Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

一种用于Yb：YAG激光器的波长分离膜的研制

以1030nm高反．940。980nm高透的波长分离膜作为实例，为提高该薄膜元件的波长分离效果，从膜系的优化方面做了一系列的研究。诸如采用带通滤光片的设计思想，在膜堆两侧加入了匹配层，调整膜堆的周期厚度，并用膜系设计软件对通带作进一步的优化。通过这一系列的优化设计后．利用RF双离子柬溅射工艺在BK7玻璃基底上沉积样品薄膜，并在基底背面加镀通带增透膜。结果显示，透射带在940和980nm处的透过率分别为97．73％和93．63％．反射带在1030nm的反射率为99．99％。对所制备的样品薄膜进行了激光损伤阈

Antiphase state in passively Q-switched Yb : YAG microchip multimode lasers with a saturable absorber GaAs

We report on recent experimental results of the spontaneous antiphase dynamics that occurs in a laser-diode-pumped multimode passively Q-switched microchip Yb:YAG (where YAG is yttrium aluminum garnet) lasers with a saturable absorber GaAs. We observe that the pulse sequence of the first mode characterized by one, two, and three pulses as a group and all the modes display an antiphase state as the pumping ratio rises. We modify the multimode rate equations to account for nonlinear absorption due to GaAs in the presence of spatial hole burning. We perform numerical simulations based on the proposed rate equations and reproduce the observed antiphase state of two and three active modes.

Observation of antiphase states in a passively Q-switched multimode microchip Yb : YAG laser with a GaAs saturable absorber

Antiphase dynamics has been observed experimentally for the laser modes operation in a laser-diode-pumped Q-switched microchip Yb:YAG laser with GaAs as a saturable absorber in the presence of spatial hole-burning. The Q-switched pulses sequences of two modes at different pump power have been obtained. The experimental results have shown that the pulses sequences displayed classic antiphase dynamics. (C) 2003 Elsevier B.V. All rights reserved.

Diode-pumped passively Q-switched Yb : YAG microchip laser with a GaAs as saturable absorber

A passively Q-switched Yb: YAG microchip laser has been constructed by using a doped GaAs as the saturable absorber as well as the output coupler. At 13.5 W of pump power the device produces high-quality 3.4 muJ 52 ns pulses at 1030nm with a pulse repetition rate of 7.8kHz in a TEM00-mode.

用表面态型半导体可饱和吸收镜实现Yb∶YAG激光器被动调Q锁模

制作了一种新型的半导体可饱和吸收镜--表面态型半导体可饱和吸收镜.用表面态型半导体可饱和吸收镜作为被动锁模吸收体实现了半导体端面泵浦Yb∶YAG激光器被动调Q锁模.在泵浦功率仅有1.4 W的情况下,获得了调Q锁模脉冲序列,锁模平均输出功率1 mW,锁模脉冲重复频率200 MHz.

Passive Q-switching of diode-pumped Yb:YAG microchip laser with ion-implanted GaAs

We reported a passive Q-switched diode laser pumped Yb:YAG microchip laser with an ion-implanted semi-insulating GaAs wafer. The wafer was implanted with 400-keV As^(+) in the concentration of 10^(16) ions/cm^(2). To decrease the non-saturable loss, we annealed the ion-implanted GaAs at 500 oC for 5 minutes and coated both sides of the ion-implanted GaAs with antireflection (AR) and highreflection (HR) films, respectively. Using GaAs wafer as an absorber and an output coupler, we obtained 52-ns pulse duration of single pulse.

表面态型半导体可饱和吸收镜实现Yb:YAG激光器被动锁模

制作了一种新型的半导体可饱和吸收镜:表面态型半导体可饱和吸收镜.用表面态型半导体可饱和吸收镜作为被动锁模吸收体,实现了半导体端面泵浦Yb:YAG激光器被动连续锁模.在泵浦功率为10W时,获得了连续锁模脉冲序列,重复频率200MHz,锁模脉冲平均输出功率为70mW.在未加任何色散补偿的情况下,脉冲宽度为4.35ps.

