 pm x 2 nun demonstrated high performance, with a maximum DC current density of 1360 mA/mm, a transconductance of 460 mS/mm, a breakdown voltage larger than 80 V, a current gain cut-off frequency of 24 GHz and a maximum oscillation frequency of 34 GHz. Under the condition of continuous-wave (CW) at 9 GHz, the device achieved 18.1 W output power with a power density of 9.05 W/mm and power-added-efficiency (PAE) of 36.4%. While the corresponding results of pulse condition at 8 GHz are 22.4 W output power with 11.2 W/mm power density and 45.3% PAE. These are the state-of-the-art power performance ever reported for this physical dimension of GaN HEMTs based on SiC substrate at 8 GHz. (c) 2008 Elsevier Ltd. All rights reserved.

InAs/GaSb superlattices for photodetection in short wavelength infrared range

The first report of a short wavelength infrared detector based on type II InAs/GaSb superlattices is presented. Very short period superlattices containing InAs (2ML)/GaSb (8ML) superlattices (SLs) were grown by molecular-beam epitaxy on GaSb substrates. The photoluminescence showed a cut-off wavelength at 2.1 mu m at 10 K and 2.6 mu m at 300 K. Room-temperature optical transmittance spectra shows obvious absorption in InAs (2ML)/GaSb (8ML) SL in the range of 450-680 meV, i.e. 1.8-2.7 mu m. The cut-off wavelength moved from 2.3 mu m to 2.6 mu m with temperature rising from 77 K to 300 K in photoresponse spectra. The blackbody response R-v exponentially decreased as a function of 1/T in two temperature sections (130-200 K and 230-300 K). The blackbody detectivity D-bb(center dot) was beyond 1 x 10(8) cmHz(1/2)/W at room temperature. (C) 2009 Elsevier B.V. All rights reserved.

Comparison of short period InAs/GaSb superlattices on GaSb and GaAs substrates

Type II superlattices (SLs) short period InAs(4ML)/GaSb(8ML) were grown by molecular-beam epitaxy on lattice-mismatched GaAs substrates and on GaSb substrates. A smooth GaSb epilayer was formed on GaAs substrates by inserting mulit-buffer layers including an interfacial misfit mode AlSb quantum dot layer and AlSb/GaSb superlattices smooth layer. SLs grown on GaAs substrates (GaAs-based SLs) showed well-resolved satellite peaks in XRD. GaSb-based SLs with better structural quality and smoother surface showed strong photoluminescence at 2.55 mu m with a full width at half maximum (FWHM) of 20 meV, narrower than 31 meV of GaAs-based SLs. Inferior optical absorption of GaAs-based SL was observed in the range of 2-3 mu m. Photoresponse of GaSb-based SLs showed the cut-off wavelength at 2.6 mu m.

Characteristics of high Al content AlxGa1-xN grown by metalorganic chemical vapor deposition

The epitaxial growth of AlxGa1-xN film with high Al content by metalorganic chemical vapor deposition (MOCVD) has been accomplished. The resulting Al content was determined to be 54% by high resolution X-ray diffraction (HRXRD) and Vegard's law. The full width at half maximum (FWHM) of the AlGaN (0002) HRXRD rocking curve was about 597 arcsec. Atomic force microscopy (AFM) image showed a relatively rough surface with grain-like islands, mainly coming from the low surface mobility of adsorbed Alspecies. From transmittance measurement, the cut-off wavelength was around 280 nm and Fabry-Perot fringes were clearly visible in the transmission region. Cathodoluminescence (CL) measurement indicated that there existed a uniformity in the growth direction and a non-uniformity in the lateral direction. (C) 2007 Elsevier Ltd. All rights reserved.

InAs0.3Sb0.7 films grown on (100) GaSb substrates with a buffer layer by liquid-phase epitaxy

The growth of InAsxSb1-x films on (100) GaSb substrates by liquid-phase epitaxy (LPE) has been investigated and epitaxial InAs0.3Sb0.7 films with InAs0.9Sb0.09 buffer layers have been successfully obtained. The low X-ray rocking curve FHWM values of InAs0.3Sb0.7 layer shows the high quality of crystal-orientation structure. Hall measurements show that the highest electron mobility in the samples obtained is 2.9 x 10(4) cm(2) V-1 s(-1) and the carrier density is 2.78 x 10(16)cm(-3) at room temperature (RT). The In As0.3Sb0.7 films grown on (10 0) GaSb substrates exhibit excellent optical performance with a cut-off wavelength of 12 mu m. (c) 2007 Elsevier B.V. All rights reserved.

