Effect of Heat Treatment Temperature on the Catalytic Performances of PtRu/C Catalysts for Methanol Electro-Oxidation

Non-ionic surfactant Triton X-100 was used as a stabilizer to prepare PtRu/C catalysts for methanol oxidation reaction (MOR). The cyclic voltammogram was used to investigate the catalytic activity for MOR of different PtRu/C catalysts. TG-DTA, EDX, XRD, XPS and TEM were Used to characterize the composition, structure and morphology of the as-prepared PtRu/C catalysts. It is found that the heat treatment plays a crucial role in the particles size, particles distribution of the PtRu/C catalysts and the oxidation state of platinum. The results show that 350 degrees C is an optimum heat treatment temperature. The as-synthesized catalyst heat-treated at this temperature exhibits the best catalytic performance for MOR.

Study on the phase behavior of BaEu2Mn2O7 through heat treatment of a single crystal

A new orthorhombic phase of BaEu2Mn2O7 with the space group of Ccmm (no.63) was identified for single crystals after heat treatment and its Crystal Structure was determined by single crystal X-ray diffractometry. The volume Of the unit cell has twice the fundamental tetragonal cell and corner-shared MnO6 octahedra are slightly distorted and Mn-O-Mn angle between the neighboring octahedra tilts with an angle by around 3 degrees from b-axis. It is concluded from the results of the heat treatment of single crystals at various temperatures that this orthorhombic phase changes into a tetragonal One With superstructure (P4(2)/mnm) at 402 K and changes once more into the fundamental tetragonal phase (I4/mmm) above 552 K. The tetragonal phase with superstructure which has been expected to be an unstable one is stable between the two temperatures.

Variation of crystallographic parameters in PEEKK with heat treatment temperature

Using the wide-angle X-ray diffraction method, the variation of crystallographic parameters of poly(aryl ether ether ketone ketone) (PEEKK) has been studied in different heat treatment temperatures. All the reflections and their intensities as well as their Miller indices are presented in detail according to an orthorhombic system. The investigation indicates that the unit cell parameters a, b, c and the unit cell volume V systematically decrease with increasing heat treatment temperature. This variation is interpreted by the change of conformation of polymer molecular chains during thermal treatment. The results calculated from the formula of degree of crystallinity (W-c,W-x) for PEEKK, which was derived based on X-ray scattering intensity theory and the graphic multipeak resolution method, are compatible with the density measurement (W-c,W-d) and calorimetry (W-c,W-h) values. (C) 1997 Elesevier Science Ltd.

The influence of heat treatment on structures of the aggregated state of polyamide-1010

The structural parameters of the aggregated state of polyamide (PA)-1010 annealed at various temperatures were computed by means of the desmearing intensity from Smalt Angle X-ray Scattering (SAXS) measurements and by using the concept of the distance distribution function. The results indicated that the structural parameters of the aggregated state were strongly dependent upon heat treatment conditions and the maximum values of the structural parameters were obtained for the samples annealed at T = 175 degrees C. The particle size Z annealed at different temperature was ranged between 8.1-12.8nm, and the values of the distance distribution function P-max(Z) were obtained when Z = 4.0-6.8 nm. Using one dimension electron density correlation function (1D EDCF) method long period (L) and thickness of the lamellar (d(0)) were estimated and were found to increase with the increase of the degree of crystallinity.

Effect of heat treatment on the parameters of crystal structure and degree of crystallinity of poly(aryl-ether-ether-ketone)

The variations of unit cell parameters and crystallite size of nine PEEK samples treated at various temperatures have been studied by using Wide-Angle X-ray Diffraction (WAXD), The results indicate a decrease in unit cell parameter a,b and c but an increase in crystallite size L(hkl) With the increase beat treatment temperature. Based on X-ray scattering intensity theory and using the graphic multipeak resolution method, the formula of degree of crystallinity (W-c,W-X) for PEEK is derived. The results calculated are compatible with the density measurement and calorimetry.

The influence of heat treatment on polyamide-1010 structures of the aggregated state

The structural parameters of the aggregated state under various heat treatment for PA-1010 samples were computed by means of the desmearing intensity from SAYS, and by using the concept of the distance distribution function and 1D EDCF method. The results revealed that the maximum values of Q, I(0), P-max(Z), dtr, Rg and W-c,W-x were obtained nearby T=175 degreesC for PA-1010 samples with various annealing treatment. The higher degree of the crystallinity, the greater values of all the structural parameters of the aggregated state for PA-1010 samples were.

Eu:Y2O3 nano-phosphor prepared by novel energy-saving solution combustion method

A novel energy- and time-saving solution combustion method has been developed to prepare Eu:Y2O3 nano-crystal line phosphor. This novel method employs anhydrous ethanol as solvent and fuel. The prepared nano-crystals after heat-treatment own narrow size distribution, well dispersibility and sinterability, confirmed by XRD, TEM and FTIR. The emission spectra of nano-Eu:Y2O3 Samples show clear nano-size related phenomena. (c) 2007 Elsevier B.V. All rights reserved.

In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer During Surface Mechanical Attrition Treatment of Zirconium

The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC) layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 mu m thick and consisted of the intermetallic compound FeCr with an average grain size of 25 +/- 10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa.

Torsion fracture behavior of drawn pearlitic steel wires with different heat treatments

In this paper, torsion fracture behavior of drawn pearlitic steel wires with different heat treatments was investigated. Samples with different heat treatments was investigated. Samples with different heat treatment conditions were subjected to torsion and tensile tests. The shear strain along the torsion sample after fracture was measured. Fracture surface of wires was examined by Scanning Electron Microscopy. In addition, the method of Differential Scanning Calorimetry was used to characterize the thermodynamic process in the heat treatment. A numerical simulation via finite element method on temperature field evolution for the wire during heat treatment process was performed. The results show that both strain aging and recovery process occur in the material within the temperature range between room temperature and 435 degrees C. It was shown that the ductility measured by the number of twists drops at short heating times and recovers after further heating in the lead bath of 435 degrees C. On the other hand, the strenght of the wire increases at short heating times and decreases after further heating. The microstructure inhomogeneity due to short period of heat treatment, coupled with the gradient characteristics of shear deformation during torsion results in localized shear deformation of the wire. In this situation, shear cracks nucleate between lamella and the wire breaks with low number of twists.