Stable mode-locking in an Yb:YAG laser with a fast SESAM

Stable mode-locking in a diode-pumped Yb:YAG laser was obtained with a very fast semiconductor saturable absorber mirror (SESAM). The pulse width was measured to be 4 ps at the central wavelength of 1047 nm. The average power was 200 mW and the repetition rate was 200 MHz.

Yb：Y2O3透明陶瓷的光学性能研究

介绍了一种基于纳米粉末真空烧结技术的新型固体激光材料——Yb：Y2O3多晶陶瓷的制备工艺、物理化学特性、能级结构和光谱特性，并与Yb：YAG单晶进行了对比．采用紧凑型有源镜激光器（CAMIL）的抽运方式，验证了Yb：Y2O3透明陶瓷的激光输出性能．在35W的最大抽运功率下，得到波长1078nm，功率10．5w的连续激光输出，斜率效率达到37．5％．实验中还观察到激光输出波长随抽运功率增加而红移以及随输出耦合镜变化而漂移的现象．Yb：Y2O3多晶陶瓷是一种理想的激光材料，不仅具有与Yb：YAG单晶同样优秀的

Effects of Yb concentration on the spectroscopic properties of Yb : Y3Al5O12

Yb:YAG single crystals with Yb doping concentration 5.4, 16.3, 27.1, 53.6, and 100 at.% were grown by the Czochralski process. The effects of Yb concentration on the absorption spectra (190-1 100nm), fluorescence spectra under 940nm and X-ray excitation were studied. The concentration quenching of fluorescence was observed when the Yb doping concentration reaches to as high as 27.1 at.% for Yb:YAG. Under 940 nm excitation, the influence of the self-absorption at 969 and 1029 nrn on the fluorescence spectra is not evident when the Yb doping concentration is as high as 27.1 at.%. However, it can greatly change the shape of fluorescence spectra of Yb:YAG when the Yb doping concentration reaches to above 53.6 at.%. (c) 2005 Elsevier B.V. All rights reserved.

Efficient laser oscillation of Yb : Y3Al5O12 single crystal grown by temperature gradient technique

Low-threshold and highly efficient continuous-wave laser performance of Yb:Y3Al5O12 (Yb:YAG) single crystal grown by a temperature gradient technique (TGT) was achieved at room temperature. The laser can be operated at 1030 and 1049 nm by varying the transmission of the output coupler. Slope efficiencies of 57% and 68% at 1049 and 1030 nm, respectively, were achieved for 10 at. % Yb:YAG sample in continuous-wave laser-diode pumping. The effect of pump power on the laser emission spectrum of both wavelengths is addressed. The near-diffraction-limited beam quality for different laser cavities was achieved. The excellent laser performance indicates that TGT-grown Yb:YAG crystals have very good optical quality and can be potentially used in high-power solid-state lasers.

LD抽运Yb:GSO实现1090nm低阈值激光运转

We report what we believe to be the first demonstration of laser operation with a novel laser material of Yb3(+) -doped Gd-2 SiO2 (Yb: GSO) pumped by a laser diode at 940 nm. We obtained a low lasing threshold of 1.27 kW/cm(2) with the center wavelength of 1090 nm, which is lower than the value of 1.53 kW/cm(2) predicted for Yb: YAG. The maximal output power of 360 mW was obtained with a 2% output, which corresponds to a slope efficiency up to 19%.

Comparison of spectroscopic parameters of 15 at% Yb : YAlO3 and 15 at% Yb : Y3Al5O12

Yb: YAlO3 (YAP) (15 at %) and Yb: Y3Al5O12 (YAG)(15 at %) have been grown using the Czochralski method. Their absorption and fluorescence spectra were measured at room temperature and important spectroscopic parameters were calculated. Through the comparison of spectroscopic parameters of Yb:YAP and Yb: YAG, all results indicate that 15 at % Yb:YAP crystal is a potential candidate used for compact, efficient thin chip lasers when the laser output wavelength is 1012 or 103 8 nm. (C) 2004 Elsevier B.V. All rights reserved.