A base-emitter self-aligned multi-finger Si1-xGex/Si power heterojunction bipolar transistor

With a crystal orientation dependent on the etch rate of Si in KOH-based solution, a base-emitter self-aligned large-area multi-linger configuration power SiGe heterojunction bipolar transistor (HBT) device (with an emitter area of about 880 mu m(2)) is fabricated with 2 mu m double-mesa technology. The maximum dc current gain is 226.1. The collector-emitter junction breakdown voltage BVCEO is 10 V and the collector-base junction breakdown voltage BVCBO is 16 V with collector doping concentration of 1 x 10(17) cm(-3) and thickness of 400 nm. The device exhibited a maximum oscillation frequency f(max) of 35.5 GHz and a cut-off frequency f(T) of 24.9 GHz at a dc bias point of I-C = 70 mA and the voltage between collector and emitter is V-CE = 3 V. Load pull measurements in class-A operation of the SiGe HBT are performed at 1.9 GHz with input power ranging from 0 dBm to 21 dBm. A maximum output power of 29.9 dBm (about 977 mW) is obtained at an input power of 18.5 dBm with a gain of 11.47 dB. Compared to a non-self-aligned SiGe HBT with the same heterostructure and process, f(max) and f(T) are improved by about 83.9% and 38.3%, respectively.

AlGaN/AlN/GaN/SiC HEMT structure with high mobility GaN thin layer as channel grown by MOCVD

Enhancement of the electrical properties in an AlGaN/GaN high electron mobility transistor (HEMT) structures was demonstrated by employing the combination of a high mobility GaN channel layer and an AlN interlayer. The structures were grown on 50 mm semi-insulating (SI) 6H-SiC substrates by metalorganic chemical vapor deposition (MOCVD). The room temperature (RT) two-dimensional electron gas (2DEG) mobility was as high as 2215 cm(2)/V s, with a 2DEG concentration of 1.044 x 10(13)cm(-2). The 50 mm HEMT wafer exhibited a low average sheet resistance of 251.0 Omega/square, with a resistance uniformity of 2.02%. The 0.35 Pin gate length HEMT devices based on this material structure, exhibited a maximum drain current density of 1300 mA/mm, a maximum extrinsic transconductance of 314 mS/mm, a current gain cut-off frequency of 28 GHz and a maximum oscillation frequency of 60 GHz. The maximum output power density of 4.10 W/mm was achieved at 8 GHz, with a power gain of 6.13 dB and a power added efficiency (PAE) of 33.6%. (c) 2006 Elsevier B.V. All rights reserved.

Simple method for estimating minimum bend radii of SOI single mode curved rib waveguides

A simple method based on the effective index method was used to estimate the minimum bend radii of curved SOI waveguides. An analytical formula was obtained to estimate the minimum radius of curvature at which the mode becomes cut off due to the side radiative loss.

Using photoluminescence as optimization criterion to achieve high-quality InGaAs/AlGaAs pHEMT structure

The single delta -doped InGaAs/AlGaAs pseudomorphic HEMT structure materials were grown by molecular beam epitaxy. The photoluminescence spectra of the materials were studied. There are two peaks in the photoluminescence spectra of the materials, corresponding to two sub energy levels of InGaAs quantum well. The ratio of the two peak's intensity was used as criterion to optimize the layer structures of the materials. The material with optimized layer ;tructures exhibits the 77 It mobility and two-dimensional electron gas density of 16 500 cm(2)/Vs and 2.58 x 10(12) cm(-2) respectively, and the 300 K mobility and two-dimensional electron gas density of 6800 cm(2)/Vs and 2.55 x 10(12) cm(-2) respectively. The pseudomorphic HEMT devices with gate length of 0.2 mum were fabricated using this material. The maximum transconductance of 650 mS/mm and the cut-off frequency of 81 GHz were achieved. (C) 2001 Elsevier Science B.V. All rights reserved.

The keys to get high transconductance of AlGaAs/InGaAs/GaAs pseudomorphic HEMTs devices

There are two key points to get high transconductance of pseudomorphic HEMTS (pHEMTs) devices. From the point view of materials, the transfer efficiency of the electrons from the delta -doped AlGaAs layer to the InGaAs channel must be high. From the point view of device processing, the gate recess depth must be carefully controlled. In the present work, AlGaAs/InGaAs/GaAs pHEMTs structures were grown by molecular beam epitaxy. Layer structures of the pHEMTs were optimized to get high transfer efficiency of the electrons. Gate recess depth was also optimized. A 0.2 mum pHEMT was fabricated on the materials with optimized layer structure using the optimized gate recess depth. The maximum transconductance of 650 mS/mm and the cut-off frequency of 81 GHz were achieved. (C) 2001 published by Elsevier Science Ltd.

Growth of SiGe heterojunction bipolar transistor using Si2H6 gas and Ge solid sources molecular beam epitaxy

N-p-n Si/SiGe/Si heterostructure has been grown by a disilane (Si2H6) gas and Ge solid sources molecular beam epitaxy system using phosphine (PH3) and diborane (B2H6) as n- and p-type in situ doping sources, respectively. X-ray diffraction (XRD) and secondary ion mass spectroscopy (SIMS) measurements show that the grown heterostructure has a good quality, the boron doping is confined to the SiGe base layer, and the Ge has a trapezoidal profile. Postgrowth P implantation was performed to prepare a good ohmic contact to the emitter. Heterojunction bipolar transistor (HBT) has been fabricated using the grown heterostructure and a common-emitter current gain of 75 and a cut-off frequency of 20 GHz at 300 K have been obtained. (C) 2001 Elsevier Science B.V. All rights reserved.